Laser Printing of Silver and Silver Oxide
Authors:
Jordan M. Adams,
Daniel Heligman,
Ryan O'Dell,
Christine Y. Wang,
Daniel Young
Abstract:
We show that direct laser writing (DLW) in aqueous silver nitrate with a 1030 nm femtosecond (fs) laser results in deposition of a mixture of silver oxide and silver, in contrast to the pure silver deposition previously reported with 780 nm fs DLW. However, adding photoinitiator prevents silver oxide formation in a concentration-dependent manner. As a result, the resistivity of the material can al…
▽ More
We show that direct laser writing (DLW) in aqueous silver nitrate with a 1030 nm femtosecond (fs) laser results in deposition of a mixture of silver oxide and silver, in contrast to the pure silver deposition previously reported with 780 nm fs DLW. However, adding photoinitiator prevents silver oxide formation in a concentration-dependent manner. As a result, the resistivity of the material can also be controlled by photoinitiator concentration with resistivity being reduced from approximately 9e-3 $Ωm$ to 3e-7 $Ωm$. Silver oxide peaks dominate the X-ray diffraction spectra when no photoinitiator is present, while the peaks disappear with photoinitiator concentrations above 0.05wt%. While femtosecond pulses are needed to initiate deposition, a continues-wave laser when well overlapped with the previously written material and supplying enough average power can lead to further printing, suggesting thermal deposition can also occur where the photoinitiator molecule also acts as a general reducing agent that prevents oxide formation. We also compare the surface quality of printed lines for different photoinitiator concentrations and laser printing conditions. A THz polarizer and metamaterial are printed as a demonstration of silver oxide printing.
△ Less
Submitted 3 June, 2024; v1 submitted 15 May, 2024;
originally announced May 2024.
-
Transient shear banding in the nematic dumbbell model of liquid crystalline polymers
Authors:
James M Adams,
Daniel Corbett
Abstract:
In the shear flow of liquid crystalline polymers (LCPs) the nematic director orientation can align with the flow direction for some materials, but continuously tumble in others. The nematic dumbbell (ND) model was originally developed to describe the rheology of flow-aligning semi-flexible LCPs, and flow-aligning LCPs are the focus in this paper. In the shear flow of monodomain LCPs it is usually…
▽ More
In the shear flow of liquid crystalline polymers (LCPs) the nematic director orientation can align with the flow direction for some materials, but continuously tumble in others. The nematic dumbbell (ND) model was originally developed to describe the rheology of flow-aligning semi-flexible LCPs, and flow-aligning LCPs are the focus in this paper. In the shear flow of monodomain LCPs it is usually assumed that the spatial distribution of the velocity is uniform. This is in contrast to polymer solutions, where highly non-uniform spatial velocity profiles have been observed in experiments. We analyse the ND model, with an additional gradient term in the constitutive model, using a linear stability analysis. We investigate the separate cases of constant applied shear stress, and constant applied shear rate. We find that the ND model has a transient flow instability to the formation of a spatially inhomogeneous flow velocity for certain starting orientations of the director. We calculate the spatially resolved flow profile in both constant applied stress and constant applied shear rate in start up from rest, using a model with one spatial dimension to illustrate the flow behaviour of the fluid. For low shear rates flow reversal can be seen as the director realigns with the flow direction, whereas for high shear rates the director reorientation occurs simultaneously across the gap. Experimentally, this inhomogeneous flow is predicted to be observed in flow reversal experiments in LCPs.
△ Less
Submitted 20 February, 2018;
originally announced February 2018.
