Condensed Matter > Materials Science
[Submitted on 14 Mar 2022]
Title:Revisiting stress-corrosion cracking and hydrogen embrittlement in 7xxx-Al alloys at the near-atomic-scale
View PDFAbstract:Hydrogen embrittlement (HE) affects all major high-strength structural materials and as such is a major impediment to lightweighting e.g. vehicles and help reduce carbon-emissions and reach net-zero. The high-strength 7xxx series aluminium alloys can fulfil the need for light, high strength materials, and are already extensively used in aerospace for weight reduction purposes. However, depending on the thermomechanical and loading state, these alloys can be sensitive to stress-corrosion cracking (SCC) through anodic dissolution and hydrogen embrittlement. Here, we study at the near-atomic-scale the intra- and inter-granular microstructure ahead and in the wake of a propagating SCC crack. Moving away from model cases not strictly relevant to application, we performed an industry-standard test on an engineering Al-7XXX alloy. H is found segregated to planar arrays of dislocations and to grain boundaries that we can associate to the combined effects of hydrogen-enhanced localized plasticity (HELP) and hydrogen-enhanced decohesion (HEDE) mechanisms. We report on a Mg-rich H-rich amorphous oxide on the corroded crack surface and evidence of Mg-related diffusional processes leading to dissolution of the strengthening eta-phase precipitates ahead of the crack. We show ingress of up to 1 at% O, i.e. well above the solubility limit of O in Al, near the oxide-metal interface, while no increased level of H is found in the matrix. We provide an array of discussion points relative to the interplay of structural defects, transport of solutes, thereby changing the resistance against crack propagation, which have been overlooked across the SCC literature and prevent accurate service life predictions.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.