Demonstration of an iron-pnictide bulk superconducting magnet capable of trap** over 1 T
Authors:
J. D. Weiss,
A. Yamamoto,
A. A. Polyanskii,
R. B. Richardson,
D. C. Larbalestier,
E. E. Hellstrom
Abstract:
A trapped field of over 1 T at 5 K and 0.5 T at 20 K has been measured between a stack of magnetized cylinders of bulk polycrystalline Ba0.6K0.4Fe2As2 superconductors 10 mm in diameter and 18 mm in combined thickness. The trapped field showed a low magnetic creep rate (~3% after 24 hours at 5 K), while magneto-optical imaging revealed a trapped field distribution corresponding to uniform macroscop…
▽ More
A trapped field of over 1 T at 5 K and 0.5 T at 20 K has been measured between a stack of magnetized cylinders of bulk polycrystalline Ba0.6K0.4Fe2As2 superconductors 10 mm in diameter and 18 mm in combined thickness. The trapped field showed a low magnetic creep rate (~3% after 24 hours at 5 K), while magneto-optical imaging revealed a trapped field distribution corresponding to uniform macroscopic current loops circulating through the sample. The superconductors were manufactured by hot isostatic pressing of pre-reacted powders using the scalable powder-in-tube technique. A high Vickers hardness of ~3.5 GPa and a reasonable fracture toughness of ~2.35 MPa m0.5 were measured. Given the untextured polycrystalline nature of the cylinders and their large irreversibility field (> 90 T), it is expected that larger bulks could trap fields in excess of 10 T.
△ Less
Submitted 8 October, 2015;
originally announced October 2015.
-
Roles of intrinsic anisotropy and pi-band pairbreaking effects on critical currents in tilted c-axis MgB2 films probed by magneto-optical and transport measurements
Authors:
A. A. Polyanskii,
F. Kametani,
D. Abraimov,
A. Gurevich,
A. Yamamoto,
I. Pallecchi,
M. Putti,
C. Zhuang,
T. Tan,
X. X. Xi
Abstract:
Investigations of MgB2 and Fe-based superconductors in recent years have revealed many unusual effects of multiband superconductivity but manifestations of anisotropic multiband effects in the critical current density Jc have not been addressed experimentally, mostly because of the difficulties to measure Jc along the c-axis. To investigate the effect of very different intrinsic anisotropies of si…
▽ More
Investigations of MgB2 and Fe-based superconductors in recent years have revealed many unusual effects of multiband superconductivity but manifestations of anisotropic multiband effects in the critical current density Jc have not been addressed experimentally, mostly because of the difficulties to measure Jc along the c-axis. To investigate the effect of very different intrinsic anisotropies of sigma and pi electron bands in MgB2 on current transport, we grew epitaxial films with tilted c-axis (THETA ~ 19.5°), which enabled us to measure the components of Jc both along the ab-plane and the c-axis using magneto-optical and transport techniques. These measurements were combined with scanning and transmission electron microscopy, which revealed terraced steps on the surface of the c-axis tilted films. The measured field and temperature dependencies of the anisotropic Jc(H) show that Jc,L parallel to the terraced steps is higher than Jc,T perpendicular to the terraced steps, and Jc of thinner films (50 nm) obtained from transport experiments at 0.1 T reaches ~10% of the depairing current density Jd in the ab plane, while magneto-optical imaging revealed much higher Jc at lower fields. To analyze the experimental data we developed a model of anisotropic vortex pinning which accounts for the observed behavior of Jc in the c-axis tilted films and suggests that the apparent anisotropy of Jc is affected by current pairbreaking effects in the weaker π band. Our results indicate that the out-of-plane current transport mediated by the π band could set the ultimate limit of Jc in MgB2 polycrystals.
△ Less
Submitted 6 December, 2014;
originally announced December 2014.