-
A numerical study of stretched smectic-A elastomer sheets
Authors:
Andrew W. Brown,
James M. Adams
Abstract:
We present a numerical study of stretching monodomain smectic-A elastomer sheets, computed using the finite element method. When stretched parallel to the layer normal the microscopic layers in smectic elastomers are unstable to a transition to a buckled state. We account for the layer buckling by replacing the microscopic energy with a coarse grained effective free energy that accounts for the fi…
▽ More
We present a numerical study of stretching monodomain smectic-A elastomer sheets, computed using the finite element method. When stretched parallel to the layer normal the microscopic layers in smectic elastomers are unstable to a transition to a buckled state. We account for the layer buckling by replacing the microscopic energy with a coarse grained effective free energy that accounts for the fine scale deformation of the layers. We augment this model with a term to describe the energy of deforming buckled layers, which is necessary to reproduce the experimentally observed Poisson's ratios post-buckling. We examine the spatial distribution of the microstructure phases for various stretching angles relative to the layer normal, and for different length-to-width aspect ratios. When stretching parallel to the layer normal the majority of the sample forms a bi-directionally buckled microstructure, except at the clamps where uni-directional microstructure is predicted. When stretching at small inclinations to the layer normal the phase of the sample is sensitive to the aspect ratio of the sample, with the bi-directionally buckled phase persistent to large angles only for small aspect ratios. We relate these theoretical results to experiments on smectic-A elastomers.
△ Less
Submitted 8 May, 2013;
originally announced May 2013.
-
Tack energy and switchable adhesion of liquid crystal elastomers
Authors:
D. R. Corbett,
J. M. Adams
Abstract:
The mechanical properties of liquid crystal elastomers (LCEs) make them suitable candidates for pressure-sensitive adhesives (PSAs). Using the nematic dumbbell constitutive model, and the block model of PSAs, we study their tack energy and the debonding process as could be measured experimentally in the probe-tack test. To investigate their performance as switchable PSAs we compare the tack energy…
▽ More
The mechanical properties of liquid crystal elastomers (LCEs) make them suitable candidates for pressure-sensitive adhesives (PSAs). Using the nematic dumbbell constitutive model, and the block model of PSAs, we study their tack energy and the debonding process as could be measured experimentally in the probe-tack test. To investigate their performance as switchable PSAs we compare the tack energy for the director aligned parallel, and perpendicular to the substrate normal, and for the isotropic state. We find that the tack energy is larger in the parallel alignment than the isotropic case by over a factor of two. The tack energy for the perpendicular alignment can be 50% less than the isotropic case. We propose a mechanism for reversibly switchable adhesion based on the reversibility of the isotropic to nematic transition. Finally we consider the influence of several material parameters that could be used to tune the stress-strain response.
△ Less
Submitted 11 August, 2012;
originally announced August 2012.
-
Negative Poisson's ratio and semi-soft elasticity of smectic-C liquid crystal elastomers
Authors:
A. W. Brown,
J. M. Adams
Abstract:
Models of smectic-C liquid crystal elastomers predict that it can display soft elasticity, in which the shape of the elastomer changes at no energy cost. The amplitude of the soft mode and the accompanying shears are dependent on the orientation of the layer normal and the director with respect to the stretch axis. We demonstrate that in some geometries the director is forced to rotate perpendicul…
▽ More
Models of smectic-C liquid crystal elastomers predict that it can display soft elasticity, in which the shape of the elastomer changes at no energy cost. The amplitude of the soft mode and the accompanying shears are dependent on the orientation of the layer normal and the director with respect to the stretch axis. We demonstrate that in some geometries the director is forced to rotate perpendicular to the stretch axis, causing lateral expansion of the sample; a negative Poisson's ratio. Current models do not include the effect of imperfections that must be present in the physical sample. We investigate the effect of a simple model of these imperfections on the soft modes in monodomain smectic-C elastomers in a variety of geometries. When stretching parallel to the layer normal (with imposed strain) the elastomer has a negative stiffness once the director starts to rotate. We show that this is a result of the negative Poisson's ratio in this geometry through a simple scalar model.
△ Less
Submitted 28 July, 2011; v1 submitted 27 July, 2011;
originally announced July 2011.
