Magnetic irreversibility in ultrafine ZnFe2O4 partices
Authors:
G. F. Goya,
H. R. Rechenberg,
M. Chen,
W. B. Yelon
Abstract:
Pure ultrafine ZnFe2O4 particles have been obtained from mechanosynthesis of the ZnO and Fe2O3 oxides. The average grain diameter was estimated from x-ray diffraction to be <d> = 36(6) nm. Refinement of neutron diffraction (ND) data showed that the resulting cubic spinel structure is oxygen-deficient, with ~7% of Fe3+ ions occupying the tetrahedral A sites. Magnetization curves taken at 4.2 K show…
▽ More
Pure ultrafine ZnFe2O4 particles have been obtained from mechanosynthesis of the ZnO and Fe2O3 oxides. The average grain diameter was estimated from x-ray diffraction to be <d> = 36(6) nm. Refinement of neutron diffraction (ND) data showed that the resulting cubic spinel structure is oxygen-deficient, with ~7% of Fe3+ ions occupying the tetrahedral A sites. Magnetization curves taken at 4.2 K showed absence of saturation up to fields H = 9 Tesla, associated to a spin-canted produced by the milling process. Field-cooled (FC) and zero-field-cooled (ZFC) curves showed irreversible behavior extending well above room temperature, which is associated to spin disorder. Annealing samples at 300 °C yields an average grain size <d> = 50(6) nm, and ~16% of Fe3+ ions at A sites. Partial oxygen recovery is also deduced from neutron data refinement in annealed samples. Concurrently, decrease of magnetic irreversibility is noticed, assigned to partial recovery of the collinear spin structure. Complex Mössbauer spectra were observed at room temperature and 80 K, with broad hyperfine field distributions spanning from ~10 T to ~40 T. At T = 4.2 K, hyperfine field distributions indicate high disorder in Fe local environments. The above data suggest the existence of Fe-rich clusters, yielding strong superexchange interactions between Fe ions at A and B sites of the spinel structure.
△ Less
Submitted 6 February, 2013;
originally announced February 2013.
-
Observation of spin glass state in weakly ferromagnetic Sr$_2$FeCoO$_6$ double perovskite
Authors:
R. Pradheesh,
Harikrishnan S. Nair,
C. M. N. Kumar,
Jagat Lamsal,
R. Nirmala,
P. N. Santhosh,
W. B. Yelon,
S. K. Malik,
V. Sankaranarayanan,
K. Sethupathi
Abstract:
We report the observation of spin glass state in the double perovskite oxide Sr$_{2}$FeCoO$_{6}$ prepared through sol-gel technique. Initial structural studies using x rays reveal that the compound crystallizes in tetragonal $I 4/m$ structure with lattice parameters, $a$ = 5.4609(2) Åand $c$ = 7.7113(7) Å. The temperature dependent powder x ray studies reveal no structural phase transition in the…
▽ More
We report the observation of spin glass state in the double perovskite oxide Sr$_{2}$FeCoO$_{6}$ prepared through sol-gel technique. Initial structural studies using x rays reveal that the compound crystallizes in tetragonal $I 4/m$ structure with lattice parameters, $a$ = 5.4609(2) Åand $c$ = 7.7113(7) Å. The temperature dependent powder x ray studies reveal no structural phase transition in the temperature range 10 -- 300 K. However, the unit cell volume shows an anomaly coinciding with the magnetic transition temperature thereby suggesting a close connection between lattice and magnetism. Neutron diffraction studies and subsequent bond valence sums analysis show that in Sr$_{2}$FeCoO$_{6}$, the $B$ site is randomly occupied by Fe and Co in the mixed valence states of Fe$^{3+}$/Fe$^{4+}$ and Co$^{3+}$/Co$^{4+}$. The random occupancy and mixed valence sets the stage for inhomogeneous magnetic exchange interactions and in turn, for the spin glass like state in this double perovskite which is observed as an irreversibility in temperature dependent dc magnetization at $T_f\sim$ 75 K. Thermal hysteresis observed in the magnetization profile of Sr$_{2}$FeCoO$_{6}$ is indicative of the mixed magnetic phases present. The dynamic magnetic susceptibility displays characteristic frequency dependence and confirms the spin glass nature of this material. Dynamical scaling analysis of $χ'(T)$ yields a critical temperature $T_{ct}$ = 75.14(8) K and an exponent $zν$ = 6.2(2) typical for spin glasses. The signature of presence of mixed magnetic interactions is obtained from the thermal hysteresis in magnetization of Sr$_{2}$FeCoO$_{6}$. Combining the neutron and magnetization results of Sr$_2$FeCoO$_6$, we deduce the spin states of Fe to be in low spin while that of Co to be in low spin and intermediate spin.
