Thickness effect on superconducting properties of niobium films for radio-frequency cavity applications
Authors:
Antonio Bianchi,
Marco Bonura,
Carlota P. A. Carlos,
Stewart Leith,
Guillaume Rosaz,
Carmine Senatore,
Walter Venturini Delsolaro
Abstract:
Niobium-coated copper radio-frequency cavities are cost-effective alternatives to bulk niobium cavities, given the lower material costs of copper substrates and their operation in liquid helium at around 4.2 K. However, these cavities historically exhibited a gradual degradation in performance with the accelerating field. This phenomenon, not yet fully understood, limits the application of niobium…
▽ More
Niobium-coated copper radio-frequency cavities are cost-effective alternatives to bulk niobium cavities, given the lower material costs of copper substrates and their operation in liquid helium at around 4.2 K. However, these cavities historically exhibited a gradual degradation in performance with the accelerating field. This phenomenon, not yet fully understood, limits the application of niobium thin film cavities in accelerators where the real-estate gradient needs to be maximized. Recent studies on niobium films deposited on copper using high power impulse magnetron sputtering (HiPIMS) technique show promising results in mitigating the performance degradation of niobium thin film radio-frequency cavities. This paper examines the effect of film thickness on the superconducting properties of niobium films deposited on copper using HiPIMS. The study provides insights into how the critical temperature, transition width, lower and upper critical fields, and critical current density vary with the film thickness. Increasing the thickness of niobium films deposited through HiPIMS is found to enhance superconducting properties and reduce densities of defects and structural irregularities in the crystalline lattice. This shows potential for enhancing overall performance and potentially mitigating the observed performance degradation in niobium thin film radio-frequency cavities. Additionally, the Ivry's scaling relation among critical temperature, thickness, and sheet resistance at the normal state appears applicable to niobium films up to approximately 4 $μ$m. This extends the previously confirmed validity for niobium films, which was limited to around 300 nm thickness.
△ Less
Submitted 17 March, 2024;
originally announced March 2024.
-
Towards a Muon Collider
Authors:
Carlotta Accettura,
Dean Adams,
Rohit Agarwal,
Claudia Ahdida,
Chiara Aimè,
Nicola Amapane,
David Amorim,
Paolo Andreetto,
Fabio Anulli,
Robert Appleby,
Artur Apresyan,
Aram Apyan,
Sergey Arsenyev,
Pouya Asadi,
Mohammed Attia Mahmoud,
Aleksandr Azatov,
John Back,
Lorenzo Balconi,
Laura Bandiera,
Roger Barlow,
Nazar Bartosik,
Emanuela Barzi,
Fabian Batsch,
Matteo Bauce,
J. Scott Berg
, et al. (272 additional authors not shown)
Abstract:
A muon collider would enable the big jump ahead in energy reach that is needed for a fruitful exploration of fundamental interactions. The challenges of producing muon collisions at high luminosity and 10 TeV centre of mass energy are being investigated by the recently-formed International Muon Collider Collaboration. This Review summarises the status and the recent advances on muon colliders desi…
▽ More
A muon collider would enable the big jump ahead in energy reach that is needed for a fruitful exploration of fundamental interactions. The challenges of producing muon collisions at high luminosity and 10 TeV centre of mass energy are being investigated by the recently-formed International Muon Collider Collaboration. This Review summarises the status and the recent advances on muon colliders design, physics and detector studies. The aim is to provide a global perspective of the field and to outline directions for future work.
△ Less
Submitted 27 November, 2023; v1 submitted 15 March, 2023;
originally announced March 2023.
-
A Work Proposal for a Collaborative Study of Magnet Technology for a Future Muon Collider
Authors:
L. Bottura,
D. Aguglia,
B. Auchmann,
T. Arndt,
J. Beard,
A. Bersani,
F. Boattini,
M. Breschi,
B. Caiffi,
X. Chaud,
M. Dam,
F. Debray,
H. De Gersem,
E. De Matteis,
A. Dudarev,
S. Farinon,
A. Kario,
R. Losito,
S. Mariotto,
M. Mentink,
R. Musenich,
T. Ogitsu,
M. Prioli,
L. Quettier,
L. Rossi
, et al. (8 additional authors not shown)
Abstract:
In this paper we elaborate on the nature and challenges for the magnet systems of a muon collider as presently considered within the scope of the International Muon Collider Collaboration (IMCC). We outline the structure of the work proposed over the coming period of five years to study and demonstrate relevant magnet technology. The proposal, which is part of the overall work planned to establish…
▽ More
In this paper we elaborate on the nature and challenges for the magnet systems of a muon collider as presently considered within the scope of the International Muon Collider Collaboration (IMCC). We outline the structure of the work proposed over the coming period of five years to study and demonstrate relevant magnet technology. The proposal, which is part of the overall work planned to establish feasibility of a muon collider, is in direct response to the recent recommendations received from the Laboratories Directors Group (LDG). The plan is to profit from joint activities, within the scope of the IMCC and beyond, implemented through direct and EU-funded contributions.
△ Less
Submitted 29 March, 2022; v1 submitted 26 March, 2022;
originally announced March 2022.
-
High Field Magnet Development for HEP in Europe: A Proposal from LDG HFM Expert Panel
Authors:
Pierre Védrine,
Luis Garcia-Tabarès,
Bernhard Auchmann,
Amalia Ballarino,
Bertrand Baudouy,
Luca Bottura,
Philippe Fazilleau,
Mathias Noe,
Soren Prestemon,
Etienne Rochepault,
Lucio Rossi,
Carmine Senatore,
Ben Shepherd
Abstract:
The European Laboratory Directors Group (LDG) was mandated by CERN Council in 2021 to oversee the development of an Accelerator R&D Roadmap. To this end, a set of expert panels was convened, covering the five broad areas of accelerator R&D highlighted in the ESPPU. The High Field Magnet (HFM) Panel is proposing a programme to demonstrate Nb3Sn magnet technology for large-scale deployment and to in…
▽ More
The European Laboratory Directors Group (LDG) was mandated by CERN Council in 2021 to oversee the development of an Accelerator R&D Roadmap. To this end, a set of expert panels was convened, covering the five broad areas of accelerator R&D highlighted in the ESPPU. The High Field Magnet (HFM) Panel is proposing a programme to demonstrate Nb3Sn magnet technology for large-scale deployment and to investigate the suitability of high temperature superconductors (HTS) for accelerator magnet applications. A summary of this programme is presented here.
△ Less
Submitted 15 March, 2022;
originally announced March 2022.
