A phonon-driven mechanism for an emergent and reversible chirality in crystals
Abstract
We demonstrate from first-principles calculations applied to the K3NiO2 crystal that a structural phase transition from an achiral to a chiral phase can be mediated by a soft zone boundary phonon and that it can be controlled by pressure and epitaxial strain. Calculations in the presence of an electric field hint at a rich physics dominated by the competition between chirality, polar, and achiral distortions. Induced by the interaction between chiral, polar, and axial phonons, an optimal parameter window for the permanent reversal of chirality is observed.
Periodic solids are chiral if their structures are described by space groups containing only proper symmetry operations that map, for example, a right-handed coordinate system onto a right-handed one, and not onto a left-handed one (“operations of the first kind”), [1] otherwise they are achiral [2]. In recent years there has been a growing interest in investigating certain chiral effects (both in real- and spin-space) in crystals such as the Chiral Induced Spin Selectivity (CISS) and spin spirals [3, 4], polar [5] and magnetic skyrmions [6, 7], topological states [8, 9] and chiral phonons [10, 11, 12] to mention a few. Noticeably, the crystallization process fixes the chirality and associated properties in most of these instances. While the concept of spontaneous symmetry breaking has so far been a fertile ground for important discoveries in condensed matter physics [13], with phenomena such as ferroelectricity, magnetism, or superconductivity, to date, it has not been applied to study the possibility of chirality spontaneously emerging from an achiral inorganic solid phase. Nevertheless, a chiral irreducible representation (IRREP) or order parameter can be formally defined [14], so that a group-subgroup relationship of the type achiral chiral between two phases is a physical possibility [15]. Despite the recent experimental reports about the spontaneous formation of gyrotropic domains observed in certain materials [16, 17, 18, 19, 20, 21, 22] below a critical temperature, many questions remain to be answered about their physical origin and properties. At the most fundamental level, we know little about which mechanisms stabilize a chiral order. Furthermore, we do not know if an enantiomeric excess mediated by external fields or other parameters in a nonpolar crystal and can be realized in the solid state.
In this work, we attempt to address these issues by exploring the achiral to chiral enantiomorphic phase transition observed in K3NiO2 (KNO) [23]. Using symmetry analysis and density functional theory (DFT) calculations (see the Supplementary file [24] for technical details and references [25, 26, 27, 28, 29, 30, 31, 32, 33] there included), we show that a soft zone boundary phonon mode triggers the emergence of chirality in this material with four well-like shapes in the energy landscape. We then explore how this structural chiral energy surface is enhanced or reduced by pressure or strain, and going further, we analyze how the chiral distortion can couple non-linearly with infrared (IR) and axial Raman active modes activated by an electric field. We prove that direct control over these polar and axial distortions is crucial to attain a permanent enantiomeric excess in a hysteresis-like manner and after said external field is removed. Our results can, therefore, be extrapolated to other chiral systems and allow us to explore strategies that may be adopted to optimize an enantiomeric excess in crystals via physical rather than possibly more invasive chemical procedures.
![Refer to caption](extracted/2405.12696v1/figure_1.png)
The high symmetry phase of KNO adopts an achiral tetragonal structure described by space group symmetry (no. 136). On cooling below 423 K, it undergoes a first-order phase transition to a low-temperature enantiomorphic phase of either 2 (no. 92) or 2 (no. 96) space groups [23]. Figure 1 shows the achiral high-temperature structure and illustrates the chiral distortion. Our symmetry analysis reveals that the 2/2 non-invariant distortion decomposes into symmetry adapted modes (SAMs) as , where Z4 and A1u are respectively the representation of the zone boundary () mode (that triggers the instability, as we will see below) and of an associated -point deformation which isotropy subgroup is 212. The mode involves the mostly in-plane motion of all the atom sites (although with larger K and O contributions in KNO) to form a spiral that preserves the 4-fold screw rotation of the parent phase. The pseudoscalar SAM describes a nonpolar K displacement along the direction. As a consequence of the O - K - O bond angle becomes a little smaller than 180∘ whilst the NiO units remain close to linear, consistent with experimental structure reports [23, 34, 35].
