Effects of Defects on the Strength of Nanotubes: Experimental-Computational Comparisons
Authors:
T. Belytschko,
S. P. Xiao,
R. Ruoff
Abstract:
The failure stresses and strains of nanotubes given by theoretical or numerical predictions are much higher than observed in experiments. We show that defects can explain part of this discrepancy: for an n-atom defect with 2<=n<=8, the range of failure stresses for a molecular mechanics calculation is found to be 36GPa to 64GPa. This compares quite well with upper end of the experimental failure…
▽ More
The failure stresses and strains of nanotubes given by theoretical or numerical predictions are much higher than observed in experiments. We show that defects can explain part of this discrepancy: for an n-atom defect with 2<=n<=8, the range of failure stresses for a molecular mechanics calculation is found to be 36GPa to 64GPa. This compares quite well with upper end of the experimental failure stresses, 11GPa to 63GPa. The computed failure strains are 4% to 8%, whereas the experimental values are 2% to 13%. The underprediction of failure strains can be explained by the slippage that occurred in the experiments. The failure processes of nanotubes are clearly brittle in both the experiments and our calculations.
△ Less
Submitted 30 May, 2002;
originally announced May 2002.
-
Atomistic Simulations of Nanotube Fracture
Authors:
T. Belytschko,
S. P. Xiao,
G. C. Schatz,
R. Ruoff
Abstract:
The fracture of carbon nanotubes is studied by atomistic simulations. The fracture behavior is found to be almost independent of the separation energy and to depend primarily on the inflection point in the interatomic potential. The rangle of fracture strians compares well with experimental results, but predicted range of fracture stresses is marketly higher than observed. Various plausible smal…
▽ More
The fracture of carbon nanotubes is studied by atomistic simulations. The fracture behavior is found to be almost independent of the separation energy and to depend primarily on the inflection point in the interatomic potential. The rangle of fracture strians compares well with experimental results, but predicted range of fracture stresses is marketly higher than observed. Various plausible small-scale defects do not suffice to bring the failure stresses into agreement with available experimental results. As in the experiments, the fracture of carbon nanotubes is predicted to be brittle. The results show moderate dependence of fracture strength on chirality.
△ Less
Submitted 27 March, 2002;
originally announced March 2002.