Microstructure evolution and characteristics of laser-clad lightweight refractory NbxMo$_{0.5}$Ti$_{1.5}$Ta$_{0.2}$Cr high-entropy alloy
Authors:
C. Y. Cui,
H. H. Xu,
J. Yang,
X. G. Cui
Abstract:
Lightweight refractory high-entropy alloy coatings (RHEAcs) of NbxMo$_{0.5}$Ti$_{1.5}$Ta$_{0.2}$Cr (where $x=$ 1, 1.3, 1.5, and 2) were fabricated on the surface of 316L stainless steel using laser cladding (LC) technology. A comprehensive study was conducted to elucidate the effect of Nb content on the microstructure, microhardness and wear resistance of NbxMo$_{0.5}$Ti$_{1.5}$Ta$_{0.2}$Cr RHEAcs…
▽ More
Lightweight refractory high-entropy alloy coatings (RHEAcs) of NbxMo$_{0.5}$Ti$_{1.5}$Ta$_{0.2}$Cr (where $x=$ 1, 1.3, 1.5, and 2) were fabricated on the surface of 316L stainless steel using laser cladding (LC) technology. A comprehensive study was conducted to elucidate the effect of Nb content on the microstructure, microhardness and wear resistance of NbxMo$_{0.5}$Ti$_{1.5}$Ta$_{0.2}$Cr RHEAcs before and after annealing at 900 for 10 h. The results show that the grains are gradually refined with the increase of Nb content. The coating consists mainly of a body-centered cubic (BCC) solid solution, C15-Laves phase, and a small amount of hexagonal close-packed (HCP) solid solution containing Ti. The microhardness of RHEAcs is significantly higher compared to the base material. Notably, at Nb1.3, due to the influence of lattice dislocations, the microhardness reaches a peak of 1066.5 HV, which is about 7.11 times higher than that of the base material. On the contrary, at Nb$_2$, the microhardness is at its lowest point, averaging 709.31 HV, but 4.72 times that of the base material. After annealing, an increase in microhardness is observed at all Nb concentrations, up to 31.2% at Nb$_2$. Before annealing, the wear resistance of RHEAcs was slightly better than that of 316L stainless steel at different Nb contents. However, after annealing, the coefficient of friction (COF) and wear rate of the coatings are lower than those of annealed 316L stainless steel, highlighting their excellent wear resistance. It is noteworthy that the loss of wear properties after annealing at Nb1 is at a minimum, obtaining the most balanced wear resistance before and after annealing. The enhanced wear resistance after annealing can be attributed to the presence of ultra-fine grain oxide friction layers, mainly composed of TiO2 and Ta2O5 . The main mode of wear is oxidative wear, with a small amount of wear from abrasive wear.
△ Less
Submitted 22 October, 2023;
originally announced October 2023.