The first-order structural phase transition at low-temperature in GaPt$_{5}$P and its rapid enhancement with pressure
Authors:
A. Sapkota,
T. J. Slade,
S. Huyan,
N. K. Nepal,
J. M. Wilde,
N. Furukawa,
S. H. Laupidus,
L. -L. Wang,
S. L. Bud'ko,
P. C. Canfield
Abstract:
Single crystals of XPt$_{5}$P (X = Al, Ga, and In) were grown from a Pt-P solution at high temperatures, and ambient-pressure measurements of temperature-dependent magnetization, resistivity, and X-ray diffraction were made. Also, the ambient-pressure Hall resistivity and temperature-dependent resistance under pressure were measured on GaPt$_{5}$P. All three compounds have tetragonal $P4/mmm$ crys…
▽ More
Single crystals of XPt$_{5}$P (X = Al, Ga, and In) were grown from a Pt-P solution at high temperatures, and ambient-pressure measurements of temperature-dependent magnetization, resistivity, and X-ray diffraction were made. Also, the ambient-pressure Hall resistivity and temperature-dependent resistance under pressure were measured on GaPt$_{5}$P. All three compounds have tetragonal $P4/mmm$ crystal structure at room-temperature with metallic transport and weak diamagnetism over the $2-300$~K temperature range. Surprisingly, at ambient pressure, both the transport and magnetization measurements on GaPt$_{5}$P show a step-like feature in $70-90$~K region suggesting a possible structural phase transition, and no such features were observed in (Al/In)Pt$_{5}$P. Both the hysteretic nature and sharpness of the feature suggest the first-order transition, and single-crystal X-ray diffraction measurements provided further details of the structural transition with a crystal symmetry likely different than $P4/mmm$ below transition. The transition is characterized by anisotropic changes in the lattice parameters, a volume collapse, and satellite peaks at two distinct wave-vectors. Density functional theory calculations present phonon softening as a possible driving mechanism. Additionally, the structural transition temperature increases rapidly with increasing pressure, reaching room temperature by $\sim 2.2$~GPa, highlighting the high degree of pressure sensitivity and fragile nature of GaPt$_{5}$P room-temperature structure. Although the volume collapse and extreme pressure sensitivity suggest chemical pressure should drive a similar structural change in AlPt$_{5}$P, with smaller unit cell dimensions and volume, its structure is found to be $P4/mmm$ as well. Overall, GaPt$_{5}$P stands out as a sole member of the 1-5-1 family of compounds with a temperature-driven structural change.
△ Less
Submitted 10 June, 2024;
originally announced June 2024.
-
Effect of Ni substitution on the fragile magnetic system ${\text{La}_{5}\text{Co}_{2}\text {Ge}_{3}}$
Authors:
Atreyee Das,
Tyler J. Slade,
Rustem Khasanov,
Sergey L. Bud'ko,
Paul C. Canfield
Abstract:
$\text{La}_{5}\text{Co}_{2}\text{Ge}_{3}$ is an itinerant ferromagnet with a Curie temperature, $T_C$, of $\sim$ 3.8 K and a remarkably small saturated moment of 0.1 $μ_{B}/\text{Co}$. Here we present the growth and characterization of single crystals of the ${\text{La}_{5}\text{(Co}_{1-x}\text {Ni}_{x})_2\text {Ge}_{3}}$ series for 0.00 $\leq x \leq…
▽ More
$\text{La}_{5}\text{Co}_{2}\text{Ge}_{3}$ is an itinerant ferromagnet with a Curie temperature, $T_C$, of $\sim$ 3.8 K and a remarkably small saturated moment of 0.1 $μ_{B}/\text{Co}$. Here we present the growth and characterization of single crystals of the ${\text{La}_{5}\text{(Co}_{1-x}\text {Ni}_{x})_2\text {Ge}_{3}}$ series for 0.00 $\leq x \leq$ 0.186. We measured powder X-ray diffraction, composition as well as anisotropic temperature dependent resistivity, temperature and field dependent magnetization along with heat capacity on these single crystals. We also measured muon-spin rotation/relaxation ($μ\text{SR}$) for some Ni substitutions ($x$ = 0.027, 0.036, 0.074) to study the evolution of internal field with Ni substitution. Using the measured data we infer a low temperature, transition temperature-composition phase diagram for ${\text{La}_{5}\text{(Co}_{1-x}\text {Ni}_{x})_2\text {Ge}_{3}}$. We find that $T_{C}$ is suppressed for low do**s, $x \leq 0.014 $; whereas for $0.036 \leq {x} \leq 0.186 $, the samples are antiferromagnetic with a Neel temperature, $T_{N}$, that goes through a weak and shallow maximum ($T_N \sim$ 3.4 K for $ x \sim$ 0.07) and then gradually decreases to 2.4 K by $x$ = 0.186. For intermediate Ni substitutions, $0.016 \leq {x} \leq 0.027 $, two transition temperatures are inferred with $T_N > T_C$. Whereas the $T-x$ phase diagram for ${\text{La}_{5}\text{(Co}_{1-x}\text {Ni}_{x})_2\text {Ge}_{3}}$ and the $T-p$ phase diagram determined for the parent $\text{La}_{5}\text{Co}_{2}\text{Ge}_{3}$ under hydrostatic pressure are grossly similar, changing from a low do** or low pressure ferromagnetic (FM) ground state to a high doped or pressure antiferromagnetic (AFM) state, perturbation by Ni substitution enabled us to identify an intermediate do** regime where both FM and AFM transitions occur.