-
European Strategy for Particle Physics -- Accelerator R&D Roadmap
Authors:
C. Adolphsen,
D. Angal-Kalinin,
T. Arndt,
M. Arnold,
R. Assmann,
B. Auchmann,
K. Aulenbacher,
A. Ballarino,
B. Baudouy,
P. Baudrenghien,
M. Benedikt,
S. Bentvelsen,
A. Blondel,
A. Bogacz,
F. Bossi,
L. Bottura,
S. Bousson,
O. Brüning,
R. Brinkmann,
M. Bruker,
O. Brunner,
P. N. Burrows,
G. Burt,
S. Calatroni,
K. Cassou
, et al. (111 additional authors not shown)
Abstract:
The 2020 update of the European Strategy for Particle Physics emphasised the importance of an intensified and well-coordinated programme of accelerator R&D, supporting the design and delivery of future particle accelerators in a timely, affordable and sustainable way. This report sets out a roadmap for European accelerator R&D for the next five to ten years, covering five topical areas identified…
▽ More
The 2020 update of the European Strategy for Particle Physics emphasised the importance of an intensified and well-coordinated programme of accelerator R&D, supporting the design and delivery of future particle accelerators in a timely, affordable and sustainable way. This report sets out a roadmap for European accelerator R&D for the next five to ten years, covering five topical areas identified in the Strategy update. The R&D objectives include: improvement of the performance and cost-performance of magnet and radio-frequency acceleration systems; investigations of the potential of laser / plasma acceleration and energy-recovery linac techniques; and development of new concepts for muon beams and muon colliders. The goal of the roadmap is to document the collective view of the field on the next steps for the R&D programme, and to provide the evidence base to support subsequent decisions on prioritisation, resourcing and implementation.
△ Less
Submitted 30 March, 2022; v1 submitted 19 January, 2022;
originally announced January 2022.
-
Determination of the electromechanical limits of high-performance Nb$_3$Sn Rutherford cables under transverse stress from a single-wire experiment
Authors:
Luc Gamperle,
Jose Ferradas,
Christian Barth,
Bernardo Bordini,
Davide Tommasini,
Carmine Senatore
Abstract:
The development of high-field accelerator magnets capable of providing 16 T dipolar fields is an indispensable technological breakthrough needed for the 100 TeV energy-frontier targeted by the Future Circular Collider (FCC). As these magnets will be based on Nb$_3$Sn Rutherford cables, the degradation of the conductor performance due to the large electro-magnetic stresses becomes a parameter with…
▽ More
The development of high-field accelerator magnets capable of providing 16 T dipolar fields is an indispensable technological breakthrough needed for the 100 TeV energy-frontier targeted by the Future Circular Collider (FCC). As these magnets will be based on Nb$_3$Sn Rutherford cables, the degradation of the conductor performance due to the large electro-magnetic stresses becomes a parameter with a profound impact on the magnet design. In this work, we investigated the stress dependence and the irreversible reduction of the critical current under compressive transverse load in high performance Powder-In-Tube (PIT) Nb$_3$Sn wires. Tests were performed in magnetic fields ranging between 16 T and 19 T on wires that were resin-impregnated similarly to the wires in the Rutherford cables of accelerator magnets. The scope was to predict the degradation of the cable under stress from a single-wire experiment. Interestingly, the irreversible stress limit, $σ_{irr}$, defined as the stress level corresponding to a permanent reduction of the critical current by 5$\%$ with respect to its initial value, was found to depend on the applied magnetic field. This observation allowed us to shed light on the mechanism dominating the irreversible reduction of the wire performance and to compare and reconcile our results with the irreversible limits measured on Rutherford cables, typically tested at fields below 12 T.
△ Less
Submitted 30 September, 2019;
originally announced September 2019.
-
AMS-100: The Next Generation Magnetic Spectrometer in Space -- An International Science Platform for Physics and Astrophysics at Lagrange Point 2
Authors:
Stefan Schael,
Alexander Atanasyan,
Javier Berdugo,
Thomas Bretz,
Markus Czupalla,
Bernd Dachwald,
Philip von Doetinchem,
Matteo Duranti,
Henning Gast,
Waclaw Karpinski,
Thomas Kirn,
Klaus Lübelsmeyer,
Carlos Maña,
Pier Simone Marrocchesi,
Philipp Mertsch,
Igor V. Moskalenko,
Thomas Schervan,
Michael Schluse,
Kai-Uwe Schröder,
Arndt Schultz von Dratzig,
Carmine Senatore,
L. Spies,
Scott P. Wakely,
Michael Wlochal,
Davide Uglietti
, et al. (1 additional authors not shown)
Abstract:
The next generation magnetic spectrometer in space, AMS-100, is designed to have a geometrical acceptance of $100\,\mathrm{m}^2\,\mathrm{sr}$ and to be operated for at least ten years at the Sun-Earth Lagrange Point 2. Compared to existing experiments, it will improve the sensitivity for the observation of new phenomena in cosmic rays, and in particular in cosmic antimatter, by at least a factor o…
▽ More
The next generation magnetic spectrometer in space, AMS-100, is designed to have a geometrical acceptance of $100\,\mathrm{m}^2\,\mathrm{sr}$ and to be operated for at least ten years at the Sun-Earth Lagrange Point 2. Compared to existing experiments, it will improve the sensitivity for the observation of new phenomena in cosmic rays, and in particular in cosmic antimatter, by at least a factor of 1000. The magnet design is based on high temperature superconductor tapes, which allow the construction of a thin solenoid with a homogeneous magnetic field of 1 Tesla inside. The inner volume is instrumented with a silicon tracker reaching a maximum detectable rigidity of 100 TV and a calorimeter system that is 70 radiation lengths deep, equivalent to four nuclear interaction lengths, which extends the energy reach for cosmic-ray nuclei up to the PeV scale, i.e. beyond the cosmic-ray knee. Covering most of the sky continuously, AMS-100 will detect high-energy gamma rays in the calorimeter system and by pair conversion in the thin solenoid, reconstructed with excellent angular resolution in the silicon tracker.
△ Less
Submitted 9 July, 2019;
originally announced July 2019.
-
Modeling of the interaction of rigid wheels with dry granular media
Authors:
Shashank Agarwal,
Carmine Senatore,
Tingnan Zhang,
Mark Kingsbury,
Karl Iagnemma,
Daniel I. Goldman,
Ken Kamrin
Abstract:
We analyze the capabilities of various recently developed techniques, namely Resistive Force Theory (RFT) and continuum plasticity implemented with the Material Point Method (MPM), in capturing dynamics of wheel--dry granular media interactions. We compare results to more conventionally accepted methods of modeling wheel locomotion. While RFT is an empirical force model for arbitrarily-shaped bodi…
▽ More
We analyze the capabilities of various recently developed techniques, namely Resistive Force Theory (RFT) and continuum plasticity implemented with the Material Point Method (MPM), in capturing dynamics of wheel--dry granular media interactions. We compare results to more conventionally accepted methods of modeling wheel locomotion. While RFT is an empirical force model for arbitrarily-shaped bodies moving through granular media, MPM-based continuum modeling allows the simulation of full granular flow and stress fields. RFT allows for rapid evaluation of interaction forces on arbitrary shaped intruders based on a local surface stress formulation depending on depth, orientation, and movement of surface elements. We perform forced-slip experiments for three different wheel types and three different granular materials, and results are compared with RFT, continuum modeling, and a traditional terramechanics semi-empirical method. Results show that for the range of inputs considered, RFT can be reliably used to predict rigid wheel granular media interactions with accuracy exceeding that of traditional terramechanics methodology in several circumstances. Results also indicate that plasticity-based continuum modeling provides an accurate tool for wheel-soil interaction while providing more information to study the physical processes giving rise to resistive stresses in granular media.
