Clathrate formation in the systems Sr-Cu-Ge and {Ba,Sr}-Cu-Ge
Authors:
I. Zeiringer,
A. Grytsiv,
F. Kneidinger,
E. Royanian,
E. Bauer,
G. Giester,
M. Falmbigl,
P. Rogl
Abstract:
In the ternary system Sr-Cu-Ge, a clathrate type-I phase, Sr8Cu5.3Ge40.7 (a = 1.06311(3), exists close to the Zintl limit in a small temperature interval. Sr8Cu5.3Ge40.7 decomposes eutectoidally on cooling at 730°C into (Ge), SrGe2 and tau1-SrCu2-xGe2+x. Phase equilibria at 700°C have been established for the Ge rich part and are characterized by the appearance of only one ternary compound, tau1-S…
▽ More
In the ternary system Sr-Cu-Ge, a clathrate type-I phase, Sr8Cu5.3Ge40.7 (a = 1.06311(3), exists close to the Zintl limit in a small temperature interval. Sr8Cu5.3Ge40.7 decomposes eutectoidally on cooling at 730°C into (Ge), SrGe2 and tau1-SrCu2-xGe2+x. Phase equilibria at 700°C have been established for the Ge rich part and are characterized by the appearance of only one ternary compound, tau1-SrCu2-xGe2+x, which crystallizes with the ThCr2Si2 structure type and forms a homogeneity range up to x=0.4 (a = 0.42850(4), c = 1.0370(1) nm). Additionally, the extent of the clathrate type-I solid solution Ba8-xSrxCuyGe46-y (5.2 < y < 5.4) has been studied at various temperatures. The clathrate type-I crystal structure (space group ) has been proven by X-ray single crystal diffraction on two single crystals with composition Sr8Cu5.3Ge40.7 (a = 1.06368(2) nm) and Ba4.9Sr3.1Cu5.3Ge40.7 (a = 1.06748(2) nm) measured at 300, 200 and 100 K. From the temperature dependency of the lattice parameters and the atomic displacement parameters, the thermal expansion coefficients, the Debye- and Einstein-temperatures and the speed of sound have been determined. From heat capacity measurements of Sr8Cu5.3Ge40.7 at low temperatures, the Sommerfeld coefficient and the Debye temperature have been extracted, whereas from a detailed analysis of these data at higher temperatures, Einstein branches of the phonon dispersion relation have been derived and compared with those obtained from the atomic displacement parameters. Electrical resistivity measurements of Sr8Cu5.3Ge40.7 reveal a rather metallic behaviour in the low temperature range (< 300 K).
△ Less
Submitted 15 February, 2017;
originally announced February 2017.
-
On Ni-Sb-Sn based skutterudites
Authors:
W. Paschinger,
P. F. Rogl,
G. Rogl,
A. Grytsiv,
E. Bauer,
H. Michor,
Ch. Eisenmenger-Sitter,
E. Royanian,
P. R. Heinrich,
M. Zehetbauer,
J. Horky,
S. Puchegger,
M. Reinecker,
G. Giester,
P. Broz,
A. Bismarck
Abstract:
Novel filled skutterudites EpyNi4Sb12-xSnx (Ep = Ba and La) have been prepared by arc melting followed by annealing at 250C, 350C and 450C up to 30 days in sealed quartz vials. A maximum filling level of y = 0.93 and y = 0.65 was achieved for the Ba and La filled skutterudite, respectively. Single-phase samples with the composition Ni4Sb8.2Sn3.8, Ba0.42Ni4Sb8.2Sn3.8 and Ba0.92Ni4Sb6.7Sn5.3 were em…
▽ More
Novel filled skutterudites EpyNi4Sb12-xSnx (Ep = Ba and La) have been prepared by arc melting followed by annealing at 250C, 350C and 450C up to 30 days in sealed quartz vials. A maximum filling level of y = 0.93 and y = 0.65 was achieved for the Ba and La filled skutterudite, respectively. Single-phase samples with the composition Ni4Sb8.2Sn3.8, Ba0.42Ni4Sb8.2Sn3.8 and Ba0.92Ni4Sb6.7Sn5.3 were employed for measurements of the physical properties i.e. temperature dependent electrical resistivity, Seebeck coefficient and thermal conductivity.