△ Less
Submitted 28 May, 2024;
originally announced May 2024.
-
La$_4$Co$_4$X (X = Pb, Bi, Sb): a demonstration of antagonistic pairs as a route to quasi-low dimensional ternary compounds
Authors:
Tyler J. Slade,
Nao Furukawa,
Matthew Dygert,
Siham Mohamed,
Atreyee Das,
Weiyi Xia,
Cai-Zhuang Wang,
Sergey L. Budko,
Paul C. Canfield
Abstract:
We outline how pairs of strongly immiscible elements, referred to here as antagonistic pairs, can be used to synthesize ternary compounds with quasi-reduced dimensional motifs. By identifying third elements that are compatible with a given antagonistic pair, ternary compounds can be formed in which the third element segregates the immiscible atoms into spatially separated substructures. Quasi-low…
▽ More
We outline how pairs of strongly immiscible elements, referred to here as antagonistic pairs, can be used to synthesize ternary compounds with quasi-reduced dimensional motifs. By identifying third elements that are compatible with a given antagonistic pair, ternary compounds can be formed in which the third element segregates the immiscible atoms into spatially separated substructures. Quasi-low dimensional structural units are a natural consequence of the immiscible atoms seeking to avoid contact in the solid-state. As proof of principle, we present the discovery and physical properties of La$_4$Co$_4$X (X = Pb, Bi, Sb), a new family of intermetallics based on the antagonistic pairs Co-Pb and Co-Bi. La$_4$Co$_4$X adopts a new orthorhombic crystal structure (space group Pbam) containing quasi-2D Co slabs and La-X layers that stack along the a-axis. Consistent with our proposal, the La atoms separate the Co and X substructures, ensuring there are no direct contacts between immiscible atoms. Within the Co slabs, the atoms occupy the vertices of corner sharing tetrahedra and triangles, and this motif produces flat electronic bands near the Fermi level that favor magnetism. The Co is moment bearing in La$_4$Co$_4$X, and we show that whereas La$_4$Co$_4$Pb behaves as a three dimensional antiferromagnet with T$_N$ = 220 K, La$_4$Co$_4$Bi and La$_4$Co$_4$Sb have behavior consistent with low dimensional magnetic coupling and ordering, with T$_N$ = 153 K and 143 K respectively. In addition to the Pb, Bi, and Sb based La$_4$Co$_4$X compounds, we were likely able to produce an analogous La$_4$Co$_4$Sn in polycrystalline form, although we were unable to isolate single crystals. We anticipate that using mutually compatible third elements with an antagonistic pair represents a generalizable design principle for discovering new materials and structure types containing low-dimensional substructures.
△ Less
Submitted 29 February, 2024;
originally announced March 2024.
-
Suppression of metal-to-insulator transition and stabilization of superconductivity by pressure in Re3Ge7
Authors:
S. Huyan,
E. Mun,
H. Wang,
T. J. Slade,
Z. Li,
J. Schmidt,
R. A. Ribeiro,
W. Xie,
S. L. Bud'ko,
P. C. Canfield
Abstract:
The effect of pressure on the low-temperature states of the Re3Ge7 is investigated by both electrical and Hall resistance and magnetization measurements. At ambient pressure, the temperature dependent resistance of Re3Ge7 behaves quasi-linearly from room temperature down to 60 K, then undergoes a two-step metal-to-insulator transitions (MIT) at temperatures T1 = 59.4 K and T2 = 58.7 K which may be…
▽ More
The effect of pressure on the low-temperature states of the Re3Ge7 is investigated by both electrical and Hall resistance and magnetization measurements. At ambient pressure, the temperature dependent resistance of Re3Ge7 behaves quasi-linearly from room temperature down to 60 K, then undergoes a two-step metal-to-insulator transitions (MIT) at temperatures T1 = 59.4 K and T2 = 58.7 K which may be related to a structural phase transition or occurrence of charge density wave ordering. Upon applying pressure, the two-step (T1, T2) MIT splits into three steps (T1, T2 and T3) above 1 GPa, and all traces of MITs are fully suppressed by ~8 GPa. Subsequently, the onset of bulk superconductivity (SC) occurs between 10.8 and 12.2 GPa and persists to our highest pressure of 26.8 GPa. At 12.2 GPa the superconducting transition temperature, Tc, and upper critical field, Hc2 reach the maximum of Tc (onset) ~5.9 K and Hc2 (1.8 K) ~ 14 kOe. Our results not only present the observation of SC under high pressure in Re3Ge7 but also delineate the interplay between SC and other competing electronic states by creating a T - p phase diagram for this potentially topologically nontrivial system Re3Ge7.
