Quantifying the effect of oxygen on micro-mechanical properties of a near-alpha titanium alloy
Authors:
H. M. Gardner,
P. Gopon,
C. M. Magazzeni,
A. Radecka,
K. Fox,
D. Rugg,
J. Wade,
D. E. J. Armstrong,
M. P. Moody,
P. A. J. Bagot
Abstract:
Atom probe tomography (APT), electron probe microanalysis (EPMA) and nanoindentation were used to characterise the oxygen-rich layer on an in-service jet engine compressor disc, manufactured from the titanium alloy TIMETAL 834. Oxygen ingress was quantified and related to changes in mechanical properties through nanoindentation studies. The relationship between oxygen concentration, microstructure…
▽ More
Atom probe tomography (APT), electron probe microanalysis (EPMA) and nanoindentation were used to characterise the oxygen-rich layer on an in-service jet engine compressor disc, manufactured from the titanium alloy TIMETAL 834. Oxygen ingress was quantified and related to changes in mechanical properties through nanoindentation studies. The relationship between oxygen concentration, microstructure, crystal orientation and hardness has been explored through correlative hardness map**, EPMA and electron backscatter diffraction (EBSD). The role of microstructure on oxygen ingress has been studied and oxygen ingress along a potential alpha/ beta interface was directly observed on the nanoscale using APT.
△ Less
Submitted 10 September, 2020;
originally announced September 2020.
-
The Kinetics of Primary Alpha Plate Growth in Titanium Alloys
Authors:
Abigail K Ackerman,
Alexander J. Knowles,
Hazel M. Gardner,
Andre A N Nemeth,
Ioannis Bantounas,
Anna Radecka,
Michael P. Moody,
Paul A. J. Bagot,
Roger C. Reed,
David Rugg,
David Dye
Abstract:
The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the beta are examined, comparing model to experiment. The plate growth velocity depends sensitively both on the diffusivity D(T) of the rate-limiting species and on the supersaturation around the growing plate. These result in a maxima in growth velocity around 40 K below the transus, once sufficient supersaturation is availab…
▽ More
The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the beta are examined, comparing model to experiment. The plate growth velocity depends sensitively both on the diffusivity D(T) of the rate-limiting species and on the supersaturation around the growing plate. These result in a maxima in growth velocity around 40 K below the transus, once sufficient supersaturation is available to drive plate growth. In Ti-6246, the plate growth velocity was found to be around 0.32 um min-1 at 850 oC, which was in good agreement with the model prediction of 0.36 um min-1 . The solute field around the growing plates, and the plate thickness, was found to be quite variable, due to the intergrowth of plates and soft im**ement. This solute field was found to extend to up to 30 nm, and the interface concentration in the beta was found to be around 6.4 at.% Mo. It was found that increasing O content will have minimal effect on the plate lengths expected during continuous cooling; in contrast, Mo approximately doubles the plate lengths obtained for every 2 wt.% Mo reduction. Alloys using V as the beta stabiliser instead of Mo are expected to have much faster plate growth kinetics at nominally equivalent V contents. These findings will provide a useful tool for the integrated design of alloys and process routes to achieve tailored microstructures.
△ Less
Submitted 31 July, 2019; v1 submitted 24 May, 2018;
originally announced May 2018.
-
Characterizing solute hydrogen and hydrides in pure and alloyed titanium at the atomic scale
Authors:
Yanhong Chang,
Andrew J. Breen,
Zahra Tarzimoghadam,
Philipp Kürnsteiner,
Hazel Gardner,
Abigail Ackerman,
Anna Radecka,
Paul A. J. Bagot,
Wenjun Lu,
Tong Li,
Eric A. Jägle,
Michael Herbig,
Leigh T. Stephenson,
Michael P. Moody,
David Rugg,
David Dye,
Dirk Ponge,
Dierk Raabe,
Baptiste Gault
Abstract:
Ti has a high affinity for hydrogen and is a typical hydride formers. Ti-hydride are brittle phases which probably cause premature failure of Ti-alloys. Here, we used atom probe tomography and electron microscopy to investigate the hydrogen distribution in a set of specimens of commercially pure Ti, model and commercial Ti-alloys. Although likely partly introduced during specimen preparation with…
▽ More
Ti has a high affinity for hydrogen and is a typical hydride formers. Ti-hydride are brittle phases which probably cause premature failure of Ti-alloys. Here, we used atom probe tomography and electron microscopy to investigate the hydrogen distribution in a set of specimens of commercially pure Ti, model and commercial Ti-alloys. Although likely partly introduced during specimen preparation with the focused-ion beam, we show formation of Ti-hydrides along α grain boundaries and α/\b{eta} phase boundaries in commercial pure Ti and α+\b{eta} binary model alloys. No hydrides are observed in the α phase in alloys with Al addition or quenched-in Mo supersaturation.
△ Less
Submitted 11 March, 2018;
originally announced March 2018.