Resistivity data showed a crossover from metallic to semiconducting behaviour. The corresponding gap width was extracted from maxima in the Seebeck coefficient data as a function of temperature. Temperature dependent single crystal X-ray structure analyses (at 100 K, 200 K and 300 K) revealed the thermal expansion coefficients, Einstein and Debye temperatures for two selected samples Ba0.73Ni4Sb8.1Sn3.9 and Ba0.95Ni4Sb6.1Sn5.9. These data compare well with Debye temperatures from measurements of specific heat (4.4 K < T < 200 K).
Several mechanical properties were measured and evaluated. Thermal expansion coefficients are 11.8.10-6 K-1 for Ni4Sb8.2Sn3.8 to 13.8.10-6 K-1 for Ba0.92Ni4Sb6.7Sn5.3. Room temperature Vicker's hardness values (up to a load of 24.5 mN) vary within the range of 2.6 GPa to 4.7 GPa. Severe plastic deformation (SPD) via high-pressure torsion (HPT) was used to introduce nanostructuring. Physical properties before and after HPT were compared, showing no significant effect on the material's thermoelectric behaviour.
△ Less
Submitted 15 February, 2017;
originally announced February 2017.
-
Unconventional superconductivity in weakly correlated, non-centrosymmetric $\rm{Mo_3Al_2C}$
Authors:
E. Bauer,
G. Rogl,
Xing-Qiu Chen,
R. T. Khan,
H. Michor,
G. Hilscher,
E. Royanian,
K. Kumagai,
D. Z. Li,
Y. Y. Li,
R. Podloucky,
P. Rogl
Abstract:
Electrical resistivity, specific heat and NMR measurements classify non-centrosymmetric $\rm Mo_3Al_2C$ ($β$-Mn type, space group $P4_132$) as a strong-coupled superconductor with $T_c = 9$~K deviating notably from BCS-like behaviour. The absence of a Hebbel-Slichter peak, a power law behaviour of the spin-lattice relaxation rate (from $^{27}$Al NMR), a $T^3$ temperature dependence of the specific…
▽ More
Electrical resistivity, specific heat and NMR measurements classify non-centrosymmetric $\rm Mo_3Al_2C$ ($β$-Mn type, space group $P4_132$) as a strong-coupled superconductor with $T_c = 9$~K deviating notably from BCS-like behaviour. The absence of a Hebbel-Slichter peak, a power law behaviour of the spin-lattice relaxation rate (from $^{27}$Al NMR), a $T^3$ temperature dependence of the specific heat and a pressure enhanced $T_c$ suggest unconventional superconductivity with a nodal structure of the superconducting gap. Relativistic DFT calculations reveal a splitting of degenerate electronic bands due to the asymmetric spin-orbit coupling, favouring a mix of spin-singlet and spin triplet components in the superconducting condensate, in absence of strong correlations among electrons.
△ Less
Submitted 2 July, 2010;
originally announced July 2010.
-
Superconductivity in novel Ge-based skutterudites: {Sr,Ba}Pt_4Ge_{12}
Authors:
E. Bauer,
A. Grytsiv,
Xing-Qiu Chen,
N. Melnychenko-Koblyuk,
G. Hilscher,
H. Kaldarar,
H. Michor,
E. Royanian,
G. Giester,
M. Rotter,
R. Podloucky,
P. Rogl
Abstract:
Combining experiments and ab initio models we report on $\rm SrPt_4Ge_{12}$ and $\rm BaPt_4Ge_{12}$ as members of a novel class of superconducting skutterudites, where Sr or Ba atoms stabilize a framework entirely formed by Ge-atoms. Below $T_c=5.35$ K, and 5.10 K for $\rm BaPt_4Ge_{12}$ and $\rm SrPt_4Ge_{12}$, respectively, electron-phonon coupled superconductivity emerges, ascribed to intrins…
▽ More
Combining experiments and ab initio models we report on $\rm SrPt_4Ge_{12}$ and $\rm BaPt_4Ge_{12}$ as members of a novel class of superconducting skutterudites, where Sr or Ba atoms stabilize a framework entirely formed by Ge-atoms. Below $T_c=5.35$ K, and 5.10 K for $\rm BaPt_4Ge_{12}$ and $\rm SrPt_4Ge_{12}$, respectively, electron-phonon coupled superconductivity emerges, ascribed to intrinsic features of the Pt-Ge framework, where Ge-$p$ states dominate the electronic structure at the Fermi energy.
△ Less
Submitted 3 October, 2007;
originally announced October 2007.