△ Less
Submitted 29 January, 2019;
originally announced January 2019.
-
Strong improvement of the transport characteristics of YBa$_\textrm{2}$Cu$_\textrm{3}$O$_\textrm{7-x}$ grain boundaries using ionic liquid gating
Authors:
A. Fête,
C. Senatore
Abstract:
For more than 30 years, the remarkable superconducting properties of REBa$_\textrm{2}$Cu$_\textrm{3}$O$_\textrm{7-x}$ (RE = rare earth) compounds have triggered research studies across the world. Accordingly, significant progresses have been made both from a basic understanding and a fabrication processes perspective. Yet, today, the major technological bottleneck towards the spread of their pract…
▽ More
For more than 30 years, the remarkable superconducting properties of REBa$_\textrm{2}$Cu$_\textrm{3}$O$_\textrm{7-x}$ (RE = rare earth) compounds have triggered research studies across the world. Accordingly, significant progresses have been made both from a basic understanding and a fabrication processes perspective. Yet, today, the major technological bottleneck towards the spread of their practical uses remains the exponential decay of their critical current with grain misorientation in polycrystalline samples. In this work, we used an ionic liquid to apply extremely high transverse electric fields to YBa$_\textrm{2}$Cu$_\textrm{3}$O$_\textrm{7-x}$ thin films containing a single well-defined low-angle grain boundary. Our study shows that this technique is very effective to tune the IV characteristics of these weak-links. In-magnetic field measurements allow us to discuss the type of the vortices present at the grain boundary and to unveil a large variation of the local depairing current density with gating. Comparing our results with the ones obtained on chemically-doped grain boundaries, we discuss routes to evaluate the role of local strain in the loss of transparency at cuprates low-angle grain boundaries. In short, this study offers a new opportunity to discuss scenarios leading to the reduced transport capabilities of grain boundaries in cuprates.
△ Less
Submitted 23 November, 2018; v1 submitted 29 April, 2018;
originally announced April 2018.
-
Ionic liquid gating of ultra-thinYBa$_2$Cu$_3$O$_{7-x}$ films
Authors:
A. Fête,
L. Rossi,
A. Augieri,
C. Senatore
Abstract:
In this paper, we present a detailed investigation of the self-field transport properties of an ionic liquid gated ultra-thin YBa$_2$Cu$_3$O$_{7-x}$ film. From the high temperature dynamic of the resistivity ($> 220 \textrm{ K}$) different scenarios pertaining to the interaction between the liquid and the thin film are proposed. From the low temperature evolution of $J_{\textrm{c}}$ and…
▽ More
In this paper, we present a detailed investigation of the self-field transport properties of an ionic liquid gated ultra-thin YBa$_2$Cu$_3$O$_{7-x}$ film. From the high temperature dynamic of the resistivity ($> 220 \textrm{ K}$) different scenarios pertaining to the interaction between the liquid and the thin film are proposed. From the low temperature evolution of $J_{\textrm{c}}$ and $T_{\textrm{c}}$ a comparison between the behavior of our system and the standard properties of YBCO is drawn.
△ Less
Submitted 16 November, 2016;
originally announced November 2016.
-
Assessing composition gradients in multifilamentary superconductors by means of magnetometry methods
Authors:
T. Baumgartner,
J. Hecher,
J. Bernardi,
S. Pfeiffer,
C. Senatore,
M. Eisterer
Abstract:
We present two magnetometry-based methods suitable for assessing gradients in the critical temperature and hence the composition of multifilamentary superconductors: AC magnetometry and Scanning Hall Probe Microscopy. The novelty of the former technique lies in the iterative evaluation procedure we developed, whereas the strength of the latter is the direct visualization of the temperature depende…
▽ More
We present two magnetometry-based methods suitable for assessing gradients in the critical temperature and hence the composition of multifilamentary superconductors: AC magnetometry and Scanning Hall Probe Microscopy. The novelty of the former technique lies in the iterative evaluation procedure we developed, whereas the strength of the latter is the direct visualization of the temperature dependent penetration of a magnetic field into the superconductor. Using the example of a PIT Nb3Sn wire, we demonstrate the application of these techniques, and compare the respective results to each other and to EDX measurements of the Sn distribution within the sub-elements of the wire.
△ Less
Submitted 7 November, 2016;
originally announced November 2016.
-
An equation for the quench propagation velocity valid for high field magnet use of REBCO coated conductors
Authors:
Marco Bonura,
Carmine Senatore
Abstract:
Based on a study of the thermophysical properties, we derived a practical formula for the normal zone propagation velocity appropriate for REBa$_2$Cu$_3$O$_{7-x}$ coated conductors in high magnetic fields. An analytical expression to evaluate the current sharing temperature as a function of the operating conditions is also proposed. The presented study has allowed us to account for experimental re…
▽ More
Based on a study of the thermophysical properties, we derived a practical formula for the normal zone propagation velocity appropriate for REBa$_2$Cu$_3$O$_{7-x}$ coated conductors in high magnetic fields. An analytical expression to evaluate the current sharing temperature as a function of the operating conditions is also proposed. The presented study has allowed us to account for experimental results not fully understood in the framework of the models widely used in the literature. In particular, we provided a fundamental understanding of the experimental evidence that the normal zone propagation velocity in REBa$_2$Cu$_3$O$_{7-x}$ coated conductors can be mainly determined by the operating current, regardless of the applied field and temperature.
△ Less
Submitted 16 June, 2016;
originally announced June 2016.
-
General scaling relations for locomotion in granular media
Authors:
James Slonaker,
D. Carrington Motley,
Qiong Zhang,
Stephen Townsend,
Carmine Senatore,
Karl Iagnemma,
Ken Kamrin
Abstract:
We derive a general dimensionless form for granular locomotion, which is validated in experiments and Discrete Element Method (DEM) simulations. The form instructs how to scale size, mass, and driving parameters in order to relate dynamic behaviors of different locomotors in the same granular media. The scaling can be derived by assuming intrusion forces arise from Resistive Force Theory (RFT) or…
▽ More
We derive a general dimensionless form for granular locomotion, which is validated in experiments and Discrete Element Method (DEM) simulations. The form instructs how to scale size, mass, and driving parameters in order to relate dynamic behaviors of different locomotors in the same granular media. The scaling can be derived by assuming intrusion forces arise from Resistive Force Theory (RFT) or equivalently by assuming the granular material behaves as a continuum obeying a frictional yield criterion. The scalings are experimentally confirmed using pairs of wheels of various shapes and sizes under many driving conditions in a common sand bed. We discuss why the two models provide such a robust set of scaling laws even though they neglect a number of the complexities of granular rheology. Motivated by potential extra-planetary applications, the dimensionless form also implies a way to predict wheel performance in one ambient gravity based on tests in a different ambient gravity. We confirm this using DEM simulations, which show that scaling relations are satisfied over an array of driving modes even when gravity differs between scaled tests.
△ Less
Submitted 18 March, 2017; v1 submitted 8 April, 2016;
originally announced April 2016.
