Novel materials for next-generation accelerator target facilities
Authors:
K. Ammigan,
G. Arora,
S. Bidhar,
A. Burleigh,
F. Pellemoine,
A. Couet,
N. Crnkovich,
I. Szlufarska
Abstract:
As beam power continues to increase in next-generation accelerator facilities, high-power target systems face crucial challenges. Components like beam windows and particle-production targets must endure significantly higher levels of particle fluence. The primary beam's energy deposition causes rapid heating (thermal shock) and induces microstructural changes (radiation damage) within the target m…
▽ More
As beam power continues to increase in next-generation accelerator facilities, high-power target systems face crucial challenges. Components like beam windows and particle-production targets must endure significantly higher levels of particle fluence. The primary beam's energy deposition causes rapid heating (thermal shock) and induces microstructural changes (radiation damage) within the target material. These effects ultimately deteriorate the components' properties and lifespan. With conventional materials already stretched to their limits, we are exploring novel materials including High-Entropy Alloys and Electrospun Nanofibers that offer a fresh approach to enhancing tolerance against thermal shock and radiation damage. Following an introduction to the challenges facing high-power target systems, we will give an overview of the promising advancements we have made so far in customizing the compositions and microstructures of these pioneering materials. Our focus is on optimizing their in-beam thermomechanical and physics performance. Additionally, we will outline our ongoing plans for in-beam irradiation experiments and advanced material characterizations. The primary goal of this research is to push the frontiers of target materials, thereby enabling future multi-MW facilities that will benefit various programs in high-energy physics and beyond.
△ Less
Submitted 28 May, 2024;
originally announced May 2024.
-
Novel Materials and Concepts for Next-Generation High Power Target Applications
Authors:
Kavin Ammigan,
Sujit Bidhar,
Frederique Pellemoine,
Vitaly Pronskikh,
David Pushka,
Katsuya Yonehara,
Robert Zwaska,
Adrien Couet,
Michael Moorehead,
Taku Ishida,
Shunsuke Makimura,
Christopher Densham,
Michael Fitton,
Eric Harvey-Fishenden,
Tristan Davenne,
David Jenkins,
Peter Loveridge,
Joe O'Dell,
Chris Rogers,
Dan Wilcox,
Marco Calviani,
Simone Gilardoni,
Francois-Xavier Nuiry,
Antonio Perillo-Marcone,
Nathan Bultman
, et al. (14 additional authors not shown)
Abstract:
Novel beam-intercepting materials and targetry concepts are essential to improve the performance, reliability and operation lifetimes of next generation multi-megawatt (multi-MW) accelerator target facilities. The beam-intercepting materials and components must sustain an order-of-magnitude increase in particle beam intensities and are beyond the current state-of-the-art. With conventional materia…
▽ More
Novel beam-intercepting materials and targetry concepts are essential to improve the performance, reliability and operation lifetimes of next generation multi-megawatt (multi-MW) accelerator target facilities. The beam-intercepting materials and components must sustain an order-of-magnitude increase in particle beam intensities and are beyond the current state-of-the-art. With conventional materials already limiting the scope of experiments, it is crucial to investigate novel target materials, technologies and concepts that will satisfy the requirements and maximize the physics benefits of future energy and intensity frontier experiments. This paper provides an overview of the related targetry R&D required over the next 10 years to support and enable future high-power accelerator target facilities.
△ Less
Submitted 15 March, 2022;
originally announced March 2022.
-
Irradiation Facilities and Irradiation Methods for High Power Target
Authors:
F. Pellemoine,
C. Barbier,
Y. Sun,
K. Ammigan,
S. Bidhar,
B. Zwaska,
D. McClintock,
S. Taller,
D. Winder,
C. S. Cutler,
D. Kim,
Y. Chiu,
M. Freer,
C. Wheldon,
A. Gottberg,
F. Boix Pamies,
M. Calviani,
N. Charitonidis,
R. Garcia Alia,
F. Ravotti,
S. Danzeca,
A. P. Bernardes,
N. Moncoffre,
S. Meigo,
T. Ishida
, et al. (16 additional authors not shown)
Abstract:
High Power Target systems are key elements in future neutrino and other rare particle production in accelerators. These systems transform an intense source of protons into secondary particles of interest to enable new scientific discoveries. As beam intensity and energies increase, target systems face significant challenges. Radiation damages and thermal shocks in target materials were identified…
▽ More
High Power Target systems are key elements in future neutrino and other rare particle production in accelerators. These systems transform an intense source of protons into secondary particles of interest to enable new scientific discoveries. As beam intensity and energies increase, target systems face significant challenges. Radiation damages and thermal shocks in target materials were identified as the leading cross-cutting challenges of high-power target facilities. Target material R&D to address these challenges are essential to enable and ensure reliable operation of future-generation accelerators. Irradiation facilities and alternative methods are critical to provide a full support of material R&D and better address these critical challenges.
