Adhesive Transfer operates during Galling

Authors: Samuel R Rogers, Jaimie Daure, Philip Shipway, David Stewart, David Dye

Abstract: In order to reduce cobalt within the primary circuit of pressurised water reactors (PWRs), wear-resistant steels are being researched and developed. In particular interest is the understanding of galling mechanisms, an adhesive wear mechanism which is particularly prevalent in PWR valves. Here we show that large shear stresses and adhesive transfer occur during galling by exploiting the 2 wt per c… ▽ More In order to reduce cobalt within the primary circuit of pressurised water reactors (PWRs), wear-resistant steels are being researched and developed. In particular interest is the understanding of galling mechanisms, an adhesive wear mechanism which is particularly prevalent in PWR valves. Here we show that large shear stresses and adhesive transfer occur during galling by exploiting the 2 wt per cent manganese difference between 304L and 316L stainless steels, even at relatively low compressive stresses of 50 MPa. Through these findings, the galling mechanisms of stainless steels can be better understood, which may help with the development of galling resistant stainless steels. △ Less

Submitted 3 October, 2022; v1 submitted 27 May, 2022; originally announced May 2022.

Influence of KCl and HCl on a Laser Clad FeCrAl Alloy: In-Situ SEM and Controlled Environment High Temperature Corrosion

Authors: L. Reddy, M. Sattari, C. J. Davis, P. H. Shipway, M. Halvarsson, T. Hussain

Abstract: Increasing pressure on the power industry to reduce carbon emissions has led to increased research into the use of biomass feedstocks. This work investigates the effects of HCl and KCl, key species influencing biomass boiler corrosion, on a laser clad coating of the FeCrAl alloy Kanthal APMT. In-Situ SEM exposure of the coating at 450 oC for 1 h was performed to investigate the initial effects of… ▽ More Increasing pressure on the power industry to reduce carbon emissions has led to increased research into the use of biomass feedstocks. This work investigates the effects of HCl and KCl, key species influencing biomass boiler corrosion, on a laser clad coating of the FeCrAl alloy Kanthal APMT. In-Situ SEM exposure of the coating at 450 oC for 1 h was performed to investigate the initial effects of KCl on the corrosion process. The same coatings were exposed to 250 h exposures in both an air environment and a HCl rich environment. The influence of KCl was investigated in both. Evidence of a slow growing aluminium oxide was observed. It was found that HCl allowed chlorine based corrosion to occur suggesting it can interact from the gas phase. It was also observed that the presence of both HCl and KCl reduced the mass gain compared to KCl in an air environment. △ Less

Submitted 27 September, 2018; originally announced September 2018.