Showing 1–50 of 67 results for author: Dhaka, R S

Structural properties, dielectric relaxation and impedance spectroscopy of NASICON type Na$_{3+x}$Zr$_{2-x}$Pr$_{x}$Si$_2$PO$_{\rm 12}$ ceramics

Authors: Ramcharan Meena, Rajendra S. Dhaka

Abstract: We investigate the dielectric and impedance spectroscopic investigation of Pr-doped NASICON type Na$_{3+x}$Zr$_{2-x}$Pr$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) samples as a function of temperature and frequency. The Rietveld refinement of x-ray diffraction patterns confirms the monoclinic phase having C2/c space groups for all the samples. The scanning electron microscopy shows the granular-like… ▽ More We investigate the dielectric and impedance spectroscopic investigation of Pr-doped NASICON type Na$_{3+x}$Zr$_{2-x}$Pr$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) samples as a function of temperature and frequency. The Rietveld refinement of x-ray diffraction patterns confirms the monoclinic phase having C2/c space groups for all the samples. The scanning electron microscopy shows the granular-like structure and energy dispersive x-ray analysis confirms the desired compositions. The temperature (90--400~K) and frequency (20 Hz-2 MHz) dependence of electric permittivity are explained using Maxwell-Wagner-Sillars (MWS) polarization and space charge polarization mechanisms. The dielectric relaxation shows nearly equal activation energy for all the samples with a non-Debye type of relaxation in the measured temperature range. The complex impedance analysis shows the presence of broad grain and grain boundary relaxation peaks. The stretched exponent analysis of electric modulus using the Kohlrausch-Williams-Watts (KWW) function further confirms the non-Debye type of relaxation. Moreover, scaling analysis of the electric modulus shows a similar type of relaxation for all the samples. The {\it a.c.} conductivity data are fitted using modified power law, where the temperature dependence of exponent ($s$) confirms the correlated barrier hop** (CBH) type conduction for all the samples. Our results indicate that the Pr doped NASICON samples are potential candidates for charge storage devices due to their large electric permittivity. △ Less

Submitted 19 May, 2024; originally announced May 2024.

Comments: submitted

Observation of an unconventional giant negative exchange bias effect in La$_{0.5}$Sr$_{0.5}$Co$_{0.85}$Nb$_{0.15}$O$_3$

Authors: Rishabh Shukla, B. Schwarz, R. S. Dhaka

Abstract: We find an unconventional giant negative exchange bias (EB) of $H_{\rm EB}$ = --14.1~kOe at 2~K (cooling field of 50~kOe) in the cluster spin-glass (CSG) La$_{0.5}$Sr$_{0.5}$Co$_{0.85}$Nb$_{0.15}$O$_3$ perovsikte cobaltites. The magnetic memory effect, aging measurements, and nonlineraity in specific heat capacity reveal the glassy magnetic state at low temperatures. Further, the detailed analysis… ▽ More We find an unconventional giant negative exchange bias (EB) of $H_{\rm EB}$ = --14.1~kOe at 2~K (cooling field of 50~kOe) in the cluster spin-glass (CSG) La$_{0.5}$Sr$_{0.5}$Co$_{0.85}$Nb$_{0.15}$O$_3$ perovsikte cobaltites. The magnetic memory effect, aging measurements, and nonlineraity in specific heat capacity reveal the glassy magnetic state at low temperatures. Further, the detailed analysis of {\it ac-}magnetic susceptibility confirms the glassy state below $\sim$58~K and the obtained characteristic spin-relaxation time-scale of $τ_0$ = 8.4$\times$10$^{-10}$~s indicates the presence of CSG. Moreover, the analysis of magnetic training effect using the classical EB relaxation model reveals that the frozen spins relax slowly as compared to the rotatable spins at the interface of antiferromagnetic/ferromagnetic (AFM/FM) regions in CSG. Interestingly, the dependence of EB parameters is found to be unconventional for cooling field $>$50~kOe as the $H\rm_{EB}$ and $M\rm_{EB}$ show decreasing trend instead of expected saturation at higher fields. This unusual nature emerges due to large negative values of intrinsic interface exchange coupling ($J_i$), i.e., --10.24$\pm$0.22~meV and --12.55$\pm$0.49~meV for the measuring fields of $\pm$50~kOe and $\pm$90~kOe, respectively, whereas the number of spins in the FM cluster ($N_{\rm FM}$) are found to be small in the range of 2.4--3.1. These obtained values of $J_i $ and $N_{\rm FM}$ indicate the dominant AFM interactions and the presence of FM clusters in the AFM matrix, respectively, which correlate well with the observed unconventional behavior of giant negative exchange bias in the present sample. △ Less

Submitted 8 May, 2024; originally announced May 2024.

Comments: submitted

Mixed Polyanionic NaFe$_{1.6}$V$_{0.4}$(PO$_{4}$)(SO$_{4}$)$_{2}$@CNT Cathode for Sodium-ion Batteries: Electrochemical Diffusion Kinetics and Distribution of Relaxation Time Analysis at Different Temperatures

Authors: Jayashree Pati, Rajendra S. Dhaka

Abstract: We report the electrochemical sodium-ion kiinetics and distribution of relaxation time (DRT) analysis of a newly designed mixed polyanionic NaFe$_{1.6}$V$_{0.4}$(PO$_{4}$)(SO$_{4}$)$_{2}$@CNT composite as a cathode. The specific capacity of 104 mAhg$^{-1}$ is observed at 0.1~C with the average working voltage of $\sim$3~V. Intriguingly, a remarkable rate capability and reversibility are demonstrat… ▽ More We report the electrochemical sodium-ion kiinetics and distribution of relaxation time (DRT) analysis of a newly designed mixed polyanionic NaFe$_{1.6}$V$_{0.4}$(PO$_{4}$)(SO$_{4}$)$_{2}$@CNT composite as a cathode. The specific capacity of 104 mAhg$^{-1}$ is observed at 0.1~C with the average working voltage of $\sim$3~V. Intriguingly, a remarkable rate capability and reversibility are demonstrated up to very high current rate of 25~C. The long cycling test up to 10~C shows high capacity retention even after 2000 cycles. The detailed analysis of galvanostatic intermittent titration technique (GITT) and cyclic voltammetry (CV) data reveal the diffusion coefficient of 10$^{-8}$--10$^{-11}$ cm$^{2}$s$^{-1}$. We find excellent stability in the thermal testing between 25--55$^\circ$C temperatures and 80\% capacity retention up to 100 cycles at 5~C. Further, we analyse the individual electrochemical processes in the time domain using the novel DRT technique at different temperatures. The {\it ex-situ} investigation shows the stable and reversible structure, morphology and electronic states of the long cycled cathode material. More importantly, we demonstrate relatively high specific energy of $\approx$155 Wh kg$^{-1}$ (considering the total active material loading of both the electrodes) at 0.2~C for full cell battery having excellent rate capability up to 10~C and long cyclic stability at 1~C. △ Less

Submitted 19 April, 2024; originally announced April 2024.

Comments: submitted

Temperature dependent conductivity, dielectric relaxation, electrical modulus and impedance spectroscopy of Ni substituted Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$

Authors: Ramcharan Meena, Rajendra S. Dhaka

Abstract: We investigate the structural, dielectric relaxation, electric modulus and impedance behavior of Ni-doped NASICON ceramic Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) prepared using the solid-state reaction method. The increase in dielectric constant with temperature and decrease with frequency is explained on the basis of space charge polarization using the two-layer model of… ▽ More We investigate the structural, dielectric relaxation, electric modulus and impedance behavior of Ni-doped NASICON ceramic Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) prepared using the solid-state reaction method. The increase in dielectric constant with temperature and decrease with frequency is explained on the basis of space charge polarization using the two-layer model of Maxwell-Wagner relaxation. The dielectric loss peak at lower temperatures follows the Arrhenius-type behavior with frequency having activation energy of 0.27$\pm$0.01~eV of dipolar relaxation, suggests similar type of defects are responsible for all the doped samples. The real ($ε$ $^{'}$) and imaginary ($ε$ $^{''}$) permittivity variation with frequency shows the broad relaxation behavior indicates the non-Debye type of relaxation in the measured temperature range. The permittivity values decrease with the amount of do** due to the increased number of charge carriers upon Ni do** at the Zr site. The grain contributions are observed at higher frequencies, while grain-boundary contributions occur at the lower side of frequencies. The imaginary part of the electric modulus also shows two types of relaxation peaks for all the samples indicating similar activation energy at low temperatures and variable activation energy at higher temperatures. The fitting of the imaginary modulus using KWW function shows the non-Debye type of relaxation. We find that all modulus curves merge with each other at low temperatures showing a similar type of relaxation, while curves at high temperatures show the dispersed behavior above the peak frequency. The {\it a.c.} conductivity data are fitted using the double power law confirming the grain and grain boundary contributions in total conductivity. △ Less

Submitted 21 March, 2024; originally announced March 2024.

Comments: submitted

Antiferromagnetic ordering and glassy nature in NASICON type NaFe$_2$PO$_4$(SO$_4$)$_2$

Authors: Manish Kr. Singh, A. K. Bera, Ajay Kumar, S. M. Yusuf, R. S. Dhaka

Abstract: We investigate crystal structure and magnetic properties including spin relaxation and magnetocaloric effect in NASICON type NaFe$_2$PO$_4$(SO$_4$)$_2$ sample. The Rietveld refinement of x-ray and neutron diffraction patterns show a rhombohedral crystal structure with the R$\bar{3}$c space group. The core-level spectra confirm the desired oxidation state of constituent elements. The {\it dc}--magn… ▽ More We investigate crystal structure and magnetic properties including spin relaxation and magnetocaloric effect in NASICON type NaFe$_2$PO$_4$(SO$_4$)$_2$ sample. The Rietveld refinement of x-ray and neutron diffraction patterns show a rhombohedral crystal structure with the R$\bar{3}$c space group. The core-level spectra confirm the desired oxidation state of constituent elements. The {\it dc}--magnetic susceptibility ($χ$) behavior in zero field-cooled (ZFC) and field-cooled (FC) modes show the ordering temperature $\approx$50~K. Interestingly, the analysis of temperature dependent neutron diffraction patterns reveal an A-type antiferromagnetic (AFM) structure with the ordered moment of 3.8 $μ_{B}$/Fe$^{3+}$ at 5~K, and a magnetostriction below $T_{\rm N}=$ 50~K. Further, the peak position in the {\it ac}--$χ$ is found to be invariant with the excitation frequency supporting the notion of dominating AFM transition. Also, the unsaturated isothermal magnetization curve supports the AFM ordering of the moments; however, the observed coercivity suggests the presence of weak ferromagnetic (FM) correlations at 5~K. On the other hand, a clear bifurcation between ZFC and FC curves of {\it dc}--$χ$ and the observed decrease in peak height of {\it ac}--$χ$ with frequency suggest for the complex magnetic interactions. The spin relaxation behavior in thermo-remanent magnetization and aging measurements indicate the glassy states at 5~K. Moreover, the Arrott plots and magnetocaloric analysis reveal the AFM--FM interactions in the sample at lower temperatures. △ Less

Submitted 13 March, 2024; originally announced March 2024.

Comments: submitted

Understanding the electrochemical performance and diffusion kinetics of HC$||$Na$_3$V$_2$(PO$_4$)$_3$/C full cell battery for energy storage applications

Authors: Madhav Sharma, Rajendra S. Dhaka

Abstract: The efficient energy storage devices are crucial to meet the soaring global energy demand for sustainable future. Recently, the sodium-ion batteries (SIBs) have emerged as one of the excellent cost effective solution due to the uniform geographical distribution and abundance of sodium. Here, we use hard carbon (HC) as an anode and Na$_3$V$_2$(PO$_4$)$_3$/C (NVP/C) as a cathode to fabricate a HC… ▽ More The efficient energy storage devices are crucial to meet the soaring global energy demand for sustainable future. Recently, the sodium-ion batteries (SIBs) have emerged as one of the excellent cost effective solution due to the uniform geographical distribution and abundance of sodium. Here, we use hard carbon (HC) as an anode and Na$_3$V$_2$(PO$_4$)$_3$/C (NVP/C) as a cathode to fabricate a HC$||$NVP/C full cell battery and understand its electrochemical performance and diffusion kinetics. These materials are characterized through the analysis of x-ray diffraction and Raman spectroscopy to confirm their single phase and structure. The full cell demonstrates a high operating voltage of $\sim$3.3 V, with minimal polarization of 0.05 V, attributed to the lower working voltage of the HC. Interestingly, for the full cell battery we find the specific capacity of around 70 mAh/g at 0.1 C and even around 35 mAh/g at high current rate of 5 C along with high rate capability up to 55 cycles. The diffusion kinetics of the full cell battery is investigated through detailed analysis of CV curves at various scan rates, and the diffusion coefficient is found to be 5--8$\times$10$^{-11}$ cm$^2$/s for the anodic as well as cathodic peaks. △ Less

Submitted 27 January, 2024; originally announced January 2024.

