White Paper on Leading-Edge technology And Feasibility-directed (LEAF) Program aimed at readiness demonstration for Energy Frontier Circular Colliders by the next decade
Authors:
G. Ambrosio,
G. Apollinari,
M. Baldini,
R. Carcagno,
C. Boffo,
B. Claypool,
S. Feher,
S. Hays,
D. Hoang,
V. Kashikhin,
V. V. Kashikhin,
S. Krave,
M. Kufer,
J. Lee,
V. Lombardo,
V. Marinozzi,
F. Nobrega,
X. Peng,
H. Piekarz,
V. Shiltsev,
S. Stoynev,
T. Strauss,
N. Tran,
G. Velev,
X. Xu
, et al. (17 additional authors not shown)
Abstract:
In this White Paper for the Snowmass 2021 Process, we propose the establishment of a magnet Leading-Edge technology And Feasibility-directed Program (LEAF Program) to achieve readiness for a future collider decision on the timescale of the next decade.
The LEAF Program would rely on, and be synergetic with, generic R&D efforts presently covered - in the US - by the Magnet Development Program (MD…
▽ More
In this White Paper for the Snowmass 2021 Process, we propose the establishment of a magnet Leading-Edge technology And Feasibility-directed Program (LEAF Program) to achieve readiness for a future collider decision on the timescale of the next decade.
The LEAF Program would rely on, and be synergetic with, generic R&D efforts presently covered - in the US - by the Magnet Development Program (MDP), the Conductor Procurement and R&D (CPRD) Program and other activities in the Office of HEP supported by Early Career Awards (ECA) or Lab Directed R&D (LDRD) funds. Where possible, ties to synergetic efforts in other Offices of DOE or NSF are highlighted and suggested as wider Collaborative efforts on the National scale. International efforts are also mentioned as potential partners in the LEAF Program.
We envision the LEAF Program to concentrate on demonstrating the feasibility of magnets for muon colliders as well as next generation high energy hadron colliders, pursuing, where necessary and warranted by the nature of the application, the transition from R&D models to long models/prototypes. The LEAF Program will naturally drive accelerator-quality and experiment-interface design considerations. LEAF will also concentrate, where necessary, on cost reduction and/or industrialization steps.
△ Less
Submitted 15 March, 2022;
originally announced March 2022.
-
A model for the compositions of non-stoichiometric intermediate phases formed by diffusion reactions, and its application to Nb3Sn superconductors
Authors:
Xingchen Xu,
Mike D. Sumption
Abstract:
In this work we explore the compositions of non-stoichiometric intermediate phases formed by diffusion reactions: a mathematical framework is developed and tested against the specific case of Nb3Sn superconductors. In the first part, the governing equations for the bulk diffusion and inter-phase interface reactions during the growth of a compound are derived, numerical solutions to which give both…
▽ More
In this work we explore the compositions of non-stoichiometric intermediate phases formed by diffusion reactions: a mathematical framework is developed and tested against the specific case of Nb3Sn superconductors. In the first part, the governing equations for the bulk diffusion and inter-phase interface reactions during the growth of a compound are derived, numerical solutions to which give both the composition profile and growth rate of the compound layer. The analytic solutions are obtained with certain approximations made. In the second part, we explain an effect that the composition characteristics of compounds can be quite different depending on whether it is the bulk diffusion or grain boundary diffusion that dominates in the compounds, and that frozen bulk diffusion leads to unique composition characteristics quite distinct from equilibrium expectations; then the model is modified for the case of grain boundary diffusion. Finally, we apply this model to the Nb3Sn superconductors and propose the approaches to control their compositions.
△ Less
Submitted 16 November, 2015;
originally announced November 2015.
-
Effect of Chemical Pressure on High Temperature Ferrimagnetic Double Perovskites Sr2CrOsO6 and Ca2CrOsO6
Authors:
Ryan Morrow,
Jennifer R. Soliz,
Adam J. Hauser,
James C. Gallagher,
Michael A. Susner,
Michael D. Sumption,
Adam A. Aczel,
Jiaqiang Yan,
Fengyuan Yang,
Patrick M. Woodward
Abstract:
The ordered double perovskites Sr2CrOsO6 and Ca2CrOsO6 have been synthesized and characterized with neutron powder diffraction, electrical transport measurements, and high field magnetization experiments. Sr2CrOsO6 and Ca2CrOsO6 crystallize with R-3 and P21/n space group symmetry, respectively. Both materials are found to be ferrimagnetic insulators with saturation magnetizations near 0.2 μB. Sr2C…
▽ More
The ordered double perovskites Sr2CrOsO6 and Ca2CrOsO6 have been synthesized and characterized with neutron powder diffraction, electrical transport measurements, and high field magnetization experiments. Sr2CrOsO6 and Ca2CrOsO6 crystallize with R-3 and P21/n space group symmetry, respectively. Both materials are found to be ferrimagnetic insulators with saturation magnetizations near 0.2 μB. Sr2CrOsO6 orders at 660 K, showing non-monotonic magnetization temperature dependence, while Ca2CrOsO6 orders at 490 K and does not show non-monotonic behavior. Evidence for a theoretically predicted canted magnetic structure in Sr2CrOsO6 is sought and not found.
△ Less
Submitted 2 September, 2015;
originally announced September 2015.
-
Magnetic Structure of the Quasi-One-Dimensional La3OsO7 as Determined by Neutron Powder Diffraction
Authors:
Ryan Morrow,
Michael A. Susner,
Michael D. Sumption,
Patrick M. Woodward
Abstract:
Insulating 5d3 La3OsO7 and hole doped La2.8Ca0.2OsO7 materials featuring well separated pseudo-one-dimensional zig-zag chains of corner-sharing OsO6 octahedra have been synthesized and their magnetic and electrical transport properties characterized. Long range magnetic order between the antiferromagnetic chains is determined with a propagation vector k = 1/2, 1/2, 0 and TN = 45 and 53 K for the p…
▽ More
Insulating 5d3 La3OsO7 and hole doped La2.8Ca0.2OsO7 materials featuring well separated pseudo-one-dimensional zig-zag chains of corner-sharing OsO6 octahedra have been synthesized and their magnetic and electrical transport properties characterized. Long range magnetic order between the antiferromagnetic chains is determined with a propagation vector k = 1/2, 1/2, 0 and TN = 45 and 53 K for the parent and doped materials. An Os5+ moment of 1.7(1) μB for La3OsO7 and 1.2(2) μB for La2.8Ca0.2OsO7 is refined. The long range magnetic structure is compared to the few currently known for isostructural Ln3MO7 compounds.