We perform our calculations with the collinear spins and the Hubbard-U correction (U = 4.2 eV) on Ni ions (required to open a band gap) [24]. We calculate the phonon spectrum in the phase and identify a doubly degenerate soft mode at the Z point with frequency = 1.35i THz and Z4 irreducible representation, consistently with the aforementioned SAM analysis. Despite the proposals in the past of different mechanisms for the emergence of chirality from an achiral reference - such as Jahn-Teller [36] as in CsCuClO3, or Peierls transitions [37] and orbital orders [38] as in the MgTi2O4 compound - in KNO the driving force thus appears to be solely of phononic nature. While other soft modes (at , X and M points [24]) are detected, the Z mode leads to the most stable low-symmetric configuration, as confirmed by the experiment. Since the Z4 soft boundary mode is doubly degenerate, we can build arbitrary linear combinations of eigenstates and calculate the energy as a function of their amplitude as illustrated in fig. 2. In particular, while the diagonal directions (a,a) and (a,-a) are associated with the realization of the P41212 and P43212 enantiomorphic domains, respectively, different settings lead to structures with different symmetries. In particular, the (a,0) and (0,b) directions produce degenerate orthorhombic phases with (no. 63) symmetry, which are achiral and optically inactive, while arbitrary (a,b) (with a0, b0 and ab) combinations generate systems with symmetry. The free energy F - which includes the chiral SAMs amplitudes - thus reads .
![Refer to caption](extracted/2405.12696v1/figure_2.png)
The electronic density of states (DOS) near the Fermi level (see Fig. 3(a)) is mainly populated by weakly hybridized O-/Ni- valence and K- conduction states with the ground state in a low-spin configuration. We find the density of states to be negligibly affected by the phase transition [24], which also agrees with the rather nominal calculated Born effective charges [24] and possibly suggests a short-range interaction mechanism for the emergence of chirality, in agreement with its zone boundary nature [39]. Concerning the behavior under mechanical perturbations, our results in Fig. 3(b)) show that even a tiny amount of hydrostatic pressure (above a value between 1.0 and 1.5 GPa) hardens the chiral mode and destroys the phase transition. This hardening under pressure may explain the observed decrease of the transition temperature upon replacing K with Rb or Cs, namely in Rb3NiO2 (Tc = 390 K) and Cs3NiO2 (achiral at room temperature) [34]. Conversely, an even more nuanced effect can be observed in the presence of strain. Indeed, the Z4 mode is respectively hardened or softened if the applied in-plane lattice deformation is tensile or compressive, as shown in Fig. 3(c). These results stem from a tension-compression asymmetry of the energy response in both the high and low symmetry phases. Nevertheless E() > E() always in the considered strain range (E is the energy, formula unit). Noticeably we find the instability, which is polar ( representation) and comes from short-range forces (due to the non-anomalous Born charges [24]), to persist under tensile strain, with E() = -2.3 meV upon = 3 %. While this value lies higher than the corresponding chiral state energy, it is possible that ferroelectricity may coexist with chirality at this or at a larger magnitude of . We leave this possibility open for future exploration.
![Refer to caption](extracted/2405.12696v1/figure_3.png)
Handedness flip**. Synthesized samples prepared by an azide-nitrate route resulted in racemic twinned crystals with approximately equal amounts of each enantiomorph (Flack parameter = 0.53) [23], illustrating the difficulty of preparing enantiomerically pure samples. At the same time, the free energy expansion in presence of both chiral of zone-centre pseudoscalar amplitudes gets modified as , which shows that the chiral order parameter can couple trilinearly to the A1u zone center mode. Therefore, any tensor containing the pseudoscalar irreducible representation can couple to the chiral Z4 mode as well through an invariant of the form and possibly induce control over the handedness of the system. One such tensor may be obtained by taking the product between vector () and axial () quantities. Indeed, the representation of this product can be decomposed into its irreducible components as (note that both the and products contain ), thus revealing a pseudoscalar component.
