Real-Time Stress Measurements in Lithium-ion Battery Negative-electrodes
Authors:
Vijay A. Sethuraman,
Nathan Van Winkle,
Daniel P. Abraham,
Allan F. Bower,
Pradeep R. Guduru
Abstract:
Real-time stress evolution in a graphite-based lithium-ion battery negative-electrode during electrolyte wetting and electrochemical cycling is measured through wafer-curvature method. Upon electrolyte addition, the composite electrode rapidly develops compressive stress of the order of 1-2 MPa due to binder swelling; upon continued exposure, the stress continues to evolve towards an apparent plat…
▽ More
Real-time stress evolution in a graphite-based lithium-ion battery negative-electrode during electrolyte wetting and electrochemical cycling is measured through wafer-curvature method. Upon electrolyte addition, the composite electrode rapidly develops compressive stress of the order of 1-2 MPa due to binder swelling; upon continued exposure, the stress continues to evolve towards an apparent plateau. During electrochemical intercalation at a slow rate, the compressive stress increases with the electrode's state-of-charge, reaching a maximum value of 10 - 12 MPa. There appears to be an approximate correlation between the rate of stress rise and the staging behavior of the lithiated graphite. De-intercalation at a slow rate results in a similar linear decrease in electrode stress. Tensile stress of a few MPa develops at the end of deintercalation in the first few cycles, after which the electrode remains under compressive stress only. Although higher peak stresses are seen at high C-rates, the dependence appears to be relatively weak (up to 5C). These measurements reveal, for the first time, the nature of stress evolution in practical lithium-ion-battery electrodes and provide useful data to quantify the driving force for mechanical damage that accrues in composite electrodes upon repeated cycling. While the reported results can serve as reference for calibrating theoretical and computational models to predict electrode stress and damage evolution, the methodology demonstrated can be used to measure stresses and characterize fatigue damage in any composite lithium-ion-battery electrode as well as optimize its microstructure to mitigate stress-related damage mechanisms.
△ Less
Submitted 10 January, 2012;
originally announced January 2012.
In situ Measurement of Biaxial Modulus of Si Anode for Li-ion Batteries
Authors:
Vijay A. Sethuraman,
Michael J. Chon,
Maxwell Shimshak,
Nathan Van Winkle,
Pradeep R. Guduru
Abstract:
We report in situ measurement of biaxial moduli of a Si thin-film electrode as a function of its lithium concentration. During lithiation, biaxial compressive stress is induced in the Si film and it undergoes plastic flow. At any state-of-charge (SOC), a relatively small delithiation-relithiation sequence unloads and reloads the film elastically. From the stress and strain changes during a delithi…
▽ More
We report in situ measurement of biaxial moduli of a Si thin-film electrode as a function of its lithium concentration. During lithiation, biaxial compressive stress is induced in the Si film and it undergoes plastic flow. At any state-of-charge (SOC), a relatively small delithiation-relithiation sequence unloads and reloads the film elastically. From the stress and strain changes during a delithiation-relithiation cycle, the biaxial modulus of the film is calculated. Stress change is obtained by measuring the change in substrate curvature using a Multi-beam Optical Sensor; the elastic strain change is obtained from the change in SOC. By repeating these measurements at several different values of SOC, the biaxial modulus was seen to decrease from ca. 70 GPa for Li0.32Si to ca. 35 GPa for Li3.0Si. Such a significant reduction in elastic modulus has important implications for modeling stress evolution and mechanical degradation in Si-based anodes.
△ Less
Submitted 2 August, 2011;
originally announced August 2011.