△ Less
Submitted 11 June, 2015; v1 submitted 5 June, 2015;
originally announced June 2015.
-
Internally Oxidized Nb3Sn Strands with Fine Grain Size and High Critical Current Density
Authors:
Xingchen Xu,
Michael D. Sumption,
Xuan Peng
Abstract:
Nb3Sn superconducting strands are the most practical conductors to generate high magnetic fields (12-16 T), and thus have significant applications in nuclear magnetic resonance (NMR), and great potential for fusion reactors and particle accelerator magnets. High critical current density (Jc) is a key parameter for such applications. Significant efforts towards optimization of various factors led t…
▽ More
Nb3Sn superconducting strands are the most practical conductors to generate high magnetic fields (12-16 T), and thus have significant applications in nuclear magnetic resonance (NMR), and great potential for fusion reactors and particle accelerator magnets. High critical current density (Jc) is a key parameter for such applications. Significant efforts towards optimization of various factors led to an 80% improvement in Jc from the early 1990s to 2003, when the 4.2 K, 12 T non-matrix Jc reached 3000 A/mm2 (corresponding to 5000 A/mm2 in Nb3Sn layer Jc). However, further efforts over the past decade have failed to bring about further increase beyond this level, leading some researchers to conclude that the Jc of conventional Nb3Sn strands had reached its maximum. Here, however, by applying an internal oxidation method, we reduce the grain size by a factor of three and nearly double the 12 T Jc. In this method, a Nb3Sn strand is fabricated with Nb-Zr alloy as starting material; with oxygen supplied properly via an oxide powder, the Zr atoms in the Nb-Zr alloy are internally oxidized, forming fine intra-granular and inter-granular ZrO2 particles in Nb3Sn layer, which effectively refine Nb3Sn grain size. At a reaction temperature of 625 °C, grain size down to 20-50 nm (36 nm on average) has been achieved. For this sample the 4.2 K, 12 T Nb3Sn layer Jc reached 9600 A/mm2.
△ Less
Submitted 19 November, 2014;
originally announced November 2014.
-
Enhanced higher temperature (20-30 K) transport properties and irreversibility field in nano-Dy2O3 doped advanced internal Mg infiltration processed MgB2 composites
Authors:
G. Z. Li,
M. D. Sumption,
M. A. Rindfleisch,
C. J. Thong,
M. J. Tomsic,
E. W. Collings
Abstract:
A series of MgB2 superconducting composite strands co-doped with Dy2O3 and C were prepared via an advanced internal Mg infiltration (AIMI) route.The transport properties and MgB2 layer growth were studied in terms of the Dy2O3 do** level, reaction temperature, and reaction time. Transport studies showed that both critical current densities, Jcs, and irreversibility fields, Birrs, were increased…
▽ More
A series of MgB2 superconducting composite strands co-doped with Dy2O3 and C were prepared via an advanced internal Mg infiltration (AIMI) route.The transport properties and MgB2 layer growth were studied in terms of the Dy2O3 do** level, reaction temperature, and reaction time. Transport studies showed that both critical current densities, Jcs, and irreversibility fields, Birrs, were increased with Dy2O3 do**. The highest layer Jc was 1.35 x 10^5 A/cm2 at 4.2 K, 10 T, 30% higher than that of the best AIMI wires without Dy2O3 do**. The highest "non-barrier" Jc reached 3.6 x 10^4 A/cm2 at 4.2 K, 10 T, which was among the best results reported so far. The improvements were even more pronounced at higher temperatures where the field at which the layer Jc reached 10^4 A/cm2 was pushed out by 0.9 T at 20 K, 1.2 T at 25 K, and 1.4 T at 30 K. While little or no enhancement in Birr was seen at 10 K and 15 K, the increases in Jc at higher temperatures were consistent with observed increases in Birr of 17% at 20 K, 44% at 25 K, and 400% at 30 K. Also, there were some indications that the reaction and layer growth of MgB2 was enhanced by Dy2O3 do**.
△ Less
Submitted 22 September, 2014;
originally announced September 2014.
-
Effects of carbon concentration and filament number on advanced internal-Mg-infiltration-processed MgB2 Strands
Authors:
G Z Li,
M D Sumption,
J B Zwayer,
M A Susner,
M A Rindfleisch,
C J Thong,
M J Tomsic,
E W Collings
Abstract:
An advanced internal Mg infiltration method (AIMI) in this paper has been shown to be effective in producing superconducting wires containing dense MgB2 layers with high critical current densities. In this study, the in-field critical current densities of a series of AIMI-fabricated MgB2 strands were investigated in terms of C do** levels, heat treatment (HT) time and filament numbers. The highe…
▽ More
An advanced internal Mg infiltration method (AIMI) in this paper has been shown to be effective in producing superconducting wires containing dense MgB2 layers with high critical current densities. In this study, the in-field critical current densities of a series of AIMI-fabricated MgB2 strands were investigated in terms of C do** levels, heat treatment (HT) time and filament numbers. The highest layer Jc for our monofilamentary AIMI strands is 1.5 x 10^5 A/cm2 at 10 T, 4.2 K, when the C concentration was 3 mol% and the strand was heat-treated at 675 °C for 4 hours. Transport critical currents were also measured at 4.2 K on short samples and one-meter segments of eighteen-filament C-doped AIMI strands. The layer Jcs reached 4.3 x 10^5 A/cm2 at 5 T and 7.1 x 10^4 A/cm2 at 10 T, twice as high as those of the best PIT strands. The analysis of these results indicates that the AIMI strands, possessing both high layer Jcs and engineering Jes after further optimization, have strong potential for commercial applications.
△ Less
Submitted 3 July, 2013;
originally announced July 2013.
