Adsorption of Gases on Ti3C2Tx MXene: Implications from X-ray Photoelectron Spectroscopy
Authors:
Lars-Åke Näslund,
Esko Kokkonen,
Martin Magnuson
Abstract:
One of the most explored MXenes is the Ti3C2Tx, where Tx is designated to inherently formed termination species. Among many applications, Ti3C2Tx is an excellent material for energy storage, energy converting, and CO2-capturing devices. However, active sites for adsorption and surface reactions on the Ti3C2Tx-surface are still open questions to explore, which have implications for preparation meth…
▽ More
One of the most explored MXenes is the Ti3C2Tx, where Tx is designated to inherently formed termination species. Among many applications, Ti3C2Tx is an excellent material for energy storage, energy converting, and CO2-capturing devices. However, active sites for adsorption and surface reactions on the Ti3C2Tx-surface are still open questions to explore, which have implications for preparation methods when to obtain correct and optimized surface requirements. Here we use X-ray photoelectron spectroscopy to study adsorption of common gas molecules such as H2, CO2, and H2O, which all might be present in energy storage, energy converting, and CO2-capturing devices based on 2D flakes of Ti3C2Tx. The study shows that H2O, with a strong bonding to the Ti-Ti bridge-sites, can be considered as a termination species. An H2O terminated Ti3C2Tx-surface restricts the CO2 adsorption to the Ti on-top sites and reduces the ability to store positive ions, such as Li+ and Na+. On the other hand, an H2O terminated Ti3C2Tx-surface shows the capability to split water. The study further shows that H2 has the ability to remove F at moderate temperatures. The results from this study have implications for correct selection of MXene preparations and the environment around the MXene in different implementations.
△ Less
Submitted 4 April, 2024;
originally announced April 2024.
-
Electronic structure and thermoelectric properties of epitaxial Sc1-xVxNy thin films grown on MgO(001)
Authors:
Susmita Chowdhury,
Niraj Kumar Singh,
Sanath Kumar Honnali,
Grzegorz Greczynski,
Per Eklund,
Arnaud le Febvrier,
Martin Magnuson
Abstract:
The electronic structure of Sc1-xVxNy epitaxial films with different alloying concentrations of V are investigated with respect to effects on thermoelectric properties. Band structure calculations on Sc0.75V0.25N indicate that V 3d states lie in the band gap of the parent ScN compound in the vicinity of the Fermi level. Thus, theoretically the presence of light (dispersive) bands at the Γ-point wi…
▽ More
The electronic structure of Sc1-xVxNy epitaxial films with different alloying concentrations of V are investigated with respect to effects on thermoelectric properties. Band structure calculations on Sc0.75V0.25N indicate that V 3d states lie in the band gap of the parent ScN compound in the vicinity of the Fermi level. Thus, theoretically the presence of light (dispersive) bands at the Γ-point with band multiplicity is expected to lead to lower electrical resistivity while flat (heavy) bands at X-W-K symmetry points are associated with higher Seebeck coefficient than that of ScN. With this aim, epitaxial Sc1-xVxNy thin film samples were deposited on MgO(001) substrates. All the samples showed N substoichiometry and pseudocubic crystal structure. The N-vacancy-induced states were visible in the Sc 2p XAS spectra. The reference ScN and Sc1-xVxNy samples up to x = 0.12 were n type, exhibiting carrier concentration of 1021 cm-3, typical for degenerate semiconductors. For the highest V alloying of x = 0.15, holes became the majority charge carrier as indicated by the positive Seebeck coefficient. The underlying electronic structure and bonding mechanism in Sc1-xVxNy influence the electrical resistivity, Seebeck coefficient, and Hall effect. Thus, the work contributes to the fundamental understanding of the correlated defects and thermoelectric properties to the electronic structure in Sc-N system with V alloying.
△ Less
Submitted 1 April, 2024;
originally announced April 2024.
-
Thermoelectric properties and electronic structure of Cr(Mo,V)Nx thin films studied by synchrotron and lab-based X-ray spectroscopy
Authors:
Susmita Chowdhury,
Victor Hjort,
Rui Shu,
Grzegorz Greczynski,
Arnaud le Febvrier,
Per Eklund,
Martin Magnuson
Abstract:
Chromium-based nitrides are used in hard, resilient coatings, and show promise for thermoelectric applications due to their combination of structural, thermal, and electronic properties. Here, we investigated the electronic structures and chemical bonding correlated to the thermoelectric properties of epitaxially grown chromium-based multicomponent nitride Cr(Mo,V)Nx thin films. Due to minuscule N…
▽ More
Chromium-based nitrides are used in hard, resilient coatings, and show promise for thermoelectric applications due to their combination of structural, thermal, and electronic properties. Here, we investigated the electronic structures and chemical bonding correlated to the thermoelectric properties of epitaxially grown chromium-based multicomponent nitride Cr(Mo,V)Nx thin films. Due to minuscule N vacancies, finite population of Cr 3d and N 2p states appear at the Fermi level and diminishes the band opening for Cr0.51N0.49. Incorporating holes by alloying V in N deficient CrN matrix results in enhanced thermoelectric power factor with marginal change in the charge transfer of Cr to N compared to Cr0.51N0.49. Further alloying Mo isoelectronic to Cr increases the density of states across the Fermi level due to hybridization of the (Cr, V) 3d and Mo 4d-N 2p states in Cr(Mo,V)Nx. The hybridization effect with reduced N 2p states off from stoichiometry drives the system towards metal like electrical resistivity and reduction in Seebeck coefficient compensating the overall power factor still comparable to Cr0.51N0.49. The N deficiency also depicts a critical role in reduction of the charge transfer from metal to N site. The present work envisages ways for enhancing thermoelectric properties through electronic band engineering by alloying and competing effects of N vacancies.
△ Less
Submitted 24 August, 2023; v1 submitted 21 August, 2023;
originally announced August 2023.
-
The Origin of Ti 1s XANES Main Edge Shifts and EXAFS Oscillations in the Energy Storage Materials Ti2CTx and Ti3C2Tx MXenes
Authors:
Lars-Åke Näslund,
Martin Magnuson
Abstract:
A potential application of two-dimensional (2D) MXenes, such as Ti2CTx and Ti3C2Tx, is energy storage devices, such as supercapacitors, batteries, and hydride electrochemical cells, where intercalation of ions between the 2D layers is considered as a charge carrier. Electrochemical cycling investigations in combination with Ti 1s X-ray absorption spectroscopy (XAS) have therefore been performed wi…
▽ More
A potential application of two-dimensional (2D) MXenes, such as Ti2CTx and Ti3C2Tx, is energy storage devices, such as supercapacitors, batteries, and hydride electrochemical cells, where intercalation of ions between the 2D layers is considered as a charge carrier. Electrochemical cycling investigations in combination with Ti 1s X-ray absorption spectroscopy (XAS) have therefore been performed with the objective to study oxidation state changes during potential variations. In some of these studies Ti3C2Tx has shown main edge shifts in the Ti 1s X-ray absorption near-edge structure (XANES). Here we show that these main edge shifts originate from the Ti 4p orbital involvement in the bonding between the surface Ti and the termination species at the fcc-sites. The study further shows that the t2g-eg crystal field splitting (10Dq) observed in the pre-edge absorption region indicate weaker Ti-C bonds in Ti2CTx and Ti3C2Tx compared to TiC and the corresponding MAX phases. The results from this study provide information necessary for improved electronic modeling and subsequently a better description of the materials properties of the MXenes. In general, potential applications, where surface interactions with intercalation elements are important processes, will benefit from the new knowledge presented.
△ Less
Submitted 12 June, 2023;
originally announced June 2023.
-
Rhombohedral and Turbostratic Boron Nitride Polytypes Investigated by X-ray Absorption Spectroscopy
Authors:
Weine Olovsson,
Martin Magnuson
Abstract:
The electronic structure of rhombohedral sp2 hybridized boron nitride (r-BN) is characterized by X-ray absorption near-edge structure spectroscopy. Measurements are performed at the boron and nitrogen K-edges (1s) and interpreted with first-principles density functional theory calculations, including final state effects by applying a core-hole. We show that it is possible to distinguish between di…
▽ More
The electronic structure of rhombohedral sp2 hybridized boron nitride (r-BN) is characterized by X-ray absorption near-edge structure spectroscopy. Measurements are performed at the boron and nitrogen K-edges (1s) and interpreted with first-principles density functional theory calculations, including final state effects by applying a core-hole. We show that it is possible to distinguish between different 2D planar polytypes such as rhombohedral, twinned rhombohedral, hexagonal and turbostratic BN by the difference in chemical shifts. In particular, the chemical shift at the B 1s-edge is shown to be significant for the turbostratic polytype. This implies that the band gap can be tuned by a superposition of different polytypes and stacking of lattice planes.
△ Less
Submitted 15 December, 2022;
originally announced December 2022.
-
Structural changes in Ti1-xAlxN coatings during turning: A XANES and EXAFS study of worn tools
Authors:
L. Rogström,
M. Moreno,
J. Andersson,
M. Johansson-Jõesaar,
M. Odén,
K. Klementiev,
L. -Å. Näslund,
M. Magnuson
Abstract:
Structural changes in Ti1-xAlxN coated tool inserts used for turning in 316L stainless steel were investigated by XANES, EXAFS, EDS, and STEM. For coarse-grained fcc-structured Ti1-xAlxN coatings, with 0 \leq x \leq 0.62, the XANES spectrum changes with Al-content. XANES Ti 1s line-scans across the rake face of the worn samples reveals that TiN-enriched domains have formed during turning in Ti0.47…
▽ More
Structural changes in Ti1-xAlxN coated tool inserts used for turning in 316L stainless steel were investigated by XANES, EXAFS, EDS, and STEM. For coarse-grained fcc-structured Ti1-xAlxN coatings, with 0 \leq x \leq 0.62, the XANES spectrum changes with Al-content. XANES Ti 1s line-scans across the rake face of the worn samples reveals that TiN-enriched domains have formed during turning in Ti0.47Al0.53N and Ti0.38Al0.62N samples as a result of spinodal decomposition. The XANES spectra reveal the locations on the tool in which the most TiN-rich domains have formed, indicating which part of the tool-chip contact area that experienced the highest temperature during turning. Changes in the pre-edge features in the XANES spectra reveal that structural changes occur also in the w-TiAlN phase in fine-grained Ti0.38Al0.62N during turning. EDS shows that Cr and Fe from the steel adhere to the tool rake face during machining. Cr 1s and Fe 1s XANES show that Cr is oxidized in the end of the contact length while the adhered Fe retains in the same fcc-structure as that of the 316L stainless steel.