△ Less
Submitted 17 January, 2024;
originally announced January 2024.
-
Double-domed temperature-pressure phase diagram found for CePd3S4
Authors:
S. Huyan,
T. J. Slade,
H. Wang,
R. Flint,
R. A. Ribeiro,
W. Xie,
S. L. Bud'ko,
P. C. Canfield
Abstract:
CePd3S4 exhibits interplay between ferromagnetism (FM), quadrupolar order, and the Kondo effect at low temperatures with a FM transition temperature that is much higher than the value expected from the de Gennes scaling of the heavier RPd3S4 compounds. In this work, we investigated the electrical transport and magnetic properties of CePd3S4 under pressure up through 12 GPa so as to better understa…
▽ More
CePd3S4 exhibits interplay between ferromagnetism (FM), quadrupolar order, and the Kondo effect at low temperatures with a FM transition temperature that is much higher than the value expected from the de Gennes scaling of the heavier RPd3S4 compounds. In this work, we investigated the electrical transport and magnetic properties of CePd3S4 under pressure up through 12 GPa so as to better understand the interplay between electronic and magnetic phases in this material. Our findings show that the low pressure FM state is suddenly replaced by a new magnetically ordered phase that is most likely antiferromagnetic that spans from ~ 7 GPa to ~ 11 GPa. Whereas this could be described as an example of avoided quantum criticality, given that clear changes in resistance and Hall data are detected near 6.3 GPa for all temperatures below 300 K, it is also possible that the change in ground state is a response to a pressure induced change in structure. The lack of any discernible change in the pressure dependence of the room temperature unit cell parameter/volume across this whole pressure range suggests that this change in structure is either more subtle than could be detected by our measurements (i.e. development of weak, new wave vector) or the transition is electronic (such as a Lifshitz transition).
△ Less
Submitted 5 January, 2024;
originally announced January 2024.
-
Vacancy Tuned Magnetism in LaMn$_x$Sb$_2$
Authors:
Tyler J. Slade,
Aashish Sapkota,
John M. Wilde,
Qiang Zhang,
Lin-Lin Wang,
Saul H. Lapidus,
Juan Schmidt,
Thomas Heitmann,
Sergey L. Budko,
Paul C. Canfield
Abstract:
The layered ATMPn$_2$ (A = alkali earth or rare earth atom, TM = transition metal, Pn = Sb, Bi) compounds are widely studied for their rich magnetism and electronic structure topology. Here, we characterize the physical properties of LaMn$_x$Sb$_2$, an understudied member of the ATMPn$_2$ family. LaMn$_x$Sb$_2$ forms with intrinsic Mn vacancies, and we demonstrate synthetic control of the Mn occup…
▽ More
The layered ATMPn$_2$ (A = alkali earth or rare earth atom, TM = transition metal, Pn = Sb, Bi) compounds are widely studied for their rich magnetism and electronic structure topology. Here, we characterize the physical properties of LaMn$_x$Sb$_2$, an understudied member of the ATMPn$_2$ family. LaMn$_x$Sb$_2$ forms with intrinsic Mn vacancies, and we demonstrate synthetic control of the Mn occupancy to produce single crystals with x = 0.74-0.97. Magnetization and transport measurements indicate LaMn$_x$Sb$_2$ has a rich temperature-composition (T-x) magnetic phase diagram with physical properties strongly influenced by the Mn occupancy. LaMn$_x$Sb$_2$ orders antiferromagnetically at T$_{1}$ = 130--180 K, where T$_{1}$ increases with x. Below T$_{1}$, the T-x phase diagram is complicated. At high x, there is a second transition T$_2$ that decreases in temperature as x is lowered, vanishing below x $\leq$ 0.85. A third, first-order, transition T$_3$ is detected at x $\approx$ 0.92, and the transition temperature increases as x is lowered, crossing above T$_2$ near x $\approx$ 0.9. On moving below x $<$ 0.79, we find the crystal structure changes from the P4/nmm arrangement to a I$\bar{4}$2m structure with partially ordered Mn vacancies. The change in crystal structure results in the appearance of two new low temperature phases and a crossover between regimes of negative and positive magnetoresistance. Finally, we provide neutron diffraction for x = 0.93, and find that the high x compositions first adopt a G-type AFM structure with the Mn moments aligned within the ab-plane which is followed on cooling by a second transition to a different, non-collinear structure where the moments are rotated within the basal plane. Our results demonstrate that LaMn$_x$Sb$_2$ is a highly tunable material with six unique magnetically ordered phases, depending on T and x.