-
Field and temperature scaling of the critical current density in commercial REBCO coated conductors
Authors:
Carmine Senatore,
Christian Barth,
Marco Bonura,
Miloslav Kulich,
Giorgio Mondonico
Abstract:
Scaling relations describing the electromagnetic behaviour of coated conductors (CCs) greatly simplify the design of REBCO-based devices. The performance of REBCO CCs is strongly influenced by fabrication route, conductor architecture and materials, and these parameters vary from one manufacturer to the others. In the present work we have examined the critical surface for the current density, Jc(T…
▽ More
Scaling relations describing the electromagnetic behaviour of coated conductors (CCs) greatly simplify the design of REBCO-based devices. The performance of REBCO CCs is strongly influenced by fabrication route, conductor architecture and materials, and these parameters vary from one manufacturer to the others. In the present work we have examined the critical surface for the current density, Jc(T,B,$θ$), of coated conductors from six different manufacturers: American Superconductor Co. (US), Bruker HTS GmbH (Germany), Fujikura Ltd. (Japan), SuNAM Co. Ltd. (Korea), SuperOx ZAO (Russia) and SuperPower Inc. (US). Electrical transport and magnetic measurements were performed at temperatures between 4.2 K and 77 K and in magnetic field up to 19 T. Experiments were conducted at three different orientations of the field with respect to the crystallographic c-axis of the REBCO layer, $θ$ = 0$°$, 45$°$ and 90$°$, in order to probe the angular anisotropy of Jc. In spite of the large variability of CCs performance, we show here that field and temperature dependences of Jc at a given angle can be reproduced over wide ranges using a scaling relation based only on three parameters. Furthermore, we present and validate a new approach combining magnetic and transport measurements for the determination of the scaling parameters with minimal experimental effort.
△ Less
Submitted 7 December, 2015;
originally announced December 2015.
-
Thermal conductivity and stability of commercial MgB$_2$ conductors
Authors:
Marco Bonura,
Carmine Senatore
Abstract:
This paper presents a study of the thermal transport properties of MgB$_2$ tapes differing in architecture, stabilization and constituent materials. The temperature and field dependence of thermal conductivity, $κ(T,B)$, was investigated both along the conductor and in the direction perpendicular to the tape. These data provide fundamental input parameters to describe the 3D heat diffusion process…
▽ More
This paper presents a study of the thermal transport properties of MgB$_2$ tapes differing in architecture, stabilization and constituent materials. The temperature and field dependence of thermal conductivity, $κ(T,B)$, was investigated both along the conductor and in the direction perpendicular to the tape. These data provide fundamental input parameters to describe the 3D heat diffusion process in a winding. Thermal transport properties - even in field - are typically deduced using semi-empirical formulas based on the residual resistivity ratio of the stabilizer measured in absence of magnetic field. The accuracy of these procedures was evaluated comparing the calculated $κ$ values with the measured ones. Based on the experimental thermal conduction properties $κ(T,B)$ and critical current surface $J_C(T,B)$ we determined the dependence of minimum quench energy and normal zone propagation velocity on the operating parameters of the conductor. The correlation between thermal properties and tape layout allowed us to provide information on how to optimize the thermal stability of MgB$_2$ conductors.
△ Less
Submitted 28 September, 2015;
originally announced September 2015.
-
Electro-mechanical properties of REBCO coated conductors from various industrial manufacturers at 77 K, self-field and 4.2 K, 19 T
Authors:
Christian Barth,
Giorgio Mondonico,
Carmine Senatore
Abstract:
Rare-earth-barium-copper-oxide (REBCO) tapes are now available from several industrial manufacturers and are very promising conductors in high field applications. Due to diverging materials and deposition processes, these manufacturers' tapes can be expected to differ in their electro-mechanical and mechanical properties. For magnets designers, these are together with the conductors' in-field crit…
▽ More
Rare-earth-barium-copper-oxide (REBCO) tapes are now available from several industrial manufacturers and are very promising conductors in high field applications. Due to diverging materials and deposition processes, these manufacturers' tapes can be expected to differ in their electro-mechanical and mechanical properties. For magnets designers, these are together with the conductors' in-field critical current performance of the highest importance in choosing a suitable conductor. In this work, the strain and stress dependence of the current carrying capabilities as well as the stress and strain correlation are investigated for commercial coated conductors from Bruker HTS, Fujikura, SuNAM, SuperOx and SuperPower at 77 K, self-field and 4.2 K, 19 T.
△ Less
Submitted 24 February, 2015;
originally announced February 2015.
-
Transverse Thermal Conductivity of REBCO Coated Conductors
Authors:
Marco Bonura,
Carmine Senatore
Abstract:
REBCO coated conductors (CCs) have the potential to widen considerably the application areas of superconductivity. Quench protection of REBCO-based devices represents one of the major obstacles to this expansion. Thermal conductivity data are mandatory ingredients for quench simulation studies. In particular, the transverse thermal conductivity ($κ_T$) of the CC plays a key role in case of quenche…
▽ More
REBCO coated conductors (CCs) have the potential to widen considerably the application areas of superconductivity. Quench protection of REBCO-based devices represents one of the major obstacles to this expansion. Thermal conductivity data are mandatory ingredients for quench simulation studies. In particular, the transverse thermal conductivity ($κ_T$) of the CC plays a key role in case of quenches in superconducting magnets. In the present work, we report $κ_T$ of thermally stabilized REBCO CCs produced by different manufacturers. We have measured $κ_T$ on single CCs rather than on stacks of soldered tapes, this excludes spurious contributions in the measurements. We have found that the presence of the stabilizer at the tape edges in Cu-electroplated CCs increases the overall $κ_T$. In the absence of this effect, the overall thermal resistance is dominated by the substrate.
△ Less
Submitted 3 December, 2014;
originally announced December 2014.
-
High-field thermal transport properties of REBCO coated conductors
Authors:
Marco Bonura,
Carmine Senatore
Abstract:
The use of REBCO coated conductors is envisaged for many applications, extending from power cables to high-field magnets. Whatever the case, thermal properties of REBCO tapes play a key role for the stability of superconducting devices. In this work, we present the first study on the longitudinal thermal conductivity ($κ$) of REBCO coated conductors in magnetic fields up to 19 T applied both paral…
▽ More
The use of REBCO coated conductors is envisaged for many applications, extending from power cables to high-field magnets. Whatever the case, thermal properties of REBCO tapes play a key role for the stability of superconducting devices. In this work, we present the first study on the longitudinal thermal conductivity ($κ$) of REBCO coated conductors in magnetic fields up to 19 T applied both parallelly and perpendicularly to the thermal-current direction. Copper-stabilized tapes from six industrial manufacturers have been investigated. We show that zero-field $κ$ of coated conductors can be calculated with an accuracy of $\pm 15%$ from the residual resistivity ratio of the stabilizer and the Cu/non-Cu ratio. Measurements performed at high fields have allowed us to evaluate the consistency of the procedures generally used for estimating in-field $κ$ in the framework of the Wiedemann-Franz law from an electrical characterization of the materials. In-field data are intended to provide primary ingredients for the thermal stability analysis of high-temperature superconductor-based magnets.