-
Mechanochemical synthesis of pnictide compounds and superconducting Ba0.6K0.4Fe2As2 bulks with high critical current density
Authors:
J. D. Weiss,
J. Jiang,
A. A. Polyanskii,
E. E. Hellstrom
Abstract:
BaFe2As2 (Ba-122) and (Ba0.6K0.4)Fe2As2 (K-doped Ba-122) powders were successfully synthesized from the elements using a reaction method, which incorporates a mechanochemical reaction using high-impact ball milling. Mechanically-activated, self-sustaining reactions (MSR) were observed while milling the elements together to form these compounds. After the MSR, the Ba-122 phase had formed, the powde…
▽ More
BaFe2As2 (Ba-122) and (Ba0.6K0.4)Fe2As2 (K-doped Ba-122) powders were successfully synthesized from the elements using a reaction method, which incorporates a mechanochemical reaction using high-impact ball milling. Mechanically-activated, self-sustaining reactions (MSR) were observed while milling the elements together to form these compounds. After the MSR, the Ba-122 phase had formed, the powder had an average grain size < 1 μm, and the material was effectively mixed. X-ray diffraction confirmed Ba-122 was the primary phase present after milling. Heat treatment of the K-doped MSR powder at high temperature and pressure yielded dense samples with high phase purity but only granular current flow could be visualized by magneto optical imaging. In contrast, a short, low temperature, heat treatment at ambient pressure resulted in global current flow throughout the bulk sample even though the density was lower and impurity phases were more prevalent. An optimized heat treatment involving a two-step, low temperature, heat treatment of the MSR powder produced bulk material with very high critical current density above 0.1 MAcm-2 (4.2 K, 0 T).
△ Less
Submitted 29 May, 2013;
originally announced May 2013.
-
High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks
Authors:
J. D. Weiss,
C. Tarantini,
J. Jiang,
F. Kametani,
A. A. Polyanskii,
D. C. Larbalestier,
E. E. Hellstrom
Abstract:
The K- and Co-doped BaFe2As2 (Ba-122) superconducting compounds are potentially useful for applications because they have upper critical fields (Hc2) of well over 50 T, Hc2 anisotropy Gamma < 2, and thin film critical current densities exceeding 1 MAcm-2 at 4.2 K. However, thin-film bicrystals of Co-doped Ba-122 clearly exhibit weak link behavior for [001] tilt misorientations of more than about 5…
▽ More
The K- and Co-doped BaFe2As2 (Ba-122) superconducting compounds are potentially useful for applications because they have upper critical fields (Hc2) of well over 50 T, Hc2 anisotropy Gamma < 2, and thin film critical current densities exceeding 1 MAcm-2 at 4.2 K. However, thin-film bicrystals of Co-doped Ba-122 clearly exhibit weak link behavior for [001] tilt misorientations of more than about 5 degrees, suggesting that textured substrates would be needed for applications, as in the cuprates. Here we present a contrary and very much more positive result in which untextured polycrystalline (Ba0.6K0.4)Fe2As2 bulks and round wires with high grain boundary density have transport critical current densities well over 0.1 MAcm-2 (SF, 4.2 K), more than 10 times higher than that of any other ferropnictide wire. The enhanced grain connectivity is ascribed to their much improved phase purity and to the enhanced vortex stiffness of this low-anisotropy compound (Gamma ~ 1-2) compared to YBa2Cu3O7-x (Gamma ~ 5).
△ Less
Submitted 9 November, 2012; v1 submitted 19 April, 2012;
originally announced April 2012.
-
Flux pinning characteristics in cylindrical ingot niobium used in superconducting radio frequency cavity fabrication
Authors:
Asavari S. Dhavale,
Pashupati Dhakal,
Anatolii A. Polyanskii,
Gianluigi Ciovati
Abstract:
We present the results of from DC magnetization and penetration depth measurements of cylindrical bulk large-grain (LG) and fine-grain (FG) niobium samples used for the fabrication of superconducting radio frequency (SRF) cavities. The surface treatment consisted of electropolishing and low temperature baking as they are typically applied to SRF cavities. The magnetization data were fitted using a…
▽ More
We present the results of from DC magnetization and penetration depth measurements of cylindrical bulk large-grain (LG) and fine-grain (FG) niobium samples used for the fabrication of superconducting radio frequency (SRF) cavities. The surface treatment consisted of electropolishing and low temperature baking as they are typically applied to SRF cavities. The magnetization data were fitted using a modified critical state model. The critical current density Jc and pinning force Fp are calculated from the magnetization data and their temperature dependence and field dependence are presented. The LG samples have lower critical current density and pinning force density compared to FG samples which implies a lower flux trap** efficiency. This effect may explain the lower values of residual resistance often observed in LG cavities than FG cavities.
