Grain boundary migration in polycrystalline $α$-Fe
Authors:
Zipeng Xu,
Yu-Feng Shen,
S. Kiana Naghibzadeh,
Xiaoyao Peng,
Vivekanand Muralikrishnan,
Siddharth Maddali,
David Menasche,
Amanda R. Krause,
Kaushik Dayal,
Robert M. Suter,
Gregory S. Rohrer
Abstract:
High energy x-ray diffraction microscopy was used to image the microstructure of $α$-Fe before and after a 600 $^\circ$C anneal. These data were used to determine the areas, curvatures, energies, and velocities of approximately 40,000 grain boundaries. The measured grain boundary properties depend on the five macroscopic grain boundary parameters. The velocities are not correlated with the product…
▽ More
High energy x-ray diffraction microscopy was used to image the microstructure of $α$-Fe before and after a 600 $^\circ$C anneal. These data were used to determine the areas, curvatures, energies, and velocities of approximately 40,000 grain boundaries. The measured grain boundary properties depend on the five macroscopic grain boundary parameters. The velocities are not correlated with the product of the mean boundary curvature and grain boundary energy, usually assumed to be the driving force. Boundary migration is made up of area changes (lateral motion) and translation (normal motion) and both contribute to the total migration. Through the lateral motion component of the migration, low energy boundaries tend to expand in area while high energy boundaries shrink, reducing the average energy through grain boundary replacement. The driving force for this process is not related to curvature and might disrupt the expected curvature-velocity relationship.
△ Less
Submitted 18 November, 2023;
originally announced November 2023.
-
Relative Grain Boundary Energies from Triple Junction Geometry: Limitations to Assuming the Herring Condition in Nanocrystalline Thin Films
Authors:
Matthew J. Patrick,
Gregory S. Rohrer,
Ooraphan Chirayutthanasak,
Sutach Ratanaphan,
Eric R. Homer,
Gus L. W. Hart,
Yekaterina Epshteyn,
Katayun Barmak
Abstract:
Grain boundary character distributions (GBCD) are routinely measured from bulk microcrystalline samples by electron backscatter diffraction (EBSD) and serial sectioning can be used to reconstruct relative grain boundary energy distributions (GBED) based on the 3D geometry of triple lines, assuming that the Herring condition of force balance is satisfied. These GBEDs correlate to those predicted fr…
▽ More
Grain boundary character distributions (GBCD) are routinely measured from bulk microcrystalline samples by electron backscatter diffraction (EBSD) and serial sectioning can be used to reconstruct relative grain boundary energy distributions (GBED) based on the 3D geometry of triple lines, assuming that the Herring condition of force balance is satisfied. These GBEDs correlate to those predicted from molecular dynamics (MD); furthermore, the GBCD and GBED are found to be inversely correlated. For nanocrystalline thin films, orientation map** via precession enhanced electron diffraction (PED) has proven effective in measuring the GBCD, but the GBED has not been extracted. Here, the established relative energy extraction technique is adapted to PED data from four sputter deposited samples: a 40 nm-thick tungsten film and a 100 nm aluminum film as-deposited, after 30 and after 150 minutes annealing at 400°C. These films have columnar grain structures, so serial sectioning is not required to determine boundary inclination. Excepting the most energetically anisotropic and highest population boundaries, i.e. aluminum Σ3 boundaries, the relative GBED extracted from these data do not correlate with energies calculated using MD nor do they inversely correlate with the experimentally determined GBCD for either the tungsten or aluminum films. Failure to reproduce predicted energetic trends implies that the conventional Herring equation cannot be applied to determine relative GBEDs and thus geometries at triple junctions in these films are not well described by this condition; additional geometric factors must contribute to determining triple junction geometry and boundary network structure in spatially constrained, polycrystalline materials.
△ Less
Submitted 21 October, 2022; v1 submitted 5 July, 2022;
originally announced July 2022.
-
Comparison of simulated and measured grain volume changes during grain growth
Authors:
Xiaoyao Peng,
Aditi Bhattacharya,
S. Kiana Naghibzadeh,
David Kinderlehrer,
Robert Suter,
Kaushik Dayal,
Gregory S. Rohrer
Abstract:
The three-dimensional microstructure of Ni, observed after five annealing intervals, was compared to simulations of grain growth using the threshold dynamics method with the assumption of capillarity as the only driving force. A grain-by-grain comparison made it possible to identify the sources of differences between the simulation and experiment. The most significant difference was for grains of…
▽ More
The three-dimensional microstructure of Ni, observed after five annealing intervals, was compared to simulations of grain growth using the threshold dynamics method with the assumption of capillarity as the only driving force. A grain-by-grain comparison made it possible to identify the sources of differences between the simulation and experiment. The most significant difference was for grains of the smallest sizes, which the simulation predicted would lose volume and disappear at a greater rate than observed in the experiment. The loss of grains created errors in the numbers of neighbors of the remaining grains, and it was found that errors in the simulated grain volume were correlated to errors in the number of near neighbors. While anisotropic grain boundary properties likely play a role in the differences, the size dependence of the errors suggest that it might be necessary to include a size dependence in the model for grain boundary migration kinetics.