We will now construct a model - based on the interaction between chiral, polar, and axial modes - that breaks the / degeneracy, realizes field-induced enantioselectivity and potentially creates a permanent enantiomeric excess. Applying an electric field results in the activation of polar in-plane and out-of-plane modes (with and representations respectively). The axial Raman active modes with representation can be switched on as well via trilinear interaction, following a scheme analogous to that of orthorhombic ErFeO3 [40]. In the following we will explore how these field-induced distortions couple with the Z4 instability. Along with the always present biquadratic couplings, the following terms are allowed:
(1) |
and
(2) |
![Refer to caption](extracted/2405.12696v1/figure_4.png)
While is an enantioselective mechanism that requires the activation of the modes, breaks the (,0)/(0,) degeneracy of the achiral distortion. It is interesting to check if the energy barrier that separates the right- and left-handed domains can in practice be overcome by . This would lead to a permanent enantiomeric excess (i.e. surviving the 0 condition). To numerically test these ideas, we have extracted the relevant and modes via DFT structural relaxations in the presence of an electric field [41]. Importantly and since including collinear magnetism and the Hubbard-U interaction proves too numerically cumbersome in the presence of an electric field, we replace the K and Ni positions with Na and Au respectively to form a filled -shell paramagnetic Na3AuO2 (NAO) system with the same asymmetric unit of KNO and with a 2.1 eV DFT-computed band gap (without Hubbard correction). We note that although Na3AuO2 has been shown experimentally to adopt a slightly different structure [42], our "toy model" (see the SI [24] for the details of its construction) provides a helpful approximation of KNO. We apply an electric field E = 4.63x kV/m along the [1,1,1] direction to the high symmetry phase of Na3AuO2, perform a structural relaxation and extract the mixed polar-Raman distortion . Applied to the energy landscape, we observe that the overall effect of is to stabilize the (0,b) distortion while hardening all other orthogonal directions ((a,a) and (a,0)) as a consequence of the effect of [24]). Importantly, no energy difference between mirror-symmetric structures is detected. These features are also robust in the presence of an additional inducing compressive strain along the x-direction ( = 1 % [24]). The lack of right/left splitting can be explained if one realises that when [24]. Thus while the gyrotropic properties of KNO could be affected by the field, the absence of any or crossing prevents the realization of a permanent enantiomeric excess. Instead of exploiting the aforementioned nonlinear coupling in the presence of a constant bias along the [1,1,1] direction, we could use an axial external field - such as or [43, 44] (where defines an ionic displacement) - to switch the modes on. Assuming we can activate and phonons along the and directions respectively ( along the direction is set to zero), then 0 and the energy landscape may admit a sizable if the axial mode is large enough. For the sake of simplicity, we can assume to retain the polar-activated mode, although admitting a linear scaling of its amplitude to mimic an axial conjugate field. The effect of this strategy is shown in Fig. 4(a,b,c). Fixing the amplitude, a small polar mode as in Fig. 4(a) ( x 0.5) breaks the degeneracy between mirror equivalent enantiomers but cannot result in the crossing of the barrier. On the other hand, increasing the polar scaling amplitude to 1 shows in Fig. 4(b) that there exists an optimal window for the realization of a permanent enantiomeric excess, as measured by the difference between and concerning the distortion and reference. Finally, a larger amplitude (e.g. x 2) has the effect of stabilizing the polar state as reported in Fig. 4(c). Once the corresponding barrier has been crossed the system is expected to be remain scalemic (e.g. non racemic) in zero-field conditions. The overall handedness of the system can therefore be inverted, by flip** the sign of the electric field direction and with a magnitude consistent with fig. 4(b), consistently with a mechanism that is analogous to a hysteresis process.
