Temperature-Induced Hexagonal-Orthorhombic Phase Transition in Lutetium Ferrite Nanoparticles
Authors:
Olena M. Fesenko,
Igor V. Fesych,
Igor V. Zatovsky,
Andrii D. Yaremkevych,
Maxim Rallev,
Andrii V. Bodnaruk,
Eugene A. Eliseev,
Anna N. Morozovska
Abstract:
The X-ray diffraction, Raman and infrared spectroscopies and magnetic measurements were used to explore the correlated changes of the structure, lattice dynamics and magnetic properties of the LuFeO3 nanoparticles, which appear in dependence on their sintering temperature. We revealed a gradual substitution of the hexagonal phase by the orthorhombic phase in the nanoparticles, which sintering temp…
▽ More
The X-ray diffraction, Raman and infrared spectroscopies and magnetic measurements were used to explore the correlated changes of the structure, lattice dynamics and magnetic properties of the LuFeO3 nanoparticles, which appear in dependence on their sintering temperature. We revealed a gradual substitution of the hexagonal phase by the orthorhombic phase in the nanoparticles, which sintering temperature increases from 700 C to 1100 C. The origin and stability of the hexagonal phase in the LuFeO3 nanoparticles is of the special interest, because the nanoparticle in the phase can be a room-temperature multiferroic with a weak ferromagnetic and pronounced structural and ferroelectric long-range ordering, while the antiferromagnetic and nonpolar orthorhombic phase is more stable in the bulk LuFeO3. To define the ranges of the hexagonal phase stability, we determine the bulk and interface energy densities of different phases from the comparison of the Gibbs model with experimental results. Using the Gibbs model parameters, we predict the influence of size effects and temperature on the structural and polar properties of the LuFeO3 nanoparticles. Analysis of the obtained results shows that the combination of the X-ray diffraction, Raman and infrared spectroscopy, magnetic measurements and theoretical modelling of structural and polar properties allows to establish the interplay between the phase composition, lattice dynamics and multiferroic properties of the LuFeO3 nanoparticles prepared in different conditions.
△ Less
Submitted 16 June, 2024; v1 submitted 16 September, 2023;
originally announced September 2023.
The multifunctionality of lanthanum-strontium cobaltite nanopowder: high-pressure magnetic and excellent electrocatalytic properties for OER
Authors:
Hanlin Yu,
N. A. Liedienov,
I. V. Zatovsky,
D. S. Butenko,
I. V. Fesych,
Wei Xu,
Songchun Rui,
Quanjun Li,
Bingbing Liu,
A. V. Pashchenko,
G. G. Levchenko
Abstract:
Simultaneous study of magnetic and electrocatalytic properties of cobaltites under extreme conditions expands understanding of physical and chemical processes proceeding in them with the possibility of their further practical application. Therefore, La0.6Sr0.4CoO3 (LSCO) nanopowders have been synthesized at different annealing temperatures tann = 850, 875, 900 C, and their multifunctional properti…
▽ More
Simultaneous study of magnetic and electrocatalytic properties of cobaltites under extreme conditions expands understanding of physical and chemical processes proceeding in them with the possibility of their further practical application. Therefore, La0.6Sr0.4CoO3 (LSCO) nanopowders have been synthesized at different annealing temperatures tann = 850, 875, 900 C, and their multifunctional properties have been studied comprehensively. As tann increases, the rhombohedral perovskite structure of the LSCO becomes more single-phase, whereas average particle size and dispersion grow. Co ions are in mixed valence states, including major Co3+ and Co4+ components. It has been found that the LSCO-900 shows two main Curie temperatures, TC1 and TC2, associated with a particle size distribution. As an external hydrostatic pressure P increases, average <TC1> and <TC2> increase from 253 and 175 K under ambient pressure to 268 and 180 K under P = 0.8 GPa, respectively. At the same time, the antiferromagnetic temperature TAFM and blocking temperature TB also increase from 145 and 169 K to 158 and 170 K, respectively. The increment of <dTC/dP> for the smaller and bigger particles is sufficiently high and equals 10 and 13 K/GPa, respectively. The magnetocaloric effect in the LSCO-900 nanopowder is relatively weak but with an extremely wide peak > 50 K that makes this composition interesting to be used as one of the components of the composite expanding its working temperature window. Moreover, all LSCO samples showed excellent electrocatalytic performance for the overall water splitting (OER) process (overpotentials only 265-285 mV at a current density of 10 mA/cm2) with minimal values for LSCO-900. Based on the XPS data, it was found that the formation of a dense amorphous layer on the surface of the particles ensures high stability as a catalyst (at least 24 h) during electrolysis in 1 M KOH electrolyte.
△ Less