△ Less
Submitted 14 March, 2022;
originally announced March 2022.
-
Preferential Orientation Relationships in Ca$_2$MnO$_4$ Ruddlesden-Popper thin films
Authors:
M. Lacotte,
A. David,
G. S. Rohrer,
P. A. Salvador,
W. Prellier
Abstract:
A high-throughput investigation of local epitaxy (called combinatorial substrate epitaxy) was carried out on Ca$_2$MnO$_4$ Ruddlesden-Popper thin films of six thicknesses (from 20 to 400 nm), all deposited on isostructural polycrystalline Sr$_2$TiO$_4$ substrates. Electron backscatter diffraction revealed grain-over-grain local epitaxial growth for all films, resulting in a single orientation rela…
▽ More
A high-throughput investigation of local epitaxy (called combinatorial substrate epitaxy) was carried out on Ca$_2$MnO$_4$ Ruddlesden-Popper thin films of six thicknesses (from 20 to 400 nm), all deposited on isostructural polycrystalline Sr$_2$TiO$_4$ substrates. Electron backscatter diffraction revealed grain-over-grain local epitaxial growth for all films, resulting in a single orientation relationship ($OR$) for each substrate-film grain pair. Two preferred epitaxial $ORs$ accounted for more than 90 \% of all ORs on 300 different microcrystals, based on analyzing 50 grain pairs for each thickness. The unit cell over unit cell $OR$ ([100][001]$_{film}$ $\parallel$ [100][001]$_{substrate}$, or $OR1$) accounted for approximately 30 \% of each film. The $OR$ that accounted for 60 \% of each film ([100][001]$_{film}$ $\parallel$ [100][010]$_{substrate}$, or $OR2$) corresponds to a rotation from $OR1$ by 90$^{\circ}$ about the a-axis. $OR2$ is strongly favored for substrate orientations in the center of the stereographic triangle, and $OR1$ is observed for orientations very close to (001) or to those near the edge connecting (100) and (110). While $OR1$ should be lower in energy, the majority observation of $OR2$ implies kinetic hindrances decrease the frequency of $OR1$. Persistent grain over grain growth and the absence of variations of the $OR$ frequencies with thickness implies that the growth competition is finished within the first few \si{\nano\meter}, and local epitaxy persists thereafter during growth.
△ Less
Submitted 6 May, 2015;
originally announced May 2015.
-
Growth of Ca$_2$MnO$_4$ Ruddlesden-Popper structured thin films using Combinatorial Substrate Epitaxy
Authors:
M. Lacotte,
A. David,
D. Pravarthana,
C. grygiel,
G. S rohrer,
PA. Salvador,
M. Velasquez,
K. de Kloe,
W. Prellier
Abstract:
The local epitaxial growth of pulsed laser deposited Ca$_2$MnO$_4$ films on polycrystalline spark plasma sintered Sr$_2$TiO$_4$ substrates was investigated to determine phase formation and preferred epitaxial orientation relationships ($ORs$) for isostructural Ruddlesden-Popper (RP) heteroepitaxy, further develo** the high-throughput synthetic approach called Combinatorial Substrate Epitaxy (CSE…
▽ More
The local epitaxial growth of pulsed laser deposited Ca$_2$MnO$_4$ films on polycrystalline spark plasma sintered Sr$_2$TiO$_4$ substrates was investigated to determine phase formation and preferred epitaxial orientation relationships ($ORs$) for isostructural Ruddlesden-Popper (RP) heteroepitaxy, further develo** the high-throughput synthetic approach called Combinatorial Substrate Epitaxy (CSE). Both grazing incidence X-ray diffraction and electron backscatter diffraction (EBSD) patterns of the film and substrate were indexable as single-phase RP-structured compounds. The optimal growth temperature (between 650 $^{\circ}$C and 800 $^{\circ}$C) was found to be 750 $^{\circ}$C using the maximum value of the average image quality (IQ) of the backscattered diffraction patterns. Films grew in a grain-over-grain pattern such that each Ca$_2$MnO$_4$ grain had a single $OR$ with the Sr$_2$TiO$_4$ grain on which it grew. Three primary $ORs$ described 47 out of 49 grain pairs that covered nearly all of RP orientation space. The first $OR$, found for 20 of the 49, was the expected RP unit-cell over RP unit-cell $OR$, expressed as [100][001]$_{film}$||[100][001]$_{sub}$. The other two $ORs$ were essentially rotated from the first by 90$^{\circ}$, with one (observed for 17 of 49 pairs) being rotated about the [100] and the other (observed for 10 of 49 pairs) being rotated about the [110] (and not exactly by 90$^{\circ}$). These results indicate that only a small number of $ORs$ are needed to describe isostructural RP heteroepitaxy and further demonstrate the potential of CSE in the design and growth of a wide range of complex functional oxides.
△ Less
Submitted 8 December, 2014;
originally announced December 2014.