How much gallium do we need for a p-type Cu(In,Ga)Se2?
Authors:
Omar Ramírez,
Evandro Martin Lanzoni,
Ricardo G. Poeira,
Thomas P. Weiss,
Renaud Leturcq,
Alex Redinger,
Susanne Siebentritt
Abstract:
Do** in the chalcopyrite Cu(In,Ga)Se2 is determined by intrinsic point defects. In the ternary CuInSe2, both N-type and P-type conductivity can be obtained depending on the growth conditions and stoichiometry: N-type is obtained when grown Cu-poor, Se-poor and alkali-free. CuGaSe2, on the other hand, is found to be always a P-type semiconductor that seems to resist all kinds of N-type do** no…
▽ More
Do** in the chalcopyrite Cu(In,Ga)Se2 is determined by intrinsic point defects. In the ternary CuInSe2, both N-type and P-type conductivity can be obtained depending on the growth conditions and stoichiometry: N-type is obtained when grown Cu-poor, Se-poor and alkali-free. CuGaSe2, on the other hand, is found to be always a P-type semiconductor that seems to resist all kinds of N-type do** no matter whether it comes from native defects or extrinsic impurities. In this contribution, we study the N-to-P transition in Cu-poor Cu(In,Ga)Se2 single crystals in dependence of the gallium content. Our results show that Cu(In,Ga)Se2 can still be grown as an N-type semiconductor until the gallium content reaches the critical concentration of 15-19%, where the N-to-P transition occurs. Furthermore, trends in the Seebeck coefficient and activation energies extracted from temperature-dependent conductivity measurements, demonstrate that the carrier concentration drops by around two orders of magnitude near the transition concentration. Our proposed model explains the N-to-P transition based on the differences in formation energies of donor and acceptor defects caused by the addition of gallium.
△ Less
Submitted 27 April, 2022;
originally announced April 2022.
The perovskite/transport layer interfaces dominate non-radiative recombination in efficient perovskite solar cells
Authors:
Martin Stolterfoht,
Pietro Caprioglio,
Christian M. Wolff,
José A. Márquez,
Joleik Nordmann,
Shanshan Zhang,
Daniel Rothhardt,
Ulrich Hörmann,
Alex Redinger,
Lukas Kegelmann,
Steve Albrecht,
Thomas Kirchartz,
Michael Saliba,
Thomas Unold,
Dieter Neher
Abstract:
Charge transport layers (CTLs) are key components of diffusion controlled perovskite solar cells, however, they can induce additional non-radiative recombination pathways which limit the open circuit voltage (V_OC) of the cell. In order to realize the full thermodynamic potential of the perovskite absorber, both the electron and hole transport layer (ETL/HTL) need to be as selective as possible. B…
▽ More
Charge transport layers (CTLs) are key components of diffusion controlled perovskite solar cells, however, they can induce additional non-radiative recombination pathways which limit the open circuit voltage (V_OC) of the cell. In order to realize the full thermodynamic potential of the perovskite absorber, both the electron and hole transport layer (ETL/HTL) need to be as selective as possible. By measuring the quasi-Fermi level splitting (QFLS) of perovskite/CTL heterojunctions, we quantify the non-radiative interfacial recombination current for a wide range of commonly used CTLs, including various hole-transporting polymers, spiro-OMeTAD, metal oxides and fullerenes. We find that all studied CTLs limit the V_OC by inducing an additional non-radiative recombination current that is significantly larger than the loss in the neat perovskite and that the least-selective interface sets the upper limit for the V_OC of the device. The results also show that the V_OC equals the internal QFLS in the absorber layer of (pin, nip) cells with selective CTLs and power conversion efficiencies of up to 21.4%. However, in case of less selective CTLs, the V_OC is substantially lower than the QFLS which indicates additional losses at the contacts and/or interfaces. The findings are corroborated by rigorous device simulations which outline several important considerations to maximize the V_OC. This work shows that the real challenge to supress non-radiative recombination losses in perovskite cells on their way to the radiative limit lies in the suppression of carrier recombination at the perovskite/CTL interfaces.
△ Less
Submitted 22 October, 2018; v1 submitted 2 October, 2018;
originally announced October 2018.