△ Less
Submitted 23 August, 2023;
originally announced August 2023.
-
Strong enhancement of magnetic ordering temperature and structural/valence transitions in EuPd3S4 under high pressure
Authors:
S. Huyan,
D. H. Ryan,
T. J. Slade,
B. Lavina,
G. C. Jose,
H. Wang,
J. M. Wilde,
R. A. Ribeiro,
J. Zhao,
W. Xie,
W. Bi,
E. E. Alp,
S. L. Bud'ko,
P. C. Canfield
Abstract:
We present a comprehensive study of the mixed valent compound, EuPd3S4, by electrical transport, X-ray diffraction, time-domain 151Eu synchrotron Mössbauer spectroscopy, and X-ray absorption spectroscopy measurements under high pressure. The electrical transport measurements show that the antiferromagnetic ordering temperature, TN, increases rapidly from 2.8 K at ambient pressure to 23.5 K at ~19…
▽ More
We present a comprehensive study of the mixed valent compound, EuPd3S4, by electrical transport, X-ray diffraction, time-domain 151Eu synchrotron Mössbauer spectroscopy, and X-ray absorption spectroscopy measurements under high pressure. The electrical transport measurements show that the antiferromagnetic ordering temperature, TN, increases rapidly from 2.8 K at ambient pressure to 23.5 K at ~19 GPa and plateaus between ~19 and ~29 GPa after which no anomaly associated with TN is detected. A pressure-induced first order structural transition from cubic to tetragonal is observed, with a rather broad coexistence region (~20 GPa to ~32 GPa) that corresponds to the TN plateau. Mössbauer spectroscopy measurements show a clear valence transition from approximately 50:50 Eu2+:Eu3+ to fully Eu3+ at ~28 GPa, consistent with the vanishing of the magnetic order at the same pressure. X-ray absorption data show a transition to a fully trivalent state at a similar pressure. Our results show that pressure first greatly enhances TN, most likely via enhanced hybridization between the Eu 4f states and the conduction band, and then, second, causes a structural phase transition that coincides with the conversion of the europium to a fully trivalent state.
△ Less
Submitted 28 June, 2023;
originally announced June 2023.
-
New insight into tuning magnetic phases of $R$Mn$_6$Sn$_6$ kagome metals
Authors:
Simon X. M. Riberolles,
Tianxiong Han,
Tyler J. Slade,
J. M. Wilde,
A. Sapkota,
Wei Tian,
Qiang Zhang,
D. L. Abernathy,
L. D. Sanjeewa,
S. L. Bud'ko,
P. C. Canfield,
R. J. McQueeney,
B. G. Ueland
Abstract:
Predicting magnetic ordering in kagome compounds offers the possibility of harnessing topological or flat-band physical properties through tuning of the magnetism. Here, we examine the magnetic interactions and phases of ErMn$_6$Sn$_6$ which belongs to a family of $R$Mn$_6$Sn$_6$, $R=$ Sc, Y, Gd--Lu, compounds with magnetic kagome Mn layers, triangular $R$ layers, and signatures of topological pro…
▽ More
Predicting magnetic ordering in kagome compounds offers the possibility of harnessing topological or flat-band physical properties through tuning of the magnetism. Here, we examine the magnetic interactions and phases of ErMn$_6$Sn$_6$ which belongs to a family of $R$Mn$_6$Sn$_6$, $R=$ Sc, Y, Gd--Lu, compounds with magnetic kagome Mn layers, triangular $R$ layers, and signatures of topological properties. Using results from single-crystal neutron diffraction and mean-field analysis, we find that ErMn$_6$Sn$_6$ sits close to the critical boundary separating the spiral-magnetic and ferrimagnetic ordered states typical for nonmagnetic versus magnetic $R$ layers, respectively. Finding interlayer magnetic interactions and easy-plane Mn magnetic anisotropy consistent with other members of the family, we predict the existence of a number of temperature and field dependent collinear, noncollinear, and noncoplanar magnetic phases. We show that thermal fluctuations of the Er magnetic moment, which act to weaken the Mn-Er interlayer magnetic interaction and quench the Er magnetic anisotropy, dictate magnetic phase stability. Our results provide a starting point and outline a multitude of possibilities for studying the behavior of Dirac fermions in $R$Mn$_6$Sn$_6$ compounds with control of the Mn spin orientation and real-space spin chirality.
△ Less
Submitted 29 May, 2024; v1 submitted 22 June, 2023;
originally announced June 2023.
