Plasticity of the Nb-rich μ-Co7Nb6 phase at room temperature and 600 °C
Authors:
W. Luo,
Z. Xie,
P. -L. Sun,
J. S. K. -L. Gibson,
S. Korte-Kerzel
Abstract:
The μ-phase is a common precipitation phase in superalloys and it exists in a wide composition and temperature range. As such, we study the influences of composition and temperature on its plasticity by micropillar compression tests and transmission electron microscopy. The micropillars of the μ-Co7Nb6 phase deform plastically by basal slip at either room temperature or 600 oC. At room temperature…
▽ More
The μ-phase is a common precipitation phase in superalloys and it exists in a wide composition and temperature range. As such, we study the influences of composition and temperature on its plasticity by micropillar compression tests and transmission electron microscopy. The micropillars of the μ-Co7Nb6 phase deform plastically by basal slip at either room temperature or 600 oC. At room temperature, the Co-49Nb and Co-52Nb micropillars show high yield stresses and an abrupt large strain burst at the onset of yielding regardless of orientation, whereas the Co-54Nb micropillars oriented for basal slip yield at much lower stresses and show intermittent small strain bursts during plastic deformation. While the Co-49Nb micropillars deform by full dislocation slip on the basal plane at room temperature, the Co-54Nb micropillars deform by partial dislocation slip on the basal plane. At 600 oC, the Co-49Nb micropillars oriented for basal slip show stable and continuous plasticity and their critical resolved shear stress decreases dramatically. The plastic deformation of the Co-49Nb micropillars occurs via partial dislocation slip on the basal plane at 600 oC. Based on the geometric γ-surfaces for all potential basal slip planes, we explore where and why the glide of full and partial dislocations on the basal plane occurs in the μ-Co7Nb6 phase.
△ Less
Submitted 31 January, 2023; v1 submitted 23 January, 2023;
originally announced January 2023.
-
Plasticity of the Al$_{2}$Cu θ-phase from ambient temperature to 300°C
Authors:
D. Andre,
J. S. K. -L. Gibson,
P. -L. Sun,
N. Lohrey,
S. Sandlöbes-Haut,
S. Korte-Kerzel
Abstract:
The investigation of the deformation behaviour of intermetallic phases is mostly limited to high temperatures due to their low ductility at ambient temperature. Therefore, within this study, nanoindentation experiments on the Al$_{2}$Cu phase were performed from ambient temperature up to 300°C in conjunction with TEM investigations of the deformed material. It was found that the Al$_{2}$Cu phase s…
▽ More
The investigation of the deformation behaviour of intermetallic phases is mostly limited to high temperatures due to their low ductility at ambient temperature. Therefore, within this study, nanoindentation experiments on the Al$_{2}$Cu phase were performed from ambient temperature up to 300°C in conjunction with TEM investigations of the deformed material. It was found that the Al$_{2}$Cu phase starts to soften from temperatures above 150°C. The low temperature deformation behaviour was dominated by serrated yielding and transitioned towards a smooth deformation behaviour above 150°C. No slip traces were observed in the vicinity of the indents in both temperature regimes. The predominant dislocations observed after ambient temperature deformation and elevated temperature deformation are assumed to belong to the same operating slip systems. Therefore, the underlying deformation mechanism for both temperatures appears to be the same and thermally activated.
△ Less
Submitted 13 December, 2021;
originally announced December 2021.