On the Issue of Textured Crystallization of Ba(NO$_3$)$_2$ in Mesoporous SiO$_2$: Raman Spectroscopy and Lattice Dynamics Analysis
Authors:
Yaroslav Shchur,
Guillermo Beltramo,
Anatolii S. Andrushchak,
Svetlana Vitusevich,
Patrick Huber,
Volodymyr Adamiv,
Ihor Teslyuk,
Nazarii Boichuk,
Andriy V. Kityk
Abstract:
The lattice dynamics of preferentially aligned nanocrystals formed upon drying of aqueous Ba(NO$_3$)$_2$ solutions in a mesoporous silica glass traversed by tubular pores of approximately 12 nm are explored by Raman scattering. To interpret the experiments on the confined nanocrystals polarized Raman spectra of bulk single crystals and X-ray diffraction experiments are also performed. Since a cubi…
▽ More
The lattice dynamics of preferentially aligned nanocrystals formed upon drying of aqueous Ba(NO$_3$)$_2$ solutions in a mesoporous silica glass traversed by tubular pores of approximately 12 nm are explored by Raman scattering. To interpret the experiments on the confined nanocrystals polarized Raman spectra of bulk single crystals and X-ray diffraction experiments are also performed. Since a cubic symmetry is inherent to Ba(NO$_3$)$_2$, a special Raman scattering geometry was utilized to separate the phonon modes of A$_g$ and E$_g$ species. Combining group-theory analysis and \textit{ab initio} lattice dynamics calculations a full interpretation of all Raman lines of the bulk single crystal is achieved. Apart from a small confinement-induced line broadening, the peak positions and normalized peak intensities of the Raman spectra of the nanoconfined and macroscopic crystals are identical. Interestingly, the Raman scattering experiment indicates the existence of comparatively large, $\sim$10-20 $μ$m, single-crystalline regions of Ba(NO$_3$)$_2$ embedded in the porous host, near three orders of magnitude larger than the average size of single nanopores. This is contrast to the initial assumption of non-interconnected pores. It rather indicates an inter-pore propagation of the crystallization front, presumably via microporosity in the pore walls.
△ Less
Submitted 3 May, 2022;
originally announced May 2022.
Optical Birefringence and Domain Structure of the as-grown Rb2xTl2(1-x)Cd2(SO4)3 Solid Solutions at Phase Transitions
Authors:
A. Say,
S. Sveleba,
I. Teslyuk,
I. Martynyuk-Lototska,
I. Girnyk,
R. Vlokh
Abstract:
It is shown that the as-grown solid solutions Tl2xRb2(1-x)Cd2(SO4)3 possess a residual optical birefringence in the cubic phase at room temperature. The existence of both the residual birefringence and the residual domain structure in the compound with x=0.8 at the room temperature, along with the domain walls orientation and the orientation of extinction positions of the neighbouring domains, i…
▽ More
It is shown that the as-grown solid solutions Tl2xRb2(1-x)Cd2(SO4)3 possess a residual optical birefringence in the cubic phase at room temperature. The existence of both the residual birefringence and the residual domain structure in the compound with x=0.8 at the room temperature, along with the domain walls orientation and the orientation of extinction positions of the neighbouring domains, indicate that the above domain structure corresponds to "forbidden" ferroelastic domains of the phase P212121. On the basis of measurements for the temperature variation of the birefringence and observations of the domain structure transformations, one can conclude that the phases with the symmetries P213 and P21 coexist above Tc1 in the compounds with x = 0.7 - 1.0. The phase transition temperatures Tc1, Tc2, and Tc3 obtained from the temperature birefringence variations agree well with those obtained previously, using the studies of thermal expansion and ultrasonic wave velocities.
△ Less