Comments: to be published in Indian Journal of Physics and Applied Physics

Dielectric behavior and impedance spectroscopy of Niobium substituted Lanthanum based orthovanadates at high temperatures

Authors: Ashok Kumar, Vikas N. Thakur, Ajay Kumar, Vinod Singh, Anita Dhaka, Rajendra S. Dhaka

Abstract: We present the detailed study of the temperature dependent dielectric properties, impedance spectroscopy and electrical conductivity of LaV$_{1-x}$Nb$_x$O$_4$ ($x=$ 0-1) samples prepared by the solid-state reaction method. The dielectric constant ($ε_r'$) increases (decreases) with increase in the temperature (frequency); while, the magnitude of $ε_r'$ remains almost invariant (order of 10$^4$ at… ▽ More We present the detailed study of the temperature dependent dielectric properties, impedance spectroscopy and electrical conductivity of LaV$_{1-x}$Nb$_x$O$_4$ ($x=$ 0-1) samples prepared by the solid-state reaction method. The dielectric constant ($ε_r'$) increases (decreases) with increase in the temperature (frequency); while, the magnitude of $ε_r'$ remains almost invariant (order of 10$^4$ at 100~Hz and 600\degree C) with $x$. The single phase $x=$ 0 (monoclinic-monazite, $P2_1/n$) and $x =$ 1 (monoclinic fergusonite, $I2/a$) samples show the lower values of loss factor [tan$δ=$ (4-8)] as compared to the $x=$ 0-0.8 samples [tan$δ=$(12-18)] having mixed tetragonal and monoclinic phases, which indicates the strong correlation between the crystal structure and the dielectric properties. The real part of impedance decreases with both temperature and frequency, and the observed weak relaxation remains almost unaltered with $x$. The imaginary part of impedance shows strong relaxation peaks shifting towards higher temperatures with frequency, which is attributed to the effect of grains, grain boundaries, and electrodes in the samples. The activation energy of the relaxation process is estimated to be 0.8-1.0~eV for the $x=$ 0-0.6 samples, and $\approx$1.4~eV for the $x=$ 0.8; whereas the $x=$ 1 sample shows two values ($\approx$0.5~eV and $\approx$1.0~eV) in the higher and lower temperature range, respectively. Further, the change in total conductivity with the angular frequency, which found to be in the range of 10$^{-3}$ to 10$^{-5}$~S/m, is fitted using the Jonsher power law. The analysis suggests the OLPT model for all the samples, whereas the $x$ = 1 sample exhibit a transition near 480\degree C and at higher temperatures it shows NSPT and QMT. This transition is corroborated by the tangent loss curves and may be associated with the change in structure. △ Less

Submitted 5 November, 2023; originally announced November 2023.

Comments: submitted

Correlation between the exchange bias effect and antisite disorders in Sr$_{2-x}$La$_x$CoNbO$_6$

Authors: Ajay Kumar, B. Schwarz, R. S. Dhaka

Abstract: We unravel the effect of La substitution and hence antisite disorders on the exchange bias (EB) mechanism in Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0, 0.2) double perovskite samples using the detailed analysis of the field cooled magnetization isotherms (M--H) and training effect. The field dependence of the freezing temperature deviates from both Gabay-Toulouse (GT) and de Almeida-Thouless (AT) lines an… ▽ More We unravel the effect of La substitution and hence antisite disorders on the exchange bias (EB) mechanism in Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0, 0.2) double perovskite samples using the detailed analysis of the field cooled magnetization isotherms (M--H) and training effect. The field dependence of the freezing temperature deviates from both Gabay-Toulouse (GT) and de Almeida-Thouless (AT) lines and the analysis suggests that the $x=$ 0 sample follows a different universality class with moderate anisotropy in the frozen spins. Interestingly, we find that the EB effect is significantly suppressed in the $x=$ 0.2 sample due to increase [decrease] in the size of ferromagnetic (FM) [cluster glass (CG)] domain, which reduces the effective disordered interface responsible for the EB. The changes in fraction of FM, AFM, and CG like interactions with the La substitution and applied magnetic field are found to be crucial in governing the EB effect in these samples. Further, the training effect measurements show the unequal shift in the left and right branches of the M--H loops and their different evolution with the field cycles ($n$). The analysis reveals that the rotatable spins relax approximately one order of magnitude faster than the frozen spins at the disordered interface. We find a possible correlation between the observed EB effect and the antisite disorders in these samples. △ Less

Submitted 6 October, 2023; originally announced October 2023.

Comments: submitted

Complex magnetic interactions and critical behavior analysis in quaternary CoFeV$_{0.8}$Mn$_{0.2}$Si Heusler alloy

Authors: Guru Dutt Gupt, P. D. Babu, R. S. Dhaka

Abstract: We investigate the magnetic behavior and critical exponents of quaternary CoFeV$_{0.8}$Mn$_{0.2}$Si Heusler alloy to understand the interactions across the Curie temperature ($T_{\rm C}$). The Rietveld refinement of the x-ray diffraction pattern with the space group F$\bar{4}$3m confirms a single-phase cubic Y-type crystal structure. The magnetic susceptibility $χ(T)$ data show a ferromagnetic nat… ▽ More We investigate the magnetic behavior and critical exponents of quaternary CoFeV$_{0.8}$Mn$_{0.2}$Si Heusler alloy to understand the interactions across the Curie temperature ($T_{\rm C}$). The Rietveld refinement of the x-ray diffraction pattern with the space group F$\bar{4}$3m confirms a single-phase cubic Y-type crystal structure. The magnetic susceptibility $χ(T)$ data show a ferromagnetic nature with a second-order phase transition from paramagnetic to ferromagnetic at $446\pm1$~K. The saturation magnetization at 5~K is determined to be 2.2~$μ_B$/f.u., which found to be close to the Slater--Pauling rule and indicates its half-metallic nature. The values of asymptotic critical exponents ($β$, $γ$, and $δ$) and the $T_{\rm C}$ are extracted through detailed analytical analysis including the Modified Arrott plot, the Kouvel-Fisher (K--F) method, and the Widom scaling relation. Interestingly, the estimated values of $β$ = 0.369 and $γ$ = 1.445 closely approximate the theoretical values of the 3D Heisenberg model and second-order thermodynamic phase transition across the $T_{\rm C}$. The obtained exponents lead to the collapse of renormalized isotherms, represented by the relationship between the magnetization (m) and the applied magnetic field (h), into two distinct branches above and below the $T_{\rm C}$, which validates the reliability of the analysis. Furthermore, these exponents suggest that the spin interaction follows a decay pattern of $J(r) \sim r^{-4.99}$, indicating a short-range magnetic ordering, akin to the itinerant-electron 3D Heisenberg model. △ Less

Submitted 3 October, 2023; originally announced October 2023.

Comments: submitted

Structural, vibrational and electronic properties of Nb substituted orthovanadates LaV$_{1-x}$Nb$_x$O$_4$

Authors: Ashok Kumar, Anurag Sharma, Madhav Sharma, Vinod Singh, Anita Dhaka, Rajendra S. Dhaka

Abstract: We investigate the structural, vibrational, morphological, and electronic properties of Nb substituted orthovanadate LaV$_{1-x}$Nb$_x$O$_4$ samples prepared by the solid-state reaction method. The x-ray diffraction (XRD) analysis reveals the presence of three crystal structures [monoclinic monazite ($m-m$) type for the $x=$ 0, two-phase equilibrium of monoclinic monazite ($m-m$) and tetragonal sch… ▽ More We investigate the structural, vibrational, morphological, and electronic properties of Nb substituted orthovanadate LaV$_{1-x}$Nb$_x$O$_4$ samples prepared by the solid-state reaction method. The x-ray diffraction (XRD) analysis reveals the presence of three crystal structures [monoclinic monazite ($m-m$) type for the $x=$ 0, two-phase equilibrium of monoclinic monazite ($m-m$) and tetragonal scheelite ($t-s$) type for the 0.2$\leq$$x$$\leq$0.8, and monoclinic fergusonite ($m-f$) type for the $x=$ 1 samples] with an increase in Nb$^{5+}$ concentration. The Raman spectroscopy and x-ray photoelectron spectroscopy (XPS) were employed to study the vibrational and electronic properties of all the samples, respectively. In order to choose an excitation wavelength that does not cause undesirable fluorescence and has observable intensities of all the vibrational modes, the Raman spectra are collected using 532 nm, 633 nm, and 785 nm laser lines. With increasing the Nb$^{5+}$ concentration, new Raman modes associated with Nb-bonds are clearly visible and the intensity of V-bonds assigned modes is decreasing. The XPS analysis shows the unchanged 3+ oxidation state of La ion where the intensity of the V 2$p$ core-level decreases while the Nb 3$d$ core-level increases with $x$. The equal spin-orbit energy splitting of the states is confirmed by the average energy difference (across La core-level spectra for all the samples) for state I as well as bonding and anti-bonding of state II. Interesting, the relative intensity of La 3$d$ state I and state II show systematic change with Nb do** altering the metal ligand overlap. We discuss and provide insight into the evolution of the structural, morphological, and chemical features with Nb substitution in LaV$_{1-x}$Nb$_x$O$_4$ samples. △ Less

Submitted 1 July, 2023; originally announced July 2023.

Comments: to be published in JALCOM

Effect of the growth orientation on the physical properties of Sr$_2$CoNbO$_6$ thin films

Authors: Ajay Kumar, Ramcharan Meena, M. Miryala, K. Ueno, Rajendra S. Dhaka

Abstract: We study the effect of the growth orientation on the structural, electronic, and hence transport properties of Sr$_2$CoNbO$_6$ thin films grown on the orthorhombic NGO(100) and cubic MgO(100) substrates. The x-ray diffraction patterns show the growth of the thin film along $a$-axis resulting in the asymmetric ($b\neq c$) in-plane compressive strain in case of NGO(100), whereas along $c$-axis with… ▽ More We study the effect of the growth orientation on the structural, electronic, and hence transport properties of Sr$_2$CoNbO$_6$ thin films grown on the orthorhombic NGO(100) and cubic MgO(100) substrates. The x-ray diffraction patterns show the growth of the thin film along $a$-axis resulting in the asymmetric ($b\neq c$) in-plane compressive strain in case of NGO(100), whereas along $c$-axis with tensile strain in case of MgO(100) substrate. The temperature dependent resistivity measurements indicate the lower electronic conductivity for the film grown on the NGO(100) substrate, which is found to be correlated with the higher degree of the oxygen deficiencies and hence larger concentration of the insulating Co$^{2+}$ in this sample. Further, the x-ray photoemission spectroscopy measurements show that Sr and Nb are present in the 2+ and 4+ valence state, whereas Co exist in the 2+, 3+ as well as 4+ states, fraction of which was found to vary with the growth orientation. Moreover, the analysis of leakage current using the sum exponent model indicate the presence of two different relaxation mechanisms in these samples. △ Less

Submitted 11 June, 2023; originally announced June 2023.

Comments: submitted

Unveiling the magnetic structure and phase transition of Cr$_2$CoAl using neutron diffraction

Authors: Guru Dutt Gupt, Yousef Kareri, James Hester, Clemens Ulrich, R. S. Dhaka

Abstract: We report the detailed analysis of temperature dependent neutron diffraction pattern of the Cr$_2$CoAl inverse Heusler alloy and unveil the magnetic structure up to the phase transition as well as its fully compensated ferrimagnetic nature. The Rietveld refinement of the diffraction pattern using the space group I$\bar4${\it m}2 confirm the inverse tetragonal structure over the large temperature r… ▽ More We report the detailed analysis of temperature dependent neutron diffraction pattern of the Cr$_2$CoAl inverse Heusler alloy and unveil the magnetic structure up to the phase transition as well as its fully compensated ferrimagnetic nature. The Rietveld refinement of the diffraction pattern using the space group I$\bar4${\it m}2 confirm the inverse tetragonal structure over the large temperature range from 100~K to 900~K. The refinement of the magnetic phase considering the wave vector $k=$ (0, 0, 0) reveals the ferrimagnetic nature of the sample below 730$\pm$5~K. This transition temperature is obtained from empirical power law fitting of the variation in the ordered net magnetic moment and intensity of (110) peak as a function of temperature. The spin configuration of the microscopic magnetic structure suggests the nearly fully compensated ferrimagnetic behavior where the magnetic moments of Cr2 are antiparallel with respect to the Cr1, and Co moments. Moreover, the observed anomaly in the thermal expansion and lattice parameters at 730$\pm$5~K suggest that the distortion in crystal structure may play an important role in the magnetic phase transition. △ Less

Submitted 21 March, 2023; originally announced March 2023.