-
Transient shear banding in entangled polymers: a study using the Rolie-Poly model
Authors:
J. M. Adams,
S. M. Fielding,
P. D. Olmsted
Abstract:
Spatially inhomogeneous shear flow occurs in entangled polymer solutions, both as steady state shear banding and transiently after a large step strain or during start up to a steady uniform shear rate. Steady state shear banding is a hallmark of models with a non-monotonic constitutive relation between total shear stress and applied shear rate, but transient banding is sometimes seen in fluids tha…
▽ More
Spatially inhomogeneous shear flow occurs in entangled polymer solutions, both as steady state shear banding and transiently after a large step strain or during start up to a steady uniform shear rate. Steady state shear banding is a hallmark of models with a non-monotonic constitutive relation between total shear stress and applied shear rate, but transient banding is sometimes seen in fluids that do not shear band at steady state. We model this behavior using the diffusive Rolie-Poly model in a Newtonian solvent, whose constitutive behavior can be monotonic or non-monotonic depending on the degree of convected constraint release (CCR). We study monotonic constitutive behaviour. Linear stability analysis of start up to a sufficiently high shear rate shows that spatial fluctuations are unstable at early times. There is a strong correlation between this instability and the negative slope of the (time dependent) constitutive curve. If the time integral of the most unstable eigenvalue is sufficiently large then the system exhibits transient shear bands that later vanish in steady state. We show how perturbations, due to fluctuations or the inhomogeneous stresses, can trigger this instability. This transient behavior is similar to recent observations in entangled polymer solutions
△ Less
Submitted 2 June, 2011; v1 submitted 19 November, 2010;
originally announced November 2010.
-
Strain Analysis of a Chiral Smectic A Elastomer
Authors:
Christopher M. Spillmann,
John H. Konnert,
James M. Adams,
Jeffrey R. Deschamps,
Jawad Naciri,
Banahalli R. Ratna
Abstract:
We present a detailed analysis of the molecular packing of a strained liquid crystal elastomer composed of chiral mesogens in the smectic A phase. X-ray diffraction patterns of the elastomer collected over a range of orientations with respect to the X-ray beam were used to reconstruct the three-dimensional scattering intensity as a function of tensile strain. For the first time, we show that the s…
▽ More
We present a detailed analysis of the molecular packing of a strained liquid crystal elastomer composed of chiral mesogens in the smectic A phase. X-ray diffraction patterns of the elastomer collected over a range of orientations with respect to the X-ray beam were used to reconstruct the three-dimensional scattering intensity as a function of tensile strain. For the first time, we show that the smectic domain order is preserved in these strained elastomers. Changes in the intensity within a given scattering plane are due to reorientation, and not loss, of the molecular order in directions orthogonal to the applied strain. Incorporating the physical parameters of the elastomer, a nonlinear elastic model is presented to describe the rotation of the smectic-layered domains under strain, thus providing a fundamental analysis to the mechanical response of these unique materials.
△ Less
Submitted 31 August, 2010;
originally announced August 2010.
-
Adams and Olmsted Reply to comment on article "A non-monotonic constitutive model is not necessary to obtain shear banding phenomena in entangled polymer solution" [Phys. Rev. Lett. 102, 067801 (2009), arXiv:0805.0679]
Authors:
J. M. Adams,
P. D. Olmsted
Abstract:
Wang [Phys. Rev. Lett. 103, 219801 (2009)] makes the following points about our Letter [Phys. Rev. Lett. 102, 067801 (2009), arXiv:0805.0679]: (1) He infers that, "contrary to its title, shear banding emerged from monotonic curves only if there was a stress gradient", and he points out that nonquiescent relaxation was found (experimentally) after step strain in geometries without a stress gradie…
▽ More
Wang [Phys. Rev. Lett. 103, 219801 (2009)] makes the following points about our Letter [Phys. Rev. Lett. 102, 067801 (2009), arXiv:0805.0679]: (1) He infers that, "contrary to its title, shear banding emerged from monotonic curves only if there was a stress gradient", and he points out that nonquiescent relaxation was found (experimentally) after step strain in geometries without a stress gradient. (2) He disagrees with the values of the parameters we used. (3) In some recent experiments the flow was homogeneous after cessation of step strain, and only subsequently developed nonquiescent macroscopic motion. We only showed step strains that developed an inhomogeneity before cessation of flow. In this reply we address these points.
