Title:Isothermal Annealing of Shocked Zirconium: Stability of the Two-phase $α/ω$ Microstructure
View PDFAbstract:Under high pressure conditions, Zr undergoes a phase transformation from its ambient equilibrium hexagonal close packed $\alpha$ phase to hexagonal $\omega$ phase. Upon returning to ambient conditions, the material displays hysteretic behavior, retaining a significant amount of metastable $\omega$ phase. This study presents an in-situ synchrotron X-ray diffraction analysis of Zr samples shock-loaded to compressive peak stresses of 8 and 10.5 GPa and then annealed at temperatures of 443, 463, 483, and 503K. The evolution of the $\alpha$ phase volume fraction was tracked quantitatively, and the dislocation densities in both phases were tracked qualitatively during annealing. Upon heating, the reverse transformation of $\omega\to\alpha$ does not go to completion, but instead reaches a new metastable state. The initial rate of transformation is faster at higher temperatures. Samples shock-loaded to higher peak pressures experienced higher initial transformation rates and more extensive transformation. Dislocation content in both phases was observed to be high in the as-shocked samples. Annealing the samples reduces the dislocation content in both phases, with the reduction being lesser in the $\omega$ phase, leading to the postulation that transformation from $\omega\to\alpha$ is restricted by the pinning effect of dislocation structures within the $\omega$ phase. Electron backscatter diffraction analysis affirmed that the expected $(0\;0\;0\;1)_\alpha\parallel(1\;0\;\overline{1}\;1)_\omega$ and $[1\;0\;\overline{1}\;0]_\alpha\parallel[1\;1\;\overline{2}\;\overline{3}]_\omega$ orientation relationship is maintained during nucleation and growth of the $\alpha$ phase during the annealing. \end{abstract}
Submission history
From: Stephen Niezgoda [view email][v1] Wed, 12 Nov 2014 20:02:32 UTC (7,275 KB)
[v2] Fri, 13 Mar 2015 19:28:46 UTC (7,480 KB)
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.