Comments: submitted

Evolution of complex magnetic phases and metal-insulator transition through Nb substitution in La$_{0.5}$Sr$_{0.5}$Co$_{1-x}$Nb$_x$O$_3$

Authors: Rishabh Shukla, R. S. Dhaka

Abstract: We report the evolution of structural, magnetic, transport, and electronic properties of bulk polycrystalline La$_{0.5}$Sr$_{0.5}$Co$_{1-x}$Nb$_x$O$_3$ ($x =$ 0.025--0.25) samples. The Rietveld refinement of the x-ray diffraction patterns with R$\bar3$c space group reveals that the lattice parameters and rhombohedral distortion monotonously increase with the Nb$^{5+}$(4$d^0$) substitution ($x$). T… ▽ More We report the evolution of structural, magnetic, transport, and electronic properties of bulk polycrystalline La$_{0.5}$Sr$_{0.5}$Co$_{1-x}$Nb$_x$O$_3$ ($x =$ 0.025--0.25) samples. The Rietveld refinement of the x-ray diffraction patterns with R$\bar3$c space group reveals that the lattice parameters and rhombohedral distortion monotonously increase with the Nb$^{5+}$(4$d^0$) substitution ($x$). The magnetic susceptibility exhibits a decrease in the magnetic ordering temperature and net magnetization with $x$, which manifests that the Nb substitution dilutes the ferromagnetic (FM) double exchange interaction and enhances the antiferromagnetic (AFM) super-exchange interaction. Interestingly, for the $x>$ 0.1 samples the FM order is completely suppressed and the emergence of a glassy state is clearly evident. Moreover, the decrease in the coercivity (H$\rm_{C}$) and remanence (M$\rm_{r}$) with $x$ in the magnetic isotherms measured at 5~K further confirms the dominance of AFM interactions and reduction of FM volume fraction for the $x>$ 0.1 samples. More interestingly, we observe resistivity minima for the $x=$ 0.025 and 0.05 samples, which are analyzed using the quantum corrections in the conductivity, and found that the weak localization effect dominates over the renormalized electron-electron interactions in the 3D limit. Further, a semiconducting resistivity behavior is obtained for $x>$ 0.05, which follows the Arrhenius law at high temperatures ($\sim$160--320~K), and the 3D-variable range hop** prevails in the low-temperature region ($<$160~K). The core-level photoemission spectra confirm the valence state of constituent elements and the absence of Co$^{2+}$ is discernible. △ Less

Submitted 2 March, 2023; originally announced March 2023.

Comments: submitted

Diffusion mechanism and electrochemical investigation of 1T phase Al-MoS$_{2}$@rGO nano-composite as a high-performance anode for sodium-ion batteries

Authors: Manish Kr. Singh, Jayashree Pati, Deepak Seth, Jagdees Prasad, Manish Agarwal, M. Ali Haider, Jeng-Kuei Chang, Rajendra S. Dhaka

Abstract: We report the electrochemical investigation of 5% Al doped MoS$_2$@rGO composite as a high-performance anode for sodium (Na)-ion batteries. The x-ray diffraction (XRD), Raman spectroscopy and high-resolution transmission electron microscopy characterizations reveal that the Al do** increase the interlayer spacing of (002) plane of MoS$_2$ nanosheets and form a stable 1T phase. The galvanostatic… ▽ More We report the electrochemical investigation of 5% Al doped MoS$_2$@rGO composite as a high-performance anode for sodium (Na)-ion batteries. The x-ray diffraction (XRD), Raman spectroscopy and high-resolution transmission electron microscopy characterizations reveal that the Al do** increase the interlayer spacing of (002) plane of MoS$_2$ nanosheets and form a stable 1T phase. The galvanostatic charge-discharge measurements show the specific capacity stable around 450, 400, 350, 300 and 200 mAhg$^{-1}$ at current densities of 0.05, 0.1, 0.3, 0.5 and 1~Ag$^{-1}$, respectively. Also, we observe the capacity retentions of 86% and 66% at 0.1 and 0.3 Ag$^{-1}$, respectively, over 200 cycles with a consistent Coulombic efficiency of nearly 100%. The cyclic voltammetry, galvanostatic intermittent titration technique, and electrochemical impedance spectroscopy are used to find the kinetic behavior and the obtained value of diffusion coefficient falls in the range of 10$^{-10}$ to 10$^{-12}$ cm$^2$s$^{-1}$. Intriguingly, the in-situ EIS also explains the electrochemical kinetics of the electrode at different charge-discharge states with the variation of charge transfer resistance. Moreover, the post cycling investigation using ex-situ XRD and photoemission spectroscopy indicate the coexistence of 1T/2H phase and field-emission scanning electron microscopy confirm the stable morphology after 500 cycles. Also, the Na-ion transport properties are calculated for 1T Al--MoS$_2$@rGO interface and Al--MoS$_2$--MoS$_2$ interlayer host structure by theoretical calculations using density functional theory. △ Less

Submitted 13 October, 2022; originally announced October 2022.

Electrochemical investigation of MoSeTe as an anode for sodium-ion batteries

Authors: Priya Mudgal, Himani Arora, Jayashree Pati, Manish K. Singh, Mahantesh Khetri, Rajendra S. Dhaka

Abstract: Sodium ion batteries (SIBs) are considered as an efficient alternative for lithium-ion batteries (LIBs) owing to the natural abundance and low cost of sodium than lithium. In this context, the anode materials play a vital role in rechargeable batteries to acquire high energy and power density. In order to demonstrate transition metal dichalcogenide (TMD) as potential anode materials, we have synth… ▽ More Sodium ion batteries (SIBs) are considered as an efficient alternative for lithium-ion batteries (LIBs) owing to the natural abundance and low cost of sodium than lithium. In this context, the anode materials play a vital role in rechargeable batteries to acquire high energy and power density. In order to demonstrate transition metal dichalcogenide (TMD) as potential anode materials, we have synthesized MoSeTe sample by conventional flux method, and the structure and morphology are characterized using x-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), and Raman spectroscopy. These characterisations confirm the hexagonal crystal symmetry with p63/mmc space group and layered morphology of MoSeTe. We investigate the electrochemical performance of a MoSeTe as a negative electrode (anode) for SIBs in the working potential range of 0.01 to 3.0~V. In a half-cell configuration, the MoSeTe as an anode and Na metal as counter/reference electrode exhibits significant initial specific discharge capacities of around 475 and 355 mAhg$^{-1}$ at current densities of 50 and 100 mAg$^{-1}$, respectively. However, the capacity degraded significantly like $\approx$200~mAhg$^{-1}$ in 2nd cycle, but having $\approx$100\% Coulombic efficiency, which suggest for further modification in this material to improve its stability. The cyclic voltammetry (CV) study reveals the reversibility of the material after 1st cycle, resulting no change in the initial peak positions. The electrochemical impedance spectroscopy (EIS) measurements affirms the smaller charge transfer resistance of fresh cells than the cells after 10th cycle. Moreover, the extracted diffusion coefficient is found to be of the order of 10$^{-14}$ cm$^2$s$^{-1}$. △ Less

Submitted 23 August, 2022; originally announced August 2022.

Comments: to be published in PINSA (Springer)

High temperature dielectric and impedance spectroscopy study of LaCo$_{0.7}$Nb$_{0.3}$O$_3$

Authors: Vikas N. Thakur, Ajay Kumar, Aakash Kaushik, Guru Dutt Gupt, Rajendra S. Dhaka

Abstract: We report the high temperature dielectric and {\it ac} impedance spectroscopy investigation of Nb substituted LaCo$_{0.7}$Nb$_{0.3}$O$_3$ polycrystalline sample. The maximum dielectric constant value was observed $\approx$1400 at around 400~K where the peak value shows a decreasing trend at higher temperatures and frequency. Similar variation was reflected in the dielectric loss (tan$δ$) behavior… ▽ More We report the high temperature dielectric and {\it ac} impedance spectroscopy investigation of Nb substituted LaCo$_{0.7}$Nb$_{0.3}$O$_3$ polycrystalline sample. The maximum dielectric constant value was observed $\approx$1400 at around 400~K where the peak value shows a decreasing trend at higher temperatures and frequency. Similar variation was reflected in the dielectric loss (tan$δ$) behavior with temperature, which shows the thermal activation of the charge carriers in the material. The analysis of high temperature impedance spectroscopy data shows the grain and grain boundary contributions by fitting the Nyquist plots to the equivalent circuit. From the analysis of the impedance and modulus spectra, it was possible to discern between the effects of overlap** grains, grain boundaries, and electrode interfaces. The relaxation time decreases with an increase in the temperature and the activation energy changes from 0.44~eV to 0.56~eV at around 400~K, which is due to involvement of thermal activation in the conduction of charge carriers. The conductivity is found to be increased with temperature for a given frequency, which again shows the semiconducting behavior. Whereas the conductivity increases with increase in frequency at lower temperatures. Also, the conductivity almost saturates with frequency at high temperatures. △ Less

Submitted 16 August, 2022; originally announced August 2022.

Comments: submitted

Structural, magnetic and transport properties of Co$_2$CrAl epitaxial thin films

Authors: Guru Dutt Gupt, Rajendra S. Dhaka

Abstract: We report the physical properties of Co$_2$CrAl Heusler alloy epitaxial thin films grown on single crystalline MgO(001) substrate using pulsed laser deposition technique. The x-ray diffraction pattern in $θ$-2$θ$ mode showed the film growth in single phase B2-type ordered cubic structure with the presence of (002) and (004) peaks, and the film oriented along the MgO(001) direction. The $φ$~scan al… ▽ More We report the physical properties of Co$_2$CrAl Heusler alloy epitaxial thin films grown on single crystalline MgO(001) substrate using pulsed laser deposition technique. The x-ray diffraction pattern in $θ$-2$θ$ mode showed the film growth in single phase B2-type ordered cubic structure with the presence of (002) and (004) peaks, and the film oriented along the MgO(001) direction. The $φ$~scan along the (220) plane confirms the four-fold symmetry and the epitaxial growth relation found to be Co$_2$CrAl(001)[100]$\vert$$\vert$MgO(001)[110]. The thickness of about 12~nm is extracted through the analysis of x-ray reflectivity data. The isothermal magnetization (M--H) curves confirm the ferromagnetic (FM) nature of the thin film having significant hysteresis at 5 and 300~K. From the in-plane M--H curves, the saturation magnetization values are determined to be 2.1~$μ$$_{\rm B}$/f.u.~at 5~K and 1.6~$μ$$_{\rm B}$/f.u. at 300~K, which suggests the soft FM behavior in the film having the coercive field $\approx$ 522~Oe at 5~K. The thermo-magnetization measurements at 500~Oe magnetic field show the bifurcation between field-cooled and zero-field-cooled curves below about 100~K. The normalized field-cooled magnetization curve follows the T$^2$ dependency, and the analysis reveal the Curie temperature around 335$\pm$11~K. Moreover, the low-temperature resistivity indicates semiconducting behavior with the temperature, and we find a negative temperature coefficient of resistivity (5.2 $\times$ 10$^{-4}$ /K). △ Less

Submitted 9 August, 2022; originally announced August 2022.

Comments: submitted

Dielectric properties and impedance spectroscopy of NASICON type Na$_3$Zr$_2$Si$_2$PO$_{12}$

Authors: Ramcharan Meena, Rajendra S. Dhaka

Abstract: We report the temperature dependent dielectric properties and impedance spectroscopy investigation of Na$_3$Zr$_2$Si$_2$PO$_{12}$ in the frequency range of 20 Hz--2 MHz. The Rietveld refinement of x-ray diffraction pattern confirms the monoclinic phase with C2/c space group. The {\it d.c.} resistivity behavior shows its strong insulating nature at low temperatures, and follows Arrhenius law of the… ▽ More We report the temperature dependent dielectric properties and impedance spectroscopy investigation of Na$_3$Zr$_2$Si$_2$PO$_{12}$ in the frequency range of 20 Hz--2 MHz. The Rietveld refinement of x-ray diffraction pattern confirms the monoclinic phase with C2/c space group. The {\it d.c.} resistivity behavior shows its strong insulating nature at low temperatures, and follows Arrhenius law of thermal conduction with an activation energy of 0.68 eV. The decrease in electric permittivity ($ε_r$) with frequency is explained based on the space polarization mechanism and its increment with temperature by thermal activation of charge carriers. The dielectric loss (D=tan$δ$) peak follows the Arrhenius law of thermal activation with an energy of 0.25 eV. We observe an enhancement in {\it a.c.} conductivity with frequency and temperature due to the decrease in the activation energy, which results in enhancing the conduction between defect states. Further, we observe an abrupt increase in the {\it a.c.} conductivity at high frequencies, which is explained using the universal Jonschers power law. The analysis of {\it a.c.} conductivity shows two types of conduction mechanisms namely correlated barrier hop** and non-overlap** small polaron tunnelling in the measured temperature range. The imaginary part of the electric modulus confirms the non-Debye type relaxation in the sample. The shifting of the relaxation peak towards higher frequency side with an increase in temperature ensures its thermally activated nature. The scaling behavior of the electric modulus shows similar type of relaxation over the measured temperature range. The combined analysis of electric modulus and impedance with frequency shows the short-range mobility of charge carriers. △ Less

Submitted 7 June, 2022; originally announced June 2022.