△ Less
Submitted 3 December, 2014;
originally announced December 2014.
-
Formation and upper critical fields of the two distinct A15 phases in the subelements of Powder-In-Tube Nb3Sn wires
Authors:
Carmine Senatore,
Rene Flukiger
Abstract:
It is well known that the A15 layer in the subelements of a Powder-In-Tube (PIT) Nb3Sn wire exhibits two different grain morphologies: a region with fine grains (~200 nm in size) representing about 60% of the total A15 area and one with large grains (1-2 μm in size). By means of high field specific heat and magnetization measurements we have shown that these two A15 phases correspond to two distin…
▽ More
It is well known that the A15 layer in the subelements of a Powder-In-Tube (PIT) Nb3Sn wire exhibits two different grain morphologies: a region with fine grains (~200 nm in size) representing about 60% of the total A15 area and one with large grains (1-2 μm in size). By means of high field specific heat and magnetization measurements we have shown that these two A15 phases correspond to two distinctly different Tc distributions, the large grains region exhibiting a higher Tc and a lower Bc2, the fine grains region a lower Tc and a higher Bc2. We report here the values of the superconducting parameters (Tc, Bc2) of the two A15 phases, as determined from an original model to fit the experimental Tc distribution. After a prolonged reaction treatment (625°C/320h), an increase of the fine grain region was observed at the expenses of the large grain region, the Bc2(0K) value of the former being raised from 28.8 to 31.7 T. These changes explain the marked increase of Jc to 2'700 A/cm2 at 4.2K/12T, the highest value measured so far in PIT wires.
△ Less
Submitted 22 January, 2013;
originally announced January 2013.
-
Thermal Conductivity of Industrial Nb3Sn Wires Fabricated by Various Techniques
Authors:
Marco Bonura,
Carmine Senatore
Abstract:
We have developed a new experimental setup specifically designed for measuring thermal conductivity on technical superconductors in the range of temperatures from 3 to 330 K in magnetic fields up to 21 T. Three Nb3Sn wires, produced by the powder in tube technique, the bronze route and the internal tin restacked rod process, respectively, have been investigated. We show that, due to the complexity…
▽ More
We have developed a new experimental setup specifically designed for measuring thermal conductivity on technical superconductors in the range of temperatures from 3 to 330 K in magnetic fields up to 21 T. Three Nb3Sn wires, produced by the powder in tube technique, the bronze route and the internal tin restacked rod process, respectively, have been investigated. We show that, due to the complexity of the architecture of these wires, direct measurement of thermal conductivity is required for a correct estimation of thermal stability in superconducting magnets.
△ Less
Submitted 12 December, 2012;
originally announced December 2012.
-
Temperature and time scaling of the peak-effect vortex configuration in FeTe$_{0.7}$Se$_{0.3}$
Authors:
Marco Bonura,
Enrico Giannini,
Romain Viennois,
Carmine Senatore
Abstract:
An extensive study of the magnetic properties of FeTe$_{0.7}$Se$_{0.3}$ crystals in the superconducting state is presented. We show that weak collective pinning, originating from spatial variations of the charge carrier mean free path ($δl$ pinning), rules in this superconductor. Our results are compatible with the nanoscale phase separation observed on this compound and indicate that in spite of…
▽ More
An extensive study of the magnetic properties of FeTe$_{0.7}$Se$_{0.3}$ crystals in the superconducting state is presented. We show that weak collective pinning, originating from spatial variations of the charge carrier mean free path ($δl$ pinning), rules in this superconductor. Our results are compatible with the nanoscale phase separation observed on this compound and indicate that in spite of the chemical inhomogeneity spatial fluctuations of the critical temperature are not important for pinning. A power law dependence of the magnetization vs time, generally interpreted as signature of single vortex creep regime, is observed in magnetic fields up to $8 ~ T$. For magnetic fields applied along the c axis of the crystal the magnetization curves exhibit a clear peak effect whose position shifts when varying the temperature, following the same dependence as observed in YBa$_2$Cu$_3$O$_{7-δ}$. The time and temperature dependence of the peak position has been investigated. We observe that the occurrence of the peak at a given magnetic field determines a specific vortex configuration that is independent on the temperature. This result indicates that the influence of the temperature on the vortex-vortex and vortex-defect interactions leading to the peak effect in FeTe$_{0.7}$Se$_{0.3}$ is negligible in the explored range of temperatures.
△ Less
Submitted 26 April, 2012;
originally announced April 2012.
-
Vortex phase diagram and temperature-dependent second-peak effect in overdoped Bi$_{2}$Sr$_{2}$CuO$_{6 + δ}$ crystals
Authors:
Alexandre Piriou,
Enrico Giannini,
Yanina Fasano,
Carmine Senatore,
Øystein Fischer
Abstract:
We study the vortex phase diagram of the single-layer Bi2Sr2CuO6+d (Bi2201) superconductor by means of bulk magnetization measurements on high-quality oxygen-overdoped crystals. In striking contrast with the results found in the moderately-doped two and three-layer Bi-based cuprates, Bi2201 exhibits a strong temperature-dependent second-peak effect. By means of measurements of the in and out-of-pl…
▽ More
We study the vortex phase diagram of the single-layer Bi2Sr2CuO6+d (Bi2201) superconductor by means of bulk magnetization measurements on high-quality oxygen-overdoped crystals. In striking contrast with the results found in the moderately-doped two and three-layer Bi-based cuprates, Bi2201 exhibits a strong temperature-dependent second-peak effect. By means of measurements of the in and out-of-plane first-penetration field we provide direct evidence that this phenomenon is mainly associated to an increase of the electromagnetic anisotropy on warming. The effect of oxygen-do** d on the vortex phase diagram results in both the irreversibility and second-peak lines shifting to higher temperatures and fields. This enhanced stability of the Bragg glass phase suggests that the interlayer coupling between Cu-O layers increases with d. In addition, we found that the critical temperature follows the parabolic relation with the number of holes per Cu-O plane that holds for most single and two-layer cuprates.
△ Less
Submitted 7 April, 2010;
originally announced April 2010.
-
BiOCuS: A new superconducting compound with oxypnictide - related structure
Authors:
A. Ubaldini,
E. Giannini,
C. Senatore,
D. van de Marel
Abstract:
The discovery of about 50 K superconductivity in the tetragonal Fe-based pnictides has stimulated the search for superconductivity in a wide class of materials with similar structure. Copper forms compounds isostructural to LaOFeAs. Single phase BiOCuS can be prepared by a solid state reaction at temperature lower than 500 C from a mixture of Bi2O3, Bi2S3 and Cu2S. The samples have been characte…
▽ More
The discovery of about 50 K superconductivity in the tetragonal Fe-based pnictides has stimulated the search for superconductivity in a wide class of materials with similar structure. Copper forms compounds isostructural to LaOFeAs. Single phase BiOCuS can be prepared by a solid state reaction at temperature lower than 500 C from a mixture of Bi2O3, Bi2S3 and Cu2S. The samples have been characterized by means of EDX analysis, X-ray diffraction, magnetic and electrical measurements. The cell parameters are a = 3.8708 A, c = 8.565 A. Charge carrier do** can be realized either by F substitutions for O, or by Cu off-stoichiometry. The latter do** route leads to the occurrence of superconductivity below Tc = 5.8 K.
