Impact of cation redox chemistry on continuous hydrothermal synthesis of 2D-Ni(Co/Fe) hydroxides
Authors:
Massimo Rosa,
Debora Marani,
Giovanni Perin,
Søren Bredmose Simonsen,
Philipp Zielke,
Antonella Glisenti,
Ragnar Kiebach,
Andreas Lesch,
Vincenzo Esposito
Abstract:
Continuous hydrothermal flow synthesis (CHFS) is a facile, upscalable and cost-efficient synthetic method enabling the nanostructuring of advanced functional materials in steady conditions, i.e. not in batch synthesis. In this paper, we use CHFS to crystallize NiCo- and NiFe-hydroxides in water solution with 2D nanofeatures. By tuning the synthetic parameters, we disclose the key role of the catio…
▽ More
Continuous hydrothermal flow synthesis (CHFS) is a facile, upscalable and cost-efficient synthetic method enabling the nanostructuring of advanced functional materials in steady conditions, i.e. not in batch synthesis. In this paper, we use CHFS to crystallize NiCo- and NiFe-hydroxides in water solution with 2D nanofeatures. By tuning the synthetic parameters, we disclose the key role of the cation redox chemistry in the transition between two competitive phases: from 2D-nanoplatelets of brucite to layered double hydroxides (LDH). For controlling the precipitation of different Ni, Fe, Co-hydroxide phases, we propose the combined use of an oxidizing (H2O2) and a complexing (NH3) agent. At temperatures as low as 80 °C, the presence of H2O2 and a low concentration of NH3 favour the Ni2+/Co3+ over Ni2+/Co2+ oxidation states, shifting the product structure from brucite phase (temperatures > 80 °C) to LDH. Conversely, for the NiFe-hydroxides the transition from LDH (temperatures < 80 °C) to brucite phase (temperatures > 80 °C) is controlled by the reaction temperature only. Due to the high stability of Fe3+, the synthesis of NiFe products by CHFS does not require oxidizing and complexing agents, resulting in a robust process for large-scale production.
△ Less
Submitted 11 October, 2019;
originally announced October 2019.
-
Continuous hydrothermal flow synthesis of Gd-doped CeO2 (GDC) nanoparticles for inkjet printing of SOFC electrolytes
Authors:
Yu Xu,
Nicholas Farandos,
Massimo Rosa,
Philipp Zielke,
Vincenzo Esposito,
Peter Vang Hendriksen,
Søren Højgaard Jensen,
Tao Li,
Geoffrey Kelsall,
Ragnar Kiebach
Abstract:
GdxCe1-xO2-d (GDC) nanoparticles were synthesized, using continuous hydrothermal flow synthesis. By varying the synthesis conditions, particle size and morphology could be tailored. Here, particle sizes between 6 and 40 nm with polyhedral or octahedral shape could be obtained. Gd0.2Ce0.8O2-d nanoparticles were further processed into inks for inkjet printing. Despite the small particle size/large s…
▽ More
GdxCe1-xO2-d (GDC) nanoparticles were synthesized, using continuous hydrothermal flow synthesis. By varying the synthesis conditions, particle size and morphology could be tailored. Here, particle sizes between 6 and 40 nm with polyhedral or octahedral shape could be obtained. Gd0.2Ce0.8O2-d nanoparticles were further processed into inks for inkjet printing. Despite the small particle size/large surface area, inks with excellent printing behavior were formulated. For proof-of-concept, thin GDC layers were printed on a) green NiO-GDC substrates, and on b) presintered NiO-YSZ substrates. While no dense layers could be obtained on the green NiO-GDC substrates, GDC nanoparticles printed on NiO-YSZ substrates formed a dense continuous layer after firing.
△ Less
Submitted 8 April, 2019;
originally announced April 2019.
-
Stabilization of binary NiO-YSZ nanocolloids for direct inkjet deposition
Authors:
Massimo Rosa,
Philippe Zielke,
Ragnar Kiebach,
Victor Costa Bassetto,
Andreas Lesch,
Vincenzo Esposito
Abstract:
Water-based inks, containing nanometric NiO and YSZ particles in 66/34 vol. % ratio, are produced by colloidal stabilization of a binary dispersion obtained via continuous hydrothermal synthesis at supercritical conditions, i.e. 280 bar and 400 C. The method yields single-crystal particles with diameter < 10 nm for both phases in a single-step process, achieving a highly mixed composite. Two diffe…
▽ More
Water-based inks, containing nanometric NiO and YSZ particles in 66/34 vol. % ratio, are produced by colloidal stabilization of a binary dispersion obtained via continuous hydrothermal synthesis at supercritical conditions, i.e. 280 bar and 400 C. The method yields single-crystal particles with diameter < 10 nm for both phases in a single-step process, achieving a highly mixed composite. Two different approaches are applied to formulate inks printable with piezoelectric printheads, i.e. an electrostatic and an electrosteric stabilization path. The use of the electrosteric dispersant results in colloids with superior stability > 200 days, more uniform thin films and finely nanostructured porous cermet films with thickness below 500 nm, after reducing NiO to Ni. Particles coarsening to 50-150 nm is obtained at 1000 C, accompanied by a shrinkage of ca. 43 % in thickness without the formation of cracks or delamination of the zirconia substrates.
△ Less
Submitted 18 March, 2019;
originally announced March 2019.
-
Zirconia nano-colloids transfer from continuous hydrothermal synthesis to inkjet printing
Authors:
M. Rosa,
P. N. Gooden,
S. Butterworth,
P. Zielke,
R. Kiebach,
Y. Xu,
C. Gadea,
V. Esposito
Abstract:
Water dispersion of nanometric yttria stabilized zirconia (YSZ) particles synthesized by continuous hydrothermal synthesis are transferred into nanoinks for thin film deposition. YSZ nanoparticles are synthesized in supercritical conditions resulting in highly dispersed crystals of 10 nm in size. The rheology of the colloid is tailored to achieve inkjet printability (Z) by using additives for regu…
▽ More
Water dispersion of nanometric yttria stabilized zirconia (YSZ) particles synthesized by continuous hydrothermal synthesis are transferred into nanoinks for thin film deposition. YSZ nanoparticles are synthesized in supercritical conditions resulting in highly dispersed crystals of 10 nm in size. The rheology of the colloid is tailored to achieve inkjet printability (Z) by using additives for regulating viscosity and surface tension. Inks with a wide range of properties are produced. A remarkable effect of nanoparticles on the ink printability is registered even at solid load < 1% vol. In particular, nanoparticles hinder the droplet formation at low values of the printability while suitable jetting is observed at high Z values, i.e. Z ca. 20. For the optimized inks, we achieve high quality printing with lateral and thickness resolution of 70 um and ca. 250 nm respectively, as well as self levelling effect with a reduction of the substrate roughness. Densification is achieved at sintering temperatures below 1200 C.
△ Less
Submitted 18 March, 2019;
originally announced March 2019.