Comments: submitted

Journal ref: Ceramics International, 48, 35150-35159 (2022)

Investigation of lattice dynamics, magnetism and electronic transport in $β$-Na$_{0.33}$V$_2$O$_{5}$

Authors: Rishabh Shukla, Clemens Ulrich, R. S. Dhaka

Abstract: We investigate the electronic and magnetic properties as well as lattice dynamics and spin-phonon coupling of $β$-Na$_{0.33}$V$_2$O$_5$ using temperature-dependent Raman scattering, dc-magnetization and dc-resistivity, x-ray photoemission, and absorption spectroscopy. The Rietveld refinement of XRD pattern with space group C2/m confirms the monoclinic structure. The analysis of temperature-depende… ▽ More We investigate the electronic and magnetic properties as well as lattice dynamics and spin-phonon coupling of $β$-Na$_{0.33}$V$_2$O$_5$ using temperature-dependent Raman scattering, dc-magnetization and dc-resistivity, x-ray photoemission, and absorption spectroscopy. The Rietveld refinement of XRD pattern with space group C2/m confirms the monoclinic structure. The analysis of temperature-dependent Raman spectra in a temperature range of 13--673~K reveals an anharmonic dependence of the phonon frequency and full width at half maximum, which is accredited to the symmetric phonon decay. However, below about 40 K, the hardening of the phonon frequency beyond anharmonicity is attributed to the spin-phonon coupling. Interestingly, the estimated effective magnetic moment $μ_{\rm eff}=$ 0.63~$μ_B$ from the magnetization data manifests a mixed-valence state of V ions in 4+ (18$\pm$1\%) and 5+ (82$\pm$1\%). A similar ratio of V$^{4+}$ to V$^{5+}$ is also observed in the x-ray photoemission and x-ray absorption near-edge spectra and that is found to be consistent with the sample stoichiometry. In addition, the V$^{4+}$ ions are distributed between different vanadium (V1 and V3) sites. The analysis of extended x-ray absorption fine structure at different V-sites gives the corresponding V--O bond lengths, which are utilized in the assignment of Raman modes. Moreover, the temperature-dependent resistivity resembles a semiconducting behavior where the charge carrier transport is facilitated by the band conduction at higher temperatures and via hop** $\le$260~K. △ Less

Submitted 21 September, 2022; v1 submitted 12 May, 2022; originally announced May 2022.

Comments: to be published in PRB

Journal ref: Physical Review B, 106, 125148 (2022)

Probing the electronic and local structure of Sr$_{2-x}$La$_x$CoNbO$_6$ using near-edge and extended x-ray absorption fine structures

Authors: Ajay Kumar, Rishabh Shukla, Ravi Kumar, R. J. Choudhary, S. N. Jha, R. S. Dhaka

Abstract: We report the electronic and local structural investigation of double pervoskites Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0--1) using x-ray absorption near edge structure (XANES) and extended x-ray absorption fine structures (EXAFS) at the Nb, Co, and Sr $K$-edges. The $ab$ $initio$ simulations and detailed analysis of the Nb and Co $K$-edge XANES spectra demonstrate that the observed pre-edge features ar… ▽ More We report the electronic and local structural investigation of double pervoskites Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0--1) using x-ray absorption near edge structure (XANES) and extended x-ray absorption fine structures (EXAFS) at the Nb, Co, and Sr $K$-edges. The $ab$ $initio$ simulations and detailed analysis of the Nb and Co $K$-edge XANES spectra demonstrate that the observed pre-edge features arise from the transition of 1$s$ electrons to the mixed $p-d$ hybridized states. We reveal a $z$-out Jahn-Teller (JT) distortion in the CoO$_6$ octahedra, which decreases monotonically due to an enhancement in the JT inactive Co$^{2+}$ ions with $x$ . On the other hand, the $z$-in distortion in NbO$_6$ octahedra remains unaltered up to $x=$ 0.4 and then decreases with further increase in $x$. This sudden change in the local coordination around Nb atoms is found to be responsible for the evolution of the antiferromagnetic interactions in $x \geqslant$ 0.6 samples. Also, we establish a correlation between the degree of octahedral distortion and intensity of the white line feature in the XANES spectra and possible reason for this are discussed. More interestingly, we observe the signature of KN$_1$ double electron excitation in the Sr $K$-edge EXAFS spectra for all the samples, which is found to be in good agreement with the $Z$+1 approximation. Further, the Co L$_{2,3}$ edge shows the reduction in the crystal field strength and hence an increase in the charge transfer energy ($Δ_{ct}$) with the La substitution. △ Less

Submitted 24 March, 2022; originally announced March 2022.

Comments: submitted

Journal ref: Physical Review B, 105, 245155 (2022)

Observation of anisotropic thermal expansion and Jahn-Teller effect in double perovskites Sr$_{2-x}$La$_x$CoNbO$_6$ using neutron diffraction

Authors: Ajay Kumar, Anil Jain, S. M. Yusuf, R. S. Dhaka

Abstract: We use temperature dependent neutron powder diffraction (NPD) to investigate the structural changes and magnetic interactions in double perovskite Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0.4 and 0.6). A structural phase transition from tetragonal ($I4/m$) to monoclinic ($P2_1/n$) is observed between $x=$ 0.4 and 0.6 samples. Interestingly, temperature evolution of the unit cell parameters follow the Grüne… ▽ More We use temperature dependent neutron powder diffraction (NPD) to investigate the structural changes and magnetic interactions in double perovskite Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0.4 and 0.6). A structural phase transition from tetragonal ($I4/m$) to monoclinic ($P2_1/n$) is observed between $x=$ 0.4 and 0.6 samples. Interestingly, temperature evolution of the unit cell parameters follow the Grüneisen approximation, and the analysis suggest the isotropic thermal expansion in case of the $x=$ 0.4 sample, whereas the $x=$ 0.6 sample shows the anisotropy where the thermal expansion along the $c$-axis significantly deviates from the Grüneisen function. We observe the $z$-out Jahn-Teller distortion in the CoO$_6$ and consequently $z$-in distortion in the adjacent NbO$_6$ octahedra. With increase in the La substitution, a decrease in the degree of octahedral distortion is evident from the significant reduction in the local distortion parameter $Δ$ around the B-site atoms. △ Less

Submitted 21 February, 2022; originally announced February 2022.

Comments: submitted

Unraveling diffusion kinetics of honeycomb structured Na$_2$Ni$_2$TeO$_6$ as a high-potential and stable electrode for sodium-ion batteries

Authors: Jayashree Pati, Hari Raj, Simranjot K. Sapra, Anita Dhaka, A. K. Bera, S. M. Yusuf, R. S. Dhaka

Abstract: In search of the potential cathode materials for sodium-ion batteries and to understand the diffusion kinetics, we report the detailed analysis of electrochemical investigation of honeycomb structured Na$_{2}$Ni$_{2}$TeO$_{6}$ material using cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), galvanostatic charge-discharge (GCD) and galvanostatic intermittent titration technique… ▽ More In search of the potential cathode materials for sodium-ion batteries and to understand the diffusion kinetics, we report the detailed analysis of electrochemical investigation of honeycomb structured Na$_{2}$Ni$_{2}$TeO$_{6}$ material using cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), galvanostatic charge-discharge (GCD) and galvanostatic intermittent titration technique (GITT). We found the discharge capacities of 82 and 77 mAhg$^{-1}$ at 0.05~C and 0.1~C current rates, respectively, and the mid-working potential of $\approx$3.9~V at 1~C and high capacity retention of 80\% after 500 cycles at 0.5~C as well as excellent rate capability. The analysis of CV data at different scan rates reveals the pseudo-capacitive mechanism of sodium-ion storage. Interestingly, the {\it in-situ} EIS measurements show a systematic change in the charge-transfer resistance at different charge/discharge stages as well as after different number of cycles. The diffusion coefficient extracted using CV, EIS and GITT lies mainly in the range of 10$^{-10}$ to 10$^{-12}$ cm$^{2}$s$^{-1}$ and the de-insertion/insertion of Na$^+$-ion concentration during electrochemical cycling is consistent with the ratio of Ni$^{3+}$/Ni$^{2+}$ valence state determined by photoemission study. Moreover, the post-cyclic results of retrieved active material show very stable structure and morphology even after various charge-discharge cycles. Our detailed electrochemical investigation and diffusion kinetics studies establish the material as a high working potential and long life electrode for sodium-ion batteries. △ Less

Submitted 1 December, 2021; originally announced December 2021.

Comments: submitted

Electronic structure of $A$Co$_2$As$_2$ ($A=$ Ca, Sr, Ba, Eu) studied using angle-resolved photoemission spectroscopy and theoretical calculations

Authors: R. S. Dhaka, Y. Lee, V. K. Anand, Abhishek Pandey, D. C. Johnston, B. N. Harmon, Adam Kaminski

Abstract: We present a comprehensive study of the low-energy band structure and Fermi surface (FS) topology of $A$Co$_2$As$_2$ ($A=$ Ca, Sr, Ba, Eu) using high-resolution angle-resolved photoemission spectroscopy. The experimental FS topology and band dispersion data are compared with theoretical full-potential linearized augmented-plane-wave (FP-LAPW) calculations, which yielded reasonably good agreement.… ▽ More We present a comprehensive study of the low-energy band structure and Fermi surface (FS) topology of $A$Co$_2$As$_2$ ($A=$ Ca, Sr, Ba, Eu) using high-resolution angle-resolved photoemission spectroscopy. The experimental FS topology and band dispersion data are compared with theoretical full-potential linearized augmented-plane-wave (FP-LAPW) calculations, which yielded reasonably good agreement. We demonstrate that the FS maps of $A$Co$_2$As$_2$ are significantly different from those of the parent compounds of Fe-based high-temperature superconductors. Further, the FSs of CaCo$_2$As$_2$ do not show significant changes across its antiferromagnetic transition temperature. The band dispersions extracted in different momentum $(k_{\it x}, k_{\it y})$ directions show a small electron pocket at the center and a large electron pocket at the corner of the Brillouin zone (BZ). The absence of the hole FS in these compounds does not allow nesting between pockets at the Fermi energy ({\it E}$_{\rm F}$), which is in contrast to $A$Fe$_2$As$_2$-type parent compounds of the iron-based superconductors. Interestingly, we find that the hole bands are moved 300--400~meV below $E_{\rm F}$ depending on the $A$ element. Moreover, the existence of nearly flat bands in the vicinity of $E_{\rm F}$ are consistent with the large density of states at $E_{\rm F}$. These results are important to understand the physical properties as well as the possibility of the emergence of superconductivity in related materials. △ Less

Submitted 11 July, 2021; originally announced July 2021.

Comments: submitted

X-ray Absorption Spectroscopy Study of La$_{1-y}$Sr$_{y}$Co$_{1-x}$Nb$_x$O$_3$

Authors: Rishabh Shukla, Ajay Kumar, Ravi Kumar, S. N. Jha, R. S. Dhaka

Abstract: We use x-ray absorption spectroscopy to investigate the local structure and electronic properties of bulk La$_{1-y}$Sr$_{y}$Co$_{1-x}$Nb$_x$O$_3$ ($y=$ 2$x$ as LSCNO and $y=$ 0 as LCNO) samples. The x-ray absorption near-edge spectra (XANES) of LSCNO at Co K-edge affirm the valence state of Co in 3+. However, in the case of the LCNO, a subtle variation in the valence state of Co ions from 3+ to 2+… ▽ More We use x-ray absorption spectroscopy to investigate the local structure and electronic properties of bulk La$_{1-y}$Sr$_{y}$Co$_{1-x}$Nb$_x$O$_3$ ($y=$ 2$x$ as LSCNO and $y=$ 0 as LCNO) samples. The x-ray absorption near-edge spectra (XANES) of LSCNO at Co K-edge affirm the valence state of Co in 3+. However, in the case of the LCNO, a subtle variation in the valence state of Co ions from 3+ to 2+ is evident with Nb substitution. The detailed analysis of the Fourier transform (FT) of the extended x-ray absorption fine structure (EXAFS) for the LSCNO samples exhibit the two groups of the bond-lengths owing to the Jahn-Teller (JT) distortion in the CoO$_6$ octahedra, which manifest that the Co$^{3+}$ ions exist in the intermediate spin-state (t$^5_{2g}$e$^1_g$) at room temperature. However, we find that the JT distortion is not present in LCNO samples for $x>$0.025 due to an increase in the high-spin Co$^{2+}$/Co$^{3+}$ ions accompanied by the Nb--induced structural transformation. Intriguingly, the La L$_3$-edge spectra for the LSCNO samples exhibit that the La ions exist in the trivalent state and the local disorder around La atoms decreases with Sr and Nb substitution. Interestingly, the simulated FT of the EXAFS spectra at the La L$_3$-edge demonstrates the three groups of La--O bond lengths, which exhibit a monotonous change with Sr and Nb substitution. Moreover, the XANES measured at Sr and Nb K-edges confirm their oxidation state to be in 2+ and 5+, respectively. △ Less

Submitted 22 April, 2021; originally announced April 2021.