△ Less
Submitted 4 December, 2009; v1 submitted 27 November, 2009;
originally announced November 2009.
-
Real-space vortex glass imaging and the vortex phase diagram of SnMo6S8
Authors:
A. P. Petrovic,
Y. Fasano,
R. Lortz,
C. Senatore,
A. Demuer,
A. B. Antunes,
A. Paré,
D. Salloum,
P. Gougeon,
M. Potel,
Ø. Fischer
Abstract:
Using scanning tunnelling microscopy at 400mK, we have obtained maps of around 100 vortices in SnMo6S8 from 2 - 9T. The orientational and positional disorder at 5 and 9T show that these are the first large-scale images of a vortex glass. At higher temperature a magnetisation peak effect is observed, whose upper boundary coincides with a lambda anomaly in the specific heat. Our data favour a kine…
▽ More
Using scanning tunnelling microscopy at 400mK, we have obtained maps of around 100 vortices in SnMo6S8 from 2 - 9T. The orientational and positional disorder at 5 and 9T show that these are the first large-scale images of a vortex glass. At higher temperature a magnetisation peak effect is observed, whose upper boundary coincides with a lambda anomaly in the specific heat. Our data favour a kinetic glass description of the vortex melting transition, indicating that vortex topological disorder persists at fields and temperatures far below the peak effect in low-Tc superconductors.
△ Less
Submitted 13 March, 2009;
originally announced March 2009.
-
Strong enhancement of Jc in binary and alloyed in-situ MgB2 wires by a new approach: Cold high pressure densification
Authors:
R. Flukiger,
M. S. A. Hossain,
C. Senatore
Abstract:
Cold high pressure densification (CHPD) is presented as a new way to substantially enhance the critical current density of in situ MgB2 wires at 4.2 and 20 K at fields between 5 and 14 T. The results on two binary MgB2 wires and an alloyed wire with 10 wt.% B4C are presented The strongest enhancement was measured at 20K, where cold densification at 1.85 GPa on a binary Fe/MgB2 wire raised both J…
▽ More
Cold high pressure densification (CHPD) is presented as a new way to substantially enhance the critical current density of in situ MgB2 wires at 4.2 and 20 K at fields between 5 and 14 T. The results on two binary MgB2 wires and an alloyed wire with 10 wt.% B4C are presented The strongest enhancement was measured at 20K, where cold densification at 1.85 GPa on a binary Fe/MgB2 wire raised both Jcpara and Jcperp by more than 300% at 5T, while Birr was enhanced by 0.7 T. At 4.2K, the enhancement of Jc was smaller, but still reached 53% at 10 T. After applying pressures up to 6.5 GPa, the mass density dm of the unreacted (B+Mg) mixture inside the filaments reached 96% of the theoretical density. After reaction under atmospheric pressure, this corresponds to a highest mass density df in the MgB2 filaments of 73%. After reaction, the electrical resistance of wires submitted to cold densification was found to decrease, reflecting an improved connectivity. A quantitative correlation between filament mass density and the physical properties was established. Monofilamentary rectangular wires with aspect ratios a/b < 1.25 based on low energy ball milled powders exhibited very low anisotropy ratios, Gamma = Jcpara/Jcperp being < 1.4 at 4.2 K and 10T. The present results can be generalized to alloyed MgB2 wires, as demonstrated on a wire with B4C additives. Based on the present data, it follows that cold densification has the potential of further improving the highest Jcpara and Jcperp values reported so far for in situ MgB2 tapes and wires with SiC and C additives. Investigations are under work in our laboratory to determine whether the densification method CHPD can be applied to longer wire or tape lengths.
△ Less
Submitted 28 January, 2009;
originally announced January 2009.
-
Far-infrared probe of superconductivity in SmO$_{1-x}$F$_{x}$FeAs}
Authors:
S. I. Mirzaei,
V. Guritanu,
A. B. Kuzmenko,
C. Senatore,
D. van der Marel,
G. Wu,
R. H. Liu,
X. H. Chen
Abstract:
We report far-infrared reflectance measurements on polycrystalline superconducting samples of SmO$_{1-x}$F$_{x}$FeAs ($x$ = 0.12, 0.15 and 0.2). We clearly observe superconductivity induced changes of reflectivity in a broad range of energies, which resembles earlier optical measurements on high $T_{c}$ cuprates. The superconducting-to-normal reflectivity ratio $R_{s}/R_{n}$ grows for the photon…
▽ More
We report far-infrared reflectance measurements on polycrystalline superconducting samples of SmO$_{1-x}$F$_{x}$FeAs ($x$ = 0.12, 0.15 and 0.2). We clearly observe superconductivity induced changes of reflectivity in a broad range of energies, which resembles earlier optical measurements on high $T_{c}$ cuprates. The superconducting-to-normal reflectivity ratio $R_{s}/R_{n}$ grows for the photon energies below 18 meV and shows a complicated structure due to the presence of a strong infrared-active phonon at about 10 meV.
△ Less
Submitted 13 June, 2008;
originally announced June 2008.
-
Upper critical fields well above 100 T for the superconductor SmFeAsO$_{0.85}$F$_{0.15}$ with T$_c$ = 46 K
Authors:
C. Senatore,
M. Cantoni,
G. Wu,
R. H. Liu,
X. H. Chen,
R. Flukiger
Abstract:
We report specific heat measurements at magnetic fields up to 20 T on the recently discovered superconductor SmFeAsO$_{0.85}$F$_{0.15}$. The B-T diagram of a polycrystalline SmFeAsO$_{0.85}$F$_{0.15}$ sample with T$_c$ = 46 K was investigated. The temperature dependence of B$_{c2}$ was extracted from the specific heat curves, the corresponding B$_{c2}$(T = 0) value derived from the Werthamer-Hel…
▽ More
We report specific heat measurements at magnetic fields up to 20 T on the recently discovered superconductor SmFeAsO$_{0.85}$F$_{0.15}$. The B-T diagram of a polycrystalline SmFeAsO$_{0.85}$F$_{0.15}$ sample with T$_c$ = 46 K was investigated. The temperature dependence of B$_{c2}$ was extracted from the specific heat curves, the corresponding B$_{c2}$(T = 0) value derived from the Werthamer-Helfand-Hohenberg formula being 150 T. Based on magnetization measurements up to 9 T, a first estimation of the field dependence of the inductive critical current J$_c$ is given. Evidence for granularity is found. The presence of a peak effect is reported, suggesting a crossover in the vortex dynamics, in analogy to the behaviour observed in high T$_c$ cuprates.
△ Less
Submitted 31 July, 2008; v1 submitted 15 May, 2008;
originally announced May 2008.