△ Less
Submitted 14 December, 2022; v1 submitted 15 March, 2022;
originally announced March 2022.
-
Tensile behavior of dual-phase titanium alloys under high-intensity proton beam exposure: radiation-induced omega phase transformation in Ti-6Al-4V
Authors:
Taku Ishida,
Eiichi Wakai,
Shunsuke Makimura,
Andrew M. Casella,
Danny J. Edwards,
Ramprashad Prabhakaran,
David J. Senor,
Kavin Ammigan,
Sujit Bidhar,
Patrick G. Hurh,
Frederique Pellemoine,
Christopher J. Densham,
Michael D. Fitton,
Joe M. Bennett,
Dohyun Kim,
Nikolaos Simos,
Masayuki Hagiwara,
Naritoshi Kawamura,
Shin-ichiro Meigo,
Katsuya Yonehara
Abstract:
A high-intensity proton beam exposure with 181 MeV energy has been conducted at Brookhaven Linac Isotope Producer facility on various material specimens for accelerator targetry applications, including titanium alloys as a beam window material. The radiation damage level of the analyzed capsule was 0.25 dpa at beam center region with an irradiation temperature around 120 degree C. Tensile tests sh…
▽ More
A high-intensity proton beam exposure with 181 MeV energy has been conducted at Brookhaven Linac Isotope Producer facility on various material specimens for accelerator targetry applications, including titanium alloys as a beam window material. The radiation damage level of the analyzed capsule was 0.25 dpa at beam center region with an irradiation temperature around 120 degree C. Tensile tests showed increased hardness and a large decrease in ductility for the dual alpha+beta-phase Ti-6Al-4V Grade-5 and Grade-23 extra low interstitial alloys, with the near alpha-phase Ti-3Al-2.5V Grade-9 alloy still exhibiting uniform elongation of a few % after irradiation. Transmission Electron Microscope analyses on Ti-6Al-4V indicated clear evidence of a high-density of defect clusters with size less than 2 nm in each alpha-phase grain. The beta-phase grains did not contain any visible defects such as loops or black dots, while the diffraction patterns clearly indicated omega-phase precipitation in an advanced formation stage. The radiation-induced omega-phase transformation in the beta-phase could lead to greater loss of ductility in Ti-6Al-4V alloys in comparison with Ti-3Al-2.5V alloy with less beta-phase.
△ Less
Submitted 30 July, 2020; v1 submitted 24 April, 2020;
originally announced April 2020.
-
Radiation Damage Studies on Titanium Alloys as High Intensity Proton Accelerator Beam Window Materials
Authors:
Taku Ishida,
Eiichi Wakai,
Shunsuke Makimura,
Patrick G. Hurh,
Kavin Ammigan,
Andrew M. Casella,
Danny J. Edwards,
David J. Senor,
Christopher J. Densham,
Michael Fitton,
Joe Bennett,
Dohyun Kim,
Nikolaos Simos,
Marco Calviani,
Claudio Torregrosa Martin
Abstract:
A high-strength dual alpha+beta phase titanium alloy Ti-6Al-4V is utilized as a material for beam windows in several accelerator target facilities. However, relatively little is known about how material properties of this alloy are affected by high-intensity proton beam irradiation. With plans to upgrade neutrino facilities at J-PARC and Fermilab to over 1 MW beam power, the radiation damage in th…
▽ More
A high-strength dual alpha+beta phase titanium alloy Ti-6Al-4V is utilized as a material for beam windows in several accelerator target facilities. However, relatively little is known about how material properties of this alloy are affected by high-intensity proton beam irradiation. With plans to upgrade neutrino facilities at J-PARC and Fermilab to over 1 MW beam power, the radiation damage in the window material will reach a few displacements per atom (dpa) per year, significantly above the ~0.3 dpa level of existing data. The RaDIATE collaboration has conducted a high intensity proton beam irradiation of various target and window material specimens at BLIP facility, including a variety of titanium alloys. Post-Irradiation Examination of the specimens in the 1st capsule, irradiated at up to 0.25 dpa, is in progress. Tensile tests in a hot cell at PNNL exhibited a clear signature of radiation hardening and loss of ductility for Ti-6Al-4V, while Ti-3Al-2.5V, with less beta phase, exhibited less severe hardening. Microstructural investigations will follow to study the cause of the difference in tensile behavior between these alloys. High-cycle fatigue (HCF) performance is critical to the lifetime estimation of beam windows exposed to a periodic thermal stress from a pulsed proton beam. The 1st HCF data on irradiated titanium alloys are to be obtained by a conventional bend fatigue test at Fermilab and by an ultrasonic mesoscale fatigue test at Culham Laboratory. Specimens in the 2nd capsule, irradiated at up to ~1 dpa, cover typical titanium alloy grades, including possible radiation-resistant candidates. These systematic studies on the effects of radiation damage of titanium alloys are intended to enable us to predict realistic lifetimes of current beam windows made of Ti-6Al-4V and to extend the lifetime by choosing a more radiation and thermal shock tolerant alloy.