Comments: submitted

Structural phase transition and its consequences on optical behavior of LaV$_{1-x}$Nb$_x$O$_4$

Authors: Hemanshu Dua, Rishabh Shukla, R. S. Dhaka

Abstract: We present the structural, electronic, vibrational, and photoluminescence properties of polycrystalline LaV$_{1-x}$Nb$_x$O$_4$ ($x =$ 0--0.2) samples at room temperature. The substitution of Nb at the V site shows the fascinating structural and optical behavior due to their isoelectronic character and larger ionic radii of Nb$^{5+}$ as compared to the V$^{5+}$. The Rietveld refinement of x-ray dif… ▽ More We present the structural, electronic, vibrational, and photoluminescence properties of polycrystalline LaV$_{1-x}$Nb$_x$O$_4$ ($x =$ 0--0.2) samples at room temperature. The substitution of Nb at the V site shows the fascinating structural and optical behavior due to their isoelectronic character and larger ionic radii of Nb$^{5+}$ as compared to the V$^{5+}$. The Rietveld refinement of x-ray diffraction patterns demonstrate that the $x=$ 0 sample exist in a monoclinic (P2$_1$/n) phase, whereas for the $x >$ 0, both monoclinic and scheelite-tetragonal (I4$_1$/a) phases co-exist in a certain proportion. Interestingly, a monotonous enhancement in the Raman spectral intensity with Nb substitution is correlated with the substitution induced increase in the scheelite-tetragonal phase. The x-ray absorption measurements reveal that the La ions exist in a trivalent oxidation state, while V and Nb cations possess 5+ oxidation state in tetrahedral coordination. Moreover, the Fourier-transform infrared (FTIR) spectra indicate that the Nb substitution give origin to some additional IR modes owing to the deformation of the VO$_4$$^{3-}$ tetrahedra and mixing of monoclinic and tetragonal phases. The photoluminescence measurements on these samples exhibit broadband spectra and their deconvolution designate the availability of more than one electron-hole pairs recombination center. △ Less

Submitted 2 May, 2021; v1 submitted 4 February, 2021; originally announced February 2021.

Comments: submitted

Journal ref: Phys. Rev. B 103, 174107 (2021)

Evidence of discrete energy states and cluster-glass behavior in Sr$_{2-x}$La$_x$CoNbO$_6$

Authors: Ajay Kumar, B. Schwarz, H. Ehrenberg, R. S. Dhaka

Abstract: We report the detailed analysis of specific heat [C$_{\rm P}$(T)] and ac-susceptibility for magnetically frustrated Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0--1) double perovskites to understand low temperature complex magnetic interactions and their evolution with $x$. Interestingly, the observed Schottky anomaly in the $x\leqslant$ 0.4 samples shifts gradually towards higher temperature with magnetic fi… ▽ More We report the detailed analysis of specific heat [C$_{\rm P}$(T)] and ac-susceptibility for magnetically frustrated Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0--1) double perovskites to understand low temperature complex magnetic interactions and their evolution with $x$. Interestingly, the observed Schottky anomaly in the $x\leqslant$ 0.4 samples shifts gradually towards higher temperature with magnetic field as well as $x$, and the analysis reveal the persistence of the discrete energy states in these samples resulting from the spin-orbit coupling and octahedral distortion. Moreover, the extracted values of Landé g--factor indicate the existence of high-spin state Co$^{3+}$ ions close to non-magnetic low-spin state. The specific heat data show the $λ$-type anomaly for the $x\geqslant$ 0.6 samples due to evolution of the long range antiferromagnetic ordering. Our analysis of low temperature C$_{\rm P}$(T) data for the $x\geqslant$ 0.6 samples demonstrate the 3D isotropic Heisenberg antiferromagnetic (AFM) interactions and the temperature induced second order AFM--paramagnetic phase transition. More interestingly, we demonstrate the presence of the free Co$^{2+}$ like Kramers doublet ground state in the $x =$1 sample. Further, the ac susceptibility and time evolution of the magnetization data reveal the low temperature cluster-glass like behavior in the $x=$ 0--0.4 samples, where spin-spin correlation strength decreases with $x$. △ Less

Submitted 14 October, 2020; originally announced October 2020.

Comments: accepted for publication in PRB

Journal ref: Physical Review B, 102, 184414 (2020

Structural, transport, optical and electronic properties of Sr$_2$CoNbO$_6$ thin films

Authors: Ajay Kumar, Rishabh Shukla, Akhilesh Pandey, Sandeep Dalal, M. Miryala, K. Ueno, M. Murakami, R. S. Dhaka

Abstract: We study the effect of substrate induced strain on the structural, transport, optical and electronic properties of Sr$_2$CoNbO$_6$ double perovskite thin films. The reciprocal space map**, $φ$-scan and high-resolution $θ$-2$θ$ scans of x-ray diffraction patterns suggest the epitaxial nature and high-quality of the films deposited on various single crystal ceramic substrates. A systematic enhance… ▽ More We study the effect of substrate induced strain on the structural, transport, optical and electronic properties of Sr$_2$CoNbO$_6$ double perovskite thin films. The reciprocal space map**, $φ$-scan and high-resolution $θ$-2$θ$ scans of x-ray diffraction patterns suggest the epitaxial nature and high-quality of the films deposited on various single crystal ceramic substrates. A systematic enhancement in the dc electronic conductivity is observed with increase in the compressive strain, while a sharp reduction in case of tensile strain, which are further supported by change in the activation energy and density of states near the Fermi level. The optical band gap extracted from two distinct absorption bands, observed in the visible-near infrared spectroscopy show a non-monotonic behavior in case of compressive strain while significant enhancement with tensile strain. Unlike the bulk Sr$_2$CoNbO$_6$ (Co$^{3+}$ and Nb$^{5+}$), we observe different valence states of Co namely 2+, 3+ and 4+, and tetravalent Nb (4$d^1$) in the x-ray photoemission spectroscopy measurements. Moreover, a reduction in the average oxygen valency with the compressive strain due to enhancement in the covalent character of Co/Nb--O bond is evident. Interestingly, we observe sharp Raman active modes in these thin films, which indicates a significant enhancement in structural ordering as compared to the bulk. △ Less

Submitted 19 May, 2020; originally announced May 2020.

Comments: submitted

Journal ref: Journal of Applied Physics 128, 025303 (2020)

Structural and magnetic behavior of Cr$_2$Co$_{(1-x)}$Cr$_x$Al inverse Heusler alloys

Authors: Manisha Srivastava, Guru Dutt Gupt, Priyanka Nehla, Anita Dhaka, R. S. Dhaka

Abstract: We report the structural and magnetic behavior of single phase inverse Heusler alloys Cr$_2$Co$_{(1-x)}$Cr$_x$Al ($x = $ 0, 0.2, 0.4) using x-ray diffraction (XRD), Raman spectroscopy, isothermal magnetization, and magnetic susceptibility measurements. Interestingly, the Rietveld refinement of XRD data with the space group I$\bar{4}m2$ reveal a tetragonal distortion with c/a ratio around 1.38 in t… ▽ More We report the structural and magnetic behavior of single phase inverse Heusler alloys Cr$_2$Co$_{(1-x)}$Cr$_x$Al ($x = $ 0, 0.2, 0.4) using x-ray diffraction (XRD), Raman spectroscopy, isothermal magnetization, and magnetic susceptibility measurements. Interestingly, the Rietveld refinement of XRD data with the space group I$\bar{4}m2$ reveal a tetragonal distortion with c/a ratio around 1.38 in these inverse Heusler structures. The bulk compositions have been confirmed by energy dispersive x-ray spectroscopy measurements. The active Raman mode F$_{2g}$ is observed at 320~cm$^{-1}$, which confirms the X-type Heusler structure as the A2 and B2 type structures are known to be not Raman active. The area of F$_{2g}$ mode decreases with Cr concentration, which indicate the origin of this mode due to Co vibrations. The isothermal magnetization data confirm the magnetic moment close to zero ($\le$0.02 $μ_B/f.u.$) at $\approx$70~kOe and negligible coercive field suggest the fully compensated ferrimagnetic nature of these samples. The susceptibility behavior indicates irreversibility between zero-field and field-cooled curves and complex magnetic interactions at low temperatures. △ Less

Submitted 7 May, 2020; originally announced May 2020.

Comments: AIP Advances (2020)

Journal ref: AIP Advances 10, 055118 (2020)

Magneto-transport and Berry phase in magnetically doped Bi$_{0.97-x}$Sb$_{0.03}$ single crystals

Authors: V. K. Maurya, Manju Mishra Patidar, Anita Dhaka, R. Rawat, V. Ganesan, R. S. Dhaka

Abstract: We report large magnetoresistance (MR) and Shubnikov-de Haas (SdH) oscillations in single crystals of magnetically (M= Ni and Fe) doped M$_x$Bi$_{0.97-x}$Sb$_{0.03}$ ($x=$ 0, 0.02) topological insulators. The R$\bar{3}$m symmetry and phase have been confirmed by the Rietveld refinement of x-ray diffraction data. Interestingly, a magnetic field induced phase transition from semi-metallic to semi-co… ▽ More We report large magnetoresistance (MR) and Shubnikov-de Haas (SdH) oscillations in single crystals of magnetically (M= Ni and Fe) doped M$_x$Bi$_{0.97-x}$Sb$_{0.03}$ ($x=$ 0, 0.02) topological insulators. The R$\bar{3}$m symmetry and phase have been confirmed by the Rietveld refinement of x-ray diffraction data. Interestingly, a magnetic field induced phase transition from semi-metallic to semi-conducting type is found with the energy gap around 80 meV at 15 Tesla in the $x=$ 0 sample. Moreover, we observe linear behavior of MR up to 15 Tesla in transverse mode and SdH oscillations in longitudinal mode where the field direction is with respect to the current and crystal plane. For the parent sample, we found the coherence length L$_φ=$ 12.7 nm through the fitting of MR data in transverse mode with modified H-L-N equation. The extracted frequencies of SdH oscillations using the fast Fourier transform method and Landau level (LL) fan diagram are found to be consistent for the parent and Ni doped samples. The determined Fermi surface area is found to be slightly larger in Ni doped as compared to the parent sample possibly due to change in the Fermi energy. The Kohler's plot indicates a single scattering mechanism below 100 K. More importantly, the analysis with the help of LL fan diagram reveals the non-zero Berry phase $φ_{\rm B}= -$(1$\pm$0.1)$π$, which demonstrates the non-trivial topological states near the Dirac point in the parent and Ni doped samples. △ Less

Submitted 22 July, 2020; v1 submitted 28 April, 2020; originally announced April 2020.

Comments: submitted, added fig2c, corrected fig4

Journal ref: Phys. Rev. B 102, 144412 (2020)

Structural and transport properties of La$_{1-x}$Sr$_x$Co$_{1-y}$Nb$_y$O$_3$ thin films

Authors: Rishabh Shukla, Ajay Kumar, Sandeep Dalal, Akhilesh Pandey, R. S. Dhaka

Abstract: We present the structural and transport properties of La$_{1-x}$Sr$_x$Co$_{1-y}$Nb$_y$O$_3$ ($y=$ 0.1 and $x=$ 0; $y=$ 0.15 and $x=$ 0.3) thin films grown on (001) orientated single crystalline ceramic substrates to investigate the effect of lattice induced compressive and tensile strain. The high resolution x-ray diffraction measurements, including $θ$-2$θ$ scan, $Φ$-scan, and reciprocal space ma… ▽ More We present the structural and transport properties of La$_{1-x}$Sr$_x$Co$_{1-y}$Nb$_y$O$_3$ ($y=$ 0.1 and $x=$ 0; $y=$ 0.15 and $x=$ 0.3) thin films grown on (001) orientated single crystalline ceramic substrates to investigate the effect of lattice induced compressive and tensile strain. The high resolution x-ray diffraction measurements, including $θ$-2$θ$ scan, $Φ$-scan, and reciprocal space map**, affirm single phase; four-fold symmetry; good quality of deposited thin films. The atomic force micrographs confirm that these films have small root mean square roughness in the range of $\sim$0.5--7~nm. We observed additional Raman active modes in the films owing to the lowered crystal symmetry as compared to the bulk. More interestingly, the temperature dependent dc-resistivity measurements reveal that films become insulating due to induced lattice strain in comparison to bulk, however for the larger compressive strained films conductivity increase significantly owing to the higher degree of $p-d$ hybridization and reduction in bandwidth near the Fermi level. △ Less

Submitted 20 April, 2020; originally announced April 2020.

Comments: submitted

Journal ref: Thin Solid Films, 709, 138250 (2020)

Unraveling the magnetic interactions and spin state in insulating Sr$_{2-x}$La$_x$CoNbO$_6$

Authors: Ajay Kumar, R. S. Dhaka

Abstract: We investigate the structural, magnetic and spin-state transitions, and magnetocaloric properties of Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0--1) double perovskites. The structural transition from tetragonal to monoclinic phase at $x$ $\geqslant$ 0.6, and an evolution of (101)/(103) superlattice reflections and Raman active modes indicate the enhancement in the B-site ordering with $x$. The magnetic susc… ▽ More We investigate the structural, magnetic and spin-state transitions, and magnetocaloric properties of Sr$_{2-x}$La$_x$CoNbO$_6$ ($x=$ 0--1) double perovskites. The structural transition from tetragonal to monoclinic phase at $x$ $\geqslant$ 0.6, and an evolution of (101)/(103) superlattice reflections and Raman active modes indicate the enhancement in the B-site ordering with $x$. The magnetic susceptibility data reveal the transition from weak ferromagnetic (FM) to antiferromagnetic (AFM) ordering for $x$ $\geqslant$ 0.6 with T$_{\rm N}$$\approx$9--15~K. Interestingly, the La substitution drives towards more insulating state due to increase in high-spin Co$^{2+}$, whereas a spin-state crossover is observed in Co$^{3+}$ from high-spin to intermediate/low-spin states with $x$. We discuss the correlation between complex magnetic interactions and the presence of various Co spin-states in the system. Moreover, the emergence of metamagnetic nature due to the competition between FM and AFM interactions as well as crossover from conventional to inverse magnetocaloric effect have been demonstrated by detailed analysis of temperature and field dependent change in magnetic entropy. △ Less

Submitted 9 March, 2020; originally announced March 2020.