Realizing a reversible and controllable enantiomeric excess is therefore interlaced with the direct activation of polar and axial modes. The absence of a true conjugate field for the chiral order indicates that any handedness-flip** interaction can activate achiral competing degrees of freedom as well (polar and in this case). While it is possible for a phonon state to be polar and chiral at the same time [21], so that the chirality and associated gyrotropic properties can be controlled by an electric field [45, 46] as in the case of the Pb5Ge3O11 compound [22], this requires the axial mode to be invariant [22] which is not the case for enantiomorphic crystals such as KNO. In practice realizing an enantiomeric excess (or "chirality poling") could be achieved via chiral phonon-light coupling. By symmetry, the tensor coupling with the Z soft eigenmode may take the form of the so-called "Lipkin zilch" [43], which defines the chirality density - - of a circularly polarised electromagnetic (EM) field. While no detailed study of an enantiomeric excess realized in the presence of a chiral phonon instability has been reported, the control over the phonon handedness in quartz has recently been obtained with the aid of circularly polarized X-rays[12].
Conclusions. In this work, we have explored the crystal chirality as a spontaneous order driven by a phonon instability with the K3NiO2 compound as a model. In particular, a high-symmetry phase is lowered by a degenerate point soft mode to a pair of enantiomorphic structures with and symmetries. We have shown that an epitaxial strain can be used to either soften or harden the unstable mode, while a moderate hydrostatic pressure stabilizes the achiral phase. Finally, we have explored the possible realization of an enantiomeric excess in KNO mediated by a coupling between chiral, polar, and axial orders. Our findings highlight the rich phenomenology triggered by a static electric field, including a competition between chirality and orthorhombic () phases and enantioselectivity. Nevertheless, we have numerically shown that the modes, when activated via polar-polar-Raman coupling [40], cannot efficiently lift the right/left degeneracy, so realizing a permanent handedness flip** could more likely be achieved by using an axial conjugate field (on top of an electric field) such as rotating EM fields or structural deformations. Additional theoretical and experimental analysis would be appealing to further understand our predictions on phonon-mediated chirality and the related new perspectives for enantioselectivity.
Acknowledgements
Computational resources have been provided by the Consortium des Équipements de Calcul Intensif (CÉCI), funded by the Fonds de la Recherche Scientifique (F.R.S.-FNRS) under Grant No. 2.5020.11. MF & EB acknowledges FNRS for support and the PDR project CHRYSALID No.40003544. Work at West Virginia University was supported by the U.S. Department of Energy (DOE), Office of Science, Basic Energy Sciences (BES) under Award DE-SC0021375. This work used Bridges2 and Expanse at the Pittsburgh Supercomputer (Bridges2) and the San Diego Supercomputer Center (Expanse) through allocation DMR140031 from the Advanced Cyberinfrastructure Coordination Ecosystem: Services & Support (ACCESS) program, which National Science Foundation supports grants 2138259, 2138286, 2138307, 2137603, and 2138296.
References
- Nespolo et al. [2018] M. Nespolo, M. I. Aroyo, and B. Souvignier, Crystallographic shelves: space-group hierarchy explained, Journal of Applied Crystallography 51, 1481 (2018).
- Flack [2003] H. Flack, Chiral and achiral crystal structures, Helvetica Chimica Acta 86, 905 (2003).
- Yang et al. [2021] S.-H. Yang, R. Naaman, Y. Paltiel, and S. S. P. Parkin, Chiral spintronics, Nature Reviews Physics 3, 328 (2021).
- Evers et al. [2022] F. Evers, A. Aharony, N. Bar-Gill, O. Entin-Wohlman, P. Hedegård, O. Hod, P. Jelinek, G. Kamieniarz, M. Lemeshko, K. Michaeli, V. Mujica, R. Naaman, Y. Paltiel, S. Refaely-Abramson, O. Tal, J. Thijssen, M. Thoss, J. M. van Ruitenbeek, L. Venkataraman, D. H. Waldeck, B. Yan, and L. Kronik, Theory of chirality induced spin selectivity: Progress and challenges, Advanced Materials 34, 2106629 (2022).