△ Less
Submitted 23 November, 2009;
originally announced November 2009.
-
Mechanical switching of ferro-electric rubber
Authors:
J. M. Adams,
M. Warner
Abstract:
At the A to C transition, smectic elastomers have recently been observed to undergo $\sim$35% spontaneous shear strains. We first explicitly describe how strains of up to twice this value could be mechanically or electrically induced in Sm-$C$ elastomers by rotation of the director on a cone around the layer normal at various elastic costs depending on constraints. Secondly, for typical sample g…
▽ More
At the A to C transition, smectic elastomers have recently been observed to undergo $\sim$35% spontaneous shear strains. We first explicitly describe how strains of up to twice this value could be mechanically or electrically induced in Sm-$C$ elastomers by rotation of the director on a cone around the layer normal at various elastic costs depending on constraints. Secondly, for typical sample geometries, we give the various microstructures in Sm-$C$ akin to those seen in nematic elastomers under distortions with constraints. It is possible to give explicit results for the nature of the textures. Chiral Sm-$C$ elastomers are ferro-electric. We calculate how the polarization could be mechanically reversed by large, hard or soft strains of the rubber, depending upon sample geometry.
△ Less
Submitted 9 December, 2008;
originally announced December 2008.
-
A non-monotonic constitutive model is not necessary to obtain shear banding phenomena in entangled polymer solutions
Authors:
J. M. Adams,
P. D. Olmsted
Abstract:
In 1975 Doi and Edwards predicted that entangled polymer melts and solutions can have a constitutive instability, signified by a decreasing stress for shear rates greater than the inverse of the reptation time. Experiments did not support this, and more sophisticated theories incorporated Marrucci's idea (1996) of removing constraints by advection; this produced a monotonically increasing stress…
▽ More
In 1975 Doi and Edwards predicted that entangled polymer melts and solutions can have a constitutive instability, signified by a decreasing stress for shear rates greater than the inverse of the reptation time. Experiments did not support this, and more sophisticated theories incorporated Marrucci's idea (1996) of removing constraints by advection; this produced a monotonically increasing stress and thus stable constitutive behavior. Recent experiments have suggested that entangled polymer solutions may possess a constitutive instability after all, and have led some workers to question the validity of existing constitutive models. In this Letter we use a simple modern constitutive model for entangled polymers, the non-stretching Rolie-Poly model with an added solvent viscosity, and show that (1) instability and shear banding is captured within this simple class of models; (2) shear banding phenomena is observable for weakly stable fluids in flow geometries that impose a sufficiently inhomogeneous total shear stress; (3) transient phenomena can possess inhomogeneities that resemble shear banding, even for weakly stable fluids. Many of these results are model-independent.
△ Less
Submitted 14 December, 2008; v1 submitted 6 May, 2008;
originally announced May 2008.
-
Smectic-$A$ elastomers with weak director anchoring
Authors:
J. M. Adams,
M. Warner,
O. Stenull,
T. C. Lubensky
Abstract:
Experimentally it is possible to manipulate the director in a (chiral) smectic-$A$ elastomer using an electric field. This suggests that the director is not necessarily locked to the layer normal, as described in earlier papers that extended rubber elasticity theory to smectics. Here, we consider the case that the director is weakly anchored to the layer normal assuming that there is a free ener…
▽ More
Experimentally it is possible to manipulate the director in a (chiral) smectic-$A$ elastomer using an electric field. This suggests that the director is not necessarily locked to the layer normal, as described in earlier papers that extended rubber elasticity theory to smectics. Here, we consider the case that the director is weakly anchored to the layer normal assuming that there is a free energy penalty associated with relative tilt between the two. We use a recently developed weak-anchoring generalization of rubber elastic approaches to smectic elastomers and study shearing in the plane of the layers, stretching in the plane of the layers, and compression and elongation parallel to the layer normal. We calculate, inter alia, the engineering stress and the tilt angle between director and layer normal as functions of the applied deformation. For the latter three deformations, our results predict the existence of an instability towards the development of shear accompanied by smectic-$C$-like order.
