Ultrafast optical observation of spin-pum** induced dynamic exchange coupling in ferromagnetic semiconductor/metal bilayer
Authors:
X. Liu,
P. Liu,
H. C. Yuan,
J. Y. Shi,
H. L. Wang,
S. H. Nie,
F. **,
Z. Zheng,
X. Z. Yu,
J. H. Zhao,
H. B. Zhao,
G. Lüpke
Abstract:
Spin angular momentum transfer in magnetic bilayers offers the possibility of ultrafast and low-loss operation for next-generation spintronic devices. We report the field- and temperature- dependent measurements on the magnetization precessions in Co$_2$FeAl/(Ga,Mn)As by time-resolved magneto-optical Kerr effect (TRMOKE). Analysis of the effective Gilbert dam** and phase shift indicates a clear…
▽ More
Spin angular momentum transfer in magnetic bilayers offers the possibility of ultrafast and low-loss operation for next-generation spintronic devices. We report the field- and temperature- dependent measurements on the magnetization precessions in Co$_2$FeAl/(Ga,Mn)As by time-resolved magneto-optical Kerr effect (TRMOKE). Analysis of the effective Gilbert dam** and phase shift indicates a clear signature of an enhanced dynamic exchange coupling between the two ferromagnetic (FM) layers due to the reinforced spin pum** at resonance. The temperature dependence of the dynamic exchange-coupling reveals a primary contribution from the ferromagnetism in (Ga,Mn)As.
△ Less
Submitted 7 May, 2022; v1 submitted 7 March, 2022;
originally announced March 2022.
-
Ultrafast enhancement of interfacial exchange coupling in ferromagnetic bilayer
Authors:
X. Liu,
H. C. Yuan,
P. Liu,
J. Y. Shi,
H. L. Wang,
S. H. Nie,
F. **,
Z. Zheng,
X. Z. Yu,
J. H. Zhao,
H. B. Zhao,
G. Lüpke
Abstract:
Fast spin manipulation in magnetic heterostructures, where magnetic interactions between different materials often define the functionality of devices, is a key issue in the development of ultrafast spintronics. Although recently developed optical approaches such as ultrafast spin-transfer and spin-orbit torques open new pathways to fast spin manipulation, these processes do not fully utilize the…
▽ More
Fast spin manipulation in magnetic heterostructures, where magnetic interactions between different materials often define the functionality of devices, is a key issue in the development of ultrafast spintronics. Although recently developed optical approaches such as ultrafast spin-transfer and spin-orbit torques open new pathways to fast spin manipulation, these processes do not fully utilize the unique possibilities offered by interfacial magnetic coupling effects in ferromagnetic multilayer systems. Here, we experimentally demonstrate ultrafast photo-enhanced interfacial exchange interactions in the ferromagnetic Co$_2$FeAl/(Ga,Mn)As system at low laser fluence levels. The excitation efficiency of Co$_2$FeAl with the (Ga,Mn)As layer is 30-40 times higher than the case with the GaAs layer at 5 K due to a photo-enhanced exchange coupling interaction via photoexcited charge transfer between the two ferromagnetic layers. In addition, the coherent spin precessions persist to room temperature, excluding the drive of photo-enhanced magnetization in the (Ga,Mn)As layer and indicating a proximity-effect-related optical excitation mechanism. The results highlight the importance of considering the range of interfacial exchange interactions in ferromagnetic heterostructures and how these magnetic coupling effects can be utilized for ultrafast, low-power spin manipulation.
△ Less
Submitted 3 March, 2022; v1 submitted 1 March, 2022;
originally announced March 2022.
-
General Resolution Enhancement Method in Atomic Force Microscopy (AFM) Using Deep Learning
Authors:
Y. Liu,
Q. M. Sun,
Dr. W. H. Lu,
Dr. H. L. Wang,
Y. Sun,
Z. T. Wang,
X. Lu,
Prof. K. Y. Zeng
Abstract:
This paper develops a resolution enhancement method for post-processing the images from Atomic Force Microscopy (AFM). This method is based on deep learning neural networks in the AFM topography measurements. In this study, a very deep convolution neural network is developed to derive the high-resolution topography image from the low-resolution topography image. The AFM measured images from variou…
▽ More
This paper develops a resolution enhancement method for post-processing the images from Atomic Force Microscopy (AFM). This method is based on deep learning neural networks in the AFM topography measurements. In this study, a very deep convolution neural network is developed to derive the high-resolution topography image from the low-resolution topography image. The AFM measured images from various materials are tested in this study. The derived high-resolution AFM images are comparable with the experimental measured high-resolution images measured at the same locations. The results suggest that this method can be developed as a general post-processing method for AFM image analysis.
△ Less
Submitted 11 September, 2018;
originally announced September 2018.