- Junquera et al. [2023] J. Junquera, Y. Nahas, S. Prokhorenko, L. Bellaiche, J. Íñiguez, D. G. Schlom, L.-Q. Chen, S. Salahuddin, D. A. Muller, L. W. Martin, and R. Ramesh, Topological phases in polar oxide nanostructures, Rev. Mod. Phys. 95, 025001 (2023).
- Bogdanov and Rößler [2001] A. N. Bogdanov and U. K. Rößler, Chiral symmetry breaking in magnetic thin films and multilayers, Phys. Rev. Lett. 87, 037203 (2001).
- Fert et al. [2017] A. Fert, N. Reyren, and V. Cros, Magnetic skyrmions: advances in physics and potential applications, Nature Reviews Materials 2, 17031 (2017).
- Chang et al. [2018] G. Chang, B. J. Wieder, F. Schindler, D. S. Sanchez, I. Belopolski, S.-M. Huang, B. Singh, D. Wu, T.-R. Chang, T. Neupert, S.-Y. Xu, H. Lin, and M. Z. Hasan, Topological quantum properties of chiral crystals, Nature Materials 17, 978 (2018).
- Schröter et al. [2020] N. B. M. Schröter, S. Stolz, K. Manna, F. de Juan, M. G. Vergniory, J. A. Krieger, D. Pei, T. Schmitt, P. Dudin, T. K. Kim, C. Cacho, B. Bradlyn, H. Borrmann, M. Schmidt, R. Widmer, V. N. Strocov, and C. Felser, Observation and control of maximal chern numbers in a chiral topological semimetal, Science 369, 179 (2020).
- Zhang and Niu [2015] L. Zhang and Q. Niu, Chiral phonons at high-symmetry points in monolayer hexagonal lattices, Phys. Rev. Lett. 115, 115502 (2015).
- Ishito et al. [2023] K. Ishito, H. Mao, Y. Kousaka, Y. Togawa, S. Iwasaki, T. Zhang, S. Murakami, J.-i. Kishine, and T. Satoh, Truly chiral phonons in -hgs, Nature Physics 19, 35 (2023).
- Ueda et al. [2023] H. Ueda, M. García-Fernández, S. Agrestini, C. P. Romao, J. van den Brink, N. A. Spaldin, K.-J. Zhou, and U. Staub, Chiral phonons in quartz probed by x-rays, Nature 618, 946 (2023).
- Beekman et al. [2019] A. Beekman, L. Rademaker, and J. van Wezel, An introduction to spontaneous symmetry breaking, SciPost Physics Lecture Notes , 011 (2019).
- Hlinka [2014] J. Hlinka, Eight types of symmetrically distinct vectorlike physical quantities, Phys. Rev. Lett. 113, 165502 (2014).
- Erb and Hlinka [2018] K. C. Erb and J. Hlinka, Symmetry guide to chiroaxial transitions, Phase Transitions 91, 953 (2018).
- Hayashida et al. [2021a] T. Hayashida, K. Kimura, D. Urushihara, T. Asaka, and T. Kimura, Observation of ferrochiral transition induced by an antiferroaxial ordering of antipolar structural units in Ba(TiO)Cu4(PO4)4, J. Am. Chem. Soc. 143, 3638 (2021a).
- Kimura et al. [2016] K. Kimura, M. Sera, and T. Kimura, A2+ cation control of chiral domain formation in A(TiO)Cu4(PO4)4 (A = Ba, Sr), Inorganic Chemistry 55, 1002 (2016).
- Huang et al. [2020] P. Huang, Z. Xia, X. Gao, J. M. Rondinelli, X. Zhang, H. Zhang, K. R. Poeppelmeier, and A. Zunger, Ferri-chiral compounds with potentially switchable dresselhaus spin splitting, Phys. Rev. B 102, 235127 (2020).