△ Less
Submitted 8 December, 2022;
originally announced December 2022.
-
Review of Transition-Metal Diboride Thin Films
Authors:
Martin Magnuson,
Lars Hultman,
Hans Högberg
Abstract:
We review the thin film growth, chemistry, and physical properties of Group 4-6 transition-metal diboride (TMB2) thin films with AlB2-type crystal structure (Strukturbericht designation C32). Industrial applications are growing rapidly as TMB2 begin competing with conventional refractory ceramics like carbides and nitrides, including pseudo-binaries such as Ti1-xAlxN. The TMB2 crystal structure co…
▽ More
We review the thin film growth, chemistry, and physical properties of Group 4-6 transition-metal diboride (TMB2) thin films with AlB2-type crystal structure (Strukturbericht designation C32). Industrial applications are growing rapidly as TMB2 begin competing with conventional refractory ceramics like carbides and nitrides, including pseudo-binaries such as Ti1-xAlxN. The TMB2 crystal structure comprises graphite-like honeycombed atomic sheets of B interleaved by hexagonal close-packed TM layers. From the C32 crystal structure stems unique properties including high melting point, hardness, and corrosion resistance, yet limited oxidation resistance, combined with high electrical conductivity. We correlate the underlying chemical bonding, orbital overlap, and electronic structure to the mechanical properties, resistivity, and high-temperature properties unique to this class of materials. The review highlights the importance of avoiding contamination elements (like oxygen) and boron segregation on both the target and substrate sides during sputter deposition, for better-defined properties, regardless of the boride system investigated. This is a consequence of the strong tendency for B to segregate to TMB2 grain boundaries for boron-rich compositions of the growth flux. It is judged that sputter deposition of TMB2 films is at a tip** point towards a multitude of applications for TMB2 not solely as bulk materials, but also as protective coatings and electrically conducting high-temperature stable thin films.
△ Less
Submitted 28 December, 2021;
originally announced December 2021.
-
Elucidating Pathfinding Elements from the Kubi Gold Mine in Ghana
Authors:
Gabriel K. Nzulu,
Babak Bakhit,
Hans Högberg,
Lars Hultman,
Martin Magnuson
Abstract:
X-ray photoelectron spectroscopy (XPS) and energy-dispersive X-ray spectroscopy (EDX) are applied to investigate the properties of fine-grained concentrate on artisanal small-scale gold mining samples from the Kubi Gold Project of the Asante Gold Corporation near Dunwka-on-Offin in the Central Region of Ghana. Both techniques show that the Au-containing residual sediments are dominated by the host…
▽ More
X-ray photoelectron spectroscopy (XPS) and energy-dispersive X-ray spectroscopy (EDX) are applied to investigate the properties of fine-grained concentrate on artisanal small-scale gold mining samples from the Kubi Gold Project of the Asante Gold Corporation near Dunwka-on-Offin in the Central Region of Ghana. Both techniques show that the Au-containing residual sediments are dominated by the host elements Fe, Ag, Al, N, O, Si, Hg, and Ti that either form alloys with gold or inherent elements in the sediments. For comparison, a bulk nugget sample mainly consisting of Au forms an electrum i.e., a solid solution with Ag. Untreated (impure) sediments, fine-grained Au concentrate, coarse-grained Au concentrate, and processed ore (Au bulk/nugget) samples were found to contain cluster of O, C, N, and Ag with Au concentrations significantly lower than that of the related elements. This finding can be attributed to primary geochemical dispersion, which evolved from crystallization of magma and hydrothermal liquids as well as migration of metasomatic elements and rapid rate of chemical weathering of lateralization in secondary processes. The results indicate that Si and Ag are strongly concomitants with Au because of their eutectic characteristics N, C, and O follow alongside because of their affinity to Si. These non-noble elements thus act as pathfinders of Au ores in the exploration area. The paper further discusses relationships between gold and sediments of auriferous lodes as key to determine indicator minerals of gold in mining sites
△ Less
Submitted 29 October, 2021;
originally announced October 2021.
-
Chemical Bonding of Termination Species in 2D Carbides Investigated through Valence Band UPS/XPS of Ti3C2Tx MXene
Authors:
Lars-Åke Näslund,
Mikko-Heikki Mikkelä,
Esko Kokkonen,
Martin Magnuson
Abstract:
MXenes are technologically interesting 2D materials that show potential in numerous applications. The properties of the MXenes depend at large extent on the selection of elements that build the 2D MX-layer. Another key parameter for tuning the attractive material properties is the species that terminate the surfaces of the MX-layers. Although being an important parameter, experimental studies on t…
▽ More
MXenes are technologically interesting 2D materials that show potential in numerous applications. The properties of the MXenes depend at large extent on the selection of elements that build the 2D MX-layer. Another key parameter for tuning the attractive material properties is the species that terminate the surfaces of the MX-layers. Although being an important parameter, experimental studies on the bonding between the MX-layers and the termination species are few and thus an interesting subject of investigation. Here we show that the termination species fluorine (F) bonds to the Ti3C2-surface mainly through Ti 3p - F 2p hybridization and that oxygen (O) bonds through Ti 3p - O 2p hybridization with a significant contribution of Ti 3d and Ti 4p. The study further shows that the Ti3C2-surface is not only terminated by F and O on the threefold hollow face-centered-cubic (fcc) site. A significant amount of O sits on a bridge site bonded to two Ti surface atoms on the Ti3C2-surface. In addition, the results provide no support for hydroxide (OH) termination on the Ti3C2-surface. On the contrary, the comparison of the valence band intensity distribution obtained through ultraviolet- and x-ray photoelectron spectroscopy with computed spectra by density of states, weighed by matrix elements and sensitivity factors, reveals that OH cannot be considered as an inherent termination species in Ti3C2Tx. The results from this study have implications for correct modeling of the structure of MXenes and the corresponding materials properties. Especially in applications where surface composition and charge are important, such as supercapacitors, Li-ion batteries, electrocatalysis, and fuel- and solar cells, where intercalation processes are essential.
△ Less
Submitted 8 September, 2021;
originally announced September 2021.
-
Characterization and identification of Au pathfinder minerals from an artisanal mine site using X-ray diffraction
Authors:
Gabriel Nzulu,
Per Eklund,
Martin Magnuson
Abstract:
Gold-associated pathfinder minerals have been investigated by identifying host minerals of Au for samples collected from an artisanal mining site near a potential gold mine (Kubi Gold Project) in Dunkwa-On-Offin in the central region of Ghana. We find that for each composition of Au powder (impure) and the residual black hematite/magnetite sand that remains after gold panning, there is a unique se…
▽ More
Gold-associated pathfinder minerals have been investigated by identifying host minerals of Au for samples collected from an artisanal mining site near a potential gold mine (Kubi Gold Project) in Dunkwa-On-Offin in the central region of Ghana. We find that for each composition of Au powder (impure) and the residual black hematite/magnetite sand that remains after gold panning, there is a unique set of associated diverse indicator minerals. These indicator minerals are identified as SiO2 (quartz), Fe3O4 (magnetite), and Fe2O3 (hematite), while contributions from pyrite, arsenopyrites, iridosmine, scheelite, tetradymite, garnet, gypsum, and other sulfate materials are insignificant. This constitutes a confirmative identification of Au pathfinding minerals in this particular mineralogical area. The findings suggest that X-ray diffraction could also be applied in other mineralogical sites to aid in identifying indicator minerals of Au and the location of ore bodies at reduced environmental and exploration costs.
△ Less
Submitted 7 February, 2021;
originally announced February 2021.
-
Local chemical bonding and structural properties in Ti3AlC2 MAX phase and Ti3C2Tx MXene probed by Ti 1s X-ray absorption spectroscopy
Authors:
Martin Magnuson,
Lars-Åke Näslund
Abstract:
The chemical bonding within the transition-metal carbide materials MAX phase Ti3AlC2 and MXene Ti3C2Tx is investigated by X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopies. MAX phases are inherently nanolaminated materials that consist of alternating layers of Mn+1Xn and monolayers of an A-element from the IIIA or IVA group in the peri…
▽ More
The chemical bonding within the transition-metal carbide materials MAX phase Ti3AlC2 and MXene Ti3C2Tx is investigated by X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopies. MAX phases are inherently nanolaminated materials that consist of alternating layers of Mn+1Xn and monolayers of an A-element from the IIIA or IVA group in the periodic table, where M is a transition metal and X is either carbon or nitrogen. Replacing the A-element with surface termination species Tx will separate the Mn+1Xn-layers forming two-dimensional (2D) flakes of Mn+1XnTx. For Ti3C2Tx the Tx corresponds to fluorine (F) and oxygen (O) covering both sides of every single 2D Mn+1Xn-flake. The Ti K-edge (1s) XANES of both Ti3AlC2 and Ti3C2Tx exhibit characteristic pre-edge absorption regions of C 2p - Ti 3d hybridization with clear crystal-field splitting's while the main-edge absorption features originate from the Ti 1s -> 4p excitation, where only the latter shows sensitivity towards the fcc-site occupation of the termination species. The coordination numbers obtained from EXAFS show that Ti3AlC2 and Ti3C2Tx are highly anisotropic with a strong in-plane contribution for Ti and with a dynamic out-of-plane contribution from the Al monolayers and termination species, respectively. As shown in the temperature-dependent measurements, the O contribution shifts to shorter bond length while the F diminishes as the temperature is raised from room temperature up to 750 °C.
△ Less
Submitted 1 October, 2020;
originally announced October 2020.
