Thermal Barrier Coatings in burner rig experiment analyzed through LAser Shock for DAmage Monitoring (LASDAM) method
Authors:
Lara Mahfouz,
Vincent Maurel,
Vincent Guipont,
Basile Marchand,
Rami El Hourany,
Florent Coudon,
Daniel E. Mack,
Robert Vaßen
Abstract:
This study investigates failure mechanisms in a typical thermal barrier coating (TBC) system comprising an EB-PVD columnar top coat, an aluminide bond coat, and a Ni-based single crystal superalloy substrate, simulating gas turbine operating conditions using a burner rig. TBC degradation, initiated by interfacial defects from the LASAT method, was studied during thermal gradient cycling under fast…
▽ More
This study investigates failure mechanisms in a typical thermal barrier coating (TBC) system comprising an EB-PVD columnar top coat, an aluminide bond coat, and a Ni-based single crystal superalloy substrate, simulating gas turbine operating conditions using a burner rig. TBC degradation, initiated by interfacial defects from the LASAT method, was studied during thermal gradient cycling under fast and slow cooling. In-situ optical and infrared imaging, along with ex-situ SEM cross-sectional analysis, monitored failure mechanisms. The Laser Shock for Damage Monitoring (LASDAM) technique provided insights into gradient and cooling rate impacts on columnar TBC damage. Results showed significant effects of cooling rate on delamination and localized failure at blister sites, with LASDAM revealing significant overheating at damage sites. Analysis included full-field temperature and damage assessment, emphasizing blister-driven delamination under severe thermal gradients. Discussion focused on elastic stored energy effects, noting that fast cooling induced transient conditions where reversed temperature gradients increased damage, limiting TBC lifespan
△ Less
Submitted 29 April, 2024; v1 submitted 9 April, 2024;
originally announced April 2024.
Mechanical Characterisation of the Protective Al$_2$O$_3$ Scale in Cr$_2$AlC MAX phases
Authors:
J. S. K. -L. Gibson,
J. Gonzalez-Julian,
S. Krishnan,
R. Vaßen,
S. Korte-Kerzel
Abstract:
MAX phases have great potential under demands of both high-temperature and high-stress performance, with their mixed atomic bonding producing the temperature and oxidation resistance of ceramics with the mechanical resilience of metals. Here, we measure the mechanical properties up to 980C by nanoindentation on highly dense and pure Cr$_2$AlC, as well as after oxidation with a burner rig at 1200C…
▽ More
MAX phases have great potential under demands of both high-temperature and high-stress performance, with their mixed atomic bonding producing the temperature and oxidation resistance of ceramics with the mechanical resilience of metals. Here, we measure the mechanical properties up to 980C by nanoindentation on highly dense and pure Cr$_2$AlC, as well as after oxidation with a burner rig at 1200C for more than 29 hours. Only modest reductions in both hardness and modulus up to 980C were observed, implying no change in deformation mechanism. Furthermore, micro-cantilever fracture tests were carried out at the Cr$_2$AlC/Cr$_7$C$_3$ and Cr$_7$C$_3$/Al$_2$O$_3$ interfaces after the oxidation of the Cr$_2$AlC substrates with said burner rig. The values are typical of ceramic-ceramic interfaces, below 4 MPa/m, leading to the hypothesis that the excellent macroscopic behaviour is due to a combination of low internal strain due to the match in thermal expansion coefficient as well as the convoluted interface.
△ Less