-
Mechanism of enhancement of electromagnetic properties of MgB2 by nano-SiC do**
Authors:
S. X. Dou,
O. Shcherbakova,
W. K. Yeoh,
J. H. Kim,
S. Soltanian,
X. L. Wang,
C. Senatore,
R. Flukiger,
M. Dhalle,
O. Husnjak,
E. Babic
Abstract:
A comparative study of pure, SiC, and C doped MgB2 wires has revealed that the SiC do** allowed C substitution and MgB2 formation to take place simultaneously at low temperatures. C substitution enhances Hc2, while the defects, small grain size and nanoinclusions induced by C incorporation and low temperature processing are responsible for the improvement in Jc. The irreversibility field (Hirr…
▽ More
A comparative study of pure, SiC, and C doped MgB2 wires has revealed that the SiC do** allowed C substitution and MgB2 formation to take place simultaneously at low temperatures. C substitution enhances Hc2, while the defects, small grain size and nanoinclusions induced by C incorporation and low temperature processing are responsible for the improvement in Jc. The irreversibility field (Hirr) for the SiC doped sample reached the benchmarking value of 10 T at 20 K, exceeding that of NbTi at 4.2 K. This dual reaction model also enables us to predict desirable dopants for enhancing the performance properties of MgB2.
△ Less
Submitted 1 March, 2007; v1 submitted 16 January, 2007;
originally announced January 2007.
-
Simultaneous Addition of B4C + SiC to MgB2 Wires and Consequences for Jc and Birr
Authors:
Rene Fluekiger,
Paola Lezza,
Marco Cesaretti,
Carmine Senatore,
Roman Gladyshevskii
Abstract:
The simultaneous addition of various Carbon based additives (in the present case B4C + SiC) to Mg and B powders has been introduced as a new concept in view of enhancing the superconducting parameters Bc2, Birr and Jc values of in situ Fe/MgB2 wires. A series of Fe sheathed monofilamentary wires of 1.1 mm diameter with a MgB2 core of 600 microm diameter was prepared with various B4C:SiC ratios,…
▽ More
The simultaneous addition of various Carbon based additives (in the present case B4C + SiC) to Mg and B powders has been introduced as a new concept in view of enhancing the superconducting parameters Bc2, Birr and Jc values of in situ Fe/MgB2 wires. A series of Fe sheathed monofilamentary wires of 1.1 mm diameter with a MgB2 core of 600 microm diameter was prepared with various B4C:SiC ratios, the relation being 2.5:7.5, 5:5, 7.5:2.5 and 7.5:7.5 (values in wt. %). After reaction of 1 hour at 760 C, the wire containing 7.5 wt.% B4C and 2.5 wt.% SiC powders exhibited a Jc value of 1x104 A/cm2 at 11.3 T and 4.2 K. Although only 2.5 wt.% SiC were added, these values are considerably above those of ternary wires with B4C additions, where the same Jc value is obtained at 10T. The slope Jc vs. B for the B4C + SiC wires is steeper than for SiC additives, the Jc values at 4.2 K being superior at fields below 9 T. The lattice parameters a of the B4C + SiC added wires exhibit lower values than ternary wires with the same nominal C content, suggesting a higher C content in the MgB2 phase. The disorder in the MgB2 structure has been characterized as a partial substitution of B by Carbon. A reduction of the domain sizes in the c direction as well as in-plane to 250 Angstrom and 124 Angstrom has been determined from the FWHM and the breath values of the (110) and (002) peaks. With the simultaneous introduction of B4C + SiC, a strong improvement of Jc and Birr has been obtained with respect to B4C additions. A further enhancement of Jc is expected when using different combinations of additives with and without Carbon, aiming for a further raise of Jc in wires with multiple additives, as a result of the combination of different mechanisms.
△ Less
Submitted 29 August, 2006;
originally announced August 2006.
-
Improved critical current densities in B4C doped MgB2 based wires
Authors:
P. Lezza,
C. Senatore,
R. Flukiger
Abstract:
An improvement of the transport critical current density, Jc, of MgB2 wires was obtained after addition of 10 wt.% B4C powders, after reaction at 800 C: Jc values of 1.10^4 A/cm2 at 4.2 K and 9T were obtained for wires of 1.11 mm diameter in a Fe matrix. The starting mixture of Mg and B was doped with sub-micrometric B4C, the ratio being Mg : B : B4C = 1: 2 : 0.08, corresponding to 10 wt.% B4C.…
▽ More
An improvement of the transport critical current density, Jc, of MgB2 wires was obtained after addition of 10 wt.% B4C powders, after reaction at 800 C: Jc values of 1.10^4 A/cm2 at 4.2 K and 9T were obtained for wires of 1.11 mm diameter in a Fe matrix. The starting mixture of Mg and B was doped with sub-micrometric B4C, the ratio being Mg : B : B4C = 1: 2 : 0.08, corresponding to 10 wt.% B4C. For T > 800 C, a decrease of Jc was found, due to the reaction with the Fe sheath. In order to investigate the origin of the improvement of the transport properties for heat treatments up to 800 C, X-ray diffraction measurements were performed. A decrease of the lattice constant a from 0.30854 nm to 0.30797 nm was found, thus suggesting an effect of the substitution of Carbon on the properties of the wires. A comparison with the literature data shows that the addition of B4C powders leads to the second highest improvement of Jc reported so far after SiC, thus constituting an alternative for future applications.
△ Less
Submitted 4 July, 2006;
originally announced July 2006.
-
Magnetic relaxation of type II superconductors in a mixed state of entrapped and shielded flux
Authors:
D. Zola,
M. Polichetti,
C. Senatore,
S. Pace
Abstract:
The magnetic relaxation has been investigated in type II superconductors when the initial magnetic state is realized with entrapped and shielded flux (ESF) contemporarily. This flux state is produced by an inversion in the magnetic field ramp rate due to for example a magnetic field overshoot. The investigation has been faced both numerically and by measuring the magnetic relaxation in BSCCO tap…
▽ More
The magnetic relaxation has been investigated in type II superconductors when the initial magnetic state is realized with entrapped and shielded flux (ESF) contemporarily. This flux state is produced by an inversion in the magnetic field ramp rate due to for example a magnetic field overshoot. The investigation has been faced both numerically and by measuring the magnetic relaxation in BSCCO tapes. Numerical computations have been performed in the case of an infinite thick strip and of an infinite slab, showing a quickly relaxing magnetization in the first seconds. As verified experimentally, the effects of the overshoot cannot be neglected simply by cutting the first 10-100 seconds in the magnetic relaxation. On the other hand, at very long times, the magnetic states relax toward those corresponding to field profiles with only shielded flux or only entrapped flux, depending on the amplitude of the field change with respect to the full penetration field of the considered superconducting samples. In addition, we have performed numerical simulations in order to reproduce the relaxation curves measured on the BSCCO(2223) tapes; this allowed us to interpret correctly also the first seconds of the $M(t)$ curves.
△ Less
Submitted 2 August, 2004;
originally announced August 2004.