-
Epitaxial growth and magnetic properties of NiMnAs film on GaAs substrate
Authors:
J. L. Ma,
H. L. Wang,
X. M. Zhang,
S. Yan,
W. S. Yan,
J. H. Zhao
Abstract:
Single-phase Ni0.46Mn0.54As films with strained C1b symmetry have been successfully grown on GaAs (001) substrates by molecular-beam epitaxy. The epitaxial relationship between the film and the substrate has been studied using synchrotron radiation, and a preferred configuration of (110)-orientated Ni0.46Mn0.54As on (001)-orientated GaAs was revealed. In addition, the magnetic properties of the fi…
▽ More
Single-phase Ni0.46Mn0.54As films with strained C1b symmetry have been successfully grown on GaAs (001) substrates by molecular-beam epitaxy. The epitaxial relationship between the film and the substrate has been studied using synchrotron radiation, and a preferred configuration of (110)-orientated Ni0.46Mn0.54As on (001)-orientated GaAs was revealed. In addition, the magnetic properties of the films were found to be significantly influenced by the growth temperature. The optimized growth temperature is determined to be ~370 degree Celsius , for which relatively high Curie temperature, large saturation magnetization and coercive field, as well as the pronounced in-plane magnetic anisotropy were obtained. According to the results of X-ray absorption spectroscopy, the above phenomenon can be attributed to the variation of the local electronic structure of the Mn atoms. Our work provides useful information for the further investigations of NiMnAs, which is theoretically predicted to host robust half-metallicity.
△ Less
Submitted 7 September, 2018; v1 submitted 6 September, 2018;
originally announced September 2018.
-
Robust Zero-Field Skyrmion Formation in FeGe Epitaxial Thin Films
Authors:
J. C. Gallagher,
K. Y. Meng,
J. T. Brangham,
H. L. Wang,
B. D. Esser,
D. W. McComb,
F. Y. Yang
Abstract:
B20 phase magnetic materials, such as FeGe, have been of significant interests in recent years because they enable magnetic skyrmions, which can potentially lead to low energy cost spintronic applications. One major effort in this emerging field is the stabilization of skyrmions at room temperature and zero external magnetic field. We report the growth of phase-pure FeGe epitaxial thin films on Si…
▽ More
B20 phase magnetic materials, such as FeGe, have been of significant interests in recent years because they enable magnetic skyrmions, which can potentially lead to low energy cost spintronic applications. One major effort in this emerging field is the stabilization of skyrmions at room temperature and zero external magnetic field. We report the growth of phase-pure FeGe epitaxial thin films on Si(111) substrates by ultrahigh vacuum off-axis sputtering. The high crystalline quality of the FeGe films was confirmed by x-ray diffraction and scanning transmission electron microscopy. Hall effect measurements reveal strong topological Hall effect after subtracting out the ordinary and anomalous Hall effects, demonstrating the formation of high density skyrmions in FeGe films between 5 and 275 K. In particular, substantial topological Hall effect was observed at zero magnetic field, showing a robust skyrmion phase without the need of an external magnetic field.
△ Less
Submitted 22 April, 2016;
originally announced April 2016.
-
Granularity Controlled Non-Saturating Linear Magneto-resistance in Topological Insulator Bi2Te3 Films
Authors:
Z. H. Wang,
L. Yang,
X. J. Li,
X. T. Zhao,
H. L. Wang,
Z. D. Zhang,
Xuan P. A. Gao
Abstract:
We report on the magneto-transport properties of chemical vapor deposition grown films of interconnected Bi2Te3 nanoplates. Similar to many other topological insulator (TI) materials, these granular Bi2Te3 films exhibit a linear magneto-resistance (LMR) effect which has received much recent attention. Studying samples with different degree of granularity, we find a universal correlation between th…
▽ More
We report on the magneto-transport properties of chemical vapor deposition grown films of interconnected Bi2Te3 nanoplates. Similar to many other topological insulator (TI) materials, these granular Bi2Te3 films exhibit a linear magneto-resistance (LMR) effect which has received much recent attention. Studying samples with different degree of granularity, we find a universal correlation between the magnitude of the LMR and the average mobility (<μ>) of the films over nearly two orders of magnitude change of <μ>. The granularity controlled LMR effect here is attributed to the mobility fluctuation induced classical LMR according to the Parish-Littlewood theory. These findings have implications to both the fundamental understanding and magneto-resistive device applications of TI and small bandgap semiconductor materials.
△ Less
Submitted 28 December, 2015; v1 submitted 26 January, 2015;
originally announced January 2015.