Comments: submitted

Journal ref: Physical Review B, 101, 094434 (2020)

Achieving high figure-of-merit in Nb-doped Na$_{0.74}$CoO$_{2}$ compound at high temperature region

Authors: Arzena Khatun, Shamim Sk, Jayashree Pati, R. S. Dhaka, Sudhir K. Pandey

Abstract: We report the thermoelectric (TE) properties of Na$_{0.74}$Co$_{0.95}$Nb$_{0.05}$O$_{2}$ in the temperature range $300-1200$ K, as a potential candidate for p-type thermoelectric material. The experimental values of Seebeck coefficient (S) are $ \sim $ $82-121$ $ μ$V/K measured in the temperature range $300-620$ K. The positive values of S in the entire temperature range indicates p-type behaviour… ▽ More We report the thermoelectric (TE) properties of Na$_{0.74}$Co$_{0.95}$Nb$_{0.05}$O$_{2}$ in the temperature range $300-1200$ K, as a potential candidate for p-type thermoelectric material. The experimental values of Seebeck coefficient (S) are $ \sim $ $82-121$ $ μ$V/K measured in the temperature range $300-620$ K. The positive values of S in the entire temperature range indicates p-type behaviour of the compound. At 300 K the experimental value of thermal conductivity ($ κ$) is $ \sim $ 1.88 W/m-K that increases up to $ \sim $ 420 K, then decreases till 620 K with corresponding value $ \sim $ 1.86 W/m-K. To understand the experimentally observed transport properties, we have calculated S and $ρ$ of this compound. Then, based on theoretical understanding, we have estimated \textit{figure-of-merit} (ZT) up to 1200 K by using calculated S and $ρ$ values with extrapolated experimental $κ$. The value of ZT is found to be $\sim$ 0.03 at 300 K, whereas, the highest value is observed as $\sim$ 1.7 at 1200 K. Finally, we have calculated the efficiency ($η$) by kee** the cold end temperature (T$_{c}$) fixed at 500 K and varying hot end temperature (T$_{h}$) from 500 to 1200 K, respectively. The maximum value of $η$ is found to be $\sim$ 8 %, when T$_{c}$ and T$_{h}$ are fixed at 500 and 1200 K, respectively. This result suggests that Na$_{0.74}$Co$_{0.95}$Nb$_{0.05}$O$_{2}$ compound can be used as a p-leg for making high temperature TE generator (TEG). △ Less

Submitted 15 November, 2019; originally announced November 2019.

Exploring the possibility of enhancing the figure-of-merit ( $>$ 2) of Na$_{0.74}$CoO$_{2}$: A combined experimental and theoretical study

Authors: Shamim Sk, Jayashree Pati, R. S. Dhaka, Sudhir K. Pandey

Abstract: Search of new thermoelectric (TE) materials with high \textit{figure-of-merit} (ZT) is always inspired the researcher in TE field. Here, we present a combined experimental and theoretical study of TE properties of Na$_{0.74}$CoO$_{2}$ compound in high-temperature region. The experimental Seebeck coefficient (S) is found to vary from 64 to 118 $μ$V/K in the temperature range $300-620$ K. The positi… ▽ More Search of new thermoelectric (TE) materials with high \textit{figure-of-merit} (ZT) is always inspired the researcher in TE field. Here, we present a combined experimental and theoretical study of TE properties of Na$_{0.74}$CoO$_{2}$ compound in high-temperature region. The experimental Seebeck coefficient (S) is found to vary from 64 to 118 $μ$V/K in the temperature range $300-620$ K. The positive values of S are indicating the dominating p-type behaviour of the compound. The observed value of thermal conductivity ($κ$) is $\sim$ 2.2 W/m-K at 300 K. In the temperature region $300-430$ K, the value of $κ$ increases up to $\sim$ 2.6 W/m-K and then decreases slowly till 620 K with the corresponding value of $\sim$ 2.4 W/m-K. We have also carried out the theoretical calculations and the best matching between experimental and calculated values of transport properties are observed in spin-polarized calculation within DFT+\textit{U} by chosen \textit{U} = 4 eV. The maximum calculated value of ZT is found to be $\sim$ 0.67 at 1200 K for p-type conduction. Our computational study suggests that the possibility of n-type behaviour of the compound which can lead to a large value of ZT at higher temperature region. Electron do** of $\sim$ 5.1$\times$10$^{20}$ cm$^{-3}$ is expected to give rise the high ZT value of $\sim$ 2.7 at 1200 K. Using these temperature-dependent ZT values, we have calculated the maximum possible values of efficiency ($η$) of thermoelectric generator (TEG) made by p and n-type Na$_{0.74}$CoO$_{2}$. The present study suggests that one can get the efficiency of a TE cell as high as $\sim$ 11$\%$ when the cold and hot end temperature are fixed at 300 K and 1200 K, respectively. Such high values of ZT and efficiency suggest that Na$_{0.74}$CoO$_{2}$ can be used as a potential candidate for high-temperature TE applications. △ Less

Submitted 29 April, 2020; v1 submitted 22 October, 2019; originally announced October 2019.

Neutron diffraction and magnetic properties of Co$_2$Cr$_{1-x}$Ti$_x$Al Heusler alloys

Authors: Priyanka Nehla, Yousef Kareri, Guru Dutt Gupt, James Hester, P. D. Babu, Clemens Ulrich, R. S. Dhaka

Abstract: We report the structural, magnetic, and magnetocaloric properties of Co$_2$Cr$_{1-x}$Ti$_x$Al ($x=$ 0--0.5) Heusler alloys for spintronic and magnetic refrigerator applications. Room temperature X-ray diffraction and neutron diffraction patterns along with Rietveld refinements confirm that the samples are of single phase and possess a cubic structure. Interestingly, magnetic susceptibly measuremen… ▽ More We report the structural, magnetic, and magnetocaloric properties of Co$_2$Cr$_{1-x}$Ti$_x$Al ($x=$ 0--0.5) Heusler alloys for spintronic and magnetic refrigerator applications. Room temperature X-ray diffraction and neutron diffraction patterns along with Rietveld refinements confirm that the samples are of single phase and possess a cubic structure. Interestingly, magnetic susceptibly measurements indicate a second order phase transition from paramagnetic to ferromagnetic where the Curie temperature (T$_{\rm C}$) of Co$_2$CrAl increases from 330~K to 445~K with Ti substitution. Neutron powder diffraction data of the $x=$ 0 sample across the magnetic phase transition taken in a large temperature range confirm the structural stability and exclude the possibility of antiferromagnetic ordering. The saturation magnetization of the $x=$ 0 sample is found to be 8000~emu/mol (1.45~$μ_{\rm B}$/{\it f.u.}) at 5~K, which is in good agreement with the value (1.35$\pm$0.05~$μ_{\rm B}$/{\it f.u.}) obtained from the Rietveld analysis of the neutron powder diffraction pattern measured at temperature of 4~K. By analysing the temperature dependence of the neutron data of the $x=$ 0 sample, we find that the change in the intensity of the most intense Bragg peak (220) is consistent with the magnetization behavior with temperature. Furthermore, an enhancement of change in the magnetic entropy and relative cooling power values has been observed for the $x=$ 0.25 sample. Interestingly, the critical behavior analysis across the second order magnetic phase transition and extracted exponents ($β\approx$ 0.496, $γ\approx$ 1.348, and $δ\approx$ 3.71 for the $x=$ 0.25 sample) suggest the presence of long-range ordering, which deviates towards 3D Heisenberg type interactions above T$_{\rm C}$, consistent with the interaction range value $σ$. △ Less

Submitted 18 September, 2019; originally announced September 2019.

Comments: submitted

Journal ref: Phys. Rev. B 100, 144444 (2019)

Magnetocaloric properties and critical behavior of Co$_2$Cr$_{1-x}$Mn$_x$Al Heusler alloys

Authors: Priyanka Nehla, V. K. Anand, Bastian Klemke, Bella Lake, R. S. Dhaka

Abstract: We study the magnetocaloric effect and critical behavior of Co$_2$Cr$_{1-x}$Mn$_x$Al ($x=$ 0.25, 0.5, 0.75) Heusler alloys across the ferromagnetic (FM) transition (T$_{\rm C}$). The Rietveld refinement of x-ray diffraction patterns exhibit single phase cubic structure for all the samples. The temperature dependent magnetic susceptibility $χ$(T) data show a systematic enhancement in the Curie temp… ▽ More We study the magnetocaloric effect and critical behavior of Co$_2$Cr$_{1-x}$Mn$_x$Al ($x=$ 0.25, 0.5, 0.75) Heusler alloys across the ferromagnetic (FM) transition (T$_{\rm C}$). The Rietveld refinement of x-ray diffraction patterns exhibit single phase cubic structure for all the samples. The temperature dependent magnetic susceptibility $χ$(T) data show a systematic enhancement in the Curie temperature and effective magnetic moment with Mn concentration, which is consistent with the Slater-Pauling behavior. The M(H) isotherms also exhibit the FM ordering and the analysis of $χ$(T) data indicates the nature of the phase transition to be a second order, which is further supported by scaling of the entropy curves and Arrott plot. Interestingly, the Mn substitution causes an increase in the magnetic entropy change and hence large relative cooling power for multi-stage magnetic refrigerator applications. In order to understand the nature of the magnetic phase transition we examine the critical exponents $β$, $γ$, $δ$ for the $x=$ 0.75 sample by the modified Arrott plot and the critical isotherm analysis, which is further confirmed by Kouvel-Fisher method and Widom scaling relation, respectively. The estimated values of $β=$ 0.507, $γ=$ 1.056, $δ=$ 3.084 are found to be close to the mean field theoretical values. The renormalized isotherms (m vs h) corresponding to these exponent values collapse into two branches, above and below T$_{\rm C}$ that validates our analysis. Our results suggest for the existence of long-range FM interactions, which decays slower than power law as $J(r)\sim r^{-4.5}$ for a 3 dimensional mean field theory. △ Less

Submitted 13 July, 2019; originally announced July 2019.

Comments: originally submitted on 26/3/2019

Spin dynamics and unconventional magnetism in insulating La$_{(1-2x)}$Sr$_{2x}$Co$_{(1-x)}$Nb$_{x}$O$_3$

Authors: Rishabh Shukla, Anil Jain, M. Miryala, M. Murakami, K. Ueno, S. M. Yusuf, R. S. Dhaka

Abstract: We study the structural, magnetic, transport and electronic properties of LaCoO$_3$ with Sr/Nb co-substitution, i.e., La$_{(1-2x)}$Sr$_{2x}$Co$_{(1-x)}$Nb$_{x}$O$_3$ using x-ray and neutron diffraction, dc and ac-magnetization, neutron depolarization, dc-resistivity and photoemission measurements. The powder x-ray and neutron diffraction data were fitted well with the rhombohedral crystal symmetry… ▽ More We study the structural, magnetic, transport and electronic properties of LaCoO$_3$ with Sr/Nb co-substitution, i.e., La$_{(1-2x)}$Sr$_{2x}$Co$_{(1-x)}$Nb$_{x}$O$_3$ using x-ray and neutron diffraction, dc and ac-magnetization, neutron depolarization, dc-resistivity and photoemission measurements. The powder x-ray and neutron diffraction data were fitted well with the rhombohedral crystal symmetry (space group \textit{R$\bar{3}$c}) in Rietveld refinement analysis. The calculated effective magnetic moment ($\approx$3.85~$μ_B$) and average spin ($\approx$1.5) of Co ions from the analysis of magnetic susceptibility data are consistent with 3+ state of Co ions in intermediate-spin (IS) and high-spin (HS) states in the ratio of $\approx$50:50, i.e., spin-state of Co$^{3+}$ is preserved at least up to $x=$ 0.1 sample. Interestingly, the magnetization values were significantly increased with respect to the $x=$ 0 sample, and the M-H curves show non-saturated behavior up to an applied maximum magnetic field of $\pm$70 kOe. The ac-susceptibility data show a shift in the freezing temperature with excitation frequency and the detailed analysis confirm the slower dynamics and a non-zero value of the Vogel-Fulcher temperature T$_0$, which suggests for the cluster spin glass. The unusual magnetic behavior indicates the presence of complex magnetic interactions at low temperatures. The dc-resistivity measurements show the insulating nature in all the samples. However, relatively large density of states $\approx$10$^{22}$ eV$^{-1}$cm$^{-3}$ and low activation energy $\approx$130~meV are found in $x=$ 0.05 sample. Using x-ray photoemission spectroscopy, we study the core-level spectra of La 3$d$, Co 2$p$, Sr 3$d$, and Nb 3$d$ to confirm the valence state. △ Less

Submitted 9 June, 2019; originally announced June 2019.

