Mn2V0.5Co0.5Z (Z= Ga, Al) Heusler alloys: Fully compensated ferrimagnets with high Tc and compensation temperature
Authors:
P V Midhunlal,
J Arout Chelvane,
D Prabhu,
Raghavan Gopalan,
Harish Kumar N
Abstract:
High TC fully compensated ferrimagnets are potential candidates for spin transfer torque based spintronic devices. We report the structural and magnetic properties of high TC fully compensated ferrimagnets Mn2V0.5Co0.5Z where Z is Ga, Al, in the melt spun ribbon and arc melted bulk form. While the parent alloys Mn2YZ where Y is V, Co and Z is Ga, Al exhibits a magnetic moment value around 2 muB pe…
▽ More
High TC fully compensated ferrimagnets are potential candidates for spin transfer torque based spintronic devices. We report the structural and magnetic properties of high TC fully compensated ferrimagnets Mn2V0.5Co0.5Z where Z is Ga, Al, in the melt spun ribbon and arc melted bulk form. While the parent alloys Mn2YZ where Y is V, Co and Z is Ga, Al exhibits a magnetic moment value around 2 muB per f.u, the Mn2V0.5Co0.5Ga alloy exhibits room temperature nearly fully compensated moment value of 0.09 and 0.13 muB per f.u. in the bulk and ribbon form respectively. For Mn2V0.5Co0.5Al this turned out to be 0.04 and 0.08 muB per f.u. In Contrast to the bulk sample's Neel P type ferrimagnetic behaviour, ribbon samples exhibit Neel N type ferrimagnetic characteristic with a high compensation temperature of 420 K for Ga alloy and 275 K for Al alloy. The observed TC values are more than 640 K for all samples. The differences in the magnetic properties of arc melted and melt spun alloys indicates that even a slight variation in stoichiometry and sample preparation method can influence the physical properties of a compensated system.
△ Less
Submitted 3 December, 2018;
originally announced December 2018.
Near total magnetic moment compensation without reduction in T_C of Mn_2 V_0.5 Co_0.5 Z (Z=Ga,Al) Heusler compounds
Authors:
Midhunlal P V,
Arout Chelvane J,
Arjun Krishnan U M,
Harish Kumar N
Abstract:
Mn_2V_1-xCo_xZ (Z=Ga,Al and x=0, 0.25, 0.5, 0.75, 1) Heusler compounds have been synthesized to investigate the effect of Co substitution at the V site on the magnetic moment and Curie temperatures of half-metallic ferrimagnets Mn_2VGa and Mn_2VAl. The Co substituted compounds show a non linear decrease in lattice parameter without altering the crystal structure of the parent compounds. The end me…
▽ More
Mn_2V_1-xCo_xZ (Z=Ga,Al and x=0, 0.25, 0.5, 0.75, 1) Heusler compounds have been synthesized to investigate the effect of Co substitution at the V site on the magnetic moment and Curie temperatures of half-metallic ferrimagnets Mn_2VGa and Mn_2VAl. The Co substituted compounds show a non linear decrease in lattice parameter without altering the crystal structure of the parent compounds. The end members Mn_2VGa and Mn_2CoGa have the saturation magnetization of 1.80 μ_B/f.u and 2.05 μ_B/f.u respectively whereas for the Mn_2V_0.5Co_0.5Ga compound, a near total magnetic moment compensation (0.10 μ_B/f.u) was observed due to the ferrimagnetic coupling of Mn with parallelly aligned V and Co. The Co substituted Mn_2VAl has also shown the similar trend with compensated magnetic moment value of 0.06 μ_B/f.u for x=0.5. The Curie temperatures of the compounds including the x=0.5 composition are well above the room temperature (more than 700 K) which is in sharp contrast to the earlier reported values of 171 K for the (MnCo)VGa and 105 K for the (MnCo)VAl compounds (substitution at the Mn site). The magnetic moment compensation without significant reduction in T_C indicates that the V site substitution of Co does not weaken the magnetic interaction in Mn_2VZ (Z=Ga, Al) compounds which is in contrary to the earlier experimental reports on Mn site substitution.
△ Less
Submitted 26 October, 2017;
originally announced October 2017.