Insights on induced magnetic moments and spin textures in synthetic ferrimagnetic Pt/Co/Gd heterolayers
Authors:
J. Brandão,
P. C. Carvalho,
I. P. Miranda,
T. J. A. Mori,
F. Béron,
A. Bergman,
H. M. Petrilli,
A. B. Klautau,
J. C. Cezar
Abstract:
To develop new devices based on synthetic ferrimagnetic (S-FiM) heterostructures, understanding the material's physical properties is pivotal. Here, the induced magnetic moment (IMM), magnetic exchange-coupling, and spin textures were investigated at room-temperature in Pt/Co/Gd multilayers using a multiscale approach. The magnitude and direction of the IMM were interpreted experimentally and theo…
▽ More
To develop new devices based on synthetic ferrimagnetic (S-FiM) heterostructures, understanding the material's physical properties is pivotal. Here, the induced magnetic moment (IMM), magnetic exchange-coupling, and spin textures were investigated at room-temperature in Pt/Co/Gd multilayers using a multiscale approach. The magnitude and direction of the IMM were interpreted experimentally and theoretically in the framework of both X-ray magnetic circular dichroism (XMCD) and density functional theory (DFT). The results demonstrate that the IMM transferred by Co across the Gd paramagnetic (PM) thickness leads to a flipped spin state (FSS) within the Gd layers, in which their magnetic moments couple antiparallel/parallel with the ferromagnetic (FM) Co near/far from the Co/Gd interface, respectively. For the Pt, in both Pt/Co and Gd/Pt interfaces the IMM follows the same direction as the Co magnetic moment, with negligible IMM in the Gd/Pt interface. Additionally, zero-field spin spirals were imaged using scanning transmission X-ray microscopy (STXM), while micromagnetic simulations employed to unfold the interactions stabilizing the FiM configurations, where the existence of a sizable Dzyaloshinskii-Moriya interaction is demonstrated to be crucial for the formation of those spin textures. Our outcomes may add fundamental physical and technological aspects for using FiM films in antiferromagnetic spintronic devices.
△ Less
Submitted 6 April, 2024;
originally announced April 2024.
-
Bulk and Interface Effects Based on Rashba-Like States in Ti and Ru Nanoscale-Thick Films: Implications for Orbital-Charge Conversion in Spintronic Devices
Authors:
Eduardo S. Santos,
José E. Abrão,
Jefferson L. Costa,
João G. S. Santos,
Kacio R. Mello,
Andriele S. Vieira,
Tulio C. R. Rocha,
Thiago J. A. Mori,
Rafael O. Cunha,
Joaquim B. S. Mendes,
Antonio Azevedo
Abstract:
In this work, employing spin-pum** techniques driven by both ferromagnetic resonance (SP-FMR) and longitudinal spin Seebeck effect (LSSE) to manipulate and direct observe orbital currents, we investigated the volume conversion of spin-orbital currents into charge-current in YIG(100nm)/Pt(2nm)/NM2 structures, where NM2 represents Ti or Ru. While the YIG/Ti bilayer displayed a negligible SP-FMR si…
▽ More
In this work, employing spin-pum** techniques driven by both ferromagnetic resonance (SP-FMR) and longitudinal spin Seebeck effect (LSSE) to manipulate and direct observe orbital currents, we investigated the volume conversion of spin-orbital currents into charge-current in YIG(100nm)/Pt(2nm)/NM2 structures, where NM2 represents Ti or Ru. While the YIG/Ti bilayer displayed a negligible SP-FMR signal, the YIG/Pt/Ti structure exhibited a significantly stronger signal attributed to the orbital Hall effect of Ti. Substituting the Ti layer with Ru revealed a similar phenomenon, wherein the effect is ascribed to the combined action of both spin and orbital Hall effects. Furthermore, we measured the SP-FMR signal in the YIG/Pt(2)/Ru(6)/Ti(6) and YIG/Pt(2)/Ti(6)/Ru(6) heterostructures by just altering the stack order of Ti and Ru layers, where the peak value of the spin pum** signal is larger for the first sample. To verify the influence on the oxidation of Ti and Ru films, we studied a series of thin films subjected to controlled and natural oxidation. As Cu and CuOx is a system that is already known to be highly influenced by oxidation, this metal was chosen to carry out this study. We investigated these samples using SP-FMR in YIG/Pt(2)/CuOx(tCu) and X-ray absorption spectroscopy and concluded that samples with natural oxidation of Cu exhibit more significant results than those when the CuOx is obtained by reactive sputtering. In particular, samples where the Cu layer is naturally oxidized exhibit a Cu2O-rich phase. Our findings help to elucidate the mechanisms underlying the inverse orbital Hall and inverse orbital Rashba-Edelstein-like effects. These insights indeed contribute to the advancement of devices that rely on orbital-charge conversion.