Comments: submitted

Journal ref: Journal of Physical Chemistry C, 123, 22457 (2019)

Electrochemical properties of Na$_{0.66}$V$_4$O$_{10}$ nanostructures as cathode material in rechargeable batteries for energy storage applications

Authors: Rakesh Saroha, Tuhin S. Khan, Mahesh Chandra, Rishabh Shukla, Amrish K. Panwar, Amit Gupta, M. Ali Haider, Suddhasatwa Basu, Rajendra S. Dhaka

Abstract: We report the electrochemical performance of nanostructures of Na$_{0.66}$V$_4$O$_{10}$ as cathode material for rechargeable batteries. The Rietveld refinement of room temperature x-ray diffraction pattern shows the monoclinic phase with C2/m space group. The cyclic voltammetry curves of prepared half-cells exhibit redox peaks at ~3.1 and 2.6~V, which are due to two-phase transition reaction betwe… ▽ More We report the electrochemical performance of nanostructures of Na$_{0.66}$V$_4$O$_{10}$ as cathode material for rechargeable batteries. The Rietveld refinement of room temperature x-ray diffraction pattern shows the monoclinic phase with C2/m space group. The cyclic voltammetry curves of prepared half-cells exhibit redox peaks at ~3.1 and 2.6~V, which are due to two-phase transition reaction between V$^{5+/4+}$ and can be assigned to the single step deintercalation/intercalation of Na-ion. We observe a good cycling stability with specific discharge capacity (measured vs. Na$^+$/Na) between 80 ($\pm$2) and 30 ($\pm$2) mAh g$^{-1}$ at a current density 3 and 50~mA g$^{-1}$, respectively. The electrochemical performance of Na$_{0.66}$V$_4$O$_{10}$ electrode was also tested with Li anode, which showed higher capacity, but decay faster than Na. Using density functional theory, we calculate the Na vacancy formation energies; 3.37~eV in the bulk of the material and 2.52~eV on the (100) surface, which underlines the importance of nanostructures. △ Less

Submitted 13 May, 2019; originally announced May 2019.

Comments: submitted

Journal ref: ACS Omega, 4, 9878 (2019)

Growth and Characterization of Fe0.95Se0.6Te0.4 Single Crystal

Authors: Anmol Shukla, Vishal K. Maurya, Rajendra S. Dhaka

Abstract: In this paper we present the single crystal growth of Fe0.95Se0.6Te0.4 high TC superconducting sample by the modified Bridgman technique. The x-ray diffraction pattern shows the single crystal nature of the sample, as only (00l) peaks are detectable. The stoichiometric composition has been verified by energy dispersive x-ray analysis. The superconducting transition temperature at 14 K was confirme… ▽ More In this paper we present the single crystal growth of Fe0.95Se0.6Te0.4 high TC superconducting sample by the modified Bridgman technique. The x-ray diffraction pattern shows the single crystal nature of the sample, as only (00l) peaks are detectable. The stoichiometric composition has been verified by energy dispersive x-ray analysis. The superconducting transition temperature at 14 K was confirmed through DC magnetization (ZFC-FC) and resistivity measurements. By analyzing the isothermal M-H curves, we determined the value of H_c1 (0) ~360 Oe by extrapolating the data. The temperature coefficient of resistivity obtained using the power law fitting was found to be 0.6. The obtained Raman spectra at room temperature can be interpreted with the tetragonal crystal structure and space group P4/nmm. △ Less

Submitted 7 January, 2019; originally announced January 2019.

Comments: conference paper

Journal ref: AIP Conference Proceedings 2115, 030410 (2019)

Investigation of the structural, electronic, transport and magnetic properties of Co$_2$FeGa Heusler alloy nanoparticles

Authors: Priyanka Nehla, Clemens Ulrich, Rajendra S. Dhaka

Abstract: We report the structural, transport, electronic, and magnetic properties of Co$_2$FeGa Heusler alloy nanoparticles. The Rietveld refinements of x-ray diffraction (XRD) data with the space group Fm$\bar {3}$m clearly demonstrates that the nanoparticles are of single phase. The particle size (D) decreases with increasing the SiO$_2$ concentration. The Bragg peak positions and the inter-planer spacin… ▽ More We report the structural, transport, electronic, and magnetic properties of Co$_2$FeGa Heusler alloy nanoparticles. The Rietveld refinements of x-ray diffraction (XRD) data with the space group Fm$\bar {3}$m clearly demonstrates that the nanoparticles are of single phase. The particle size (D) decreases with increasing the SiO$_2$ concentration. The Bragg peak positions and the inter-planer spacing extracted from high-resolution transmission electron microscopy image and selected area electron diffraction are in well agreement with data obtained from XRD. The coercivity initially increases from 127~Oe to 208~Oe between D = 8.5~nm and 12.5~nm, following the D$^{-3/2}$ dependence and then decreases with further increasing D up to 21.5~nm with a D$^{-1}$ dependence, indicating the transition from single domain to multidomain regime. The effective magnetic anisotropic constant behaves similarly as coercivity, which confirms this transition. A complex scattering mechanisms have been fitted to explain the electronic transport properties of these nanoparticles. In addition we have studied core-level and valence band spectra using photoemission spectroscopy, which confirm the hybridization between $d$ states of Co/Fe. Further nanoparticle samples synthesized by co-precipitation method show higher saturation magnetization. The presence of Raman active modes can be associated with the high chemical ordering, which motivates for detailed temperature dependent structural investigation using synchrotron radiation and neutron sources. △ Less

Submitted 17 October, 2018; originally announced October 2018.

Influence of anti-site disorder and electron-electron correlations on the electronic structure of CeMnNi$_4$

Authors: Pampa Sadhukhan, Sunil Wilfred D'Souza, Vipin Kumar Singh, Rajendra Singh Dhaka, Andrei Gloskovskii, Sudesh Kumar Dhar, Pratap Raychaudhuri, Ashish Chainani, Aparna Chakrabarti, Sudipta Roy Barman

Abstract: CeMnNi$_4$ exhibits an unusually large spin polarization, but its origin has baffled researchers for more than a decade. We use bulk sensitive hard x-ray photoelectron spectroscopy (HAXPES) and density functional theory based on the Green's function technique to demonstrate the importance of electron-electron correlations of both the Ni 3$d$ ($U_{Ni}$) and Mn 3$d$ ($U_{Mn}$) electrons in explainin… ▽ More CeMnNi$_4$ exhibits an unusually large spin polarization, but its origin has baffled researchers for more than a decade. We use bulk sensitive hard x-ray photoelectron spectroscopy (HAXPES) and density functional theory based on the Green's function technique to demonstrate the importance of electron-electron correlations of both the Ni 3$d$ ($U_{Ni}$) and Mn 3$d$ ($U_{Mn}$) electrons in explaining the valence band of this multiply correlated material. We show that Mn-Ni anti-site disorder as well as $U_{Ni}$ play crucial role in enhancing its spin polarization: anti-site disorder broadens a Ni 3$d$ minority-spin peak close to the Fermi level ($E_F$), while an increase in $U_{Ni}$ shifts it towards $E_F$, both leading to a significant increase of minority-spin states at $E_F$. Furthermore, rare occurrence of a valence state transition between the bulk and the surface is demonstrated highlighting the importance of HAXPES in resolving the electronic structure of materials unhindered by surface effects. △ Less

Submitted 4 October, 2018; originally announced October 2018.

Comments: Manuscript and Supplementary material, 13 pages, 17 figures

Journal ref: Phys. Rev. B 99, 035102 (2019)

Physical properties and electrochemical performance of Zn-substituted Na$_{0.44}$Mn$_{1-x}$Zn$_x$O$_2$ nanostructures as cathode in Na-ion batteries

Authors: Mahesh Chandra, Rishabh Shukla, Rakesh Saroha, A. K. Panwar, Amit Gupta, S. Basu, R. S. Dhaka

Abstract: We report the synthesis, physical properties and electrochemical performance of Zn substituted Na$_{0.44}$Mn$_{1-x}$Zn$_x$O$_2$ ($x=$ 0 -- 0.02) nanostructures as cathode in Na-ion batteries for energy storage applications. These samples stabilize in the orthorhombic structure and the morphology is found to be slab like with 100 -- 200~nm width and few micrometer of length. The resistivity measure… ▽ More We report the synthesis, physical properties and electrochemical performance of Zn substituted Na$_{0.44}$Mn$_{1-x}$Zn$_x$O$_2$ ($x=$ 0 -- 0.02) nanostructures as cathode in Na-ion batteries for energy storage applications. These samples stabilize in the orthorhombic structure and the morphology is found to be slab like with 100 -- 200~nm width and few micrometer of length. The resistivity measurements show highly insulating nature for all the samples, where the activation energy decreases with increasing Zn concentration indicating more defect levels in the band gap. The cyclic voltammogram (CV) shows reversible oxidation and reduction peaks, which clearly shift towards higher/lower potentials with increasing Zn concentration up to 2\%. We observed the specific capacity of about 100~mAh/g at current density of 4 mA/g and improved cycle life for Zn substituted $x=$ 0.005 sample. However, with further increasing the Zn concentration ($x=$ 0.02), the specific capacity decreases, which can be a manifestation of the decreased number of reduction peaks in the CV data. △ Less

Submitted 13 August, 2018; originally announced August 2018.

Comments: accepted for publication in Ceramics International

Journal ref: Ceramics International, 44, 21127 (2018)

Novel Superconductivity in Endohedral Gallide Mo8Ga41

Authors: P. Neha, P. Sivaprakash, K. Ishigaki, G. Kalaiselvan, K. Manikandan, Y. Uwatoko, R. S. Dhaka, S. Arumugam, S. Patnaik

Abstract: We report on synthesis and characterization of gallide cluster based Mo8Ga41 superconductor. Transport and magnetization measurements confirm the superconducting transition temperature to be 9.8 K. The upper critical field, lower critical field, Ginzburg-Landau coherence length and penetration depth are estimated to be 11.8T, 150G, 5.2nm, 148nm respectively. The electronic band structure, density… ▽ More We report on synthesis and characterization of gallide cluster based Mo8Ga41 superconductor. Transport and magnetization measurements confirm the superconducting transition temperature to be 9.8 K. The upper critical field, lower critical field, Ginzburg-Landau coherence length and penetration depth are estimated to be 11.8T, 150G, 5.2nm, 148nm respectively. The electronic band structure, density of states and phonon dispersion curve calculations are obtained by using Density Functional Theory. The core level X-ray Photoelectron Spectroscopy (XPS) reveals the binding energy information of the constituting elements Mo and Ga in Mo8Ga41. The valence band spectra from XPS is in good agreement with calculated density of states (DOS). The zero field critical current density (Jc) at T = 2 K is ~ 3*10^5 A/cm^2 which is indicative of efficient flux pinning in the as grown compound. About two fold enhancement in critical current density with application of external pressure (1.1 GPa) is observed with marginal decrease in transition temperature. The fitting of current density to double exponential model confirms possibility of two gap superconductivity in Mo8Ga41. △ Less

Submitted 26 July, 2018; originally announced July 2018.

Synthesis and physical properties of Na$_x$TO$_2$ (T=Mn, Co) nanostructures for cathode materials in Na--ion batteries

Authors: Mahesh Chandra, Rishabh Shukla, Muhammad Rashid, Amit Gupta, Suddhasatwa Basu, R. S. Dhaka

Abstract: We prepared Na$_x$TO$_2$ (T = Mn, Co) nanostructures to use as cathode material in Na-ion batteries. The Rietveld refinement of x-ray diffraction data confirms the hexagonal symmetry. Scanning and transmission electron microscopy measurements show hexagonal and rod-shape morphology for T = Co and Mn, respectively. The magnetic measurements indicate the presence of variable oxidation states of Mn/C… ▽ More We prepared Na$_x$TO$_2$ (T = Mn, Co) nanostructures to use as cathode material in Na-ion batteries. The Rietveld refinement of x-ray diffraction data confirms the hexagonal symmetry. Scanning and transmission electron microscopy measurements show hexagonal and rod-shape morphology for T = Co and Mn, respectively. The magnetic measurements indicate the presence of variable oxidation states of Mn/Co ions, but no long range ordering till 5~K. We find that the Na$_{0.6}$MnO$_2$ is highly insulating whereas Na$_{0.7}$CoO$_2$ is semiconducting in nature. The conduction in Na$_{0.7}$CoO$_2$ takes place through both variable range hop** (VRH) as well as activation mechanisms in different temperature ranges. However, for Na$_{0.6}$MnO$_2$ the VRH prevails at elevated temperatures. Furthermore, the coin cells have been fabricated and tested the electrochemical behavior using cyclic voltammetry, which confirms the reversibility of Na--ions during intercalation/de-intercalation. △ Less

Submitted 17 April, 2018; originally announced April 2018.