-
Off-Resonant Manipulation of Spins in Diamond via Precessing Magnetization of a Proximal Ferromagnet
Authors:
Chris S. Wolfe,
Vidya P. Bhallamudi,
Hilong L. Wang,
Chunhui H. Du,
Sergei Manuilov,
Andrew J. Berger,
Rohan Adur,
Fengyuan Y. Yang,
P. Chris Hammel
Abstract:
We report the manipulation of nitrogen vacancy (NV) spins in diamond when nearby ferrimagnetic insulator, yttrium iron garnet, is driven into precession. The change in NV spin polarization, as measured by changes in photoluminescence, is comparable in magnitude to that from conventional optically detected magnetic resonance, but relies on a distinct mechanism as it occurs at a microwave frequency…
▽ More
We report the manipulation of nitrogen vacancy (NV) spins in diamond when nearby ferrimagnetic insulator, yttrium iron garnet, is driven into precession. The change in NV spin polarization, as measured by changes in photoluminescence, is comparable in magnitude to that from conventional optically detected magnetic resonance, but relies on a distinct mechanism as it occurs at a microwave frequency far removed from the magnetic resonance frequency of the NV spin. This observation presents a new approach to transferring ferromagnetic spin information into a paramagnet and then transducing the response into a robust optical signal. It also opens new avenues for studying ferromagnetism and spin transport at the nanoscale.
△ Less
Submitted 3 March, 2014;
originally announced March 2014.
-
Scaling of spin Hall angle in 3d, 4d and 5d metals from Y3Fe5O12/metal spin pum**
Authors:
H. L. Wang,
C. H. Du,
Y. Pu,
R. Adur,
P. C. Hammel,
F. Y. Yang
Abstract:
Pure spin currents generated by spin pum** in ferromagnet/nonmagnet (FM/NM) bilayers produce inverse spin Hall effect (ISHE) voltages in the NM, from which spin pum** and transport characteristics of the NM can be extracted. Due to its exceptionally low dam**, Y3Fe5O12 (YIG) is an important and widely used FM for microwave devices and ferromagnetic resonance (FMR) spin pum**. Here we repor…
▽ More
Pure spin currents generated by spin pum** in ferromagnet/nonmagnet (FM/NM) bilayers produce inverse spin Hall effect (ISHE) voltages in the NM, from which spin pum** and transport characteristics of the NM can be extracted. Due to its exceptionally low dam**, Y3Fe5O12 (YIG) is an important and widely used FM for microwave devices and ferromagnetic resonance (FMR) spin pum**. Here we report systematic investigation of spin pum** from 20-nm thick YIG thin films to a series of 3d, 4d and 5d normal metals (Cu, Ag, Ta, W, Pt and Au) with various spin-orbit coupling strengths. From enhanced Gilbert dam** obtained from the frequency dependence of FMR linewidths and ISHE signals, the spin Hall angles and YIG/NM interfacial spin mixing conductances are quantitatively determined for these metals. The spin Hall angles largely vary as the fourth power of the atomic number, corroborating the dominant role of spin-orbit coupling across a broad range in the inverse spin Hall effect.
△ Less
Submitted 15 January, 2014; v1 submitted 9 July, 2013;
originally announced July 2013.
-
Probing the Spin Pum** Mechanism: Exchange Coupling with Exponential Decay in Y3Fe5O12/barrier/Pt Heterostructures
Authors:
C. H. Du,
H. L. Wang,
Y. Pu,
T. L. Meyer,
P. M. Woodward,
F. Y. Yang,
P. C. Hammel
Abstract:
Ferromagnetic resonance driven spin pum** of pure spin currents from a ferromagnet into a nonmagnetic material promises new spin-functional devices with low energy consumption. The mechanism of spin pum** is under intense investigation and it is widely believed that exchange interaction between the ferromagnet and nonmagnetic material is responsible for this phenomenon. We observe a thousand-f…
▽ More
Ferromagnetic resonance driven spin pum** of pure spin currents from a ferromagnet into a nonmagnetic material promises new spin-functional devices with low energy consumption. The mechanism of spin pum** is under intense investigation and it is widely believed that exchange interaction between the ferromagnet and nonmagnetic material is responsible for this phenomenon. We observe a thousand-fold exponential decay of the spin pum** from 20-nm thick Y3Fe5O12 films to platinum across insulating barriers, from which the exponential decay lengths of 0.16 and 0.23 nm are extracted for oxide barriers with band gaps of 4.93 eV and 2.36 eV, respectively. This prototypical signature of quantum tunneling through a barrier underscores the importance of exchange coupling for spin pum** and reveals its dependence on the characteristics of the barrier material.
△ Less
Submitted 10 July, 2013; v1 submitted 6 July, 2013;
originally announced July 2013.