- Hayashida et al. [2021b] T. Hayashida, K. Kimura, D. Urushihara, T. Asaka, and T. Kimura, Observation of ferrochiral transition induced by an antiferroaxial ordering of antipolar structural units in ba(tio)cu4(po4)4, Journal of the American Chemical Society 143, 3638 (2021b).
- Hayashida et al. [2022] T. Hayashida, K. Kimura, and T. Kimura, Switching crystallographic chirality in ba(tio)cu4(po4)4 by laser irradiation, The Journal of Physical Chemistry Letters 13, 3857 (2022).
- Fava et al. [2024] M. Fava, W. Lafargue-Dit-Hauret, A. H. Romero, and E. Bousquet, Ferroelectricity and chirality in the crystal, Phys. Rev. B 109, 024113 (2024).
- Fava et al. [2023] M. Fava, W. Lafargue-Dit-Hauret, A. H. Romero, and E. Bousquet, Ferroelectricity and chirality in the pb5ge3o11 crystal (2023).
- Đuriš et al. [2012] K. Đuriš, U. Müller, and M. Jansen, K3nio2 revisited, phase transition and crystal structure refinement, Zeitschrift für anorganische und allgemeine Chemie 638, 737 (2012).
- sup [2023] Supplemental materials, Supplementalmaterials,URL_will_be_inserted_by_publisher (2023).
- Kresse and Joubert [1999] G. Kresse and D. Joubert, From ultrasoft pseudopotentials to the projector augmented-wave method, Phys. Rev. B 59, 1758 (1999).
- Perdew et al. [1996] J. P. Perdew, K. Burke, and M. Ernzerhof, Generalized gradient approximation made simple, Phys. Rev. Lett. 77, 3865 (1996).
- Dudarev et al. [1998] S. L. Dudarev, G. A. Botton, S. Y. Savrasov, C. J. Humphreys, and A. P. Sutton, Electron-energy-loss spectra and the structural stability of nickel oxide: An lsda+u study, Phys. Rev. B 57, 1505 (1998).
- Cococcioni and de Gironcoli [2005] M. Cococcioni and S. de Gironcoli, Linear response approach to the calculation of the effective interaction parameters in the method, Phys. Rev. B 71, 035105 (2005).
- Stokes et al. [2006] H. T. Stokes, D. M. Hatch, B. J. Campbell, and D. E. Tanner, Isodisplace: a web-based tool for exploring structural distortions, Journal of Applied Crystallography 39, 607 (2006), https://onlinelibrary.wiley.com/doi/pdf/10.1107/S0021889806014075 .
- Orobengoa et al. [2009] D. Orobengoa, C. Capillas, M. I. Aroyo, and J. M. Perez-Mato, AMPLIMODES: symmetry-mode analysis on the Bilbao Crystallographic Server, J. Appl. Crystallogr. 42, 820 (2009).
- Gonze et al. [2020] X. Gonze, B. Amadon, G. Antonius, F. Arnardi, L. Baguet, J.-M. Beuken, J. Bieder, F. Bottin, J. Bouchet, E. Bousquet, N. Brouwer, F. Bruneval, G. Brunin, T. Cavignac, J.-B. Charraud, W. Chen, M. Côté, S. Cottenier, J. Denier, G. Geneste, P. Ghosez, M. Giantomassi, Y. Gillet, O. Gingras, D. R. Hamann, G. Hautier, X. He, N. Helbig, N. Holzwarth, Y. Jia, F. Jollet, W. Lafargue-Dit-Hauret, K. Lejaeghere, M. A. Marques, A. Martin, C. Martins, H. P. Miranda, F. Naccarato, K. Persson, G. Petretto, V. Planes, Y. Pouillon, S. Prokhorenko, F. Ricci, G.-M. Rignanese, A. H. Romero, M. M. Schmitt, M. Torrent, M. J. van Setten, B. Van Troeye, M. J. Verstraete, G. Zérah, and J. W. Zwanziger, The abinitproject: Impact, environment and recent developments, Computer Physics Communications 248, 107042 (2020).