-
Interface Bonding of Zr1-xAlxN Nanocomposites Investigated by X-ray Spectroscopies and First Principles Calculations
Authors:
Martin Magnuson,
Weine Olovsson,
Naureen Ghafoor,
Magnus Odén,
Lars Hultman
Abstract:
The electronic structure, chemical bonding and interface component in ZrN-AlN nanocomposites formed by phase separation during thin film deposition of metastable Zr1-xAlxN (x=0.0, 0.12, 0.26, 0.40) is investigated by resonant inelastic X-ray scattering/X-ray emission and X-ray absorption spectroscopy and compared to first-principles calculations including transitions between orbital angular moment…
▽ More
The electronic structure, chemical bonding and interface component in ZrN-AlN nanocomposites formed by phase separation during thin film deposition of metastable Zr1-xAlxN (x=0.0, 0.12, 0.26, 0.40) is investigated by resonant inelastic X-ray scattering/X-ray emission and X-ray absorption spectroscopy and compared to first-principles calculations including transitions between orbital angular momentum final states. The experimental spectra are compared with different interface-slab model systems using first-principle all electron full-potential calculations where the core states are treated fully relativistic. As shown in this work, the bulk sensitivity and element selectivity of X-ray spectroscopy enables to probe the symmetry and orbital directions at interfaces between cubic and hexagonal crystals. We show how the electronic structure develop from local octahedral bond symmetry of cubic ZrN that distorts for increasing Al content into more complex bonding. This results in three different kinds of bonding originating from semi-coherent interfaces with segregated ZrN and lamellar AlN nanocrystalline precipitates. An increasing chemical shift and charge transfer between the elements takes place with increasing Al content and affects the bond strength and increases resistivity.
△ Less
Submitted 18 March, 2020;
originally announced March 2020.
-
Magnetic anisotropy in Cr$_2$GeC investigated by X-ray magnetic circular dichroism and \textit{ab initio} calculations
Authors:
Martin Magnuson,
Maurizio Mattesini
Abstract:
The magnetism in the inherently nanolaminated ternary MAX-phase Cr$_{2}$GeC is investigated by element-selective, polarization and temperature-dependent, soft X-ray absorption spectroscopy and X-ray magnetic circular dichroism. The measurements indicate an antiferro-magnetic Cr-Cr coupling along the $c$-axis of the hexagonal structure modulated by a ferromagnetic ordering in the nanolaminated…
▽ More
The magnetism in the inherently nanolaminated ternary MAX-phase Cr$_{2}$GeC is investigated by element-selective, polarization and temperature-dependent, soft X-ray absorption spectroscopy and X-ray magnetic circular dichroism. The measurements indicate an antiferro-magnetic Cr-Cr coupling along the $c$-axis of the hexagonal structure modulated by a ferromagnetic ordering in the nanolaminated $ab$-basal planes. The weak chromium magnetic moments are an order of magnitude stronger in the nanolaminated planes than along the vertical axis. Theoretically, a small but notable, non-spin-collinear component explains the existence of a non-perfect spin compensation along the $c$-axis. As shown in this work, this spin distortion generates an overall residual spin moment inside the unit cell resembling that of a ferri-magnet. Due to the different competing magnetic interactions, electron correlations and temperature effects both need to be considered to achieve a correct theoretical description of the Cr$_{2}$GeC magnetic properties.
△ Less
Submitted 17 January, 2020;
originally announced January 2020.
-
Reactive magnetron sputtering of tungsten target in krypton/trimethylboron atmosphere
Authors:
Martin Magnuson,
Lina Tengdelius,
Fredrik Eriksson,
Mattias Samuelsson,
Esteban Broitman,
Grzegorz Greczynski,
Lars Hultman,
Hans Högberg
Abstract:
W-B-C films were deposited on Si(100) substrates held at elevated temperature by reactive sputtering from a W target in Kr/trimethylboron (TMB) plasmas. Quantitative analysis by X-ray photoelectron spectroscopy (XPS) shows that the films are W-rich between ~ 73 and ~ 93 at.% W. The highest metal content is detected in the film deposited with 1 sccm TMB. The C and B concentrations increase with inc…
▽ More
W-B-C films were deposited on Si(100) substrates held at elevated temperature by reactive sputtering from a W target in Kr/trimethylboron (TMB) plasmas. Quantitative analysis by X-ray photoelectron spectroscopy (XPS) shows that the films are W-rich between ~ 73 and ~ 93 at.% W. The highest metal content is detected in the film deposited with 1 sccm TMB. The C and B concentrations increase with increasing TMB flow to a maximum of ~18 and ~7 at.%, respectively, while the O content remains nearly constant at 2-3 at.%. Chemical bonding structure analysis performed after samples sputter-cleaning reveals C-W and B-W bonding and no detectable W-O bonds. During film growth with 5 sccm TMB and 500 oC or with 10 sccm TMB and 300-600 oC thin film X-ray diffraction shows the formation of cubic 100-oriented WC1-x with a possible solid solution of B. Lower flows and lower growth temperatures favor growth of W and W2C, respectively. Depositions at 700 and 800 oC result in the formation of WSi2 due to a reaction with the substrate. At 900 oC, XPS analysis shows ~96 at.% Si in the film due to Si interdiffusion. Scanning electron microscopy images reveal a fine-grained microstructure for the deposited WC1-x films. Nanoindentation gives hardness values in the range from ~23 to ~31 GPa and reduced elastic moduli between ~220 and 280 GPa in the films deposited at temperatures lower than 600 oC. At higher growth temperatures the hardness decreases by a factor of 3 to 4 following the formation of WSi2 at 700-800 oC and Si-rich surface at 900 oC.
△ Less
Submitted 16 September, 2019;
originally announced September 2019.
-
Vibrational Effects in X-ray Absorption Spectra of 2D Layered Materials
Authors:
Weine Olovsson,
Teruyasu Mizoguchi,
Martin Magnuson,
Stefan Kontur,
Olle Hellman,
Isao Tanaka,
Claudia Draxl
Abstract:
With the examples of the C $K$-edge in graphite and the B $K$-edge in hexagonal BN, we demonstrate the impact of vibrational coupling and lattice distortions on the X-ray absorption near-edge structure (XANES) in 2D layered materials. Theoretical XANES spectra are obtained by solving the Bethe-Salpeter equation of many-body perturbation theory, including excitonic effects through the correlated mo…
▽ More
With the examples of the C $K$-edge in graphite and the B $K$-edge in hexagonal BN, we demonstrate the impact of vibrational coupling and lattice distortions on the X-ray absorption near-edge structure (XANES) in 2D layered materials. Theoretical XANES spectra are obtained by solving the Bethe-Salpeter equation of many-body perturbation theory, including excitonic effects through the correlated motion of core-hole and excited electron. We show that accounting for zero-point motion is important for the interpretation and understanding of the measured X-ray absorption fine structure in both materials, in particular for describing the $σ^*$-peak structure.
△ Less
Submitted 23 April, 2019;
originally announced April 2019.
-
Electronic Structure of Beta-Ta Films from X-ray Photoelectron Spectroscopy and First-principles Calculations
Authors:
Martin Magnuson,
Grzegorz Greczynski,
Fredrik Eriksson,
Lars Hultman,
Hans Högberg
Abstract:
The electronic structure and chemical bonding of Beta-Ta synthesized as a thin 001-oriented film (space group P421m) is investigated by 4f core level and valence band X-ray photoelectron spectroscopy and compared to alfa-Ta bulk. For the Beta-phase, the 4f7/2 peak is located at 21.91 eV and with the 4f5/2 at 23.81 eV which is 0.16 eV higher compared to the corresponding 4f peaks of the alfa-Ta ref…
▽ More
The electronic structure and chemical bonding of Beta-Ta synthesized as a thin 001-oriented film (space group P421m) is investigated by 4f core level and valence band X-ray photoelectron spectroscopy and compared to alfa-Ta bulk. For the Beta-phase, the 4f7/2 peak is located at 21.91 eV and with the 4f5/2 at 23.81 eV which is 0.16 eV higher compared to the corresponding 4f peaks of the alfa-Ta reference. We suggest that this chemical shift originates from electron screening, higher resistivity or strain in the Beta-Ta film. Furthermore, the 5d-5s states at the bottom of the valence band are shifted by 0.75 eV towards higher binding energy in Beta-Ta compared to alfa-Ta. This is a consequence of the lower number of nearest neighbors with four in Beta-Ta compared to eight in the alfa-Ta phase. The difference in the electronic structures, spectral line shapes of the valence band and the energy positions of the Ta 4f, 5p core-levels of Beta-Ta versus alfa-Ta are discussed in relation to calculated states of Beta-Ta and alfa-Ta. In particular, the lower number of states at the Fermi level of Beta-Ta (0.557 states/eV/atom) versus alfa-Ta (1.032 states/eV/atom) that according to Mott's law should decrease the conductivity in metals and affect the stability by charge redistribution in the valence band. This is experimentally supported from resistivity measurements of the film yielding a value of ~170 micro-Ohm-cm in comparison to alfa-Ta bulk with a reported value of ~13.1 micro-Ohm-cm.
△ Less
Submitted 26 November, 2018;
originally announced November 2018.
-
Polarization-dependent resonant inelastic X-ray scattering study at the Cu L and O K-edge of YBa$_2$Cu$_3$O$_{7-x}$
Authors:
Martin Magnuson,
Thorsten Schmitt,
Laurent Duda
Abstract:
We present a study on the high-Tc superconductor (HTSC) YBa2Cu3O7-x (YBCO) using polarization-dependent X-ray absorption and resonant inelastic X-ray scattering. High-resolution measurements using synchrotron-radiation are compared with calculations using a quasi-atomic multiplet approach performed at the Cu 2p3/2-edge of YBCO. We use a multiplet approach within the single impurity Anderson model…
▽ More
We present a study on the high-Tc superconductor (HTSC) YBa2Cu3O7-x (YBCO) using polarization-dependent X-ray absorption and resonant inelastic X-ray scattering. High-resolution measurements using synchrotron-radiation are compared with calculations using a quasi-atomic multiplet approach performed at the Cu 2p3/2-edge of YBCO. We use a multiplet approach within the single impurity Anderson model to reproduce and understand the character of the localized low-energy excitations in YBCO. We observe a distinct peak at about 0.5 eV in O K RIXS. This peak shows dependence on do**, incident energy, and momentum transfer that suggests that it has a different origin than the previously discussed cuprate bi-magnons. Therefore, we assign it to multi-magnon excitations between the Zhang Rice bands and/or the Upper Hubbard bands, respectively.
△ Less
Submitted 20 March, 2018;
originally announced March 2018.