△ Less
Submitted 22 November, 2011;
originally announced November 2011.
-
Neutron structural studies on the superconducting (Nd1-xCax)(Ba1.6La0.4)Cu3Oz system
Authors:
Amish G. Joshi,
R. G. Kulkarni,
W. B. Yelon,
Ram Prasad,
M. R. Gonal
Abstract:
We have investigated the influence of Ca ions substitution on the structural and superconducting properties of (Nd1-xCax)(Ba1.6La0.4)Cu3Oz system. Magnetization, X-ray diffraction and neutron diffraction studies have been carried out on a series of compounds with x = 0.0 to 0.6. The superconducting transition temperature Tc, determined from magnetization measurements increases with increasing Ca2+…
▽ More
We have investigated the influence of Ca ions substitution on the structural and superconducting properties of (Nd1-xCax)(Ba1.6La0.4)Cu3Oz system. Magnetization, X-ray diffraction and neutron diffraction studies have been carried out on a series of compounds with x = 0.0 to 0.6. The superconducting transition temperature Tc, determined from magnetization measurements increases with increasing Ca2+ substitution. Neutron diffraction studies reveal that these compounds crystallize in a tetragonal structure (space group P4/mmm). A detailed analysis of the neutron diffraction data reveals that Ca and La ions are intermixed at the nominal Ba and Nd sites. While a major fraction of Ca ions occupy the usual Nd site, a small fraction occupies the Ba site. Consequently, the corresponding amount of La substitutes at the nominal Nd site. The intermixing of Ca and La sites randomizes the chain site oxygens leading to a tetragonal structure despite an oxygen content close to 7.0 for all the Ca doped samples. Further increase of Ca content lead to change in its co-ordination from six-fold to eight-fold at x >= 0.4.
△ Less
Submitted 13 May, 2010;
originally announced May 2010.
-
Structure, magnetic and transport properties of Ti-substituted La0.7Sr0.3MnO3
Authors:
M. S. Kim,
J. B. Yang,
Q. Cai,
X. D. Zhou,
W. J. James,
W. B. Yelon,
P. E. Parris,
D. Buddhikot,
S. K. Malik
Abstract:
Ti-substituted perovskites, La0.7Sr0.3Mn1-xTixO3, with x between 0 to 0.20, were investigated by neutron diffraction, magnetization, electric resistivity, and magnetoresistance (MR) measurements. All samples show a rhombohedral structure (space group R3c) from 10 K to room temperature. At room temperature, the cell parameters a, c and the unit cell volume increase with increasing Ti content. How…
▽ More
Ti-substituted perovskites, La0.7Sr0.3Mn1-xTixO3, with x between 0 to 0.20, were investigated by neutron diffraction, magnetization, electric resistivity, and magnetoresistance (MR) measurements. All samples show a rhombohedral structure (space group R3c) from 10 K to room temperature. At room temperature, the cell parameters a, c and the unit cell volume increase with increasing Ti content. However, at 10 K, the cell parameter a has a maximum value for x = 0.10, and decreases for x greater than 0.10, while the unit cell volume remains nearly constant for x greater than 0.10. The average (Mn,Ti)-O bond length increases up to x=0.15, and the (Mn,Ti)-O-(Mn,Ti) bond angle decreases with increasing Ti content to its minimum value at x=0.15 at room temperature. Below the Curie temperature T_C, the resistance exhibits metallic behavior for the x _ 0.05 samples. A metal (semiconductor) to insulator transition is observed for the x_ 0.10 samples. A peak in resistivity appears below T_C for all samples, and shifts to a lower temperature as x increases. The substitution of Mn by Ti decreases the 2p-3d hybridization between O and Mn ions, reduces the bandwidth W, and increases the electron-phonon coupling. Therefore, the TC shifts to a lower temperature and the resistivity increases with increasing Ti content. A field-induced shift of the resistivity maximum occurs at x less than or equal to 0.10. The maximum MR effect is about 70% for La0.7Sr0.3Mn0.8Ti0.2O3. The separation of TC and the resistivity maximum temperature Tmax enhances the MR effect in these compounds due to the weak coupling between the magnetic ordering and the resistivity as compared with La0.7Sr0.3MnO3.
