Planar Ultrananocrystalline Diamond Field Emitter in Accelerator RF Electron Injector: Performance Metrics
Authors:
Sergey V. Baryshev,
Sergey Antipov,
Jiahang Shao,
Chunguang **g,
Kenneth J. PĂ©rez Quintero,
Jiaqi Qui,
Wanming Liu,
Wei Gai,
Alexei D. Kanareykin,
Anirudha V. Sumant
Abstract:
A case performance study of a planar field emission cathode (FEC) based on nitrogen-incorporated ultrananocrystalline diamond, (N)UNCD, was carried out in an RF 1.3 GHz electron gun. The FEC was a 100 nm (N)UNCD film grown on a 20 mm diameter stainless steel disk with a Mo buffer layer. At surface gradients 45-65 MV/m, peak currents of 1-80 mA (equivalent to 0.3-25 mA/cm$^2$) were achieved. Imagin…
▽ More
A case performance study of a planar field emission cathode (FEC) based on nitrogen-incorporated ultrananocrystalline diamond, (N)UNCD, was carried out in an RF 1.3 GHz electron gun. The FEC was a 100 nm (N)UNCD film grown on a 20 mm diameter stainless steel disk with a Mo buffer layer. At surface gradients 45-65 MV/m, peak currents of 1-80 mA (equivalent to 0.3-25 mA/cm$^2$) were achieved. Imaging with two YAG screens confirmed emission from the (N)UNCD surface with (1) the beam emittance of 1.5 mm$\times$mrad/mm-rms, and (2) longitudinal FWHM and rms energy spread of 0.7% and 11% at an electron energy of 2 MeV. Current stability was tested over the course of 36$\times$10$^3$ RF pulses (equivalent to 288$\times$10$^6$ GHz oscillations).
△ Less
Submitted 21 October, 2014;
originally announced October 2014.