-
Critical current densities and microstructures in Rod-in-Tube and Tube Type Nb3Sn strands - Present status and prospects for improvement
Authors:
X Xu,
M D Sumption,
S Bhartiya,
X Peng,
E W Collings
Abstract:
In this work, the transport and magnetization properties of distributed-barrier Rod-in-Tube (RIT) strands and Tube Type strands are studied. While Tube Type strands had smaller magnetizations and thus better stabilities in the low field region, their 12 T non-Cu Jcs were somewhat smaller than those of the RIT strands. Microstructures were investigated in order to find out the reasons for the diffe…
▽ More
In this work, the transport and magnetization properties of distributed-barrier Rod-in-Tube (RIT) strands and Tube Type strands are studied. While Tube Type strands had smaller magnetizations and thus better stabilities in the low field region, their 12 T non-Cu Jcs were somewhat smaller than those of the RIT strands. Microstructures were investigated in order to find out the reasons for the difference in non-Cu Jc values. Their grain size and stoichiometry were found to be comparable, leading to similar layer Jcs. Accordingly it was determined that the lower A15 area fraction rather than the quality of A15 layer was the cause of the discrepancy in non-Cu Jc. Subsequently, the area utilizations of subelements were investigated. While for a RIT strand the fine grain (FG) A15 area occupies ~60% of a subelement, for a Tube Type strand it is no more than 40%. Further analysis indicates that the low FG area fraction in a Tube Type strand is attributed to its much larger unreacted Nb area fraction. Finally, a simple change in strand architecture is proposed to reduce the unreacted Nb area fraction.
△ Less
Submitted 22 April, 2013;
originally announced April 2013.
-
The critical current density of advanced internal-Mg-diffusion-processed MgB2 wires
Authors:
G. Z. Li,
M. D. Sumption,
M. A. Susner,
Y. Yang,
K. M. Reddy,
M. A. Rindfleisch,
M. J. Tomsic,
C. J. Thong,
E. W. Collings
Abstract:
Recent advances in MgB2 conductors are leading to a new level of performance. Based on the use of proper powders, proper chemistry, and an architecture which incorporates internal Mg diffusion (IMD), a dense MgB2 structure with not only a high critical current density Jc, but also a high engineering critical current density, Je, can be obtained. In this paper, a series of these advanced (or second…
▽ More
Recent advances in MgB2 conductors are leading to a new level of performance. Based on the use of proper powders, proper chemistry, and an architecture which incorporates internal Mg diffusion (IMD), a dense MgB2 structure with not only a high critical current density Jc, but also a high engineering critical current density, Je, can be obtained. In this paper, a series of these advanced (or second - generation, "2G") conductors has been prepared. Scanning electron microscopy and associated energy dispersive X-ray spectroscopy were applied to characterize the microstructures and compositions of the wires, and a dense MgB2 layer structure was observed. The best layer Jc for our sample is 1.07x105 A/cm2 at 10 T, 4.2 K, and our best Je is seen to be 1.67x104 A/cm2 at 10 T, 4.2 K. Optimization of the transport properties of these advanced wires is discussed in terms of B-powder choice, area fraction, and the MgB2 layer growth mechanism.
△ Less
Submitted 10 October, 2012; v1 submitted 15 June, 2012;
originally announced June 2012.
-
Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in-situ processed MgB2 strands
Authors:
M. A. Susner,
T. W. Daniels,
M. D. Sumption,
E. W. Collings
Abstract:
Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macros…
▽ More
Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macrostructure and grain size. Grain size increased with HT time at both 600C and 700C. Jc and hence Fp decreased monotonically but not linearly with grain size. Overall, it was observed that at 700C, the MgB2 reaction was more or less complete after as little as 30 min; at 600C, full reaction completion did not occur until 71 h. into the HT. Transport, Jct(B) was measured in a perpendicular applied field, and the magnetic critical current densities, Jcm\bot(B) and Jcmφ(B), were measured in perpendicular and parallel (axial) applied fields, respectively. Particularly noticeable was the premature dropoff of Jcm\bot(B) at fields well below the irreversibility field of Jct(B). This effect is attributed to the fibrous macrostructure and its accompanying anisotropic connectivity. Magnetic measurements with the field directed along the strand axis yielded a critical density, Jcm\bot(B), for current flowing transversely to the strand axis that was less than and dropped off more rapidly than Jct(B). In the conventional magnetic measurement, the loop currents that support the magnetization are restricted by the lower of Jct(B) and Jcmφ (B). In the present case the latter, leading to the premature dropoff of the measured Jcm(B) compared to Jct(B) with increasing field. This result is supported by Kramer plots of the Jcmφ (B) and Jct(B) data which lead to an irreversibility field for transverse current that is very much less than the usual transport-measured longitudinal one, Birr,t.
△ Less
Submitted 21 September, 2011;
originally announced September 2011.
-
Influence of Strand Design, Boron Type, and Carbon Do** Method on the Transport Properties of Powder-in-Tube MgB2-XCX Strands
Authors:
Y. Yang,
M. Susner,
M. D. Sumption,
M. Rindfleisch,
M. Tomsic,
E. W. Collings
Abstract:
The transport properties of a number of MgB2 strands have been investigated in terms of their response to strand design, starting B powder choice, and the approach to C do** used. The strands had various designs, specifically; (i) several chemical barriers were introduced, viz: Fe and Nb, (ii) the strands were encased in various outer-sheath materials, viz.: monel, Cu+monel, monel+glidcop, Nb+mo…
▽ More
The transport properties of a number of MgB2 strands have been investigated in terms of their response to strand design, starting B powder choice, and the approach to C do** used. The strands had various designs, specifically; (i) several chemical barriers were introduced, viz: Fe and Nb, (ii) the strands were encased in various outer-sheath materials, viz.: monel, Cu+monel, monel+glidcop, Nb+monel, (iii) the filament counts were varied (1, 18, and 36), and (iv) the final strand diameter was varied. In addition, for a subset of the strand designs several B powder and C-dopant types were investigated. Specifically, two types of amorphous B powder were used: (i) Moissan based "Tangshan boron" (ii) "SMI-boron" which is produced in a plasma torch by the reduction-by-hydrogen of BCl3. Two approaches to C do** were taken: (i) "malic-acid treatment" in which C is introduced into the B powder precursor by the moderate temperature drying out a slurry of B mixed in with a malic-acid-toluene solution (during which the malic acid decomposes leaving C as the only solid residue) before the Mg powder is mixed in; (ii) direct C do** of the SMI-produced B by introducing a known percentage of CH4 into the plasma flame. Critical current densities, Jc, were measured on 1.5 m long samples at 4.2 K in fields of up to 14 T; of all the strands measured, that doped with SMI-C at a nominal 4 mol% C (in relation B) yielded the highest Jc values e.g 1.1x105 A/cm2 at 7 T, 4.5x104 at 10 T, and 2.2x104 A/cm2 at 12 T. The n-values are given for all strands at 5 and 10 T, and for a certain set of strands the magnetic field dependencies of the n-values and the influence of C-do** is presented. Finally we demonstrate that, over a wide range of B, log(Jc) decreases linearly with B with a slope -α such that the Jc(B) of any strand can be parameterized in terms of α and its zero-field intercept Jc(B=0).