△ Less
Submitted 24 April, 2024; v1 submitted 31 January, 2024;
originally announced February 2024.
-
The zero-field-cooled exchange bias effect in phase-segregated La$_{2-x}$A$_{x}$CoMnO$_{6-δ}$ (A = Ba, Ca, Sr; x = 0, 0.5)
Authors:
L. T. Coutrim,
D. Rigitano,
C. Macchiutti,
T. J. A. Mori,
R. Lora-Serrano,
E. Granado,
E. Sadrollahi,
F. J. Litterst,
M. B. Fontes,
E. Baggio-Saitovitch,
E. M. Bittar,
L. Bufaiçal
Abstract:
In the zero-field-cooled exchange bias (ZEB) effect the unidirectional magnetic anisotropy is set at low temperatures even when the system is cooled in the absence of external magnetic field. La$_{1.5}$Sr$_{0.5}$CoMnO$_{6}$ stands out as presenting the largest ZEB reported so far, while for La$_{1.5}$Ca$_{0.5}$CoMnO$_{6}$ the exchange bias field ($H_{EB}$) is one order of magnitude smaller. Here w…
▽ More
In the zero-field-cooled exchange bias (ZEB) effect the unidirectional magnetic anisotropy is set at low temperatures even when the system is cooled in the absence of external magnetic field. La$_{1.5}$Sr$_{0.5}$CoMnO$_{6}$ stands out as presenting the largest ZEB reported so far, while for La$_{1.5}$Ca$_{0.5}$CoMnO$_{6}$ the exchange bias field ($H_{EB}$) is one order of magnitude smaller. Here we show that La$_{1.5}$Ba$_{0.5}$CoMnO$_{6}$ also exhibits a pronounced shift of its magnetic hysteresis loop, with intermediate $H_{EB}$ value in respect to Ca- and Sr-doped samples. In order to figure out the microscopic mechanisms responsible for this phenomena, these compounds were investigated by means of synchrotron X-ray powder diffraction, Raman spectroscopy, muon spin rotation and relaxation, AC and DC magnetization, X-ray absorption spectroscopy (XAS) and X-ray magnetic circular dichroism (XMCD). The parent compound La$_{2}$CoMnO$_{6}$ was also studied for comparison, as a reference of a non-ZEB material. Our results show that the Ba-, Ca- and Sr-doped samples present a small amount of phase segregation, and that the ZEB effect is strongly correlated to the system's structure. We also observed that mixed valence states Co$^{2+}$/Co$^{3+}$ and Mn$^{4+}$/Mn$^{3+}$ are already present at the La$_{2}$CoMnO$_{6}$ parent compound, and that Ba$^{2+}$/Ca$^{2+}$/Sr$^{2+}$ partial substitution at La$^{3+}$ site leads to a large increase of Co average valence, with a subtle augmentation of Mn formal valence. Estimates of the Co and Mn valences from the $L$-edge XAS indicate the presence of oxygen vacancies in all samples (0.05$\leq δ\leq$0.1). Our XMCD results show a great decrease of Co moment for the doped compounds, and indicate that the shift of the hysteresis curves for these samples is related to uncompensated antiferromagnetic coupling between Co and Mn.
△ Less
Submitted 11 September, 2019;
originally announced September 2019.
-
The distribution of oxygen at the Ni81Fe19/Ta interface
Authors:
T. J. A. Mori,
R. D. D. Pace,
W. H. Flores,
M. Carara,
L. F. Schelp,
L. S. Dorneles
Abstract:
The knowledge of how oxygen atoms are distributed at a magnetic-metal / oxide, or magnetic-metal / non-magnetic-metal interface, can be an useful tool to optimize device production. Multilayered Ni81Fe19 / Ta samples consisting of 15 bilayers of 2.5 nm each, grown onto glass substrates by magnetron sputtering from Ni81Fe19 and Ta targets, have been investigated. X-ray absorption near edge structur…
▽ More
The knowledge of how oxygen atoms are distributed at a magnetic-metal / oxide, or magnetic-metal / non-magnetic-metal interface, can be an useful tool to optimize device production. Multilayered Ni81Fe19 / Ta samples consisting of 15 bilayers of 2.5 nm each, grown onto glass substrates by magnetron sputtering from Ni81Fe19 and Ta targets, have been investigated. X-ray absorption near edge structure, extended X-Ray absorption fine structure, small angle X-ray diffraction, and simulations, were used to characterize the samples. Oxygen atoms incorporated onto Ni81Fe19 films during O2 exposition are mainly bonded to Fe atoms. This partial oxidation of the Ni81Fe19 surface works as a barrier to arriving Ta atoms, preventing intermixing at the Ni81Fe19 / Ta interface. The reduction of the Ni81Fe19 surface by the formation of TaO x is observed.