-
Chemical bonding in carbide MXene nanosheets
Authors:
Martin Magnuson,
Joseph Halim,
Lars-Åke Näslund
Abstract:
The chemical bonding in the carbide core and the surface chemistry in a new group of transition-metal carbides Tin+1Cn-Tx (n=1,2) called MXenes have been investigated by surface-sensitive valence band X-ray photoelectron spectroscopy. Changes in band structures of stacked nano sheets of different thicknesses are analyzed in connection to known hybridization regions of TiC and TiO2 that affect elas…
▽ More
The chemical bonding in the carbide core and the surface chemistry in a new group of transition-metal carbides Tin+1Cn-Tx (n=1,2) called MXenes have been investigated by surface-sensitive valence band X-ray photoelectron spectroscopy. Changes in band structures of stacked nano sheets of different thicknesses are analyzed in connection to known hybridization regions of TiC and TiO2 that affect elastic and transport properties. By employing high excitation energy, the photoelectron cross-section for the C 2s - Ti 3d hybridization region at the bottom of the valence band is enhanced. As shown in this work, the O 2p and F 2p bands are shown to strongly depend both on the bond lengths to the surface groups and the adsorption sites. The effect of surface oxidation and Ar+ sputtering on the electronic structure is also discussed.
△ Less
Submitted 20 March, 2018;
originally announced March 2018.
-
Chemical Bonding in Epitaxial ZrB2 Studied by X-ray Spectroscopy
Authors:
Martin Magnuson,
Lina Tengdelius,
Grzegorz Greczynski,
Lars Hultman,
Hans Högberg
Abstract:
The chemical bonding in an epitaxial ZrB2 film is investigated by Zr K-edge (1s) X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopies and compared to the ZrB2 compound target from which the film was synthesized as well as a bulk α-Zr reference. Quantitative analysis of X-ray Photoelectron Spectroscopy spectra reveals at the surface: ~5% O…
▽ More
The chemical bonding in an epitaxial ZrB2 film is investigated by Zr K-edge (1s) X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopies and compared to the ZrB2 compound target from which the film was synthesized as well as a bulk α-Zr reference. Quantitative analysis of X-ray Photoelectron Spectroscopy spectra reveals at the surface: ~5% O in the epitaxial ZrB2 film, ~19% O in the ZrB2 compound target and ~22% O in the bulk α-Zr reference after completed sputter cleaning. For the ZrB2 compound target, X-ray diffraction (XRD) shows weak but visible -111, 111, and 220 peaks from monoclinic ZrO2 together with peaks from ZrB2 and where the intensity distribution for the ZrB2 peaks show a randomly oriented target material. For the bulk α-Zr reference no peaks from any crystalline oxide were visible in the diffractogram recorded from the 0001-oriented metal. The Zr K-edge absorption from the two ZrB2 samples demonstrate more pronounced oscillations for the epitaxial ZrB2 film than in the bulk ZrB2 attributed to the high atomic ordering within the columns of the film. The XANES exhibits no pre-peak due to lack of p-d hybridization in ZrB2, but with a chemical shift towards higher energy of 4 eV in the film and 6 eV for the bulk compared to α-Zr (17.993 keV) from the charge-transfer from Zr to B. The 2 eV larger shift in bulk ZrB2 material suggests higher oxygen content than in the epitaxial film, which is supported by XPS. In EXAFS, the modelled cell-edge in ZrB2 is slightly smaller in the thin film (a=3.165 Å, c=3.520 Å) in comparison to the bulk target material (a=3.175 Å, c=3.540 Å) while in hexagonal closest-packed metal (α-phase, a=3.254 Å, c=5.147 Å).
△ Less
Submitted 25 January, 2018;
originally announced January 2018.
-
Bonding Structures of ZrHx Thin Films by X-ray Spectroscopy
Authors:
Martin Magnuson,
Fredrik Eriksson,
Lars Hultman,
Hans Högberg
Abstract:
The variation in local atomic structure and chemical bonding of ZrHx (x=0.15, 0.30, 1.16) magnetron sputtered thin films are investigated by Zr K-edge (1s) X-ray absorption near-edge structure and extended X-ray absorption fine structure spectroscopies. A chemical shift of the Zr K-edge towards higher energy with increasing hydrogen content is observed due to charge-transfer and an ionic or polar…
▽ More
The variation in local atomic structure and chemical bonding of ZrHx (x=0.15, 0.30, 1.16) magnetron sputtered thin films are investigated by Zr K-edge (1s) X-ray absorption near-edge structure and extended X-ray absorption fine structure spectroscopies. A chemical shift of the Zr K-edge towards higher energy with increasing hydrogen content is observed due to charge-transfer and an ionic or polar covalent bonding component between the Zr 4d and the H 1s states with increasing valency for Zr. We find an increase in the Zr-Zr bond distance with increasing hydrogen content from 3.160 Å in the hexagonal closest-packed metal (alpha-phase) to 3.395 Å in the understoichiometric delta-ZrHx film (CaF2-type structure) with x=1.16 that largely resembles that of bulk delta-ZrH2. For yet lower hydrogen contents, the structures are mixed alpha and delta-phases, while sufficient hydrogen loading (x>1) yields a pure δ-phase that is understoichiometric, but thermodynamically stable. The change in the hydrogen content and strain is discussed in relation to the corresponding change of bond lengths, hybridizations, and trends in electrical resistivity.
△ Less
Submitted 26 November, 2017;
originally announced November 2017.
-
Electronic Properties and Bonding in ZrHx Thin Films Investigated by Valence-Band X-ray Photoelectron Spectroscopy
Authors:
Martin Magnuson,
Susann Schmidt,
Lars Hultman,
Hans Högberg
Abstract:
The electronic structure and chemical bonding in reactively magnetron sputtered ZrHx (x=0.15, 0.30, 1.16) thin films with oxygen content as low as 0.2 at% are investigated by 4d valence band, shallow 4p core-level and 3d core-level X-ray photoelectron spectroscopy. With increasing hydrogen content, we observe significant reduction of the 4d valence states close to the Fermi level as a result of re…
▽ More
The electronic structure and chemical bonding in reactively magnetron sputtered ZrHx (x=0.15, 0.30, 1.16) thin films with oxygen content as low as 0.2 at% are investigated by 4d valence band, shallow 4p core-level and 3d core-level X-ray photoelectron spectroscopy. With increasing hydrogen content, we observe significant reduction of the 4d valence states close to the Fermi level as a result of redistribution of intensity towards the H 1s - Zr 4d hybridization region at about 6 eV below the Fermi level. For low hydrogen content (x=0.15, 0.30), the films consist of a superposition of hexagonal closest packed metal (alpha-phase)and understoichiometric delta-ZrHx (CaF2-type structure) phases, while for x=1.16, the film form single phase ZrHx that largely resembles that of stoichiometric delta-ZrH2 phase. We show that the cubic delta-ZrHx phase is metastable as thin film up to x=1.16 while for higher H-contents, the structure is predicted to be tetragonally distorted. For the investigated ZrH1.16 film, we find chemical shifts of 0.68 and 0.51 eV towards higher binding energies for the Zr 4p3/2 and 3d5/2 peak positions, respectively. Compared to the Zr metal binding energies of 27.26 and 178.87 eV, this signifies a charge-transfer from Zr to H atoms. The change in the electronic structure, spectral line shapes, and chemical shifts as function of hydrogen content is discussed in relation to the charge-transfer from Zr to H that affects the conductivity by charge redistribution in the valence band.
△ Less
Submitted 5 November, 2017;
originally announced November 2017.
-
Chemical bonding and electronic-structure in MAX phases as viewed by X-ray spectroscopy and density functional theory
Authors:
Martin Magnuson,
Maurizio Mattesini
Abstract:
This is a critical review of MAX-phase carbides and nitrides from an electronic-structure and chemical bonding perspective. This large group of nanolaminated materials is of great scientific and technological interest and exhibit a combination of metallic and ceramic features. These properties are related to the special crystal structure and bonding characteristics with alternating strong M-C bond…
▽ More
This is a critical review of MAX-phase carbides and nitrides from an electronic-structure and chemical bonding perspective. This large group of nanolaminated materials is of great scientific and technological interest and exhibit a combination of metallic and ceramic features. These properties are related to the special crystal structure and bonding characteristics with alternating strong M-C bonds in high-density MC slabs, and relatively weak M-A bonds between the slabs. Here, we review the trend and relationship between the chemical bonding, conductivity, elastic and magnetic properties of the MAX phases in comparison to the parent binary MX compounds with the underlying electronic structure probed by polarized X-ray spectroscopy. Spectroscopic studies constitute important tests of the results of state-of-the-art electronic structure density functional theory that is extensively discussed and are generally consistent. By replacing the elements on the M, A, or X-sites in the crystal structure, the corresponding changes in the conductivity, elasticity, magnetism and other materials properties makes it possible to tailor the characteristics of this class of materials by controlling the strengths of their chemical bonds.
△ Less
Submitted 13 December, 2016;
originally announced December 2016.
-
Structure and Bonding in Amorphous Cr1-xCx Nanocomposite Thin Films: X-ray Absorption Spectra and First-Principles Calculation
Authors:
Weine Olovsson,
Björn Alling,
Martin Magnuson
Abstract:
The local structure and chemical bonding in two-phase amorphous Cr$_{1-x}$C$_{x}$ nanocomposite thin films are investigated by Cr $K$-edge ($1s$) X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopies in comparison to theory. By utilizing the computationally efficient \textit{stochastic quenching} (SQ) technique, we reveal the complexity of…
▽ More
The local structure and chemical bonding in two-phase amorphous Cr$_{1-x}$C$_{x}$ nanocomposite thin films are investigated by Cr $K$-edge ($1s$) X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopies in comparison to theory. By utilizing the computationally efficient \textit{stochastic quenching} (SQ) technique, we reveal the complexity of different Cr-sites in the transition metal carbides, highlighting the need for large scale averaging to obtain theoretical XANES and EXAFS spectra for comparison with measurements. As shown in this work, it is advantageous to use \textit{ab initio} theory as an assessment to correctly model and fit experimental spectra and investigate the trends of bond lengths and coordination numbers in complex amorphous materials. With sufficient total carbon content ($\geq$ 30 at\%), we find that the short-range coordination in the amorphous carbide phase exhibit similarities to that of a Cr$_{7}$C$_{3\pm{}y}$ structure, while excessive carbons assemble in the amorphous carbon phase.
△ Less
Submitted 25 November, 2016;
originally announced November 2016.