△ Less
Submitted 22 November, 2019;
originally announced November 2019.
-
Status and update of the RaDIATE Collaboration R&D Program
Authors:
K. Ammigan,
P. Hurh
Abstract:
The Radiation Damage In Accelerator Target Environments (RaDIATE) collaboration was founded in 2012 and currently consists of over 50 participants and 11 institutions globally. Due to the increasing power of future proton accelerator sources in target facilities, there is a critical need to further understand the physical and thermo-mechanical radiation response of target facility materials. Thus,…
▽ More
The Radiation Damage In Accelerator Target Environments (RaDIATE) collaboration was founded in 2012 and currently consists of over 50 participants and 11 institutions globally. Due to the increasing power of future proton accelerator sources in target facilities, there is a critical need to further understand the physical and thermo-mechanical radiation response of target facility materials. Thus, the primary objective of the RaDIATE collaboration is to draw on existing expertise in the nuclear materials and accelerator targets fields to generate new and useful materials data for application within the accelerator and fission/fusion communities. Current research activities of the collaboration include post irradiation examination (PIE) of decommissioned components from existing beamlines such as the NuMI beryllium beam window and graphite NT-02 target material. PIE of these components includes advanced microstructural analyses (SEM/TEM, EBSD, EDS) and micro-mechanics technique such as nano-indentation, to help characterize any microstructural radiation damage incurred during operation. New irradiation campaigns of various candidate materials at both low and high energy beam facilities are also being pursued. Beryllium helium implantation studies at the University of Surrey as well as high energy proton irradiation of various materials at Brookhaven National Laboratory's BLIP facility have been initiated. The program also extends to beam-induced thermal shock experiments using high intensity beam pulses at CERN's HiRadMat facility, followed by advanced PIE activities to evaluate thermal shock resistance of the materials. Preliminary results from ongoing research activities, as well as the future plans of the RaDIATE collaboration R&D program will be discussed.
△ Less
Submitted 22 March, 2018;
originally announced March 2018.
-
Radiation damage and thermal shock response of carbon-fiber-reinforced materials to intense high-energy proton beams
Authors:
N. Simos,
Z. Zhong,
S. Ghose,
H. G. Kirk,
L-P Trung,
K. T. McDonald,
Z. Kotsina,
P. Nocera,
R. Assmann,
S. Redaelli,
A. Bertarelli,
E. Quaranta,
A. Rossi,
R. Zwaska,
K. Ammigan,
P. Hurh,
N. Mokhov
Abstract:
A comprehensive study on the effects of energetic protons on carbon-fiber composites and compounds under consideration for use as low-Z pion production targets in future high-power accelerators and low-impedance collimating elements for intercepting TeV-level protons at the Large Hadron Collider has been undertaken addressing two key areas, namely, thermal shock absorption and resistance to irradi…
▽ More
A comprehensive study on the effects of energetic protons on carbon-fiber composites and compounds under consideration for use as low-Z pion production targets in future high-power accelerators and low-impedance collimating elements for intercepting TeV-level protons at the Large Hadron Collider has been undertaken addressing two key areas, namely, thermal shock absorption and resistance to irradiation damage.
