Isothermal Annealing of Shocked Zirconium: Stability of the Two-phase $α/ω$ Microstructure
Authors:
Thaddeus Song En Low,
Donald W. Brown,
Brian A. Welk,
Ellen K. Cerreta,
Jon S. Okasinski,
Stephen R. Niezgoda
Abstract:
Under high pressure conditions, Zr undergoes a phase transformation from its ambient equilibrium hexagonal close packed $α$ phase to hexagonal $ω$ phase. Upon returning to ambient conditions, the material displays hysteretic behavior, retaining a significant amount of metastable $ω$ phase. This study presents an in-situ synchrotron X-ray diffraction analysis of Zr samples shock-loaded to compressi…
▽ More
Under high pressure conditions, Zr undergoes a phase transformation from its ambient equilibrium hexagonal close packed $α$ phase to hexagonal $ω$ phase. Upon returning to ambient conditions, the material displays hysteretic behavior, retaining a significant amount of metastable $ω$ phase. This study presents an in-situ synchrotron X-ray diffraction analysis of Zr samples shock-loaded to compressive peak stresses of 8 and 10.5 GPa and then annealed at temperatures of 443, 463, 483, and 503K. The evolution of the $α$ phase volume fraction was tracked quantitatively, and the dislocation densities in both phases were tracked qualitatively during annealing. Upon heating, the reverse transformation of $ω\toα$ does not go to completion, but instead reaches a new metastable state. The initial rate of transformation is faster at higher temperatures. Samples shock-loaded to higher peak pressures experienced higher initial transformation rates and more extensive transformation. Dislocation content in both phases was observed to be high in the as-shocked samples. Annealing the samples reduces the dislocation content in both phases, with the reduction being lesser in the $ω$ phase, leading to the postulation that transformation from $ω\toα$ is restricted by the pinning effect of dislocation structures within the $ω$ phase. Electron backscatter diffraction analysis affirmed that the expected $(0\;0\;0\;1)_α\parallel(1\;0\;\overline{1}\;1)_ω$ and $[1\;0\;\overline{1}\;0]_α\parallel[1\;1\;\overline{2}\;\overline{3}]_ω$ orientation relationship is maintained during nucleation and growth of the $α$ phase during the annealing. \end{abstract}
△ Less
Submitted 13 March, 2015; v1 submitted 12 November, 2014;
originally announced November 2014.
The effect of shock-wave profile on dynamic brittle failure
Authors:
J. Pablo Escobedo,
Eric N. Brown,
Carl P. Trujillo,
Ellen K. Cerreta,
George T. Gray III
Abstract:
The influence of shock-wave-loading profile on the failure processes in a brittle material has been investigated. Tungsten heavy alloy (WHA) specimens have been subjected to two shock-wave loading profiles with a similar peak stress of 15.4 GPa but different pulse durations. Contrary to the strong dependence of strength on wave profile observed in ductile metals, for WHA, specimens subjected to di…
▽ More
The influence of shock-wave-loading profile on the failure processes in a brittle material has been investigated. Tungsten heavy alloy (WHA) specimens have been subjected to two shock-wave loading profiles with a similar peak stress of 15.4 GPa but different pulse durations. Contrary to the strong dependence of strength on wave profile observed in ductile metals, for WHA, specimens subjected to different loading profiles exhibited similar spall strength and damage evolution morphology. Post-mortem examination of recovered samples revealed that dynamic failure for both loading profiles is dominated by brittle cleavage fracture, with additional energy dissipation through crack branching in the more brittle tungsten particles. Overall, in this brittle material all relevant damage kinetics and the spall strength are shown to be dominated by the shock peak stress, independent of pulse duration.
△ Less
Submitted 2 March, 2013;
originally announced March 2013.