-
Induced magnetism at the interfaces of a Fe/V superlattice investigated by resonant magnetic x-ray scattering
Authors:
Martin Magnuson
Abstract:
The induced magnetic moments in the V 3d electronic states of interface atomic layers in a Fe(6ML)/V(7ML) superlattice was investigated by x-ray resonant magnetic scattering. The first V atomic layer next to Fe was found to be strongly antiferromagnetically polarized relatively to Fe and the magnetic moments of the next few atomic layers in the interior V region decay exponentially with increasing…
▽ More
The induced magnetic moments in the V 3d electronic states of interface atomic layers in a Fe(6ML)/V(7ML) superlattice was investigated by x-ray resonant magnetic scattering. The first V atomic layer next to Fe was found to be strongly antiferromagnetically polarized relatively to Fe and the magnetic moments of the next few atomic layers in the interior V region decay exponentially with increasing distance from the interface, while the magnetic moments of the Fe atomic layers largely remain bulk-like. The induced V moments decay more rapidly as observed by x-ray magnetic scattering than in standard x-ray magnetic circular dichroism. The theoretical description of the induced magnetic atomic layer profile in V was found to strongly rely on the interface roughness within the superlattice period. These results provide new insight into interface magnetism by taking advantage of the enhanced depth sensitivity to the magnetic profile over a certain resonant energy bandwidth in the vicinity of the Bragg angles.
△ Less
Submitted 12 September, 2016;
originally announced September 2016.
-
The origin of anisotropy and high density of states in the electronic structure of Cr$_2$GeC by means of polarized soft X-ray spectroscopy and ab initio calculations
Authors:
Martin Magnuson,
Maurizio Mattesini,
Matthieu Bugnet,
Per Eklund
Abstract:
The anisotropy in the electronic structure of the inherently nanolaminated ternary phase Cr$_{2}$GeC is investigated by bulk-sensitive and element selective soft x-ray absorption/emission spectroscopy. The angle-resolved absorption/emission measurements reveal differences between the in-plane and out-of-plane bonding at the (0001) interfaces of Cr$_{2}$GeC. The Cr $L_{2,3}$, C $K$, and Ge $M_{1}$,…
▽ More
The anisotropy in the electronic structure of the inherently nanolaminated ternary phase Cr$_{2}$GeC is investigated by bulk-sensitive and element selective soft x-ray absorption/emission spectroscopy. The angle-resolved absorption/emission measurements reveal differences between the in-plane and out-of-plane bonding at the (0001) interfaces of Cr$_{2}$GeC. The Cr $L_{2,3}$, C $K$, and Ge $M_{1}$, $M_{2,3}$ emission spectra are interpreted with first-principles density-functional theory (DFT) including core-to-valence dipole transition matrix elements. For the Ge $4s$ states, the x-ray emission measurements reveal two orders of magnitude higher intensity at the Fermi level than DFT within the General Gradient Approximation (GGA) predicts. We provide direct evidence of anisotropy in the electronic structure and the orbital occupation that should affect the thermal expansion coefficient and transport properties. As shown in this work, hybridization and redistribution of intensity from the shallow $3d$ core levels to the $4s$ valence band explain the large Ge density of states at the Fermi level.
△ Less
Submitted 30 September, 2015;
originally announced September 2015.
-
Structure and bonding in amorphous iron carbide thin films
Authors:
Andrej Furlan,
Ulf Jansson,
Jun Lu,
Lars Hultman,
Martin Magnuson
Abstract:
We investigate the amorphous structure, chemical bonding, and electrical properties of magnetron sputtered Fe1-xCx (0.21<x<0.72) thin films. X-ray, electron diffraction and transmission electron microscopy show that the Fe1-xCx films are amorphous nanocomposites, consisting of a two-phase domain structure with Fe-rich carbidic FeCy, and a carbon-rich matrix. Pair distribution function analysis ind…
▽ More
We investigate the amorphous structure, chemical bonding, and electrical properties of magnetron sputtered Fe1-xCx (0.21<x<0.72) thin films. X-ray, electron diffraction and transmission electron microscopy show that the Fe1-xCx films are amorphous nanocomposites, consisting of a two-phase domain structure with Fe-rich carbidic FeCy, and a carbon-rich matrix. Pair distribution function analysis indicates a close-range order similar to those of crystalline Fe3C carbides in all films with additional graphene-like structures at high carbon content (71.8 at% C). From X-ray photoelectron spectroscopy measurements, we find that the amorphous carbidic phase has a composition of 15-25 at% carbon that slightly increases with total carbon content. X-ray absorption spectra exhibit increasing number of unoccupied 3d states and decreasing number of C 2p states as a function of carbon content. These changes signify a systematic redistribution in orbital occupation due to charge-transfer effects at the domain-size dependent carbide/matrix interfaces. Four-point probe resistivity of the Fe1-xCx films increases exponentially with carbon content from 200 mu-Ohm-cm (x=0.21) to 1200 mu-Ohm-cm (x=0.72), and is found to depend on the total carbon content rather than the composition of the carbide. Our findings open new possibilities for modifying the resistivity of amorphous thin film coatings based on transition metal carbides by control of amorphous domain structures.
△ Less
Submitted 8 January, 2015;
originally announced January 2015.
-
Self-do** processes between planes and chains in the metal-to-superconductor transition of YBa2Cu3O6.9
Authors:
Martin Magnuson,
Thorsten Schmitt Vladimir N. Strocov,
Justina Schlappa,
Alex S. Kalabukhov,
Laurent Duda
Abstract:
The interplay between the quasi 1-dimensional CuO-chains and the 2-dimensional CuO2 planes of YBa2Cu3O6+x (YBCO) has been in focus for a long time. Although the CuO-chains are known to be important as charge reservoirs that enable superconductivity for a range of oxygen do** levels in YBCO, the understanding of the dynamics of its temperature-driven metal-superconductor transition (MST) remains…
▽ More
The interplay between the quasi 1-dimensional CuO-chains and the 2-dimensional CuO2 planes of YBa2Cu3O6+x (YBCO) has been in focus for a long time. Although the CuO-chains are known to be important as charge reservoirs that enable superconductivity for a range of oxygen do** levels in YBCO, the understanding of the dynamics of its temperature-driven metal-superconductor transition (MST) remains a challenge. We present a combined study using x-ray absorption spectroscopy and resonant inelastic x-ray scattering (RIXS) revealing how a reconstruction of the apical O(4)-derived interplanar orbitals during the MST of optimally doped YBCO leads to substantial hole-transfer from the chains into the planes, i.e. self-do**. Our ionic model calculations show that localized divalent charge-transfer configurations are expected to be abundant in the chains of YBCO. While these indeed appear in the RIXS spectra from YBCO in the normal, metallic, state, they are largely suppressed in the superconducting state and, instead, signatures of Cu trivalent charge-transfer configurations in the planes become enhanced. In the quest for understanding the fundamental mechanism for high-Tc-superconductivity (HTSC) in perovskite cuprate materials, the observation of such an interplanar self-do** process in YBCO opens a unique novel channel for studying the dynamics of HTSC.
△ Less
Submitted 12 November, 2014;
originally announced November 2014.
-
Crystallization characteristics and chemical bonding properties of nickel carbide thin film nanocomposites
Authors:
Andrej Furlan,
Jun Lu,
Lars Hultman,
Ulf Jansson,
Martin Magnuson
Abstract:
The crystal structure and chemical bonding of magnetron-sputtering deposited nickel carbide Ni$_{1-x}$C$_{x}$ (0.05$\leq$x$\leq$0.62) thin films have been investigated by high-resolution X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, Raman spectroscopy, and soft X-ray absorption spectroscopy. By using X-ray as well as electron diffraction, we found carbon-co…
▽ More
The crystal structure and chemical bonding of magnetron-sputtering deposited nickel carbide Ni$_{1-x}$C$_{x}$ (0.05$\leq$x$\leq$0.62) thin films have been investigated by high-resolution X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, Raman spectroscopy, and soft X-ray absorption spectroscopy. By using X-ray as well as electron diffraction, we found carbon-containing hcp-Ni (hcp-NiC$_{y}$ phase), instead of the expected rhombohedral-Ni$_{3}$C. At low carbon content (4.9 at\%) the thin film consists of hcp-NiC$_{y}$ nanocrystallites mixed with a smaller amount of fcc-NiC$_{x}$. The average grain size is about 10-20 nm. With the increase of carbon content to 16.3 at\%, the film contains single-phase hcp-NiC$_{y}$ nanocrystallites with expanded lattice parameters. With further increase of carbon content to 38 at\%, and 62 at\%, the films transform to X-ray amorphous materials with hcp-NiC$_{y}$ and fcc-NiC$_{x }$ nanodomain structures in an amorphous carbon-rich matrix. Raman spectra of carbon indicate dominant $sp^{2}$ hybridization, consistent with photoelectron spectra that show a decreasing amount of C-Ni phase with increasing carbon content. The Ni $3d$ - C $2p$ hybridization in the hexagonal structure gives rise to the salient double-peak structure in Ni $2p$ soft X-ray absorption spectra at 16.3 at\% that changes with carbon content. We also show that the resistivity is not only governed by the amount of carbon, but increases by more than a factor of two when the samples transform from crystalline to amorphous.
△ Less
Submitted 20 September, 2014;
originally announced September 2014.
-
Strain Sensitivity in the Nitrogen 1s NEXAFS Spectra of Gallium Nitride
Authors:
Andrew Ritchie,
Shaylin Eger,
Chelsey Wright,
Daniel Chelladurai,
Cuyler Borrowman,
Weine Olovsson,
Martin Magnuson,
Jai Verma,
Debdeep Jena,
Huili Grace Xing,
Christian Dubuc,
Stephen Urquhart
Abstract:
The Nitrogen 1s near edge X-ray absorption fine structure (NEXAFS) of gallium nitride (GaN) shows a strong natural linear dichroism that arises from its anisotropic wurtzite structure. An additional spectroscopic variation arises from lattice strain in epitaxially grown GaN thin films. This variation is directly proportional to the degree of strain for some spectroscopic features. This strain vari…
▽ More
The Nitrogen 1s near edge X-ray absorption fine structure (NEXAFS) of gallium nitride (GaN) shows a strong natural linear dichroism that arises from its anisotropic wurtzite structure. An additional spectroscopic variation arises from lattice strain in epitaxially grown GaN thin films. This variation is directly proportional to the degree of strain for some spectroscopic features. This strain variation is interpreted with the aid of density functional theory calculations.