△ Less
Submitted 6 March, 2008;
originally announced March 2008.
-
Smectic-C tilt under shear in Smectic-A elastomers
Authors:
Olaf Stenull,
T. C. Lubensky,
J. M. Adams,
Mark Warner
Abstract:
Stenull and Lubensky [Phys. Rev. E {\bf 76}, 011706 (2007)] have argued that shear strain and tilt of the director relative to the layer normal are coupled in smectic elastomers and that the imposition of one necessarily leads to the development of the other. This means, in particular, that a Smectic-A elastomer subjected to a simple shear will develop Smectic-C-like tilt of the director. Recent…
▽ More
Stenull and Lubensky [Phys. Rev. E {\bf 76}, 011706 (2007)] have argued that shear strain and tilt of the director relative to the layer normal are coupled in smectic elastomers and that the imposition of one necessarily leads to the development of the other. This means, in particular, that a Smectic-A elastomer subjected to a simple shear will develop Smectic-C-like tilt of the director. Recently, Kramer and Finkelmann [arXiv:0708.2024, Phys. Rev. E {\bf 78}, 021704 (2008)] performed shear experiments on Smectic-A elastomers using two different shear geometries. One of the experiments, which implements simple shear, produces clear evidence for the development of Smectic-C-like tilt. Here, we generalize a model for smectic elastomers introduced by Adams and Warner [Phys. Rev. E {\bf 71}, 021708 (2005)] and use it to study the magnitude of Smectic-C-like tilt under shear for the two geometries investigated by Kramer and Finkelmann. Using reasonable estimates of model parameters, we estimate the tilt angle for both geometries, and we compare our estimates to the experimental results. The other shear geometry is problematic since it introduces additional in-plane compressions in a sheet-like sample, thus inducing instabilities that we discuss.
△ Less
Submitted 8 August, 2008; v1 submitted 27 February, 2008;
originally announced February 2008.
-
The interplay between boundary conditions and flow geometries in shear banding: hysteresis, band configurations, and surface transitions
Authors:
J. M. Adams,
S. M. Fielding,
P. D. Olmsted
Abstract:
We study shear banding flows in models of wormlike micelles or polymer solutions, and explore the effects of different boundary conditions for the viscoelastic stress. These are needed because the equations of motion are inherently non-local and include ``diffusive'' or square-gradient terms. Using the diffusive Johnson-Segalman model and a variant of the Rolie-Poly model for entangled micelles…
▽ More
We study shear banding flows in models of wormlike micelles or polymer solutions, and explore the effects of different boundary conditions for the viscoelastic stress. These are needed because the equations of motion are inherently non-local and include ``diffusive'' or square-gradient terms. Using the diffusive Johnson-Segalman model and a variant of the Rolie-Poly model for entangled micelles or polymer solutions, we study the interplay between different boundary conditions and the intrinsic stress gradient imposed by the flow geometry. We consider prescribed gradient (Neumann) or value (Dirichlet) of the viscoelastic stress tensor at the boundary, as well as mixed boundary conditions in which an anchoring strength competes with the gradient contribution to the stress dynamics. We find that hysteresis during shear rate sweeps is suppressed if the boundary conditions favor the state that is induced by the sweep. For example, if the boundaries favor the high shear rate phase then hysteresis is suppressed at the low shear rate edges of the stress plateau. If the boundaries favor the low shear rate state, then the high shear rate band can lie in the center of the flow cell, leading to a three-band configuration. Sufficiently strong stress gradients due to curved flow geometries, such as that of cylindrical Couette flow, can convert this to a two-band state by forcing the high shear rate phase against the wall of higher stress, and can suppress the hysteresis loop observed during a shear rate sweep.
△ Less
Submitted 17 October, 2007;
originally announced October 2007.