△ Less
Submitted 20 September, 2011;
originally announced September 2011.
-
Critical Current Density and n-values of MgB2 Strands over a Wide Range of Temperatures and Fields
Authors:
G Z Li,
Y Yang,
M A Susner,
M D Sumption,
E W Collings
Abstract:
Transport measurements of critical current density, Jct, in monocore powder-in-tube MgB2 strands have been carried out at temperatures, T, of from 4.2 K to 40 K, and in transverse fields, B, of up to 14 T. Processing methods used were conventional continuous-tube-forming-filling (CTFF) and internal-magnesium-diffusion (IMD). Strands with several powder compositions were measured, including binary…
▽ More
Transport measurements of critical current density, Jct, in monocore powder-in-tube MgB2 strands have been carried out at temperatures, T, of from 4.2 K to 40 K, and in transverse fields, B, of up to 14 T. Processing methods used were conventional continuous-tube-forming-filling (CTFF) and internal-magnesium-diffusion (IMD). Strands with several powder compositions were measured, including binary (undoped) MgB2, 2% carbon doped MgB2, and 3% carbon doped MgB2. Magnetization loops (M-B) were also measured, and magnetic critical current density, Jcm, values extracted from them. The transport, Jct(B) and magnetic, Jcm(B), critical current densities were compared. Also studied was the influence of do** on the resistively measured irreversibility field, Birr and upper critical field Bc2. Critical current densities, Jct, and n-values were extracted from transport measurements and were found to be universally related (for all B and T) according to n \propto Jctm in which m = 0.52 \pm 0.11. Likewise n was found to be related to B according to n \propto B-p with a T-dependent p in the range of about 0.08~0.21. Further analysis of the field (B) and temperature (T) dependencies of n-value resulted in an expression that enabled n(B,T), for all B and T, to be estimated for a given strand based on the results of transport Jct(B) measurements made at one arbitrarily chosen temperature.
△ Less
Submitted 24 November, 2011; v1 submitted 29 August, 2011;
originally announced August 2011.
-
Do** Effect and Flux Pinning Mechanism of Nano-SiC Additions in MgB2 Strands
Authors:
Z. X. Shi,
M. A. Susner,
M. D. Sumption,
E. W. Collings
Abstract:
Superconducting MgB2 strands with nanometer-scale SiC additions have been investigated systematically using transport and magnetic measurements. A comparative study of MgB2 strands with different nano-SiC addition levels has shown C-do**-enhanced critical current density Jc through enhancements in the upper critical field, Hc2, and decreased anisotropy. The critical current density and flux pinn…
▽ More
Superconducting MgB2 strands with nanometer-scale SiC additions have been investigated systematically using transport and magnetic measurements. A comparative study of MgB2 strands with different nano-SiC addition levels has shown C-do**-enhanced critical current density Jc through enhancements in the upper critical field, Hc2, and decreased anisotropy. The critical current density and flux pinning force density obtained from magnetic measurements were found to greatly differ from the values obtained through transport measurements, particularly with regards to magnetic field dependence. The differences in magnetic and transport results are largely attributed to connectivity related effects. On the other hand, based on the scaling behavior of flux pinning force, there may be other effective pinning centers in MgB2 strands in addition to grain boundary pinning.
△ Less
Submitted 27 February, 2011;
originally announced February 2011.
-
Carbon Do** of MgB2 by Toluene and Malic-Acid-in-Toluene
Authors:
S. D. Bohnenstiehl,
M. A. Susner,
Y. Yang,
E. W. Collings,
M. D. Sumption,
M. A. Rindfleisch,
R. Boone
Abstract:
The decomposition of malic acid in the presence of Mg and B was studied using Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA) which revealed that malic acid reacted with Mg but not B. Also, the addition of toluene to dissolve malic acid followed by subsequent drying resulted in no reaction with Mg, indicating that the malic acid had decomposed during the dissolution/dr…
▽ More
The decomposition of malic acid in the presence of Mg and B was studied using Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA) which revealed that malic acid reacted with Mg but not B. Also, the addition of toluene to dissolve malic acid followed by subsequent drying resulted in no reaction with Mg, indicating that the malic acid had decomposed during the dissolution/drying stage. The total carbon contributed by toluene versus a toluene/5 wt% malic acid mixture was measured using a LECO CS600 carbon analyzer. The toluene sample contained ~0.4 wt% C while the toluene/malic acid mixture had ~1.5 wt% C, demonstrating that the toluene contributed a significant amount of carbon to the final product. Resistivity measurements on powder-in-tube MgB2 monofilamentary wires established that the toluene/malic acid doped sample had the highest Bc2. However, the toluene-only sample had the highest transport Jc over most of the magnetic field range (0-9 T), equaled only by that of toluene/malic acid sample in fields above 9 T.
△ Less
Submitted 5 October, 2010;
originally announced October 2010.
-
Enhanced superconducting properties of pre-doped B powder type MgB2 strands
Authors:
M. A. Susner,
Y. Yang,
M. D. Sumption,
M. A. Rindfleisch,
M. J. Tomsic,
J. V. Marzik,
E. W. Collings
Abstract:
Conventional do** methods that directly add C or a C-bearing species to Mg+B powder have the disadvantage of adding C inhomogeneously, yielding either under-reacted regions or blocking phases. Pre-doped B powder provides a more homogeneous distribution of the C dopant in MgB2. Powders containing varying amounts of C were used to produce in-situ MgB2 strands which showed high values of transport…
▽ More
Conventional do** methods that directly add C or a C-bearing species to Mg+B powder have the disadvantage of adding C inhomogeneously, yielding either under-reacted regions or blocking phases. Pre-doped B powder provides a more homogeneous distribution of the C dopant in MgB2. Powders containing varying amounts of C were used to produce in-situ MgB2 strands which showed high values of transport Jc (104 A/cm2 at 13.3T). Compared to SiC-added and malic acid-treated strands the pre-doped MgB2 showed both higher values of Birr and transport Jc, indicating that the pre-do** of B leads to more efficient C substitution into the B-sublattice.