△ Less
Submitted 29 August, 2014;
originally announced August 2014.
-
Electronic correlation effects in the Cr2GeC Mn+1AXn phase
Authors:
Maurizio Mattesini,
Martin Magnuson
Abstract:
The magnetic properties, electronic band structure and Fermi surfaces of the hexagonal Cr2GeC system have been studied by means of both generalized gradient approximation (GGA) and the +U corrected method (GGA+U). The effective U value has been computed within the augmented plane-wave theoretical scheme by following the constrained density functional theory formalism of Anisimov et al. [1991 Phys.…
▽ More
The magnetic properties, electronic band structure and Fermi surfaces of the hexagonal Cr2GeC system have been studied by means of both generalized gradient approximation (GGA) and the +U corrected method (GGA+U). The effective U value has been computed within the augmented plane-wave theoretical scheme by following the constrained density functional theory formalism of Anisimov et al. [1991 Phys. Rev. B 45, 7570]. On the basis of our GGA+U calculations, a compensated anti-ferromagnetic spin ordering of Cr atoms has been found to be the ground state solution for this material, where a Ge-mediated super-exchange coupling is responsible for an opposite spin distribution between the ABA stacked in-plane Cr-C networks. Structural properties have also been tested and found to be in good agreement with the available experimental data. Topological analysis of Fermi surfaces have been used to qualitatively address the electronic transport properties of Cr2GeC and found an important asymmetrical carrier-type distribution within the hexagonal crystal lattice. We conclude that an appropriate description of the strongly correlated Cr-d electrons is an essential issue for interpreting the material properties of this unusual Cr-based MAX-phase.
△ Less
Submitted 3 December, 2013;
originally announced December 2013.
-
The electronic-structure origin of the anisotropic thermopower of nanolaminated Ti3SiC2 determined by polarized x-ray spectroscopy and Seebeck measurements
Authors:
Martin Magnuson,
Maurizio Mattesini,
Ngo Van Nong,
Per Eklund,
Lars Hultman
Abstract:
Nanolaminated materials exhibit characteristic magnetic, mechanical, and thermoelectric properties, with large contemporary scientific and technological interest. Here, we report on the anisotropic Seebeck coefficient in nanolaminated Ti3SiC2 single-crystal thin films and trace the origin to anisotropies in element-specific electronic states. In bulk polycrystalline form, Ti3SiC2 has a virtually z…
▽ More
Nanolaminated materials exhibit characteristic magnetic, mechanical, and thermoelectric properties, with large contemporary scientific and technological interest. Here, we report on the anisotropic Seebeck coefficient in nanolaminated Ti3SiC2 single-crystal thin films and trace the origin to anisotropies in element-specific electronic states. In bulk polycrystalline form, Ti3SiC2 has a virtually zero Seebeck coefficient over a wide temperature range. In contrast, we find that the in-plane (basal ab) Seebeck coefficient of Ti3SiC2, measured on single-crystal films has a substantial and positive value of 4-6 muV/K. Employing a combination of polarized angle-dependent x-ray spectroscopy and density functional theory we directly show electronic structure anisotropy in inherently nanolaminated Ti3SiC2 single-crystal thin films as a model system. The density of Ti 3d and C 2p states at the Fermi level in the basal ab-plane is about 40 % higher than along the c-axis. The Seebeck coefficient is related to electron and hole-like bands close to the Fermi level but in contrast to ground state density functional theory modeling, the electronic structure is also influenced by phonons that need to be taken into account. Positive contribution to the Seebeck coefficient of the element-specific electronic occupations in the basal plane is compensated by 73 % enhanced Si 3d electronic states across the laminate plane that give rise to a negative Seebeck coefficient in that direction. Strong phonon vibration modes with three to four times higher frequency along the c-axis than along the basal ab-plane also influence the electronic population and the measured spectra by the asymmetric average displacements of the Si atoms. These results constitute experimental evidence explaining why the average Seebeck coefficient of Ti3SiC2 in polycrystals is negligible over a wide temperature range.
△ Less
Submitted 22 May, 2012;
originally announced May 2012.
-
Electronic Structure and Chemical Bonding of Amorphous Chromium Carbide Thin Films
Authors:
Martin Magnuson,
Matilda Andersson,
Jun Lu,
Lars Hultman,
Ulf Jansson
Abstract:
The microstructure, electronic structure, and chemical bonding of chromium carbide thin films with different carbon contents have been investigated with high-resolution transmission electron microscopy, electron energy loss spectroscopy and soft x-ray absorption-emission spectroscopies. Most of the films can be described as amorphous nanocomposites with non-crystalline CrCx in an amorphous carbon…
▽ More
The microstructure, electronic structure, and chemical bonding of chromium carbide thin films with different carbon contents have been investigated with high-resolution transmission electron microscopy, electron energy loss spectroscopy and soft x-ray absorption-emission spectroscopies. Most of the films can be described as amorphous nanocomposites with non-crystalline CrCx in an amorphous carbon matrix. At high carbon contents, graphene-like structures are formed in the amorphous carbon matrix. At 47 at% carbon content, randomly oriented nanocrystallites are formed creating a complex microstructure of three components. The soft x-ray absorption-emission study shows additional peak structures exhibiting non-octahedral coordination and bonding.
△ Less
Submitted 3 May, 2012;
originally announced May 2012.
-
Resonant inelastic soft-x-ray scattering spectra at the N1s and C1s edges of poly(pyridine-2,5-diyl)
Authors:
M. Magnuson,
L. Yang,
J. - H. Guo,
C. Såthe,
A. Agui,
J. Nordgren,
Y. Luo,
H. Ågren,
N. Johansson,
W. R. Salaneck,
L. E. Horsburgh,
A. P. Monkman
Abstract:
Resonant inelastic scattering measurements of poly(pyridine-2,5-diyl) have been performed at the N1s and C1s edges using synchrotron radiation. For comparison, molecular orbital calculations of the spectra have been carried out with the repeat unit as a model molecule of the polymer chain. The resonant emission spectra show depletion of the p electron bands which is consistent with symmetry select…
▽ More
Resonant inelastic scattering measurements of poly(pyridine-2,5-diyl) have been performed at the N1s and C1s edges using synchrotron radiation. For comparison, molecular orbital calculations of the spectra have been carried out with the repeat unit as a model molecule of the polymer chain. The resonant emission spectra show depletion of the p electron bands which is consistent with symmetry selection and momentum conservation rules. The depletion is most obvious in the resonant inelastic scattering spectra of carbon while the nitrogen spectra are dominated by lone pair n orbital emission of s symmetry and are less excitation energy dependent. By comparing the measurements to calculations an isomeric dependence of the resonant spectra is found giving preference to two of the four possible isomers in the polymer.
△ Less
Submitted 5 January, 2012;
originally announced January 2012.
-
The electronic structure of poly(pyridine-2,5-diyl) investigated by soft x-ray absorption and emission spectroscopies
Authors:
M. Magnuson,
L. Yang,
J. - H. Guo,
C. Såthe,
A. Agui,
J. Nordgren,
Y. Luo,
H. Ågren,
N. Johansson,
W. R. Salaneck,
L. E. Horsburgh,
A. P. Monkman
Abstract:
The electronic structure of the poly-pyridine conjugated polymer has been investigated by resonant and nonresonant inelastic X-ray scattering and X-ray absorption spectroscopies using synchrotron radiation. The measurements were made for both the carbon and nitrogen contents of the polymer. The analysis of the spectra has been carried out in comparison with molecular orbital calculations taking th…
▽ More
The electronic structure of the poly-pyridine conjugated polymer has been investigated by resonant and nonresonant inelastic X-ray scattering and X-ray absorption spectroscopies using synchrotron radiation. The measurements were made for both the carbon and nitrogen contents of the polymer. The analysis of the spectra has been carried out in comparison with molecular orbital calculations taking the repeat-unit cell as a model molecule of the polymer chain. The simulations indicate no significant differences in the absorption and in the non-resonant X-ray scattering spectra for the different isomeric geometries, while some isomeric dependence of the resonant spectra is predicted. The resonant emission spectra show depletion of the π electron bands in line with symmetry selection and momentum conservation rules. The effect is most vizual for the carbon spectra; the nitrogen spectra are dominated by lone pair n orbital emission of σ symmetry and are less frequency dependent.
△ Less
Submitted 5 January, 2012;
originally announced January 2012.
-
The electronic structure of polyaniline and doped phases studied by soft X-ray absorption and emission spectroscopies
Authors:
M. Magnuson,
J. -H. Guo,
S. M. Butorin,
A. Agui,
C. Såthe,
J. Nordgren,
A. P. Monkman
Abstract:
The electronic structure of the conjugated polymer, polyaniline, has been studied by resonant and nonresonant X-ray emission spectroscopy using synchrotron radiation for the excitation. The measurements were made on polyaniline and a few doped (protonated) phases for both the carbon and nitrogen contents. The resonant X-ray emission spectra show depletion of the π electron bands due to the selecti…
▽ More
The electronic structure of the conjugated polymer, polyaniline, has been studied by resonant and nonresonant X-ray emission spectroscopy using synchrotron radiation for the excitation. The measurements were made on polyaniline and a few doped (protonated) phases for both the carbon and nitrogen contents. The resonant X-ray emission spectra show depletion of the π electron bands due to the selective excitation which enhances the effect of symmetry selection rules. The valence band structures in the X-ray emission spectra attributed to the π bands show unambiguous changes of the electronic structure upon protonation. By comparing to X-ray absorption measurements, the chemical bonding and electronic configuration is characterized.
△ Less
Submitted 4 January, 2012;
originally announced January 2012.
-
Energy Dependence of Cu L2,3 Satellites using Synchrotron Excited X-ray Emission Spectroscopy
Authors:
M. Magnuson,
N. Wassdahl,
J. Nordgren
Abstract:
The L2,3 X-ray emission of Cu metal has been measured using monochromatic synchrotron radiation. The self-absorption effect in the spectra is shown to be very small in our experimental geometry. From the quantitative analysis of spectra recorded at different excitation energies, the L3/L2 emission intensity ratio and the partial Auger-width are extracted. High-energy satellite features on the L3 e…
▽ More
The L2,3 X-ray emission of Cu metal has been measured using monochromatic synchrotron radiation. The self-absorption effect in the spectra is shown to be very small in our experimental geometry. From the quantitative analysis of spectra recorded at different excitation energies, the L3/L2 emission intensity ratio and the partial Auger-width are extracted. High-energy satellite features on the L3 emission line are separated by a subtraction procedure. The satellite intensity is found to be slowly increasing for excitation energies between the L3, L2 and L1 core-level thresholds due to shake-up and shake-off transitions. As the excitation energy passes the L2 threshold, a step of rapidly increasing satellite intensity of the L3 emission is found due to additional Coster-Kronig processes.