△ Less
Submitted 1 December, 2017;
originally announced December 2017.
-
Design Of The LBNF Beamline
Authors:
V. Papadimitriou,
K. Ammigan,
J. Anderson Jr.,
K. E. Anderson,
R. Andrews,
V. Bocean,
C. F. Crowley,
N. Eddy,
B. D. Hartsell,
S. Hays,
P. Hurh,
J. Hylen,
J. A. Johnstone,
P. Kasper,
T. Kobilarcik,
G. E. Krafczyk,
B. Lundberg,
A. Marchionni,
N. V. Mokhov,
C. D. Moore,
D. Pushka,
I. Rakhno,
S. D. Reitzner,
P. Schlabach,
V. Sidorov
, et al. (9 additional authors not shown)
Abstract:
The Long Baseline Neutrino Facility (LBNF) will utilize a beamline located at Fermilab to provide and aim a neutrino beam of sufficient intensity and appropriate energy range toward the Deep Underground Neutrino Experiment (DUNE) detectors, placed deep underground at the SURF Facility in Lead, South Dakota. The primary proton beam (60-120 GeV) will be extracted from the MI-10 section of Fermilab's…
▽ More
The Long Baseline Neutrino Facility (LBNF) will utilize a beamline located at Fermilab to provide and aim a neutrino beam of sufficient intensity and appropriate energy range toward the Deep Underground Neutrino Experiment (DUNE) detectors, placed deep underground at the SURF Facility in Lead, South Dakota. The primary proton beam (60-120 GeV) will be extracted from the MI-10 section of Fermilab's Main Injector. Neutrinos will be produced when the protons interact with a solid target to produce mesons which will be subsequently focused by magnetic horns into a 194m long decay pipe where they decay into muons and neutrinos. The parameters of the facility were determined taking into account the physics goals, spatial and radiological constraints, and the experience gained by operating the NuMI facility at Fermilab. The Beamline facility is designed for initial operation at a proton-beam power of 1.2 MW, with the capability to support an upgrade to 2.4 MW. LBNF/DUNE obtained CD-1 approval in November 2015. We discuss here the design status and the associated challenges as well as the R&D and plans for improvements before baselining the facility.
△ Less
Submitted 14 April, 2017;
originally announced April 2017.
-
Design of the LBNF Beamline Target Station
Authors:
S. Tariq,
K. Ammigan,
K. Anderson,
S. A. Buccellato,
C. F. Crowley,
B. D. Hartsell,
P. Hurh,
J. Hylen,
P. Kasper,
G. E. Krafczyk,
A. Lee,
B. Lundberg,
A. Marchionni,
N. V. Mokhov,
C. D. Moore,
V. Papadimitriou,
D. Pushka,
I. Rakhno,
S. D. Reitzner,
V. Sidorov,
A. M. Stefanik,
I. S . Tropin,
K. Vaziri,
K. Williams,
R. M. Zwaska
, et al. (1 additional authors not shown)
Abstract:
The Long Baseline Neutrino Facility (LBNF) project will build a beamline located at Fermilab to create and aim an intense neutrino beam of appropriate energy range toward the DUNE detectors at the SURF facility in Lead, South Dakota. Neutrino production starts in the Target Station, which consists of a solid target, magnetic focusing horns, and the associated sub-systems and shielding infrastructu…
▽ More
The Long Baseline Neutrino Facility (LBNF) project will build a beamline located at Fermilab to create and aim an intense neutrino beam of appropriate energy range toward the DUNE detectors at the SURF facility in Lead, South Dakota. Neutrino production starts in the Target Station, which consists of a solid target, magnetic focusing horns, and the associated sub-systems and shielding infrastructure. Protons hit the target producing mesons which are then focused by the horns into a helium-filled decay pipe where they decay into muons and neutrinos. The target and horns are encased in actively cooled steel and concrete shielding in a chamber called the target chase. The reference design chase is filled with air, but nitrogen and helium are being evaluated as alternatives. A replaceable beam window separates the decay pipe from the target chase. The facility is designed for initial operation at 1.2 MW, with the ability to upgrade to 2.4 MW, and is taking advantage of the experience gained by operating Fermilab's NuMI facility. We discuss here the design status, associated challenges, and ongoing R&D and physics-driven component optimization of the Target Station.
△ Less
Submitted 21 December, 2016;
originally announced December 2016.