-
Formation of a simple cubic antiferromagnet through charge ordering in a double Dirac material
Authors:
T. Berry,
V. C. Morano,
T. Halloran,
X. Zhang,
T. J. Slade,
A. Sapkota,
S. L. Budko,
W. Xie,
D. H. Ryan,
Z. Xu,
Y. Zhao,
J. W. Lynn,
T. Fennell,
P. C. Canfield,
C. L. Broholm,
T. M. McQueen
Abstract:
The appearance of spontaneous charge order in chemical systems is often associated with the emergence of novel, and useful, properties. Here we show through single crystal diffraction that the Eu ions in the mixed valent metal EuPd$_3$S$_4$ undergo long-range charge ordering at $T_{\mathrm{CO}} = 340 \mathrm{~K}$ resulting in simple cubic lattices of Eu$^{2+}$ ($J = 7/2$) and Eu$^{3+}$ ($J = 0$) i…
▽ More
The appearance of spontaneous charge order in chemical systems is often associated with the emergence of novel, and useful, properties. Here we show through single crystal diffraction that the Eu ions in the mixed valent metal EuPd$_3$S$_4$ undergo long-range charge ordering at $T_{\mathrm{CO}} = 340 \mathrm{~K}$ resulting in simple cubic lattices of Eu$^{2+}$ ($J = 7/2$) and Eu$^{3+}$ ($J = 0$) ions. As only one of the two sublattices has a non-magnetic ground state, the charge order results in the emergence of remarkably simple G-type antiferromagnetic order at $T_{\mathrm{N}} = 2.85(6) \mathrm{~K}$, observed in magnetization, specific heat, and neutron diffraction. Application of a $0.3 \mathrm{~T}$ field is sufficient to induce a spin flop transition to a magnetically polarized, but still charge ordered, state. Density functional theory calculations show that this charge order also modifies the electronic degeneracies present in the material: without charge order, EuPd$_3$S$_4$ is an example of a double Dirac material containing 8-fold degenerate electronic states, greater than the maximum degeneracy of six possible in molecular systems. The symmetry reduction from charge order transmutes 8-fold double Dirac states into 4-fold Dirac states, a degeneracy that can be preserved even in the presence of the magnetic order. Our results show not only how charge order can be used to produce interesting magnetic lattices, but also how it can be used to engineer controlled degeneracies in electronic states.
△ Less
Submitted 1 November, 2023; v1 submitted 3 March, 2023;
originally announced March 2023.
-
Orbital character of the spin-reorientation transition in TbMn$_6$Sn$_6$
Authors:
S. X. M. Riberolles,
Tyler J. Slade,
R. L. Dally,
P. M. Sarte,
Bing Li,
Tianxiong Han,
H. Lane,
C. Stock,
H. Bhandari,
N. J. Ghimire,
D. L. Abernathy,
P. C. Canfield,
J. W. Lynn,
B. G. Ueland,
R. J. McQueeney
Abstract:
Ferromagnetic (FM) order in a two-dimensional kagome layer is predicted to generate a topological Chern insulator without an applied magnetic field. The Chern gap is largest when spin moments point perpendicular to the kagome layer, enabling the capability to switch topological transport properties, such as the quantum anomalous Hall effect, by controlling the spin orientation. In TbMn$_{6}$Sn…
▽ More
Ferromagnetic (FM) order in a two-dimensional kagome layer is predicted to generate a topological Chern insulator without an applied magnetic field. The Chern gap is largest when spin moments point perpendicular to the kagome layer, enabling the capability to switch topological transport properties, such as the quantum anomalous Hall effect, by controlling the spin orientation. In TbMn$_{6}$Sn$_{6}$, the uniaxial magnetic anisotropy of the Tb$^{3+}$ ion is effective at generating the Chern state within the FM Mn kagome layers while a spin-reorientation (SR) transition to easy-plane order above $T_{SR}=310$ K provides a mechanism for switching. Here, we use inelastic neutron scattering to provide key insights into the fundamental nature of the SR transition. The observation of two Tb excitations, which are split by the magnetic anisotropy energy, indicates an effective two-state orbital character for the Tb ion, with a uniaxial ground state and an isotropic excited state. The simultaneous observation of both modes below $T_{SR}$ confirms that orbital fluctuations are slow on magnetic and electronic time scales $<$ ps and act as a spatially-random orbital alloy. A thermally-driven critical concentration of isotropic Tb ions triggers the SR transition.
△ Less
Submitted 20 March, 2023; v1 submitted 2 March, 2023;
originally announced March 2023.