△ Less
Submitted 4 January, 2012;
originally announced January 2012.
-
Angular dependent resonant photoemission processes at the 2p thresholds in nickel metal
Authors:
M. Magnuson,
A. Nilsson,
M. Weinelt,
N. Mårtensson
Abstract:
Angle-resolved valence-band resonant photoemission of nickel metal has been measured close to the 2p core-level thresholds with synchrotron radiation. The well-known 6-eV correlation satellite has an intensity enhancement of about two orders of magnitude at resonance. The angular dependence of the photoemission intensity has been studied as function of photon energy and provides unambiguous eviden…
▽ More
Angle-resolved valence-band resonant photoemission of nickel metal has been measured close to the 2p core-level thresholds with synchrotron radiation. The well-known 6-eV correlation satellite has an intensity enhancement of about two orders of magnitude at resonance. The angular dependence of the photoemission intensity has been studied as function of photon energy and provides unambiguous evidence for interference effects all the way up to the resonance maximum. The observation of different angular asymmetries, β, for the valence band and the satellite is discussed in connection to the origin of the resonant photoemission process and the character of the satellite.
△ Less
Submitted 4 January, 2012;
originally announced January 2012.
-
Electronic structure investigation of CoO by means of soft X-ray scattering
Authors:
M. Magnuson,
S. M. Butorin,
J. -H. Guo,
J. Nordgren
Abstract:
The electronic structure of CoO is studied by resonant inelastic soft X-ray scattering spectroscopy using photon energies across the Co 2p absorption edges. The different spectral contributions from the energy-loss structures are identified as Raman scattering due to d-d and charge-transfer excitations. For excitation energies close to the L3 resonance, the spectral features are dominated by quart…
▽ More
The electronic structure of CoO is studied by resonant inelastic soft X-ray scattering spectroscopy using photon energies across the Co 2p absorption edges. The different spectral contributions from the energy-loss structures are identified as Raman scattering due to d-d and charge-transfer excitations. For excitation energies close to the L3 resonance, the spectral features are dominated by quartet-quartet and quartet-doublet transitions of the 3d7 configuration. At excitation energies corresponding to the satellites in the Co 2p X-ray absorption spectrum of CoO, the emission features are instead dominated by charge-transfer transitions to the 3d8L-1 final state. The spectra are interpreted and discussed with the support of simulations within the single impurity Anderson model with full multiplet effects which are found to yield consistent spectral functions to the experimental data.
△ Less
Submitted 3 January, 2012;
originally announced January 2012.
-
Electronic structure investigation of CeB6 by means of soft X-ray scattering
Authors:
M. Magnuson,
S. M. Butorin,
J. -H. Guo,
A. Agui,
J. Nordgren,
H. Ogasawara,
A. Kotani,
T. Takahashi,
S. Kunii
Abstract:
The electronic structure of the heavy fermion compound CeB6 is probed by resonant inelastic soft X-ray scattering using photon energies across the Ce 3d and 4d absorption edges. The hybridization between the localized 4f orbitals and the delocalized valence-band states is studied by identifying the different spectral contributions from inelastic Raman scattering and normal fluorescence. Pronounced…
▽ More
The electronic structure of the heavy fermion compound CeB6 is probed by resonant inelastic soft X-ray scattering using photon energies across the Ce 3d and 4d absorption edges. The hybridization between the localized 4f orbitals and the delocalized valence-band states is studied by identifying the different spectral contributions from inelastic Raman scattering and normal fluorescence. Pronounced energy-loss structures are observed below the elastic peak at both the 3d and 4d thresholds. The origin and character of the inelastic scattering structures are discussed in terms of charge-transfer excitations in connection to the dipole allowed transitions with 4f character. Calculations within the single impurity Anderson model with full multiplet effects are found to yield consistent spectral functions to the experimental data.
△ Less
Submitted 3 January, 2012;
originally announced January 2012.
-
Resonant soft X-ray Raman scattering of NiO
Authors:
M. Magnuson,
S. M. Butorin,
A. Agui,
J. Nordgren
Abstract:
Resonant soft X-ray Raman scattering measurements on NiO have been made at photon energies across the Ni 2p absorption edges. The details of the spectral features are identified as Raman scattering due to d-d and charge-transfer excitations. The spectra are interpreted within the single impurity Anderson model, including multiplets, crystal-field and charge-transfer effects. At threshold excitatio…
▽ More
Resonant soft X-ray Raman scattering measurements on NiO have been made at photon energies across the Ni 2p absorption edges. The details of the spectral features are identified as Raman scattering due to d-d and charge-transfer excitations. The spectra are interpreted within the single impurity Anderson model, including multiplets, crystal-field and charge-transfer effects. At threshold excitation, the spectral features consists of triplet-triplet and triplet-singlet transitions of the 3d8 configuration. For excitation energies corresponding to the charge-transfer region in the Ni 2p X-ray absorption spectrum of NiO, the emission spectra are instead dominated by charge-transfer transitions to the 3d9L-1 final state. Comparisons of the final states with other spectroscopical techniques are also made.
△ Less
Submitted 3 January, 2012;
originally announced January 2012.
-
X-ray fluorescence spectra of metals excited below threshold
Authors:
M. Magnuson,
J. -E. Rubensson,
A. Föhlisch,
N. Wassdahl,
A. Nilsson,
N. Mårtensson
Abstract:
X-ray scattering spectra of Cu and Ni metals have been measured using monochromatic synchrotron radiation tuned from far above to more than 10 eV below threshold. Energy conservation in the scattering process is found to be sufficient to explain the modulation of the spectral shape, neglecting momentum conservation and channel interference. At excitation energies close to and above threshold, the…
▽ More
X-ray scattering spectra of Cu and Ni metals have been measured using monochromatic synchrotron radiation tuned from far above to more than 10 eV below threshold. Energy conservation in the scattering process is found to be sufficient to explain the modulation of the spectral shape, neglecting momentum conservation and channel interference. At excitation energies close to and above threshold, the emission spectra map the occupied local partial density of states. For the sub-threshold excitations, the high-energy flank of the inelastic scattering exhibits a Raman-type linear dispersion, and an asymmetric low energy tail develops. For excitation far below threshold the emission spectra are proportional to a convolution of the occupied and unoccuppied local partial densities of states.
△ Less
Submitted 3 January, 2012;
originally announced January 2012.
-
Refractive index of vanadium determined by resonant diffraction of soft x-rays
Authors:
Martin Magnuson,
Coryn F. Hague
Abstract:
The dispersive part of the refractive index of vanadium is determined by measuring the angular displacement of the first order diffraction peak of a V/Fe superlattice. The measurements were made using elliptically polarized synchrotron radiation which was scanned through the V L2,3 absorption edges for different incident scattering angles. The x-ray scattering technique provides access to direct d…
▽ More
The dispersive part of the refractive index of vanadium is determined by measuring the angular displacement of the first order diffraction peak of a V/Fe superlattice. The measurements were made using elliptically polarized synchrotron radiation which was scanned through the V L2,3 absorption edges for different incident scattering angles. The x-ray scattering technique provides access to direct determination of the dispersive part of the refractive index through an absorption resonance. The influence of absorption at the resonances is shown by comparing the absorption correction to the dispersion correction. The results demonstrate that 1-δ is larger than unity at the L2,3 resonances of vanadium and the optical consequences are discussed.
△ Less
Submitted 30 December, 2011;
originally announced January 2012.
-
Large magnetic circular dichroism in resonant inelastic x-ray scattering at the Mn L-edge of Mn-Zn ferrite
Authors:
M. Magnuson,
L. -C. Duda,
S. M. Butorin,
P. Kuiper,
J. Nordgren
Abstract:
We report resonant inelastic x-ray scattering (RIXS) excited by circularly polarized x-rays on Mn-Zn ferrite at the Mn L2,3-resonances. We demonstrate that crystal field excitations, as expected for localized systems, dominate the RIXS spectra and thus their dichroic asymmetry cannot be interpreted in terms of spin-resolved partial density of states, which has been the standard approach for RIXS d…
▽ More
We report resonant inelastic x-ray scattering (RIXS) excited by circularly polarized x-rays on Mn-Zn ferrite at the Mn L2,3-resonances. We demonstrate that crystal field excitations, as expected for localized systems, dominate the RIXS spectra and thus their dichroic asymmetry cannot be interpreted in terms of spin-resolved partial density of states, which has been the standard approach for RIXS dichroism. We observe large dichroic RIXS at the L2-resonance which we attribute to the absence of metallic core hole screening in the insulating Mn-ferrite. On the other hand, reduced L3-RIXS dichroism is interpreted as an effect of longer scattering time that enables spin-lattice core hole relaxation via magnons and phonons occurring on a femtosecond time scale.
△ Less
Submitted 30 December, 2011;
originally announced January 2012.
-
Electronic structure investigation of Ti3AlC2, Ti3SiC2, and Ti3GeC2 by soft-X-ray emission spectroscopy
Authors:
M. Magnuson,
J. -P. Palmquist,
M. Mattesini,
S. Li,
R. Ahuja,
O. Eriksson,
J. Emmerlich,
O. Wilhelmsson,
P. Eklund,
H. Högberg,
L. Hultman,
U. Jansson
Abstract:
The electronic structures of epitaxially grown films of Ti3AlC2, Ti3SiC2 and Ti3GeC2 have been investigated by bulk-sensitive soft X-ray emission spectroscopy. The measured high-resolution Ti L, C K, Al L, Si L and Ge M emission spectra are compared with ab initio density-functional theory including core-to-valence dipole matrix elements. A qualitative agreement between experiment and theory is ob…
▽ More
The electronic structures of epitaxially grown films of Ti3AlC2, Ti3SiC2 and Ti3GeC2 have been investigated by bulk-sensitive soft X-ray emission spectroscopy. The measured high-resolution Ti L, C K, Al L, Si L and Ge M emission spectra are compared with ab initio density-functional theory including core-to-valence dipole matrix elements. A qualitative agreement between experiment and theory is obtained. A weak covalent Ti-Al bond is manifested by a pronounced shoulder in the Ti L-emission of Ti3AlC2. As Al is replaced with Si or Ge, the shoulder disappears. For the buried Al and Si-layers, strongly hybridized spectral shapes are detected in Ti3AlC2 and Ti3SiC2, respectively. As a result of relaxation of the crystal structure and the increased charge-transfer from Ti to C, the Ti-C bonding is strengthened. The differences between the electronic structures are discussed in relation to the bonding in the nanolaminates and the corresponding change of materials properties.