Comments: to appear in Materials Research Bulletin

Journal ref: Materials Research Bulletin, 105, 178 (2018)

Anomalous magnetic and spin glass behavior in Nb substituted LaCo$_{1-x}$Nb$_x$O$_3$

Authors: Rishabh Shukla, R. S. Dhaka

Abstract: We report the structural, magnetic, transport and electronic properties of Nb substituted LaCo$_{1-x}$Nb$_x$O$_3$ ($x =$ 0--0.2). The Rietveld analysis of x-ray diffraction data demonstrate structural phase transitions from rhombohedral to orthorhombic and further to monoclinic with increasing the Nb concentration up to $x \ge$ 0.2. Interestingly, we observed dramatic changes in the magnetization… ▽ More We report the structural, magnetic, transport and electronic properties of Nb substituted LaCo$_{1-x}$Nb$_x$O$_3$ ($x =$ 0--0.2). The Rietveld analysis of x-ray diffraction data demonstrate structural phase transitions from rhombohedral to orthorhombic and further to monoclinic with increasing the Nb concentration up to $x \ge$ 0.2. Interestingly, we observed dramatic changes in the magnetization (M) with increasing the Nb concentration, as the M sharply increases below 10~K even at 2.5\% substitution. Furthermore, ac susceptibility data show the spin-glass behavior in $x=$ 0.1 sample. We find that the density of states near the Fermi level decreases and the activation energy increases, which results in the decreasing conductivity with higher Nb concentration. A significant shift in the peak position of A$_{2g}$ phonon mode has been observed using Raman spectroscopy, which indicates the change in the coupling due to the structural distortion with Nb substitution. The core-level photoemission study confirms that the Nb is present in 5+ valence state. Our study reveals that the nonmagnetic Nb$^{5+}$ ($d^0$) substitution converts Co$^{3+}$ ions to Co$^{2+}$ and stabilize both in the high-spin state. Our results suggest that structural and spin-state transitions as well as the difference in the ionic radii between Nb$^{5+}$ and Co$^{3+}$ are playing an important role in tuning the physical properties. △ Less

Submitted 13 January, 2018; originally announced January 2018.

Comments: to appear in PRB

Structural and Magnetic Characterizations of Co2FeGa/SiO2 Nanoparticles Prepared via Chemical Route

Authors: Priyanka, Rajendra S. Dhaka

Abstract: We report the synthesis of Co2FeGa/SiO2 nanoparticles by sol-gel method and characterization using x-ray diffraction (XRD), transmission electron microscopy (TEM) and magnetic measurements. The Rietveld refinements of XRD data with space group Fm-3m clearly show the formation of A2 disorder single phase and the lattice constant is found to be 5.738 Å. The energy-dispersive x-ray spectroscopy (EDX)… ▽ More We report the synthesis of Co2FeGa/SiO2 nanoparticles by sol-gel method and characterization using x-ray diffraction (XRD), transmission electron microscopy (TEM) and magnetic measurements. The Rietveld refinements of XRD data with space group Fm-3m clearly show the formation of A2 disorder single phase and the lattice constant is found to be 5.738 Å. The energy-dispersive x-ray spectroscopy (EDX) confirm the elemental composition close the desired values. The value of coercivity is found to be around 283 Oe and 126 Oe, measured at 10 K and 300 K, respectively. We observed the saturation magnetization significantly lower than expected from Slater-Pauling rule. This decrease in the magnetic moment might be due to the presence of amorphous SiO2 during the synthesis process. A large content of small size SiO2 particles along with Co2FeGa nanoparticles are also found in TEM study. △ Less

Submitted 14 November, 2017; originally announced November 2017.

Comments: 4 pages, AIP conference

Effect of Cu$^{2+}$ substitution in Spin-Orbit Coupled Sr$_2$Ir$_{1-x}$Cu$_x$O$_4$: Structure, magnetism and electronic properties

Authors: Imtiaz Noor Bhatti, R. S. Dhaka, A. K. Pramanik

Abstract: Sr$_2$IrO$_4$ is an extensively studied spin-orbit coupling induced insulator with antiferromagnetic ground state. The delicate balance between competing energy scales plays crucial role for its low temperature phase, and the route of chemical substitution has often been used to tune these different energy scales. Here, we report an evolution of structural, magnetic and electronic properties in do… ▽ More Sr$_2$IrO$_4$ is an extensively studied spin-orbit coupling induced insulator with antiferromagnetic ground state. The delicate balance between competing energy scales plays crucial role for its low temperature phase, and the route of chemical substitution has often been used to tune these different energy scales. Here, we report an evolution of structural, magnetic and electronic properties in doped Sr$_2$Ir$_{1-x}$Cu$_x$O$_4$ ($x$ $\leq$ 0.2). The substitution of Cu$^{2+}$ (3$d^9$) for Ir$^{4+}$ (5$d^5$) acts for electron do**, though it tunes the related parameters such as, spin-orbit coupling, electron correlation and Ir charge state. Moreover, both Ir$^{4+}$ and Cu$^{2+}$ has single unpaired spin though it occupies different $d$-orbitals. With Cu substitution, system retains its original structural symmetry but the structural parameters show systematic changes. X-ray photoemission spectroscopy measurements show Ir$^{4+}$ equivalently converts to Ir$^{5+}$ and a significant enhancement in the density of states has been observed at the Fermi level due to the contribution from the Cu 3$d$ orbitals, which supports the observed decrease in the resistivity with Cu substitution. While the long-range magnetic ordering is much weakened and the highest doped sample shows almost paramagnetic-like behavior the overall system remains insulator. Analysis of resistivity data shows mode of charge conduction in whole series follows 2-dimensional variable-range-hop** model but the range of validity varies with temperature. Whole series of samples exhibit negative magnetoresistance at low temperature which is considered to be a signature of weak localization effect in spin-orbit coupled system, and its evolution with Cu appears to follow the variation of resistivity with $x$. △ Less

Submitted 27 October, 2017; originally announced October 2017.

Comments: 10 pages, 9 figures, appeared in Phys. Rev. B

Journal ref: Phys. Rev. B 96, 144433 (2017)

Tuning ferromagnetism and spin state in La$_{(1-x)}$$A_x$CoO$_3$ ($A=$ Sr, Ca) nanoparticles

Authors: Ravi Prakash, Rishabh Shukla, Priyanka, Anita Dhaka, R. S. Dhaka

Abstract: We use the x-ray diffraction, magnetic susceptibility, isothermal magnetization, and photoelectron spectroscopy to study the structural, magnetic and electronic properties of La$_{(1-x)}$$A_x$CoO$_3$ ($A=$ Sr, Ca; $x=$ 0 -- 0.2) nanoparticles. The Rietveld refinements of room temperature powder x-ray diffraction data confirm the single phase and the rhombohedral crystal structure with R$\bar{3}$C… ▽ More We use the x-ray diffraction, magnetic susceptibility, isothermal magnetization, and photoelectron spectroscopy to study the structural, magnetic and electronic properties of La$_{(1-x)}$$A_x$CoO$_3$ ($A=$ Sr, Ca; $x=$ 0 -- 0.2) nanoparticles. The Rietveld refinements of room temperature powder x-ray diffraction data confirm the single phase and the rhombohedral crystal structure with R$\bar{3}$C space group. We find drastic changes in the magnetic properties and spin-states with Sr/Ca substitution (hole do**). For $x=$ 0 sample, the magnetic measurements show a ferromagnetic transition at T$_{\rm C}$$\approx$85 K, which shifted significantly to higher temperatures with hole do**; simultaneously a significant increase in the spontaneous magnetic moment has been observed. Whereas, the coercive field H$_{\rm C}$ values are 7, 4.4 and 13.2~kOe for $x=$ 0, 0.2 (Sr), and 0.2(Ca) samples. Furthermore, the FC magnetization shows a ferromagnetic Brillouin function like behavior at low temperatures for Ca samples. We demonstrate that the Sr/Ca substitution increases the population of IS (Co$^{3+}$) and LS (Co$^{4+}$) states and tune the ferromagnetism in nanoparticles via double-exchange interactions between Co$^{3+}$-- Co$^{4+}$. Our results suggest an important role of hole carriers and nano-size effect in controlling the spin-state and magnetism in La$_{(1-x)}$$A_x$CoO$_3$ nanoparticles. △ Less

Submitted 6 September, 2017; originally announced September 2017.

Comments: submitted

Direct observation of enhanced magnetism in individual size- and shape-selected 3d transition metal nanoparticles

Authors: Armin Kleibert, Ana Balan, Rocio Yanes, Peter M. Derlet, C. A. F. Vaz, Martin Timm, Arantxa Fraile Rodríguez, Armand Béché, Jo Verbeeck, Rajen S. Dhaka, Milan Radovic, Ulrich Nowak, Frithjof Nolting

Abstract: Magnetic nanoparticles are important building blocks for future technologies ranging from nano-medicine to spintronics. Many related applications require nanoparticles with tailored magnetic properties. However, despite significant efforts undertaken towards this goal, a broad and poorly-understood dispersion of magnetic properties is reported, even within mono-disperse samples of the canonical fe… ▽ More Magnetic nanoparticles are important building blocks for future technologies ranging from nano-medicine to spintronics. Many related applications require nanoparticles with tailored magnetic properties. However, despite significant efforts undertaken towards this goal, a broad and poorly-understood dispersion of magnetic properties is reported, even within mono-disperse samples of the canonical ferromagnetic 3d transition metals. We address this issue by investigating the magnetism of a large number of size- and shape-selected, individual nanoparticles of Fe, Co, and Ni using a unique set of complementary characterization techniques. At room temperature only superparamagnetic behavior is observed in our experiments for all Ni nanoparticles within the investigated sizes, which range from 8 to 20 nm. However, Fe and Co nanoparticles can exist in two distinct magnetic states at any size in this range: (i) a superparamagnetic state as expected from the bulk and surface anisotropies known for the respective materials and as observed for Ni; and (ii) a state with unexpected stable magnetization at room temperature. This striking state is assigned to significant modifications of the magnetic properties arising from metastable lattice defects in the core of the nanoparticles as concluded by calculations and atomic structural characterization. Also related with the structural defects, we find that the magnetic state of Fe and Co nanoparticles can be tuned by thermal treatment enabling one to tailor their magnetic properties for applications. This work demonstrates the importance of complementary single particle investigations for a better understanding of nanoparticle magnetism and for full exploration of their potential for applications. △ Less

Submitted 13 February, 2017; originally announced February 2017.

Comments: 38 pages, 6 figures, Supplementary Material

Journal ref: Phys. Rev. B 95, 195404 (2017)

Evolution of structure, magnetism and electronic transport in doped pyrochlore iridate Y$_2$Ir$_{2-x}$Ru$_{x}$O$_7$

Authors: Harish Kumar, R. S. Dhaka, A. K. Pramanik

Abstract: The interplay between spin-orbit coupling (SOC) and electron correlation ($U$) is considered for many exotic phenomena in iridium oxides. We have investigated the evolution of structural, magnetic and electronic properties in pyrochlore iridate Y$_2$Ir$_{2-x}$Ru$_{x}$O$_7$ where the substitution of Ru has been aimed to tune this interplay. The Ru substitution does not introduce any structural phas… ▽ More The interplay between spin-orbit coupling (SOC) and electron correlation ($U$) is considered for many exotic phenomena in iridium oxides. We have investigated the evolution of structural, magnetic and electronic properties in pyrochlore iridate Y$_2$Ir$_{2-x}$Ru$_{x}$O$_7$ where the substitution of Ru has been aimed to tune this interplay. The Ru substitution does not introduce any structural phase transition, however, we do observe an evolution of lattice parameters with the do** level $x$. X-ray photoemission spectroscopy (XPS) study indicates Ru adopts charge state of Ru$^{4+}$ and replaces the Ir$^{4+}$ accordingly. Magnetization data reveal both the onset of magnetic irreversibility and the magnetic moment decreases with progressive substitution of Ru. These materials show non-equilibrium low temperature magnetic state as revealed by magnetic relaxation data. Interestingly, we find magnetic relaxation rate increases with substitution of Ru. The electrical resistivity shows an insulating behavior in whole temperature range, however, resistivity decreases with substitution of Ru. Nature of electronic conduction has been found to follow power-law behavior for all the materials. △ Less

Submitted 3 February, 2017; originally announced February 2017.

Comments: To appear in Phys. Rev. B

Journal ref: Phys. Rev. B 95, 054415 (2017)

Observation of Dirac-like band dispersion in LaAgSb$_2$

Authors: X. Shi, P. Richard, Kefeng Wang, M. Liu, C. E. Matt, N. Xu, R. S. Dhaka, Z. Ristic, T. Qian, Y. -F. Yang, C. Petrovic, M. Shi, H. Ding

Abstract: We present a combined angle-resolved photoemission spectroscopy (ARPES) and first-principles calculations study of the electronic structure of LaAgSb$_2$ in the entire first Brillouin zone. We observe a Dirac-cone-like structure in the vicinity of the Fermi level formed by the crossing of two linear energy bands, as well as the nested segments of Fermi surface pocket emerging from the cone. Our AR… ▽ More We present a combined angle-resolved photoemission spectroscopy (ARPES) and first-principles calculations study of the electronic structure of LaAgSb$_2$ in the entire first Brillouin zone. We observe a Dirac-cone-like structure in the vicinity of the Fermi level formed by the crossing of two linear energy bands, as well as the nested segments of Fermi surface pocket emerging from the cone. Our ARPES results show the close relationship of the Dirac cone to the charge-density-wave ordering, providing consistent explanations for exotic behaviors in this material. △ Less

Submitted 16 February, 2016; v1 submitted 14 December, 2015; originally announced December 2015.

Comments: 5 pages, 4 figures

Journal ref: Phys. Rev. B 93, 081105 (2016)