△ Less
Submitted 18 August, 2010;
originally announced August 2010.
-
Thermal Diffusion and Quench Propagation in YBCO Pancake Coils Wound with ZnO-and Mylar Insulations
Authors:
M. D. Sumption,
M. Majoros,
M. Susner,
D. Lyons,
X. Peng,
C. F. Clark,
W. N. Lawless,
E. W. Collings
Abstract:
The thermal diffusion properties of several different kinds of YBCO insulations and the quench properties of pancake coils made using these insulations were studied. Insulations investigated include Nomex, Kapton, and Mylar, as well as insulations based on ZnO, Zn2GeO4, and ZnO-Cu. Initially, short stacks of YBCO conductors with interlayer insulation, epoxy, and a central heater strip were made…
▽ More
The thermal diffusion properties of several different kinds of YBCO insulations and the quench properties of pancake coils made using these insulations were studied. Insulations investigated include Nomex, Kapton, and Mylar, as well as insulations based on ZnO, Zn2GeO4, and ZnO-Cu. Initially, short stacks of YBCO conductors with interlayer insulation, epoxy, and a central heater strip were made and later measured for thermal conductivity in liquid nitrogen. Subsequently, three different pancake coils were made. The first two were smaller, each using one meter total of YBCO tape present as four turns around a G-10 former. One of these smaller coils used Mylar insulation co-wound with the YBCO tape, the other used YBCO tape onto which ZnO based insulation had been deposited. One larger coil was made which used 12 total meters of ZnO-insulated tape and had 45 turns. The results for all short sample and coil thermal conductivities were ~1-3 Wm-1K-1. Finally, quench propagation velocity measurements were performed on the coils (77 K, self field) by applying a DC current and then using a heater pulse to initiate a quench. Normal zone propagation velocity (NZP) values were obtained for the coils both in the radial direction and in the azimuthal direction. Radial NZP values (0.05-0.7 mm/s) were two orders of magnitude lower than axial values (~14-17 mm/s). Nevertheless, the quenches were generally seen to propagate radially within the coils, in the sense that any given layer in the coil is driven normal by the layer underneath it.
△ Less
Submitted 27 January, 2010;
originally announced January 2010.
-
Anisotropic Connectivity and its Influence on Critical Current Densities, Irreversibility Fields, and Flux Creep in In-Situ-Processed MgB2 Strands
Authors:
Z. X. Shi,
M. A. Susner,
M Majoros,
M. D. Sumption,
X. Peng,
M. Rindfleisch,
M. J. Tomsic,
E. W. Collings
Abstract:
The anisotropy of the critical current density (Jc) and its influence on measurement of irreversibility field (Birr) has been investigated for high quality, in-situ MgB2 strands. Comparison of transport and magnetization measurements has revealed the onset of a regime where large differences exist between transport and magnetically measured values of the critical current density and Birr. These…
▽ More
The anisotropy of the critical current density (Jc) and its influence on measurement of irreversibility field (Birr) has been investigated for high quality, in-situ MgB2 strands. Comparison of transport and magnetization measurements has revealed the onset of a regime where large differences exist between transport and magnetically measured values of the critical current density and Birr. These effects, initially unexpected due to the lack of crystalline texture in these in-situ processed strands, appear to be due to a fibrous microstructure, connected with the details of the wire fabrication and MgB2 formation reactions. Scanning electron micrographs of in-situ-processed MgB2 monocore strands have revealed a fibrous microstructure. Grains (~100 nm) are randomly oriented, and there is no apparent local texture of the grains. However, this randomly oriented polycrystalline material has a fibrous texture at a larger length scale, with stringers of MgB2 (~ 60 μm long and ~5 μm in diameter) partially separated by elongated pores -- the spaces previously occupied by stringers of elemental Mg. This leads to an interpretation of the differences observed in transport and magnetically determined critical currents, in particular a large deviation between the two at higher fields, in terms of different transverse and longitudinal connectivities within the strand. The different values of connectivity also lead to different resistive transition widths, and thus irreversibility field values, as measured by transport and magnetic techniques. Finally, these considerations are seen to influence estimated pinning potentials for the strands.
△ Less
Submitted 7 January, 2010;
originally announced January 2010.
-
Prospects for Improving the Intrinsic and Extrinsic Properties of Magnesium Diboride Superconducting Strands
Authors:
E. W. Collings,
M. D. Sumption,
M. Bhatia,
M. A. Susner,
S. D. Bohnenstiehl
Abstract:
The magnetic and transport properties of magnesium diboride films represent performance goals yet to be attained by powder-processed bulk samples and conductors. Such performance limits are still out of the reach of even the best magnesium diboride magnet wire. In discussing the present status and prospects for improving the performance of powder-based wire we focus attention on (1) the intrinsi…
▽ More
The magnetic and transport properties of magnesium diboride films represent performance goals yet to be attained by powder-processed bulk samples and conductors. Such performance limits are still out of the reach of even the best magnesium diboride magnet wire. In discussing the present status and prospects for improving the performance of powder-based wire we focus attention on (1) the intrinsic (intragrain) superconducting properties of magnesium diboride, Hc2 and flux pinning, (2) factors that control the efficiency with which current is transported from grain-to-grain in the conductor, an extrinsic (intergrain) property. With regard to Item-(1), the role of dopants in Hc2 enhancement is discussed and examples presented. On the other hand their roles in increasing Jc, both via Hc2 enhancement as well as direct fluxoid/pining-center interaction, are discussed and a comprehensive survey of Hc2 dopants and flux-pinning additives is presented. Current transport through the powder-processed wire (an extrinsic property) is partially blocked by the inherent granularity of the material itself and the chemical or other properties of the intergrain surfaces. These and other such results indicate that in many cases less than 15% of the conductor's cross sectional area is able to carry transport current. It is pointed out that densification in association with the elimination of grain-boundary blocking phases would yield five-to ten-fold increases in Jc in relevant regimes, enabling the performance of magnesium diboride in selected applications to compete with that of Nb-Sn.