△ Less
Submitted 29 December, 2011;
originally announced December 2011.
-
Electronic structure and chemical bonding in Ti4SiC3 investigated by soft x-ray emission spectroscopy and first principle theory
Authors:
M. Magnuson,
M. Mattesini,
O. Wilhelmsson,
J. Emmerlich,
J. -P. Palmquist,
S. Li,
R. Ahuja,
L. Hultman,
O. Eriksson,
U. Jansson
Abstract:
The electronic structure in the new transition metal carbide Ti4SiC3 has been investigated by bulk-sensitive soft x-ray emission spectroscopy and compared to the well-studied Ti3SiC2 and TiC systems. The measured high-resolution Ti L, C K and Si L x-ray emission spectra are discussed with ab initio calculations based on density-functional theory including core-to-valence dipole matrix elements. Th…
▽ More
The electronic structure in the new transition metal carbide Ti4SiC3 has been investigated by bulk-sensitive soft x-ray emission spectroscopy and compared to the well-studied Ti3SiC2 and TiC systems. The measured high-resolution Ti L, C K and Si L x-ray emission spectra are discussed with ab initio calculations based on density-functional theory including core-to-valence dipole matrix elements. The detailed investigations of the Ti-C and Ti-Si chemical bonds provide increased understanding of the physical properties of these nanolaminates. A strongly modified spectral shape is detected for the buried Si monolayers due to Si 3p hybridization with the Ti 3d orbitals. As a result of relaxation of the crystal structure and the charge-transfer from Ti (and Si) to C, the strength of the Ti-C covalent bond is increased. The differences between the electronic and crystal structures of Ti4SiC3 and Ti3SiC2 are discussed in relation to the number of Si layers per Ti layer in the two systems and the corresponding change of materials properties.
△ Less
Submitted 29 December, 2011;
originally announced December 2011.
-
Anisotropy in the electronic structure of V2GeC investigated by soft x-ray emission spectroscopy and first-principles theory
Authors:
Martin Magnuson,
Ola Wilhelmsson,
Maurizio Mattesini,
Sa Li,
Rajeev Ahuja,
Olle Eriksson,
Hans Högberg,
Lars Hultman,
Ulf Jansson
Abstract:
The anisotropy of the electronic structure of ternary nanolaminate V2GeC is investigated by bulk-sensitive soft x-ray emission spectroscopy. The measured polarization-dependent emission spectra of V L2,3, C K, Ge M1 and Ge M2,3 in V2GeC are compared to those from monocarbide VC and pure Ge. The experimental emission spectra are interpreted with calculated spectra using ab initio density-functional…
▽ More
The anisotropy of the electronic structure of ternary nanolaminate V2GeC is investigated by bulk-sensitive soft x-ray emission spectroscopy. The measured polarization-dependent emission spectra of V L2,3, C K, Ge M1 and Ge M2,3 in V2GeC are compared to those from monocarbide VC and pure Ge. The experimental emission spectra are interpreted with calculated spectra using ab initio density-functional theory including dipole transition matrix elements. Different types of covalent chemical bond regions are revealed; V 3d - C 2p bonding at -3.8 eV, Ge 4p - C 2p bonding at -6 eV and Ge 4p - C 2s interaction mediated via the V 3d orbitals at -11 eV below the Fermi level. We find that the anisotropic effects are high for the 4p valence states and the shallow 3d core levels of Ge, while relatively small anisotropy is detected for the V 3d states. The macroscopic properties of the V2GeC nanolaminate result from the chemical bonds with the anisotropic pattern as shown in this work.
△ Less
Submitted 29 December, 2011;
originally announced December 2011.
-
Bonding mechanism in the nitrides Ti2AlN and TiN: an experimental and theoretical investigation
Authors:
M. Magnuson,
M. Mattesini,
S. Li,
C. Höglund,
M. Beckers,
L. Hultman,
O. Eriksson
Abstract:
The electronic structure of nanolaminate Ti2AlN and TiN thin films has been investigated by bulk-sensitive soft x-ray emission spectroscopy. The measured Ti L, N K, Al L1 and Al L2,3 emission spectra are compared with calculated spectra using ab initio density-functional theory including dipole transition matrix elements. Three different types of bond regions are identified; a relatively weak Ti 3…
▽ More
The electronic structure of nanolaminate Ti2AlN and TiN thin films has been investigated by bulk-sensitive soft x-ray emission spectroscopy. The measured Ti L, N K, Al L1 and Al L2,3 emission spectra are compared with calculated spectra using ab initio density-functional theory including dipole transition matrix elements. Three different types of bond regions are identified; a relatively weak Ti 3d - Al 3p bonding between -1 and -2 eV below the Fermi level, and Ti 3d - N 2p and Ti 3d - N 2s bonding which are deeper in energy observed at -4.8 eV and -15 eV below the Fermi level, respectively. A strongly modified spectral shape of 3s states of Al L2,3 emission from Ti2AlN in comparison to pure Al metal is found, which reflects the Ti 3d - Al 3p hybridization observed in the Al L1 emission. The differences between the electronic and crystal structures of Ti2AlN and TiN are discussed in relation to the intercalated Al layers of the former compound and the change of the materials properties in comparison to the isostructural carbides.
△ Less
Submitted 28 December, 2011;
originally announced December 2011.
-
Electronic structure and chemical bonding anisotropy investigation of wurtzite AlN
Authors:
M. Magnuson,
M. Mattesini,
C. Höglund,
J. Birch,
L. Hultman
Abstract:
The electronic structure and the anisotropy of the Al - N π and σ chemical bonding of wurtzite AlN has been investigated by bulk-sensitive total fluorescence yield absorption and soft x-ray emission spectroscopies. The measured N K, Al L1, and Al L2,3 x-ray emission and N 1s x-ray absorption spectra are compared with calculated spectra using first principles density-functional theory including dip…
▽ More
The electronic structure and the anisotropy of the Al - N π and σ chemical bonding of wurtzite AlN has been investigated by bulk-sensitive total fluorescence yield absorption and soft x-ray emission spectroscopies. The measured N K, Al L1, and Al L2,3 x-ray emission and N 1s x-ray absorption spectra are compared with calculated spectra using first principles density-functional theory including dipole transition matrix elements. The main N 2p - Al 3p hybridization regions are identified at -1.0 to -1.8 eV and -5.0 to -5.5 eV below the top of the valence band. In addition, N 2s - Al 3p and N 2s - Al 3s hybridization regions are found at the bottom of the valence band around -13.5 eV and -15 eV, respectively. A strongly modified spectral shape of Al 3s states in the Al L2,3 emission from AlN in comparison to Al metal is found, which is also reflected in the N 2p - Al 3p hybridization observed in the Al L1 emission. The differences between the electronic structure and chemical bonding of AlN and Al metal are discussed in relation to the position of the hybridization regions and the valence band edge influencing the magnitude of the large band gap.
△ Less
Submitted 28 December, 2011;
originally announced December 2011.
-
Electronic structure and chemical bonding of nc-TiC/a-C nanocomposites
Authors:
Martin Magnuson,
Erik Lewin,
Lars Hultman,
Ulf Jansson
Abstract:
The electronic structure of nanocrystalline (nc-) TiC/amorphous C nanocomposites has been investigated by soft x-ray absorption and emission spectroscopy. The measured spectra at the Ti 2p and C 1s thresholds of the nanocomposites are compared to those of Ti metal and amorphous C. The corresponding intensities of the electronic states for the valence and conduction bands in the nanocomposites are…
▽ More
The electronic structure of nanocrystalline (nc-) TiC/amorphous C nanocomposites has been investigated by soft x-ray absorption and emission spectroscopy. The measured spectra at the Ti 2p and C 1s thresholds of the nanocomposites are compared to those of Ti metal and amorphous C. The corresponding intensities of the electronic states for the valence and conduction bands in the nanocomposites are shown to strongly depend on the TiC carbide grain size. An increased charge-transfer between the Ti 3d-eg states and the C 2p states has been identified as the grain size decreases, causing an increased ionicity of the TiC nanocrystallites. It is suggested that the charge-transfer occurs at the interface between the nanocrystalline TiC and the amorphous C matrix and represents an interface bonding which may be essential for the understanding of the properties of nc-TiC/amorphous C and similar nanocomposites.
△ Less
Submitted 28 December, 2011; v1 submitted 15 December, 2011;
originally announced December 2011.
-
Spin transition in LaCoO3 investigated by resonant soft X-ray emission spectroscopy
Authors:
M. Magnuson,
S. M. Butorin,
C. Såthe,
J. Nordgren,
P. Ravindran
Abstract:
The spin transition in LaCoO3 is investigated by temperature-dependent resonant soft X-ray emission spectroscopy near the Co 2p absorption edges. This element-specific technique is more bulk sensitive with respect to the temperature induced spin-state of the Co3+ ions in LaCoO3 than other high-energy spectroscopic methods. The spin transition is interpreted and discussed with ab-initio density-fun…
▽ More
The spin transition in LaCoO3 is investigated by temperature-dependent resonant soft X-ray emission spectroscopy near the Co 2p absorption edges. This element-specific technique is more bulk sensitive with respect to the temperature induced spin-state of the Co3+ ions in LaCoO3 than other high-energy spectroscopic methods. The spin transition is interpreted and discussed with ab-initio density-functional theory within the fixed-spin moment method, which is found to yield consistent spectral functions to the experimental data. The spectral changes for LaCoO3 as a function of temperature suggest a change in spin-state as the temperature is raised from 85 to 300 K while the system remains in the same spin state as the temperature is further increased to 510 K.
△ Less
Submitted 29 December, 2011; v1 submitted 14 December, 2011;
originally announced December 2011.