-
Harmonics of the AC susceptibility as probes to differentiate the various creep models
Authors:
M. G. Adesso,
C. Senatore,
M. Polichetti,
S. Pace
Abstract:
We measured the temperature dependence of the 1st and the 3rd harmonics of the AC magnetic susceptibility on some type II superconducting samples at different AC field amplitudes, hAC. In order to interpret the measurements, we computed the harmonics of the AC susceptibility as function of the temperature T, by integrating the non-linear diffusion equation for the magnetic field with different c…
▽ More
We measured the temperature dependence of the 1st and the 3rd harmonics of the AC magnetic susceptibility on some type II superconducting samples at different AC field amplitudes, hAC. In order to interpret the measurements, we computed the harmonics of the AC susceptibility as function of the temperature T, by integrating the non-linear diffusion equation for the magnetic field with different creep models, namely the vortex glass-collective creep (single-vortex, small bundle and large bundle) and Kim-Anderson model. We also computed them by using a non-linear phenomenological I-V characteristics, including a power law dependence of the pinning potential on hAC. Our experimental results were compared with the numerically computed ones, by the analysis of the Cole-Cole plots. This method results more sensitive than the separate component analysis, giving the possibility to obtain detailed information about the contribution of the flux dynamic regimes in the magnetic response of the analysed samples.
△ Less
Submitted 13 September, 2003;
originally announced September 2003.
-
Third Harmonic Susceptibility and the Irreversibility Line of Fe/MgB2 Tapes
Authors:
C. Senatore,
N. Clayton,
P. Lezza,
M. Polichetti,
S. Pace,
R. Flukiger
Abstract:
We report a study of the pinning properties of Fe/MgB2 tapes performed by means of ac magnetic susceptibility measurements. In particular, the third harmonic response has been measured as a function of the dc magnetic field up to 9 T, at different temperatures, for various frequencies and amplitudes of the ac field. The irreversibility line has been determined using the third harmonic onset crit…
▽ More
We report a study of the pinning properties of Fe/MgB2 tapes performed by means of ac magnetic susceptibility measurements. In particular, the third harmonic response has been measured as a function of the dc magnetic field up to 9 T, at different temperatures, for various frequencies and amplitudes of the ac field. The irreversibility line has been determined using the third harmonic onset criterion for samples made with different ball-milled MgB2 powders. The study of the harmonic response allows us to probe the nature of the vortex pinning and to analyse its influence on the enhancement of the irreversibility field in strongly ball-milled samples. We have also investigated the dynamical regimes governing the vortex motion in the tapes by comparing the experimental curves with numerical simulations of the non-linear diffusion equation for the magnetic field.
△ Less
Submitted 11 September, 2003;
originally announced September 2003.
-
Transport Properties and Exponential n-values of Fe/MgB2 Tapes With Various MgB2 Particle Sizes
Authors:
P. Lezza,
V. Abacherli,
N. Clayton,
C. Senatore,
D. Uglietti,
H. L. Suo,
R. Flukiger
Abstract:
Fe/MgB2 tapes have been prepared starting with pre-reacted binary MgB2 powders. As shown by resistive and inductive measurements, the reduction of particle size to a few microns by ball milling has little influence on Bc2, while the superconducting properties of the individual MgB2 grains are essentially unchanged. Reducing the particle size causes an enhancement of Birr from 14 to 16 T, while J…
▽ More
Fe/MgB2 tapes have been prepared starting with pre-reacted binary MgB2 powders. As shown by resistive and inductive measurements, the reduction of particle size to a few microns by ball milling has little influence on Bc2, while the superconducting properties of the individual MgB2 grains are essentially unchanged. Reducing the particle size causes an enhancement of Birr from 14 to 16 T, while Jc has considerably increased at high fields, its slope Jc(B) being reduced. At 4.2K, values of 5.3*10^4 and 1.2*10^3 A/cm^2 were measured at 3.5 and 10 T, respectively, suggesting a dominant role of the conditions at the grain interfaces. A systematic variation of these conditions at the interfaces is undertaken in order to determine the limit of transport properties for Fe/MgB2 tapes. The addition of 5% Mg to MgB2 powder was found to affect neither Jc nor Bc2. For the tapes with the highest Jc values, very high exponential n factors were measured: n = 148, 89 and 17 at 3.5, 5 and 10T, respectively and measurements of critical current versus applied strain have been performed. The mechanism leading to high transport critical current densities of filamentary Fe/MgB2 tapes based on MgB2 particles is discussed.
△ Less
Submitted 16 July, 2003;
originally announced July 2003.
-
Detection of the Vortex Dynamic Regimes in MgB2 by Third Harmonic AC Susceptibility Measurements
Authors:
C. Senatore,
M. Polichetti,
N. Clayton,
R. Flukiger,
S. Pace
Abstract:
In a type-II superconductor the generation of higher harmonics in the magnetic response to an alternating magnetic field is a consequence of the non-linearity in the I-V relationship. The shape of the current-voltage (I-V) curve is determined by the current dependence of the thermal activation energy U(J) and is thus related to the dynamical regimes governing the vortex motion. In order to inves…
▽ More
In a type-II superconductor the generation of higher harmonics in the magnetic response to an alternating magnetic field is a consequence of the non-linearity in the I-V relationship. The shape of the current-voltage (I-V) curve is determined by the current dependence of the thermal activation energy U(J) and is thus related to the dynamical regimes governing the vortex motion. In order to investigate the vortex dynamics in MgB2 bulk superconductors we have studied the fundamental (chi1) and third (chi3) harmonics of the ac magnetic susceptibility. Measurements have been performed as a function of the temperature and the dc magnetic field, up to 9 T, for various frequencies and amplitudes of the ac field. We show that the analysis of the behaviour in frequency of chi3(T) and chi3(B) curves can provide clear information about the non-linearity in different regions of the I-V characteristic. By comparing the experimental curves with numerical simulations of the non-linear diffusion equation for the magnetic field we are able to resolve the crossover between a dissipative regime governed by flux creep and one dominated by flux flow phenomena.
△ Less
Submitted 22 May, 2003;
originally announced May 2003.
-
Vortex dynamics and pinning properties analysis of MgB2 bulk samples by ac susceptibility measurements
Authors:
C. Senatore,
M. Polichetti,
D. Zola,
T. Di Matteo,
G. Giunchi,
S. Pace
Abstract:
The flux lines dynamics have been investigated on MgB2 bulk superconductors obtained by reactive liquid infiltration by measuring the ac magnetic susceptibility. The fundamental and third harmonics have been studied as a function of temperature, dc magnetic field, ac field amplitude and frequency. In order to determine the dynamical regimes governing the vortex motion, the experimental results h…
▽ More
The flux lines dynamics have been investigated on MgB2 bulk superconductors obtained by reactive liquid infiltration by measuring the ac magnetic susceptibility. The fundamental and third harmonics have been studied as a function of temperature, dc magnetic field, ac field amplitude and frequency. In order to determine the dynamical regimes governing the vortex motion, the experimental results have been compared with susceptibility curves obtained by numerical calculations of the non-linear diffusion equation for the magnetic field. The frequency behaviour of the third harmonic response, that cannot be explained by frequency dependent critical state models, has been related to the current dependence of the flux creep activation energy U(J) in the diffusion coefficient. In this way we have shown that the measured curves are correctly interpreted within the framework of a vortex glass description.
△ Less
Submitted 24 July, 2002;
originally announced July 2002.