Investigation of the microstructure of the fine-grained YPO$_4$:Gd ceramics with xenotime structure after Xe irradiation
Authors:
D. A. Mikhailov,
E. A. Potanina,
A. V. Nokhrin,
A. I. Orlova,
P. A. Yunin,
N. V. Sakharov,
M. S. Boldin,
O. A. Belkin,
V. A. Skuratov,
A. T. Isatov,
V. N. Chuvil'deev,
N. Y. Tabachkova
Abstract:
The paper reports on the preparation of xenotime-structured ceramics by the Spark Plasma Sintering (SPS) method. Phosphates Y$_{0.95}$Gd$_{0.05}$PO$_4$ (YPO$_4$:Gd) were obtained by the sol-gel method. The synthesized nanopowders are collected in large agglomerates 10-50 mkm in size. Ceramics has a fine-grained microstructure and a high relative density (98.67%). The total time of the SPS process…
▽ More
The paper reports on the preparation of xenotime-structured ceramics by the Spark Plasma Sintering (SPS) method. Phosphates Y$_{0.95}$Gd$_{0.05}$PO$_4$ (YPO$_4$:Gd) were obtained by the sol-gel method. The synthesized nanopowders are collected in large agglomerates 10-50 mkm in size. Ceramics has a fine-grained microstructure and a high relative density (98.67%). The total time of the SPS process was approximately 18 min. High-density sintered ceramics YPO$_4$:Gd with a xenotime structure were irradiated with Xe$^{+26}$ ions (E = 167 MeV) to fluences of $1\times10^{12}$-$3\times 10^{13}$ cm$^{-2}$. Complete amorphization at maximum fluence was not achieved. As the fluence increases, an insignificant increase in the depth of the amorphous layer is observed. According to the results of grazing incidence XRD (GIXRD), with an increase in fluence from $1\times10^{12}$-$3\times 10^{13}$ cm$^{-2}$, an increase in the volume fraction of the amorphous structure from 20 to 70% is observed. The intensity of XRD peak 200 YPO$_4$:Gd after recovery annealing (700$^\circ$C, 18 h) reached a value of ~80% of the initial intensity I0.
△ Less
Submitted 26 March, 2022;
originally announced March 2022.
-
Synthesis and study of (Na, Zr) and (Ca, Zr) phosphate-molybdates and phosphate-tungstates: Thermal expansion behavior, radiation test and hydrolytic stability
Authors:
M. E. Karaeva,
D. O. Savinykh,
A. I. Orlova,
S. A. Khainakov,
A. V. Nokhrin,
M. S. Boldin,
S. Garcia-Granda,
A. A. Murashov,
V. N. Chuvildeev,
V. A. Skuratov,
N. S. Kirilkin,
P. Yu. Yunin,
N. Yu. Tabachkova
Abstract:
Thermal expansion behavior at high temperatures of synthesized Na$_{1-x}$Zr$_2$(PO$_4$)$_{3-x}$(XO$_4$)$_x$, and Ca$_{1-x}$Zr$_2$(PO$_4$)$_{3-x}$(XO$_4$)$_x$, X = Mo, W compounds has been investigated. Ceramics with relatively high density (more than 97.5%) were produced by Spark Plasma Sintering (SPS) of submicron powders obtained by sol-gel synthesis. The study of strength characteristics has re…
▽ More
Thermal expansion behavior at high temperatures of synthesized Na$_{1-x}$Zr$_2$(PO$_4$)$_{3-x}$(XO$_4$)$_x$, and Ca$_{1-x}$Zr$_2$(PO$_4$)$_{3-x}$(XO$_4$)$_x$, X = Mo, W compounds has been investigated. Ceramics with relatively high density (more than 97.5%) were produced by Spark Plasma Sintering (SPS) of submicron powders obtained by sol-gel synthesis. The study of strength characteristics has revealed that hardness the ceramics are greater than 5 GPa, and minimum fracture toughness factor was 1 MPa*m$^{1/2}$. It was found that ceramics have a high hydrolytic resistance in the static regime -- the minimum leaching rates for the Mo- and W-containing specimens were $31\times10^{-6}$ and $3.36\times 10^{-6}$ g/(cm$^2$*day), respectively. The ceramics had a high resistance to the irradiation by Xe$^{+26}$ multiple-charged ions with the energy 167 MeV up to the fluences in the range 1*10$^{12}$ - 6*10$^{13}$ cm$^{-2}$. The Mo-containing Na$_{0.5}$Zr$_2$(PO$_4$)$_{2.5}$(XO$_4$)$_{0.5}$ ceramics were shown to have a higher radiation resistance that the phosphate-tungstates.
△ Less
Submitted 1 December, 2021;
originally announced December 2021.
-
Orbital Quantization in a System of Edge Dirac Fermions in Nanoperforated Graphene
Authors:
Yu. I. Latyshev,
A. P. Orlov,
A. V. Frolov,
V. A. Volkov,
I. V. Zagorodnev,
V. A. Skuratov,
Yu. V. Petrov,
O. F. Vyvenko,
D. Yu. Ivanov,
M. Konczykowski,
P. Monceau
Abstract:
The dependence of the electric resistance R of nanoperforated graphene samples on the position of the Fermi level, which is varied by the gate voltage Vg, has been studied. Nanoperforation has been performed by irradiating graphene samples on a Si/SiO$_2$ substrate by heavy (xenon) or light (helium) ions. A series of regular peaks have been revealed on the R(Vg) dependence at low temperatures in z…
▽ More
The dependence of the electric resistance R of nanoperforated graphene samples on the position of the Fermi level, which is varied by the gate voltage Vg, has been studied. Nanoperforation has been performed by irradiating graphene samples on a Si/SiO$_2$ substrate by heavy (xenon) or light (helium) ions. A series of regular peaks have been revealed on the R(Vg) dependence at low temperatures in zero magnetic field. These peaks are attributed to the passage of the Fermi level through an equidistant ladder of levels formed by orbitally quantized states of edge Dirac fermions rotating around each nanohole. The results are in agreement with the theory of edge states for massless Dirac fermions.
△ Less
Submitted 4 March, 2015;
originally announced March 2015.