- Van Setten et al. [2018] M. Van Setten, M. Giantomassi, E. Bousquet, M. J. Verstraete, D. R. Hamann, X. Gonze, and G.-M. Rignanese, The pseudodojo: Training and grading a 85 element optimized norm-conserving pseudopotential table, Comput. Phys. Commun. 226, 39 (2018).
- Wagner and Hoppe [1987a] G. Wagner and R. Hoppe, Oxydation intermetallischer phasen: Na3[auo2] aus naau und na2o2, Zeitschrift fÃŒr anorganische und allgemeine Chemie 549, 26 (1987a).
- Duris¡ et al. [2012] K. Duris¡, O. V. Magdysyuk, and M. Jansen, Syntheses, structures and magnetic properties of the alkali oxonickelates(i) a3nio2 (a = k, rb, cs), Solid State Sciences 14, 1399 (2012).
- Moeller et al. [1995] A. Moeller, M. A. Hitchman, E. Krausz, and R. Hoppe, Synthesis, crystal structure and physical properties of kna2[nio2] and k3[nio2] containing "linear" [nio2]3- anions, Inorganic Chemistry 34, 2684 (1995).
- Hirotsu [1977] S. Hirotsu, Jahn-teller induced phase transition in CsCuCl3: structural phase transition with helical atomic displacements, J. Phys. C: Solid State Phys. 10, 967 (1977).
- Khomskii and Mizokawa [2005] D. I. Khomskii and T. Mizokawa, Orbitally induced peierls state in spinels, Phys. Rev. Lett. 94, 156402 (2005).
- Di Matteo et al. [2004] S. Di Matteo, G. Jackeli, C. Lacroix, and N. B. Perkins, Valence-bond crystal in a pyrochlore antiferromagnet with orbital degeneracy, Phys. Rev. Lett. 93, 077208 (2004).
- Samara et al. [1975] G. A. Samara, T. Sakudo, and K. Yoshimitsu, Important generalization concerning the role of competing forces in displacive phase transitions, Phys. Rev. Lett. 35, 1767 (1975).
- Juraschek et al. [2017] D. M. Juraschek, M. Fechner, and N. A. Spaldin, Ultrafast structure switching through nonlinear phononics, Phys. Rev. Lett. 118, 054101 (2017).
- Souza et al. [2002] I. Souza, J. Íñiguez, and D. Vanderbilt, First-principles approach to insulators in finite electric fields, Phys. Rev. Lett. 89, 117602 (2002).
- Wagner and Hoppe [1987b] G. Wagner and R. Hoppe, Oxydation intermetallischer phasen: Na3[auo2] aus naau und na2o2, Zeitschrift für anorganische und allgemeine Chemie 549, 26 (1987b), https://onlinelibrary.wiley.com/doi/pdf/10.1002/zaac.19875490604 .
- Tang and Cohen [2010] Y. Tang and A. E. Cohen, Optical chirality and its interaction with matter, Phys. Rev. Lett. 104, 163901 (2010).
- Oiwa and Kusunose [2022] R. Oiwa and H. Kusunose, Rotation, electric-field responses, and absolute enantioselection in chiral crystals, Phys. Rev. Lett. 129, 116401 (2022).
- Iwasaki et al. [1971] H. Iwasaki, K. Sugii, T. Yamada, and N. Niizeki, 5pbo [center-dot] 3geo[sub 2] crystal; a new ferroelectric, Appl. Phys. Lett. 18, 444 (1971).
- Iwasaki et al. [1972] H. Iwasaki, S. Miyazawa, H. Koizumi, K. Sugii, and N. Niizeki, Ferroelectric and optical properties of pb5ge3o11 and its isomorphous compound pb5ge2sio11, J. Appl. Phys. 43, 4907 (1972).