Title:Debye temperature of nanocrystalline Fe-Cr alloys obtained by mechanical alloying
View PDFAbstract:A series on nanocrystalline Fe100-xCrx alloys prepared by mechanical alloying was investigated with X-ray diffraction (XRD), scanning electron microscopy (SEM) and Mössbauer spectroscopy (MS) techniques. XRD and SEM were used to structurally characterize the samples whereas MS permitted phase analysis as well as determination of the Debye temperature, Theta_D. Concerning the latter, an enhancement relative to bulk Theta_D-values was revealed in the range of ca. 40 < x <50. In a sample of Fe55.5Cr44.5 two phases were detected viz. (1) crystalline and magnetic with Theta_D=572(56) K and (2) amorphous and paramagnetic with Theta_D=405(26) K.
Submission history
From: Stanislaw Dubiel [view email][v1] Sat, 23 May 2015 20:03:36 UTC (1,209 KB)
Current browse context:
cond-mat.str-el
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.