The nontrivial effects of annealing on superconducting properties of Nb single crystals
Authors:
Amlan Datta,
Kamal R. Joshi,
Giulia Berti,
Sunil Ghimire,
Aidan Goerdt,
Makariy A. Tanatar,
Deborah L. Schlagel,
Matthew F. Besser,
Dapeng **g,
Matthew Kramer,
Maria Iavarone,
Ruslan Prozorov
Abstract:
The effect of annealing on the superconducting properties of niobium single crystals cut from the same master boule was studied by local and global magnetic measurements, as well as scanning tunneling microscopy (STM). The formation of large hydride precipitates was observed in unannealed samples. The variation in structural and magnetic properties was studied after annealing under high vacuum at…
▽ More
The effect of annealing on the superconducting properties of niobium single crystals cut from the same master boule was studied by local and global magnetic measurements, as well as scanning tunneling microscopy (STM). The formation of large hydride precipitates was observed in unannealed samples. The variation in structural and magnetic properties was studied after annealing under high vacuum at 800 C, 1400 C, and near the melting point of niobium (2477 C) for a few seconds. The initial samples had a high hydrogen content. Polarized optics and magneto-optical studies show that the formation of large niobium hydride precipitates is suppressed already by 800 C annealing. However, the overall superconducting properties in the annealed samples did not improve after annealing, and in fact, worsened. The superconducting transition temperature decreased, the upper critical field increased, and the pinning strength increased. Parallel studies were conducted using STM, where the sample was annealed initially at 400 C, measured, annealed again at 1700 C, and measured again. These studies revealed a ``dirty'' superconducting gap with a significant spatial variation of tunneling conductance after annealing at 400 C. The clean gap was recovered after annealing at 1700 C. It is likely that these results are due to oxygen redistribution near the surface, which is always covered by oxide layers in as-grown crystals. Overall, the results indicate that vacuum annealing at least up to 1400 C, while expected to remove a large amount of hydrogen, introduces additional nanosized defects, perhaps hydride precipitates, that act as efficient pair-breaking and pinning centers.
△ Less
Submitted 24 March, 2024;
originally announced March 2024.
Quasiparticle spectroscopy in technologically-relevant niobium using London penetration depth measurements
Authors:
Sunil Ghimire,
Kamal R. Joshi,
Amlan Datta,
Aidan Goerdt,
Makariy A. Tanatar,
Deborah Schlagel,
Matthew J. Kramer,
Jayss Marshall,
Cameron J. Copas,
Joshua Y. Mutus,
Alexander Romanenko,
Anna Grassellino,
Ruslan Prozorov
Abstract:
London penetration depth was measured in niobium foils, thin films, single crystals, and superconducting radio-frequency (SRF) cavity pieces cut out from different places. The low-temperature (T<Tc/3) variation, sensitive to the low-energy quasiparticles with states inside the superconducting gap, differs dramatically between different types of samples. With the help of phenomenological modeling,…
▽ More
London penetration depth was measured in niobium foils, thin films, single crystals, and superconducting radio-frequency (SRF) cavity pieces cut out from different places. The low-temperature (T<Tc/3) variation, sensitive to the low-energy quasiparticles with states inside the superconducting gap, differs dramatically between different types of samples. With the help of phenomenological modeling, we correlate these different behaviors with known pair-breaking mechanisms and show that such measurements may help distinguish between different pair-breaking mechanisms, such as niobium hydrides and two-level systems (TLS). The conclusions also apply to SRF cavities when tracking the temperature-dependent quality factor and the resonant frequency.
△ Less
Submitted 23 June, 2023;
originally announced June 2023.