△ Less
Submitted 9 February, 2005;
originally announced February 2005.
-
The effect of Cu-do** on the magnetic and transport properties of La0.7Sr0.3MnO3
Authors:
M. S. Kim,
J. B. Yang,
Q. Cai,
X. D. Zhou,
W. J. James,
W. B. Yelon,
P. E. Parris,
D. Buddhikot,
S. K. Malik
Abstract:
The effects of Cu-do** on the structural, magnetic, and transport properties of La0.7Sr0.3Mn1-xCuxO3 (0 < x < 0.20) have been studied using neutron diffraction, magnetization and magnetoresistance (MR) measurements. All samples show the rhombohedral structure with the R3c space-group from 10K to room temperature (RT). Neutron diffraction data suggest that some of the Cu ions have a Cu3+ state…
▽ More
The effects of Cu-do** on the structural, magnetic, and transport properties of La0.7Sr0.3Mn1-xCuxO3 (0 < x < 0.20) have been studied using neutron diffraction, magnetization and magnetoresistance (MR) measurements. All samples show the rhombohedral structure with the R3c space-group from 10K to room temperature (RT). Neutron diffraction data suggest that some of the Cu ions have a Cu3+ state in these compounds. The substitution of Mn by Cu affects the Mn-O bond length and Mn-O-Mn bond angle resulting from the minimization of the distortion of the MnO6 octahedron. Resistivity measurements show that a metal to insulator transition occurs for the x more than 0.15 samples. The x = 0.15 sample shows the highest MR(_80%), which might result from the co-existence of Cu3+/Cu2+ and the dilution effect of Cu-do** on the double exchange interaction.
△ Less
Submitted 9 February, 2005;
originally announced February 2005.
-
Structural and magnetic properties of MSr2Y1.5Ce0.5Cu2Oz (M-1222) compounds with M = Fe and Co
Authors:
V. P. S. Awana,
Anurag Gupta,
H. Kishan,
S. K. Malik,
W. B. Yelon,
J. Linden,
M. Karppinen,
H. Yamauchi
Abstract:
MSr2Y1.5Ce0.5Cu2Oz (M-1222) compounds, with M = Fe and Co, have been synthesized through a solid-state reaction route. Both compounds crystallize in a tetragonal structure (space group I4/mmm). A Rietveld structural refinement of room-temperature neutron diffraction data for Fe-1222 reveals that nearly half the Fe remains at the M site, while the other half goes to the Cu site in the CuO2 planes…
▽ More
MSr2Y1.5Ce0.5Cu2Oz (M-1222) compounds, with M = Fe and Co, have been synthesized through a solid-state reaction route. Both compounds crystallize in a tetragonal structure (space group I4/mmm). A Rietveld structural refinement of room-temperature neutron diffraction data for Fe-1222 reveals that nearly half the Fe remains at the M site, while the other half goes to the Cu site in the CuO2 planes. Existence of Fe at two different lattice sites, is also confirmed by 57Fe Mossbauer spectroscopy from which it is inferred that nearly 50% of the total Fe occupies the Cu site in the CuO2 planes as Fe3+, whereas the other 50 % is located at the M site with nearly 40 % as Fe4+ and around 10% as Fe3+. For the M = Co compound, nearly 84 % of Co remains at its designated M site, while the rest occupies the Cu site in the CuO2 planes. The oxygen content, z, based on oxygen occupancies refined from the neutron diffraction data, comes close to 9.0 for both the samples The ZFC and FC magnetization curves as a function of temperature show a complex behavior for both Fe-1222 and Co-1222 compounds.