△ Less
Submitted 9 May, 2008;
originally announced May 2008.
-
Increases in the Irreversibility Field and the Upper Critical Field of Bulk MgB2 by ZrB2 Addition
Authors:
M. Bhatia,
M. D. Sumption,
E. W. Collings,
S. Dregia
Abstract:
In a study of the influence of ZrB2 additions on the irreversibility field, Birr and the upper critical field Bc2, bulk samples with 7.5 at. % ZrB2 additions were made by a powder milling and compaction technique. These samples were then heated to 700-900C for 0.5 hours. Resistive transitions were measured at 4.2 K and Birr and Bc2 values were determined. An increase in Bc2 from 20.5 T to 28.6 T…
▽ More
In a study of the influence of ZrB2 additions on the irreversibility field, Birr and the upper critical field Bc2, bulk samples with 7.5 at. % ZrB2 additions were made by a powder milling and compaction technique. These samples were then heated to 700-900C for 0.5 hours. Resistive transitions were measured at 4.2 K and Birr and Bc2 values were determined. An increase in Bc2 from 20.5 T to 28.6 T and enhancement of Birr from 16 T to 24 T were observed in the ZrB2 doped sample as compared to the binary sample at 4.2 K. Critical field increases similar to those found with SiC do** were seen at 4.2 K. At higher temperatures, increases in Birr were also determined by M-H loop extrapolation and closure. Values of Birr which were enhanced with ZrB2 do** (as compared to the binary) were seen at temperatures up to 34 K, with Birr values larger than those for SiC doped samples at higher temperatures. The transition temperature, Tc, was then measured using DC susceptibility and a 2.5 K drop of the midpoint of Tc was observed. The critical current density was determined using magnetic measurements and was found to increase at all temperatures between 4.2 K and 35 K with ZrB2 do**.
△ Less
Submitted 31 March, 2005;
originally announced March 2005.
-
Solenoidal Coils Made from Monofilamentary and Multifilamentary MgB2 strands
Authors:
M. D. Sumption,
M. Bhatia,
F. Buta,
S. Bohnenstiehl,
M. Tomsic,
M. Rindfleisch,
J. Yue,
J. Phillips,
S. Kawabata,
E. W. Collings
Abstract:
Three solenoids have been wound and with MgB2 strand and tested for transport properties. One of the coils was wound with Cu-sheathed monofilamentary strand and the other two with a seven filament strand with Nb-reaction barriers, Cu stabilization, and an outer monel sheath. The wires were first S-glass insulated, then wound onto an OFHC Cu former. The coils were then heat treated at 675C/30 min…
▽ More
Three solenoids have been wound and with MgB2 strand and tested for transport properties. One of the coils was wound with Cu-sheathed monofilamentary strand and the other two with a seven filament strand with Nb-reaction barriers, Cu stabilization, and an outer monel sheath. The wires were first S-glass insulated, then wound onto an OFHC Cu former. The coils were then heat treated at 675C/30 min (monofilamentary strand) and 700C/20 min (multifilamentary strand). Smaller (1 m) segments of representative strand were also wound into barrel-form samples and HT along with the coils. After HT the coils were epoxy impregnated. Transport Jc measurements were performed at various taps along the coil lengths. Measurements were made initially in liquid helium, and then as a function of temperature up to 30 K. Homogeneity of response along the coils was investigated and a comparison to the short sample results was made. Each coil contained more than 100 m of 0.84-1.01 mm OD strand. One of the 7 strand coils reached 222 A at 4.2 K, self field, with a Jc of 300 kA/cm2 in the SC and a winding pack Je of 23 kA/cm2. At 20 K these values were 175 kA/cm2 and 13.4 kA/cm2. Magnet bore fields of 1.5 T and 0.87 T were achieved at 4.2 K and 20 K, respectively. The other multifilamentary coil gave similar results.
△ Less
Submitted 31 March, 2005;
originally announced March 2005.
-
MgB2/Cu Racetrack Coil: Winding and Transport Testing
Authors:
M. D. Sumption,
M. Bhatia,
M. Rindfleisch,
J. Phillips,
M. Tomsic,
E. W. Collings
Abstract:
A racetrack coil using MgB2/Cu strand has been fabricated and tested for transport current density at 4.2 K in self field. The monofilamentary strand was 1.0 mm OD and insulated with S-glass braid. Eighty turns of strand (42 m) were wound onto a stainless steel former with outer dimensions 25 cm x 10 cm x 0.86 cm. The resulting racetrack coil was heat treated at 675C for 30 minutes in flowing Ar…
▽ More
A racetrack coil using MgB2/Cu strand has been fabricated and tested for transport current density at 4.2 K in self field. The monofilamentary strand was 1.0 mm OD and insulated with S-glass braid. Eighty turns of strand (42 m) were wound onto a stainless steel former with outer dimensions 25 cm x 10 cm x 0.86 cm. The resulting racetrack coil was heat treated at 675C for 30 minutes in flowing Ar. The strand, with a superconducting fraction of 26%, occupied 49% of the total coil pack cross sectional area. The coil Ic at 4.2 K and self field was 120 A (using a 1 microvolt/cm criterion). This led to a Jc,sc (across the whole coil) of 6.12 x 10^4 A/cm2, a Je in the wire of 1.59 x 10^4 A/cm2, and an overall winding Je of 7.9 x 10^3 A/cm2 at 4.2 K in self field. The n-values ranged from 17 to 56.
△ Less
Submitted 18 October, 2004;
originally announced October 2004.
