The structure of graphite oxide: Investigation of its surface chemical groups
Authors:
D. W. Lee,
L. De Los Santos V.,
J. W. Seo,
L. Leon Felix,
A. Bustamante D.,
J. M. Cole,
C. ~H. ~W. ~Barnes
Abstract:
The structure of graphite oxide (GO) has been systematically studied using various tools such as SEM, TEM, XRD, Fourier transform infrared spectroscopy (FT-IR), X-ray photoemission spectroscopy (XPS), 13C solid state NMR, and O K-edge X-ray absorption near edge structure (XANES). The TEM data reveal that GO consists of amorphous and crystalline phases. The XPS data show that some carbon atoms have…
▽ More
The structure of graphite oxide (GO) has been systematically studied using various tools such as SEM, TEM, XRD, Fourier transform infrared spectroscopy (FT-IR), X-ray photoemission spectroscopy (XPS), 13C solid state NMR, and O K-edge X-ray absorption near edge structure (XANES). The TEM data reveal that GO consists of amorphous and crystalline phases. The XPS data show that some carbon atoms have sp3 orbitals and others have sp2 orbitals. The ratio of sp2 to sp3 bonded carbon atoms decreases as sample preparation times increase. The 13C solid-state NMR spectra of GO indicate the existence of -OH and -O- groups for which peaks appear at 60 and 70 ppm, respectively. FT-IR results corroborate these findings. The existence of ketone groups is also implied by FT-IR, which is verified by O K-edge XANES and 13C solid-state NMR. We propose a new model for GO based on the results; -O-, -OH, and -C=O groups are on the surface.
△ Less
Submitted 5 August, 2010;
originally announced August 2010.
Transparent and flexible polymerized graphite oxide thin film with frequency-dependent dielectric constant
Authors:
D. W. Lee,
J. W. Seo,
G. R. Jelbert,
L. de Los Santos V.,
J. M. Cole,
C. Panagopoulos,
C. H. W. Barnes
Abstract:
Here we report on the preparation of transparent and flexible polymerized graphite oxide, which is composed of carbons with sp3-hybridized orbitals and a non-planar ring structure, and which demonstrates dispersion in its dielectric constant at room temperature. This frequency dependence renders the material suitable for creating miniaturized, flexible, and transparent variable capacitors, allowin…
▽ More
Here we report on the preparation of transparent and flexible polymerized graphite oxide, which is composed of carbons with sp3-hybridized orbitals and a non-planar ring structure, and which demonstrates dispersion in its dielectric constant at room temperature. This frequency dependence renders the material suitable for creating miniaturized, flexible, and transparent variable capacitors, allowing for smaller and simpler integrated electronic devices. We discuss this polarizability in terms of space charge effects.
△ Less
Submitted 30 May, 2010;
originally announced May 2010.