Raman Scattering Investigation of Electron Phonon Coupling in Carbon substituted MgB2
Authors:
T. Sakuntala,
A. Bharathi,
S. K. Deb,
N. Gayathri,
C. S. Sundar,
Y. Hariharan
Abstract:
Room temperature Raman scattering measurements have been carried out on well characterized samples of MgB2-xCx. The Raman line corresponding to the E2g phonon mode shows progressive hardening from 620 cm-1 in pristine MgB2 to 775 cm-1 in the sample with carbon fraction x=0.2. The corresponding line width on the other hand, increases from a value of about 220 cm-1 to 286 cm-1 in samples with x =…
▽ More
Room temperature Raman scattering measurements have been carried out on well characterized samples of MgB2-xCx. The Raman line corresponding to the E2g phonon mode shows progressive hardening from 620 cm-1 in pristine MgB2 to 775 cm-1 in the sample with carbon fraction x=0.2. The corresponding line width on the other hand, increases from a value of about 220 cm-1 to 286 cm-1 in samples with x = 0.1, beyond which it decreases to a value 167 cm-1 for x=0.2. From the average mode frequency and the line width obtained from Raman measurements and taking the values of N(0) obtained from the calculated variation in s hole density of states in MgB2-xCx, the electron phonon coupling strength to the E2g phonon, l2g, is evaluated using Allen’s formula. This remains large for low C fraction, but shows rapid decrease for x > 0.10. Using this value of l2g appropriately weighted, TC is obtained from McMillan’s equation. These values are in good agreement with the experimentally measured TC variation in MgB2-xCx.
△ Less
Submitted 27 April, 2005;
originally announced April 2005.
Raman Studies in MgB2-xCx
Authors:
T. Sakuntala,
S. K. Deb,
A. Bharathi,
S. Jemima Balaselvi,
C. S. Sundar,
Y. Hariharan
Abstract:
Raman scattering measurements have been carried out in MgB2-xCx for x=0.0 -0.30. The broad Raman band around 600cm-1 range, which corresponds to the E2g mode in MgB2 is seen to narrow and reduce in intensity with increasing carbon content. For x>0.15, new set of bands appear at 1200 cm-1 possibly arising from the B-C, E2g modes. The decrease in Tc with carbon substitution seems to correlate with…
▽ More
Raman scattering measurements have been carried out in MgB2-xCx for x=0.0 -0.30. The broad Raman band around 600cm-1 range, which corresponds to the E2g mode in MgB2 is seen to narrow and reduce in intensity with increasing carbon content. For x>0.15, new set of bands appear at 1200 cm-1 possibly arising from the B-C, E2g modes. The decrease in Tc with carbon substitution seems to correlate with this change over.
△ Less
Submitted 17 September, 2003;
originally announced September 2003.