-
Chiral and flat-band magnetic cluster excitations in a ferromagnetic kagome metal
Authors:
S. X. M. Riberolles,
Tyler J. Slade,
Tianxiong Han,
Bing Li,
D. L. Abernathy,
P. C. Canfield,
B. G. Ueland,
P. P. Orth,
Liqin Ke,
R. J. McQueeney
Abstract:
TbMn6Sn6 is a metallic ferrimagnet that displays signatures of band topology arising from a combination of uniaxial ferromagnetism and spin-orbit coupling within its Mn kagome layers. Whereas the low energy magnetic excitations can be described as collective spin waves using a local moment Heisenberg model, sharply defined optical and flat-band collective magnon modes are not observed. In their pl…
▽ More
TbMn6Sn6 is a metallic ferrimagnet that displays signatures of band topology arising from a combination of uniaxial ferromagnetism and spin-orbit coupling within its Mn kagome layers. Whereas the low energy magnetic excitations can be described as collective spin waves using a local moment Heisenberg model, sharply defined optical and flat-band collective magnon modes are not observed. In their place, we find overdamped chiral and flat-band spin correlations that are localized to hexagonal plaquettes within the kagome layer.
△ Less
Submitted 6 February, 2023;
originally announced February 2023.
-
Mn(Pt$_{1-x}$Pd$_{x}$)$_5$P: Isovalent Tuning of Mn Sublattice Magnetic Order
Authors:
Tyler J. Slade,
Ranuri S. Dissanayaka Mudiyanselage,
Nao Furukawa,
Tanner R. Smith,
Juan Schmidt,
Lin-Lin Wang,
Chang-Jong Kang,
Kaya Wei,
Zhixue Shu,
Tai Kong,
Ryan Baumbach,
Gabriel Kotliar,
Sergey L. Budko,
Weiwei Xie,
Paul C. Canfield
Abstract:
We report the growth and characterization of MnPd$_5$P, a ferromagnet with T$_C$ $\approx$ 295 K, and conduct a substitutional study with its antiferromagnetic analogue MnPt$_5$P. We grow single crystals of MnPd$_5$P and Mn(Pt$_{1-x}$Pd$_x$)$_5$P by adding Mn into (Pt$_{1-x}$Pd$_{x}$)-P based melts. All compounds in the family adopt the layered anti-CeCoIn$_5$ structure with space group P4/mmm, an…
▽ More
We report the growth and characterization of MnPd$_5$P, a ferromagnet with T$_C$ $\approx$ 295 K, and conduct a substitutional study with its antiferromagnetic analogue MnPt$_5$P. We grow single crystals of MnPd$_5$P and Mn(Pt$_{1-x}$Pd$_x$)$_5$P by adding Mn into (Pt$_{1-x}$Pd$_{x}$)-P based melts. All compounds in the family adopt the layered anti-CeCoIn$_5$ structure with space group P4/mmm, and EDS and XRD results indicate that MnPt$_5$P and MnPd$_5$P form a solid solution. Based on magnetization and resistance data, we construct a T-x phase diagram for Mn(Pt$_{1-x}$Pd$_x$)$_5$P and demonstrate the antiferromagnetic order found in MnPt$_5$P is extraordinarily sensitive to Pd substitution. At low Pd fractions (x $<$ 0.010), the single antiferromagnetic transition in pure MnPt$_5$P splits into a higher temperature ferromagnetic transition followed on cooling by a lower temperature ferromagnetic to antiferromagnetic transition and then by a re-entrant antiferromagnetic to ferromagnetic transition at lower temperatures. The antiferromagnetic region makes up a bubble that persists to x $\approx$ 0.009 for T $\approx$ 150 K, with all samples x $<$ 0.009 recovering their initial ferromagnetic state with further cooling to base temperature. Over the same low x range we find a non-monotonic change in the room temperature unit cell volume, further suggesting that pure MnPt$_5$P is close to an instability. Once x $>$ 0.010, Mn(Pt$_{1-x}$Pd$_x$)$_5$P undergoes a single ferromagnetic transition. The Curie temperature increases rapidly with x, rising from T$_C$ $\approx$ 197 K at x = 0.013 to a maximum of T$_C$ $\approx$ 312 K for x $\approx$ 0.62, and then falls back to T$_C$ $\approx$ 295 K for pure MnPd$_5$P (x = 1). Given that Pt and Pd are isoelectronic, this work raises questions as to the origin of the extreme sensitivity of the magnetic ground state in MnPt$_5$P upon introducing Pd.
△ Less
Submitted 3 November, 2022;
originally announced November 2022.
