Effects of Thermal Modification on the Flexure Properties, Fracture Energy, and Hardness of Western Hemlock
Authors:
Troy Nakagawa,
Erik Poulin,
Talbot Rueppel,
Zhisong Chen,
Juliet Swinea,
Mark O'Brien,
Guy Houser,
Geoffrey Wood,
Malloree Weinheimer,
Pouria Bahmani,
Peter Stynoski,
Marco Salviato
Abstract:
This study investigates the effect of thermal modification on the flexural properties, transverse fracture energy, and hardness of western hemlock, a material which is finding increasing applications in construction. Flexure tests on specimens featuring longitudinal and transverse grains showed that thermal modification at 167C slightly improves the flexural modulus and strength and leads to less…
▽ More
This study investigates the effect of thermal modification on the flexural properties, transverse fracture energy, and hardness of western hemlock, a material which is finding increasing applications in construction. Flexure tests on specimens featuring longitudinal and transverse grains showed that thermal modification at 167C slightly improves the flexural modulus and strength and leads to less statistical variability compared to unmodified samples. On the other hand, the fracture and Janka hardness tests revealed a more pronounced brittleness of the thermally modified samples. In fact, the total mode I fracture energy of modified Single Edge Notch Bending (SENB) samples was about 47% lower for radial-longitudinal systems and 60% lower for tangential-longitudinal systems. Similarly, the average Janka hardness in the tangential, radial, and transverse planes was 8.5%, 3.9%, and 9.4% lower in the modified specimens, respectively. The results presented in this work show that thermal modification can have a significant effect on the fracturing behavior of western hemlock and its energy dissipation capabilities. For design, this must be taken into serious consideration as these properties significantly influence the damage tolerance of this wood in the presence of stress concentrations such as e.g., those induced in bolted joints and cut outs. Fracture energy and hardness are also strongly correlated to ballistic performance.
△ Less
Submitted 31 March, 2023;
originally announced April 2023.
Effects of Out Time on the Mechanical and Fracture Properties of Chopped Fiber Composites Made From Repurposed Aerospace Prepreg Scrap and Waste
Authors:
Troy Nakagawa,
Seunghyun Ko,
Cory Slaughter,
Talal Abdullah,
Guy Houser,
Marco Salviato
Abstract:
In this study, the effects of prepreg out time on the mechanical and fracture properties of Discontinuous Fiber Composites (DFCs) are investigated. Carbon fiber prepregs are aged at 0x, 1x, 2x, and 3x the out life in an environmental chamber at constant temperature and humidity. Degree of cure is measured via Differential Scanning Calorimetry (DSC) while tension, compression, and shear tests are p…
▽ More
In this study, the effects of prepreg out time on the mechanical and fracture properties of Discontinuous Fiber Composites (DFCs) are investigated. Carbon fiber prepregs are aged at 0x, 1x, 2x, and 3x the out life in an environmental chamber at constant temperature and humidity. Degree of cure is measured via Differential Scanning Calorimetry (DSC) while tension, compression, and shear tests are performed to investigate the effects that aging has on these mechanical properties. For the first time, Mode I intra-laminar fracture and its size effect are also investigated by means of fracture tests on geometrically-scaled Single Edge Notch Tension (SENT) specimens.
From the tension, compression, and shear experiments it is seen that the out time has no effect on the elastic moduli. However, the strength increases with increasing age of the specimens for all the loading conditions. The percent increase compared to the non-aged material ranges from 15% to 33%. This is likely caused by plasticization of the matrix with age, allowing for higher energy absorption.
More complex trends are reported for the SENT specimens for all the sizes. It is found that the fracture energy and characteristic length initially decrease with age, and then finally increase for the longest out time. This trend is owed to two factors with countering effects on the fracture behavior: 1) the increase of the average number of platelets with increasing aging due to increase in resin viscosity, and 2) the plasticization of the matrix with aging.
The results from this study suggest that Discontinuous Fiber Composites (DFCs) made from reused materials can have equal, if not better, performance than non-aged DFCs. The experimental data presented in this work can be used as a baseline to design DFC composite components made from repurposed prepreg scrap and waste.
△ Less
Submitted 21 December, 2021;
originally announced December 2021.