△ Less
Submitted 27 January, 2019;
originally announced January 2019.
-
Direct detection of induced magnetic moment and efficient spin-to-charge conversion in graphene/ferromagnetic structures
Authors:
J. B. S. Mendes,
O. Alves Santos,
T. Chagas,
R. Magalhães-Paniago,
T. J. A. Mori,
J. Holanda,
L. M. Meireles,
R. G. Lacerda,
A. Azevedo,
S. M. Rezende
Abstract:
This article shows that the spin-to-charge current conversion in single-layer graphene (SLG) by means of the inverse Rashba-Edelstein effect (IREE) is made possible with the integration of this remarkable 2D-material with the unique ferrimagnetic insulator yttrium iron garnet (YIG = $Y_{3}Fe_{5}O_{12}$) as well as with the ferromagnetic metal permalloy (Py = $Ni_{81}Sb_{19}$). By means of X-ray ab…
▽ More
This article shows that the spin-to-charge current conversion in single-layer graphene (SLG) by means of the inverse Rashba-Edelstein effect (IREE) is made possible with the integration of this remarkable 2D-material with the unique ferrimagnetic insulator yttrium iron garnet (YIG = $Y_{3}Fe_{5}O_{12}$) as well as with the ferromagnetic metal permalloy (Py = $Ni_{81}Sb_{19}$). By means of X-ray absorption spectroscopy (XAS) and magnetic circular dichroism (XMCD) techniques, we show that the carbon atoms of the SLG acquires an induced magnetic moment due to the proximity effect with the magnetic layer. The spin currents are generated in the magnetic layer by spin pum** from microwave driven ferromagnetic resonance and are detected by a dc voltage along the graphene layer, at room temperature. The spin-to-charge current conversion, occurring at the graphene layer, is explained by the extrinsic spin-orbit interaction (SOI) induced by the proximity effect with the ferromagnetic layer. The results obtained for the SLG/YIG and SLG/Py systems confirm very similar values for the IREE parameter, which are larger than the values reported in previous studies for SLG. We also report systematic investigations of the electronic and magnetic properties of the SLG/YIG by means of scanning tunneling microscopy (STM).
△ Less
Submitted 2 December, 2018;
originally announced December 2018.
-
Observation of magnetic skyrmions in unpatterned symmetric multilayers at room temperature and zero magnetic field
Authors:
J. Brandão,
D. A. Dugato,
R. L. Seeger,
J. C. Denardin,
T. J. A. Mori,
J. C. Cezar
Abstract:
Magnetic skyrmions are promising candidates for the next generation of spintronic devices due to their small size and topologically protected structure. One challenge for using these magnetic states in applications lies on controlling the nucleation process and stabilization that usually requires an external force. Here, we report on the evidence of skyrmions in unpatterned symmetric Pd/Co/Pd mult…
▽ More
Magnetic skyrmions are promising candidates for the next generation of spintronic devices due to their small size and topologically protected structure. One challenge for using these magnetic states in applications lies on controlling the nucleation process and stabilization that usually requires an external force. Here, we report on the evidence of skyrmions in unpatterned symmetric Pd/Co/Pd multilayers at room temperature without prior application of neither electric current nor magnetic field. By decreasing the ferromagnetic interlayer thickness, the tuning of the physical properties across the ferromagnetic/non-magnetic interface gives rise to a transition from worm like domains patterns to isolated skyrmions as demonstrated by magnetic force microscopy. On the direct comparison of the measured and simulated skyrmions size, the quantitative interfacial Dzyaloshinskii-Moriya interaction (iDMI) was estimated, reveling that isolated skyrmions are just stabilized at zero magnetic field for low values of iDMI. Our findings provide new insights towards the use of stabilized skyrmions for room temperature devices in nominally symmetric multilayers.
△ Less
Submitted 17 October, 2018;
originally announced October 2018.