-
High Temperature Ferromagnetism in Cr$_{1+x}$Pt$_{5-x}$P
Authors:
Tyler J. Slade,
Nao Furukawa,
Tanner R. Smith,
Juan Schmidt,
Ranuri S. Dissanayaka Mudiyanselage,
Lin-Lin Wang,
Weiwei Xie,
Sergey L. Budko,
Paul C. Canfield
Abstract:
We present the growth and basic magnetic and transport properties of Cr$_{1+x}$Pt$_{5-x}$P. We show that single crystals can readily be grown from a high-temperature solution created by adding dilute quantities of Cr to Pt-P based melts. Like other 1-5-1 compounds, Cr$_{1+x}$Pt$_{5-x}$P adopts a tetragonal P4/mmm structure composed face-sharing CrPt$_3$ like slabs that are broken up along the c-ax…
▽ More
We present the growth and basic magnetic and transport properties of Cr$_{1+x}$Pt$_{5-x}$P. We show that single crystals can readily be grown from a high-temperature solution created by adding dilute quantities of Cr to Pt-P based melts. Like other 1-5-1 compounds, Cr$_{1+x}$Pt$_{5-x}$P adopts a tetragonal P4/mmm structure composed face-sharing CrPt$_3$ like slabs that are broken up along the c-axis by sheets of P atoms. EDS and X-ray diffraction measurements both suggest Cr$_{1+x}$Pt$_{5-x}$P has mixed occupancy between Cr and Pt atoms, similar to what is found in the closely related compound CrPt$_3$, giving real compositions of Cr$_{1.5}$Pt$_{4.5}$P (x = 0.5). We report that Cr$_{1.5}$Pt$_{4.5}$P orders ferromagnetically at T$_C$ = 464.5 K with a saturated moment of $\approx$ 2.1 $μ_{\textit{B}}$/Cr at 1.8 K. Likely owing to the strong spin-orbit coupling associated with the large quantity of high Z Pt atoms, Cr$_{1.5}$Pt$_{4.5}$P has exceptionally strong planar anisotropy with estimated anisotropy fields of 345 kOe and 220 kOe at 1.8 K and 300 K respectively. The resistance of Cr$_{1.5}$Pt$_{4.5}$P has a metallic temperature dependence with relatively weak magnetoresistance. Electronic band structure calculations show that CrPt$_5$P has a large peak in the density of states near the Fermi level which is split into spin majority and minority bands in the ferromagnetic state. Furthermore, the calculations suggest substantial hybridization between Cr-3d and Pt-5d states near the Fermi level, in agreement with the experimentally measured anisotropy.
△ Less
Submitted 2 November, 2022;
originally announced November 2022.
-
Low temperature competing magnetic energy scales in the topological ferrimagnet TbMn6Sn6
Authors:
S. X. M. Riberolles,
Tyler J. Slade,
D. L. Abernathy,
G. E. Granroth,
Bing Li,
Y. Lee,
P. C. Canfield,
B. G. Ueland,
Liqin Ke,
R. J. McQueeney
Abstract:
TbMn6Sn6 is a metallic ferrimagnet displaying signatures of both topological electrons and topological magnons arising from ferromagnetism and spin-orbit coupling within its Mn kagome layers. Inelastic neutron scattering measurements find strong ferromagnetic (FM) interactions within the Mn kagome layer and reveal a magnetic bandwidth of ~230 meV. The low-energy magnetic excitations are characteri…
▽ More
TbMn6Sn6 is a metallic ferrimagnet displaying signatures of both topological electrons and topological magnons arising from ferromagnetism and spin-orbit coupling within its Mn kagome layers. Inelastic neutron scattering measurements find strong ferromagnetic (FM) interactions within the Mn kagome layer and reveal a magnetic bandwidth of ~230 meV. The low-energy magnetic excitations are characterized by strong FM Mn-Mn and antiferromagnetic (AFM) Mn-Tb interlayer magnetic couplings. We observe weaker, competing long-range FM and AFM Mn-Mn interlayer interactions similar to those driving helical magnetism in the YMn6Sn6 system. Combined with density-functional theory calculations, we find that competing Mn-Mn interlayer magnetic interactions occur in all RMn6Sn6 compounds with R= Y, Gd-Lu, resulting in magnetic instabilities and tunability when Mn-R interactions are weak. In the case of TbMn6Sn6, strong AFM Mn-Tb coupling ensures a highly stable three-dimensional ferrimagnetic network.
△ Less
Submitted 24 June, 2022; v1 submitted 27 October, 2021;
originally announced October 2021.