△ Less
Submitted 14 October, 2003;
originally announced October 2003.
-
Superconductivity of up to 80 K for Tb-123 - TbSr2Cu2.7Mo0.3O7
Authors:
V. P. S. Awana,
H. Kishan,
E. Takayama-Muromachi,
T. Watanabe,
M. Karppinen,
H. Yamauchi,
S. K. Malik,
W. B. Yelon,
V. Ganesan,
A. V. Narlikar
Abstract:
The Tb-123 phase has been synthesized in single-phase form with the composition
TbSr2Cu2.7Mo0.3O7 by solid-state reaction route and its phase purity is confirmed by neutron powder diffraction experiments. As-synthesized sample does not show superconductivity down to 5 K. An unusually high antiferromagnetic ordering temperature (TN) of around 7 K is seen for Tb. After 120-atm-O2 post-annealing,…
▽ More
The Tb-123 phase has been synthesized in single-phase form with the composition
TbSr2Cu2.7Mo0.3O7 by solid-state reaction route and its phase purity is confirmed by neutron powder diffraction experiments. As-synthesized sample does not show superconductivity down to 5 K. An unusually high antiferromagnetic ordering temperature (TN) of around 7 K is seen for Tb. After 120-atm-O2 post-annealing, bulk superconductivity is achieved in the compound at around 30 K, without any significant effect on TN. To achieve higher oxygen content and higher Tc, the as-synthesized sample is subjected to high-pressure oxygenation (HPO) carried out in a closed cell at 5 GPa and 400 oC in the presence of AgO as an excess-oxygen source. This sample exhibited superconductivity onset at around 80 K with a Meissner fraction of larger than 10 % at 5 K. Our observation of superconductivity at 80 K is the highest Tc to-date among the Tb-123 compounds.
△ Less
Submitted 23 May, 2003;
originally announced May 2003.
-
Cation intermixing and ordering phenomenon in MO layer of MSr2YCu2Oz (M1212) compounds with M = Fe, Co, Al, and Ga: A neutron powder diffraction study
Authors:
V. P. S. Awana,
E. Takayama-Muromachi,
S. K. Malik,
W. B. Yelon,
M. Karppinen,
H. Yamauchi
Abstract:
Various MSr2YCu2Oz (M1212 with M = Fe, Co, Al and Ga) compounds have been synthesized through a solid state reaction route. All these compounds are derived from the basic CuBa2YCu2O7 structure. Rietveld structural refinement of the room-temperature neutron diffraction data for Fe-1212 reveals that nearly half of Fe remains at the M site, while the other half goes to the Cu site in the CuO2 plane…
▽ More
Various MSr2YCu2Oz (M1212 with M = Fe, Co, Al and Ga) compounds have been synthesized through a solid state reaction route. All these compounds are derived from the basic CuBa2YCu2O7 structure. Rietveld structural refinement of the room-temperature neutron diffraction data for Fe-1212 reveals that nearly half of Fe remains at the M site, while the other half goes to the Cu site in the CuO2 plane. For the M = Co, Al and Ga compounds, the basic unit cell gets doubled due to two distinct M sites in the M-O layer and the space group Ima2, without any cation intermixing is found more appropriate. For the M = Fe sample, magnetic ordering of Fe spins is seen from magnetization data below 70 K. In the case of the M = Co compound, a shallow down-turn in magnetic susceptibility is seen below 150 K, indicating low dimensional magnetic characteristics of the CoO layer. The compounds with M = Al and Ga show paramagnetic behaviour in their magnetization data down to 5 K. The oxygen content, established for each compound based on oxygen occupancies, refined from the neutron diffraction data comes close to 7.0 for each.
△ Less
Submitted 26 September, 2002;
originally announced September 2002.