-
Large Upper Critical Field and Irreversibility Field in MgB2 wires with SiC additions
Authors:
M. D. Sumption,
M. Bhatia,
E. W. Collings,
M. Rindfleisch,
M. Tomsic,
S. Soltanian,
S. X. Dou
Abstract:
Resistive transition measurements are reported for Magnesium diboride strands with SiC dopants. The SiC was added as 10 mol of SiC to 90 mol of binary magnesium diboride. Three different SiC powders were used, the average particle sizes were 200 nm, 30 nm, and 15 nm. The strands were heat treated for times ranging from 5 to 30 minutes at temperatures from 675 to 900. Strands with 200 nm size SiC…
▽ More
Resistive transition measurements are reported for Magnesium diboride strands with SiC dopants. The SiC was added as 10 mol of SiC to 90 mol of binary magnesium diboride. Three different SiC powders were used, the average particle sizes were 200 nm, 30 nm, and 15 nm. The strands were heat treated for times ranging from 5 to 30 minutes at temperatures from 675 to 900. Strands with 200 nm size SiC additions had Hirr and Bc2 which maximized at 25.4 T and 29.7 T after heating at 800C for 30 minutes. The highest values were seen for a strand with 15 nm SiC heated at 725C for 30 minutes which had a Hirr of 29 T and a Bc2 higher than 33 T
△ Less
Submitted 15 October, 2004;
originally announced October 2004.
-
Irreversibility Field and Flux Pinning in MgB2 with and Without SiC Additions
Authors:
M. D. Sumption,
M. Bhatia,
E. W. Collings,
M. Rhindfliesh,
M. Tomsic,
Y. Hascicek,
S. X. Dou
Abstract:
Critical current density was measured at 4.2 K for MgB2 strands with and without SiC additions. In some cases measurements were performed on longer (1 m) samples wound on barrels, and these were compared to magnetic measurements. Most measurements were performed on short samples at higher fields (up to 18 T). It was found that in-situ processed strands with 10% SiC additions HT at 700-800C show…
▽ More
Critical current density was measured at 4.2 K for MgB2 strands with and without SiC additions. In some cases measurements were performed on longer (1 m) samples wound on barrels, and these were compared to magnetic measurements. Most measurements were performed on short samples at higher fields (up to 18 T). It was found that in-situ processed strands with 10% SiC additions HT at 700-800C show improved Hr and Fp values as compared to control samples, with Hr increasing by 1.5 T. At 900C even larger improvements are seen, with Hr reaching 18 T and Fp values maximizing at 20 GN/m3.
△ Less
Submitted 12 October, 2004;
originally announced October 2004.
-
AC Loss in Striped (Filamentary) YBCO Coated Conductors Leading to Designs for High Frequencies and Field-Sweep Amplitudes
Authors:
M. D. Sumption,
P. N. Barnes,
E. W. Collings
Abstract:
AC losses of YBCO coated conductors are investigated by calculation and experiment for the higher frequency regime. Previous research using YBCO film deposited onto single crystal substrates demonstrated the effectiveness of filamentary subdivision as a technique for AC loss reduction. As a result of these studies the idea of subdividing YBCO coated conductors (both YBCO, overlayer, and even und…
▽ More
AC losses of YBCO coated conductors are investigated by calculation and experiment for the higher frequency regime. Previous research using YBCO film deposited onto single crystal substrates demonstrated the effectiveness of filamentary subdivision as a technique for AC loss reduction. As a result of these studies the idea of subdividing YBCO coated conductors (both YBCO, overlayer, and even underlayer) into such stripes suggested itself. The suggestion was implemented by burning grooves into samples of coated conductor using laser micromachining. Various machining parameters were investigated, and the stri** and slicing characteristics are presented. Loss measurements were performed on unstriped as well as striped samples by the pick-up coil technique at frequencies of from 50-200 Hz at field sweep amplitudes of up to 150 mT. The effect of soft ferromagnetic Fe shielding was also investigated. The results of the experiments form a starting point for a more general study of reduced loss coated conductor design (including hysteretic, coupling, normal eddy current, and transport losses) projected into higher ranges of frequency and field sweep amplitude with transformer and all cryogenic motor/generator applications in mind.
△ Less
Submitted 12 October, 2004;
originally announced October 2004.
-
Transport and magnetic Jc of MgB2 strands and small helical coils
Authors:
M. D. Sumption,
M. Bhatia,
M. Rindfleisch,
M. Tomsic,
E. W. Collings
Abstract:
The critical current densities of MgB2 monofilamentary strands with and without SiC additions were measured at 4.2 K. Additionally, magnetic Jc at B = 1 T was measured from 4.2 K to 40 K. Various heat treatment times and temperatures were investigated for both short samples and small helical coils. SiC additions were seen to improve high field transport Jc at 4.2 K, but improvements were not evi…
▽ More
The critical current densities of MgB2 monofilamentary strands with and without SiC additions were measured at 4.2 K. Additionally, magnetic Jc at B = 1 T was measured from 4.2 K to 40 K. Various heat treatment times and temperatures were investigated for both short samples and small helical coils. SiC additions were seen to improve high field transport Jc at 4.2 K, but improvements were not evident at 1 T at any temperature. Transport results were relatively insensitive to heat treatment times and temperatures for both short samples and coils in the 700C to 900C range.
△ Less
Submitted 24 September, 2004;
originally announced September 2004.
-
Multifilamentary, in-situ Route, Cu-stabilized MgB2 Strands
Authors:
M. D. Sumption,
M. Bhatia,
X. Wu,
M. Rindfleisch,
M. Tomsic,
E. W. Collings
Abstract:
Transport critical current densities and n-values were measured at 4.2 K in fields up to 15 T on 7, 19, and 37-stack multifilamentary MgB2 strands made using an in-situ route. Some strands included SiC additions (particle size 30 nm), while in others Mg-rich compositions were used. Two basic multifilamentary variants were measured, the first had Nb filamentary barriers, the second had Fe filamen…
▽ More
Transport critical current densities and n-values were measured at 4.2 K in fields up to 15 T on 7, 19, and 37-stack multifilamentary MgB2 strands made using an in-situ route. Some strands included SiC additions (particle size 30 nm), while in others Mg-rich compositions were used. Two basic multifilamentary variants were measured, the first had Nb filamentary barriers, the second had Fe filamentary barriers. All samples incorporated stabilizer in the form of Cu 101. Simple, one-step heat treatments were used, with temperatures ranging from 700-800C, and times from 10-30 minutes. Transport critical current densities of 1.75 x 105 A/cm2 were seen at 4.2 K and 5 T in 37 stack strands.
△ Less
Submitted 10 September, 2004;
originally announced September 2004.
