Large magnetoresistance in low temperature metallic region of manganite compounds (La0.7-2xEux)(Ca0.3Srx)MnO3 (0.05<x<0.15)
Authors:
D. S. Rana,
C. M. Thaker,
K. R. Mavani,
D. G. Kuberkar,
S. K. Malik
Abstract:
Magnetoresistance (MR) and magnetization (d.c and a.c) measurements have been carried out on the manganites, (La0.7-2xEux)(Ca0.3Srx)MnO3 (0.05<x<0.15), in the temperature range of 5K-320K. At 5K, an unusually large MR of almost 98% is observed in the x=0.15 sample, nearly up to fields of 4-5 Tesla. This large high-field MR occurs in the metallic region, far below the insulator-metal transition t…
▽ More
Magnetoresistance (MR) and magnetization (d.c and a.c) measurements have been carried out on the manganites, (La0.7-2xEux)(Ca0.3Srx)MnO3 (0.05<x<0.15), in the temperature range of 5K-320K. At 5K, an unusually large MR of almost 98% is observed in the x=0.15 sample, nearly up to fields of 4-5 Tesla. This large high-field MR occurs in the metallic region, far below the insulator-metal transition temperature, and does not vary linearly with applied field. The unusual magnetoresistance is explained the light of various possibilities of phase segregation and cluster spin-glass behavior. Keywords: Manganites, High field MR, Phase segregation.
△ Less
Submitted 16 December, 2004;
originally announced December 2004.
-
Structural and Magnetic Studies on La2-xDyxCa2xBa2Cu4+2xOz Type Superconducting Oxides
Authors:
S. Rayaprol,
Darshan C. Kundaliya,
C. M. Thaker,
D. G. Kuberkar,
Keka R. Chakraborty,
P. S. R. Krishna,
M. Ramanadham
Abstract:
The La-2125 type La2-xDyxCa2xBa2Cu4+2xOz (0.1 < x < 0.5; LDBO) compounds have been synthesized and studied for their structural and superconducting properties by room temperature neutron diffraction, high field dc magnetization, four-probe resistivity and iodometric double titration. The Rietveld analysis of the neutron diffraction data reveals tetragonal structure for all the samples, which cry…
▽ More
The La-2125 type La2-xDyxCa2xBa2Cu4+2xOz (0.1 < x < 0.5; LDBO) compounds have been synthesized and studied for their structural and superconducting properties by room temperature neutron diffraction, high field dc magnetization, four-probe resistivity and iodometric double titration. The Rietveld analysis of the neutron diffraction data reveals tetragonal structure for all the samples, which crystallizes into La-123 type tetragonal structure in P4/mmm space group. Iodometric double titrations were performed to determine the oxygen content values and calculate mobile charge carrier (holes) density. The superconducting transition temperatures (Tc) increases from ~ 20 K for x = 0.1 to a maximum of 75 K for x = 0.5. Flux pinning force (Fp) and critical current density (Jc), calculated from the low temperature hysteresis loops, also increases with increasing dopant concentration. The paper presents the studies on structure and superconducting properties of all LDBO compounds in light of the role of calcium in inducing superconductivity in the tetragonal non-superconducting oxide.
△ Less
Submitted 14 August, 2004;
originally announced August 2004.
-
Critical current density and flux pinning in La2-xPrxCa2xBa2Cu4+2xOz (x = 0.1 - 0.5) superconductors
Authors:
S. Rayaprol,
C. M. Thaker,
N. A. Shah,
D. G. Kuberkar
Abstract:
Polycrystalline La2-xPrxCa2xBa2Cu4+2xOz (LPCaBCO) compounds with x = 0.1 - 0.5 were synthesized by solid-state reaction method and studied by room temperature X-ray diffraction, dc resistivity, dc magnetization and iodometry. The superconducting transition temperatures in these tetragonal triple perovskite compounds increases from 32 to 62 K (Tconset values) with increasing dopant concentration.…
▽ More
Polycrystalline La2-xPrxCa2xBa2Cu4+2xOz (LPCaBCO) compounds with x = 0.1 - 0.5 were synthesized by solid-state reaction method and studied by room temperature X-ray diffraction, dc resistivity, dc magnetization and iodometry. The superconducting transition temperatures in these tetragonal triple perovskite compounds increases from 32 to 62 K (Tconset values) with increasing dopant concentration. The mixing of rare earth La3+ and Pr3+/4+ ions at rare earth site (La3+) along with substitution of divalent Ca2+ results in the shrinkage of unit cell volume. The contraction of unit cell volume due to larger ion being substituted by smaller ions, gives rise to creation of pinning centers in the unit cell leading to increase in critical current density and flux pinning
△ Less
Submitted 21 May, 2004;
originally announced May 2004.
