Using local GND density to study SCC initiation
Authors:
Naganand Saravanan,
Phani S Karamched,
Junliang Liu,
Claire Rainasse,
Fabio Scenini,
Sergio Lozano-Perez
Abstract:
In this work, strain and geometric necessary dislocations (GNDs) have been mapped with nm-resolution around grain boundaries affected by stress corrosion cracking (SCC) or intergranular oxidation with the aim of clarifying which local conditions trigger SCC initiation.
In this work, strain and geometric necessary dislocations (GNDs) have been mapped with nm-resolution around grain boundaries affected by stress corrosion cracking (SCC) or intergranular oxidation with the aim of clarifying which local conditions trigger SCC initiation.
△ Less
Submitted 25 June, 2020; v1 submitted 4 May, 2020;
originally announced May 2020.
The Interaction of Galling and Oxidation in 316L Stainless Steel
Authors:
Samuel R. Rogers,
David Bowden,
Rahul Unnikrishnan,
Fabio Scenini,
Michael Preuss,
David Stewart,
Daniele Dini,
David Dye
Abstract:
The galling behaviour of 316L stainless steel was investigated in both the unoxidised and oxidised states, after exposure in simulated PWR water for 850 hours. Galling testing was performed according to ASTM G196 in ambient conditions. 316L was found to gall by the wedge growth and flow mechanism in both conditions. This resulted in folds ahead of the prow and adhesive junction, forming a heavily…
▽ More
The galling behaviour of 316L stainless steel was investigated in both the unoxidised and oxidised states, after exposure in simulated PWR water for 850 hours. Galling testing was performed according to ASTM G196 in ambient conditions. 316L was found to gall by the wedge growth and flow mechanism in both conditions. This resulted in folds ahead of the prow and adhesive junction, forming a heavily sheared multilayered prow. The galling trough was seen to have failed through successive shear failure during wedge flow. Immediately beneath the surface a highly sheared nanocrystalline layer was seen, termed the tribologically affected zone (TAZ). It was observed that strain-induced martensite formed within the TAZ. Galling damage was quantified using Rt (maximum height - maximum depth) and galling area (the proportion of the sample which is considered galled), and it was shown that both damage measures decreased significantly on the oxidised samples. At an applied normal stress of 4.2 MPa the galled area was 14 % vs. 1.2 % and the Rt was 780 um vs. 26 um for the unoxidised and oxidised sample respectively. This trend was present at higher applied normal stresses, although less prominent. This difference in galling behaviour is likely to be a result of a reduction in adhesion in the case of the oxidised surface.
△ Less
Submitted 11 December, 2019;
originally announced December 2019.