-
Large Spin Pum** from Epitaxial Y3Fe5O12 Thin Films to Pt and W Layers
Authors:
H. L. Wang,
C. H. Du,
Y. Pu,
R. Adur,
P. C. Hammel,
F. Y. Yang
Abstract:
Epitaxial Y3Fe5O12 thin films have been deposited by off-axis sputtering, which exhibit excellent crystalline quality, enabling observation of large spin pum** signals in Pt/Y3Fe5O12 and W/Y3Fe5O12 bilayers driven by cavity ferromagnetic resonance. The inverse spin Hall voltages reach 2.10 mV and -5.26 mV in 5-mm long Pt/Y3Fe5O12 and W/Y3Fe5O12 bilayers, respectively, excited by a radio-frequenc…
▽ More
Epitaxial Y3Fe5O12 thin films have been deposited by off-axis sputtering, which exhibit excellent crystalline quality, enabling observation of large spin pum** signals in Pt/Y3Fe5O12 and W/Y3Fe5O12 bilayers driven by cavity ferromagnetic resonance. The inverse spin Hall voltages reach 2.10 mV and -5.26 mV in 5-mm long Pt/Y3Fe5O12 and W/Y3Fe5O12 bilayers, respectively, excited by a radio-frequency magnetic field of 0.3 Oe. From the ferromagnetic resonance linewidth broadening, the interfacial spin mixing conductance of 4.56E14 Ω-1m-2 and 2.30E14 Ω-1m-2 are obtained for Pt/Y3Fe5O12 and W/Y3Fe5O12 bilayers, respectively.
△ Less
Submitted 3 July, 2013;
originally announced July 2013.
-
Long-range FMR driven spin pum** through a nonmagnetic insulator
Authors:
Y. Pu,
H. L. Wang,
C. H. Du,
R. Adur,
A. J. Berger,
A. Hauser,
R. E. A. Williams,
D. W. McComb,
E. Johnston-Halperin,
P. C. Hammel,
F. Y. Yang
Abstract:
Ferromagnetic resonance (FMR) driven spin pum** is an emerging technique for injection of a pure spin current from a ferromagnet (FM) into a non-magnetic (NM) material without an accompanying charge current. It is widely believed that this pum** proceeds exclusively via a short-range exchange interaction at the FM/NM interface. Here we report robust, long-range spin pum** from the ferrimagne…
▽ More
Ferromagnetic resonance (FMR) driven spin pum** is an emerging technique for injection of a pure spin current from a ferromagnet (FM) into a non-magnetic (NM) material without an accompanying charge current. It is widely believed that this pum** proceeds exclusively via a short-range exchange interaction at the FM/NM interface. Here we report robust, long-range spin pum** from the ferrimagnetic double perovskite Sr2FeMoO6 (SFMO) into Pt across an insulating barrier up to 200 nm thick, and systematically rule out all known spurious effects. This result demonstrates dynamic spin injection over a distance far beyond the coupling range of the exchange interaction, exposing the need to consider other coupling mechanisms. The characteristic length scale for magnetic textures in Sr2FeMoO6 is approximately 150 nm, resulting from structural antiphase boundaries, thus raising the possibility that magnetic dipole coupling underlies the observed long range spin transfer. This discovery reveals a route to dynamic angular momentum transfer between a FM and a NM in the absence of mediation by itinerant electrons and promises new spin-functional devices employing long-range spin pum**.
△ Less
Submitted 2 April, 2014; v1 submitted 14 May, 2013;
originally announced May 2013.
-
Strain dependent twist-stretch elasticity in chiral filaments
Authors:
M. Upmanyu,
H. L. Wang,
H. Y. Liang,
R. Mahajan
Abstract:
Coupling between axial and torsional degrees of freedom often modifies the conformation and expression of natural and synthetic filamentous aggregates. Recent studies on chiral single-walled carbon nanotubes and B-DNA reveal a reversal in the sign of the twist-stretch coupling at large strains. The similarity in the response in these two distinct supramolecular assemblies and at high strains sug…
▽ More
Coupling between axial and torsional degrees of freedom often modifies the conformation and expression of natural and synthetic filamentous aggregates. Recent studies on chiral single-walled carbon nanotubes and B-DNA reveal a reversal in the sign of the twist-stretch coupling at large strains. The similarity in the response in these two distinct supramolecular assemblies and at high strains suggests a fundamental, chirality dependent non-linear elastic behaviour. Here, we seek the link between the microscopic origin of the non-linearities and the effective twist-stretch coupling using energy based theoretical frameworks and model simulations. Our analysis reveals a sensitive interplay between the deformation energetics and the sign of the coupling, highlighting robust design principles that determine both the sign and extent of these couplings. These design principles have been already exploited by Nature to dynamically engineer such couplings, and have broad implications in mechanically coupled actuation, propulsion and transport in biology and technology.
△ Less
Submitted 4 September, 2007;
originally announced September 2007.