-
Studies on La2-xPrxCayBa2Cu4+yOz (0.1 < x < 0.5) type mixed oxide superconductors
Authors:
S Rayaprol,
K R Mavani,
D S Rana,
C M Thaker,
Manglesh Dixit,
Shovit Bhattacharya,
D G Kuberkar
Abstract:
The La2-xPrxCayBa2Cu4+yOz (LaPrCaBCO) mixed oxides have been studied for their structural and superconducting properties using X-ray diffraction (XRD), d. c. resistivity, d. c. susceptibility and iodometric double titration. All the LaPrCaBCO samples for x = 0.1 - 0.5, exhibit tetragonal crystalline structure with P 4/mmm space group as determined by Rietveld analysis of the X-ray diffraction da…
▽ More
The La2-xPrxCayBa2Cu4+yOz (LaPrCaBCO) mixed oxides have been studied for their structural and superconducting properties using X-ray diffraction (XRD), d. c. resistivity, d. c. susceptibility and iodometric double titration. All the LaPrCaBCO samples for x = 0.1 - 0.5, exhibit tetragonal crystalline structure with P 4/mmm space group as determined by Rietveld analysis of the X-ray diffraction data. With increasing x, enhancement in Tc is observed, which is quite interesting for Pr substituted high Tc oxides. Maximum Tc ~ 58 K has been observed for x = 0.5(La-2125 stoichiometry). The results of structural studies and superconducting property measurements are presented in light of increase in Tc in LaPrCaBCO system with increasing Pr concentration.
△ Less
Submitted 24 May, 2003;
originally announced May 2003.
-
Effect of Mo-Substitution on Superconductivity, Flux Pinning and Critical Currents of la(1.5)Nd(0.5)Ca(1)Ba(2)Cu(5)O(z0
Authors:
S. Rayaprol,
Krushna Mavani,
C. M. Thaker,
D. S. Rana,
R. G. Kulkarni,
D. G. Kuberkar,
Darshan Kundaliya,
S. K. Malik
Abstract:
Mo-substituted triple perovskite superconducting samples with the stoichiometric composition La(1.5)Nd(0.5)Ca(1)Ba(2)[Cu(1-x)Mo(x)](5)O(z), [LNCBCuMO] with x = 0.00, 0.01, 0.03, 0.05 and 0.10, have been investigated using X-ray diffraction, electrical resistivity, magnetic susceptibility, magnetization and oxygen content measurements. The observed reduction in Tc with increasing Mo content (x) i…
▽ More
Mo-substituted triple perovskite superconducting samples with the stoichiometric composition La(1.5)Nd(0.5)Ca(1)Ba(2)[Cu(1-x)Mo(x)](5)O(z), [LNCBCuMO] with x = 0.00, 0.01, 0.03, 0.05 and 0.10, have been investigated using X-ray diffraction, electrical resistivity, magnetic susceptibility, magnetization and oxygen content measurements. The observed reduction in Tc with increasing Mo content (x) in LNCBCuMO, can be attributed to the decrease in hole concentration. Magnetization measurements as a function of temperature and field (H), exhibit an M-H hysteresis loop, which indicates moderate flux pinning, which can be attributed to the pinning centers created by Mo substitution at Cu sites. The critical current density, Jc, deduced from the M-H data satisfies the flux creep model.
△ Less
Submitted 26 April, 2003;
originally announced April 2003.