-
Transport Current in MgB2 based Superconducting Strand at 4.2 K and Self-Field
Authors:
M. D. Sumption,
X. Peng,
E. Lee,
M. Tomsic,
E. W. Collings
Abstract:
Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires were then rolled into tapes 2.56 x 0.32 mm2, with a total superconducting cross section of 0.2319 mm2. Transport measurements were performed using a standard fo…
▽ More
Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires were then rolled into tapes 2.56 x 0.32 mm2, with a total superconducting cross section of 0.2319 mm2. Transport measurements were performed using a standard four-point technique at T = 4.2 K (in liquid helium) and at self field. Three samples were prepared, with heat treatments of 900C for 1, 2, and 3 h under 1/3 at Ar. Measured values of transport current were 4.7, 7.5, and 1.1 x 104 A/cm2, respectively, at 4.2 K and self field. M-H loops taken on the sample HT for 1 h showed magnetic Jcs of 4.2 x 104 A/cm2 at 4.2 K and 1 T, indicating that the material had reasonably well connected grains.
△ Less
Submitted 26 February, 2001; v1 submitted 23 February, 2001;
originally announced February 2001.
-
Flux Jum** and a Bulk-to-Granular Transition in the Magnetization of a Compacted and Sintered MgB2 Superconductor
Authors:
S. X. Dou,
X. L. Wang,
J. Horvat,
D. Milliken,
E. W. Collings,
M. D. Sumption
Abstract:
The recent discovery of intermediate-temperature superconductivity (ITC) in MgB2 by Akimitsu et al. and its almost simultaneous explanation in terms of a hole-carrier-based pairing mechanism by Hirsch, has triggered an avalanche of studies of its structural, magnetic and transport properties. As a further contribution to the field we report the results of field (H) and temperature (T) dependent…
▽ More
The recent discovery of intermediate-temperature superconductivity (ITC) in MgB2 by Akimitsu et al. and its almost simultaneous explanation in terms of a hole-carrier-based pairing mechanism by Hirsch, has triggered an avalanche of studies of its structural, magnetic and transport properties. As a further contribution to the field we report the results of field (H) and temperature (T) dependent magnetization (M) measurements of a pellet of uniform, large-grain sintered MgB2. We show that at low temperatures the size of the pellet and its critical current density, Jc(H) - i.e. its M(H) - ensure low field flux jum**, which of course ceases when M(H) drops below a critical value. With further increase of H and T the individual grains decouple and the M(H) loops drop to lower lying branches, unresolved in the usual full M(H) representation. After taking into account the sample size and grain size, respectively, the bulk sample and the grains were deduced to exhibit the same magnetically determined Jc s (e.g. 105 A/cm2, 20 K, 0T) and hence that for each temperature of measurement Jc(H) decreased monotonically with H over the entire field range, except for a gap within the grain-decoupling zone.
△ Less
Submitted 22 February, 2001; v1 submitted 18 February, 2001;
originally announced February 2001.
-
Coupling Current Control in Stabrite-Coated Nbti Rutherford Cables by Varying the Width of a Stainless Steel Core
Authors:
M. D. Sumption,
E. W. Collings,
A. Nijhuis,
R. M. Scanlan
Abstract:
AC loss measurements were made on a series of Rutherford cables wound from stabrite-coated NbTi/Cu multifilamentary strand, from the results of which interstrand contact resistances were calculated. The 28-strand, 15 mm wide, LHC-inner type cables contained stainless steel cores of various widths. Calorimetric loss measurements were made on all samples using a sinusoidal field with an amplitude…
▽ More
AC loss measurements were made on a series of Rutherford cables wound from stabrite-coated NbTi/Cu multifilamentary strand, from the results of which interstrand contact resistances were calculated. The 28-strand, 15 mm wide, LHC-inner type cables contained stainless steel cores of various widths. Calorimetric loss measurements were made on all samples using a sinusoidal field with an amplitude of 400 mT. It is concluded that by adjusting the width of a stainless steel core the effective ICR of a stabrite-coated Rutherford cable can be varied over a wide range, and in particular that a published target of 15 micro-ohm could be attained.
△ Less
Submitted 12 November, 1999;
originally announced November 1999.
-
AC Loss and Contact Resistance In Copper-Stabilized Nb3Al Rutherford Cables with and without a Stainless Steel Core
Authors:
M. D. Sumption,
R. M. Scanlan,
A. Nijhuis,
E. W. Collings
Abstract:
Calorimetric measurements of AC loss and hence interstrand contact resistance (ICR), were measured on three samples of Rutherford cable wound with Cu-stabilized jelly-roll type unplated Nb3Al strand. One of the cable types was furnished with a thin core of AISI 316L stainless steel and the other two were both uncored but insulated in different ways. The cables were subjected to a room-temperatur…
▽ More
Calorimetric measurements of AC loss and hence interstrand contact resistance (ICR), were measured on three samples of Rutherford cable wound with Cu-stabilized jelly-roll type unplated Nb3Al strand. One of the cable types was furnished with a thin core of AISI 316L stainless steel and the other two were both uncored but insulated in different ways. The cables were subjected to a room-temperature-applied uniaxial pressure of 12 MPa that was maintained during the reaction heat treatment (RHT), then vacuum impregnated with CTD 101 epoxy, and repressurized to 100 MPa during AC-loss measurement. The measurements were performed at 4.2 K in a sinusoidal field of amplitude 400 mT at frequencies of 1 to 90 mHz (no DC-bias field) that was applied both perpendicular and parallel to the face of the cable (the face-on, FO, and edge-on, EO, directions, respectively). For the cored cable the FO-measured effective ICR (FO-ICR), was 5.27 . Those for the uncored cables were less than 0.08 . As shown previously for NbTi- and Nb3Sn-based Rutherford cables, the FO-ICR can be significantly increased by the insertion of a core, although in this case it is still below the range recommended for accelerator-magnet use. Post-measurement dissection of one of the cables showed that the impregnating resin had permeated between the strands and coated the core with a thin, insulating layer excepting for some sintered points of contact. In the uncored cables the strands were coated with resin except for the points of interstrand contact. It is suggested that in the latter case this tendency for partial coating leads to a processing-sensitive FO-ICR.
△ Less
Submitted 12 November, 1999;
originally announced November 1999.