-
A Low Temperature Structural Transition in Canfieldite, Ag$_8$SnS$_6$, Single Crystals
Authors:
Tyler J. Slade,
Volodymyr Gvozdetskyi,
John M. Wilde,
Andreas Kreyssig,
Elena Gati,
Lin-Lin Wang,
Yaroslav Mudryk,
Raquel A. Ribeiro,
Vitalij K. Pecharsky,
Julia V. Zaikina,
Sergey L. Budko,
Paul C. Canfield
Abstract:
Canfieldite, Ag$_8$SnS$_6$, is a semiconducting mineral notable for its high ionic conductivity, photosensitivity, and low thermal conductivity. We report the solution growth of large single crystals of Ag$_8$SnS$_6$ of mass up to 1 g from a ternary Ag-Sn-S melt. On cooling from high temperature, Ag$_8$SnS$_6$ undergoes a known cubic (F-43m) to orthorhombic (Pna2$_1$) phase transition at…
▽ More
Canfieldite, Ag$_8$SnS$_6$, is a semiconducting mineral notable for its high ionic conductivity, photosensitivity, and low thermal conductivity. We report the solution growth of large single crystals of Ag$_8$SnS$_6$ of mass up to 1 g from a ternary Ag-Sn-S melt. On cooling from high temperature, Ag$_8$SnS$_6$ undergoes a known cubic (F-43m) to orthorhombic (Pna2$_1$) phase transition at $\approx$ 460 K. By studying the magnetization and thermal expansion between 5-300 K, we discover a second structural transition at $\approx$ 120 K. Single crystal X-ray diffraction reveals the low temperature phase adopts a different orthorhombic structure with space group Pmn2$_1$ (a = 7.6629(5) Å, b = 7.5396(5) Å, c = 10.6300(5) Å, Z = 2 at 90 K) that is isostructural to the room temperature forms of the related Se-based compounds Ag$_8$SnSe$_6$ and Ag$_8$GeSe$_6$. The 120 K transition is first-order and has a large thermal hysteresis. Based on magnetization and thermal expansion data, the room temperature polymorph can be kinetically arrested into a metastable state by rapidly cooling to temperatures below 40 K. We lastly compare the room and low temperature forms of Ag$_8$SnS$_6$ with its argyrodite analogues, Ag$_8$TQ$_6$ (T = Si, Ge, Sn; Q = S, Se), and identify a trend relating the preferred structures to the unit cell volume, suggesting smaller phase volume favors the Pna2$_1$ arrangement. We support this picture by showing that the transition to the Pmn2$_1$ phase is avoided in Ge alloyed Ag$_8$Sn$_{1-x}$Ge$_x$S$_6$ samples as well as pure Ag$_8$GeS$_6$.
△ Less
Submitted 14 October, 2021;
originally announced October 2021.
-
Comment on "Unconventional enhancement of ferromagnetic interactions in Cd-doped GdFe2Zn20 single crystals studied by ESR and 57Fe Mossbauer spectroscopies"
Authors:
Paul C. Canfield,
Sergey L. Bud'ko,
Andriy Palasyuk,
Tyler J. Slade
Abstract:
In the recent publication, Phys. Rev. B 102, 144420 (2020), Cabrera-Baez et al. present a study of the effects of Cd-substitution for Zn in the ferromagnetic compound GdFe2Zn20. As part of this paper, they claim that for GdFe2Zn18.6Cd1.4 the effective moment of Gd is reduced by 25% and the saturated moment of Gd is reduced by over 40%. We regrew representative members of the GdFe2Zn(20-x)Cdx serie…
▽ More
In the recent publication, Phys. Rev. B 102, 144420 (2020), Cabrera-Baez et al. present a study of the effects of Cd-substitution for Zn in the ferromagnetic compound GdFe2Zn20. As part of this paper, they claim that for GdFe2Zn18.6Cd1.4 the effective moment of Gd is reduced by 25% and the saturated moment of Gd is reduced by over 40%. We regrew representative members of the GdFe2Zn(20-x)Cdx series and did not find any such reductions. In addition, we measured several crystals from the growth batch that was used by Cabrera-Baez et al. and did not see such reductions. Although there is a modest increase in TC with Cd substitution, there is no significant change in the Gd effective moment or the saturated moment associated with the low temperature ferromagnetic state.
△ Less
Submitted 8 April, 2021;
originally announced April 2021.
-
Magnetic order in van der Waals antiferromagnet CrPS4: anisotropic H-T phase diagrams and effects of pressure
Authors:
Sergey L. Bud'ko,
Elena Gati,
Tyler J. Slade,
Paul C. Canfield
Abstract:
Single crystalline samples of the van der Waals antiferromagnet CrPS4 were studied by measurements of specific heat and comprehensive anisotropic temperature- and magnetic field-dependent magnetization. In addition, measurements of the heat capacity and magnetization were performed under pressures of up to ~21 kbar and ~14 kbar respectively. At ambient pressure, two magnetic transitions are observ…
▽ More
Single crystalline samples of the van der Waals antiferromagnet CrPS4 were studied by measurements of specific heat and comprehensive anisotropic temperature- and magnetic field-dependent magnetization. In addition, measurements of the heat capacity and magnetization were performed under pressures of up to ~21 kbar and ~14 kbar respectively. At ambient pressure, two magnetic transitions are observed, second order from a paramagnetic to an antiferromagnetic state at TN ~ 37 K, and a first-order spin reorientation transition at T* ~ 34 K. Anisotropic H - T phase diagrams were constructed using the M(T,H) data. As pressure is increased, TN is weakly suppressed with dTN/dP ~ -0.1 K/kbar. T*, on the other hand, is suppressed quite rapidly, with dT*/dP ~ -2 K/kbar, extrapolating to a possible quantum phase transition at Pc ~ 15 kbar.
△ Less
Submitted 25 May, 2021; v1 submitted 23 February, 2021;
originally announced February 2021.