△ Less
Submitted 18 January, 2012;
originally announced January 2012.
-
Disorder Induced Effects on the Critical Current Density of Iron Pnictide BaFe_1.8 Co_0.2 As_2 single crystals
Authors:
M. Zehetmayer,
M. Eisterer,
H. W. Weber,
J. Jiang,
J. D. Weiss,
A. Yamamoto,
A. A. Polyanskii,
E. E. Hellstrom,
D. C. Larbalestier
Abstract:
Investigating the role of disorder in superconductors is an essential part of characterizing the fundamental superconducting properties as well as assessing potential applications of the material. In most cases, the information available on the defect matrix is poor, making such studies difficult, but the situation can be improved by introducing defects in a controlled way, as provided by neutro…
▽ More
Investigating the role of disorder in superconductors is an essential part of characterizing the fundamental superconducting properties as well as assessing potential applications of the material. In most cases, the information available on the defect matrix is poor, making such studies difficult, but the situation can be improved by introducing defects in a controlled way, as provided by neutron irradiation. In this work, we analyze the effects of neutron irradiation on a Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ single crystal. We mainly concentrate on the magnetic properties which were determined by magnetometry. Introducing disorder by neutron irradiation leads to significant effects on both the reversible and the irreversible magnetic properties, such as the transition temperature, the upper critical field, the anisotropy, and the critical current density. The results are discussed in detail by comparing them with the properties in the unirradiated state.
△ Less
Submitted 30 November, 2009;
originally announced November 2009.
-
Intergrain current flow in a randomly oriented polycrystalline SmFeAsO0.85 oxypnictide
Authors:
F. Kametani,
P. Li,
D. Abraimov,
A. A. Polyanskii,
A. Yamamoto,
J. Jiang,
E. E. Hellstrom,
A. Gurevich,
D. C. Larbalestier,
Z. A. Ren,
J. Yang,
X. L. Dong,
W. Lu,
Z. X. Zhao
Abstract:
We report a direct current transport study of the local intergrain connections in a polycrystalline SmFeAsO0.85 (Sm1111) bulk, for which we earlier estimated significant intergranular critical current density Jc. Our combined low temperature laser scanning microscopy (LTLSM) and scanning electron microscopy observations revealed only few grain-to-grain transport current paths, most of which swit…
▽ More
We report a direct current transport study of the local intergrain connections in a polycrystalline SmFeAsO0.85 (Sm1111) bulk, for which we earlier estimated significant intergranular critical current density Jc. Our combined low temperature laser scanning microscopy (LTLSM) and scanning electron microscopy observations revealed only few grain-to-grain transport current paths, most of which switched off when a magnetic field was applied. These regions typically occur where current crosses Fe-As, which is a normal-metal wetting-phase that surrounds Sm1111 grains, producing a dense array of superconducting-normal-superconducting contacts. Our study points out the need to reduce the amount of grain boundary-wetting Fe-As phase, as well as the crack density within pnictide grains, as these defects produce a multiply connected current-blocking network.
△ Less
Submitted 25 July, 2009;
originally announced July 2009.
-
Neutron Irradiation of Sm-1111
Authors:
M. Eisterer,
H. W. Weber,
J. Jiang,
J. D. Weiss,
A. Yamamoto,
A. A. Polyanskii,
E. E. Hellstrom,
D. C. Larbalestier
Abstract:
SmFeAsO$_{1-x}$F$_x$ was irradiated in a fission reactor to a fast (E > 0.1 MeV) neutron fluence of 4x10^${21}$ m$^{-2}$. The introduced defects increase the normal state resistivity due to a reduction in the mean free path of the charge carriers. This leads to an enhancement of the upper critical field at low temperatures. The critical current density within the grains, Jc, increases upon irrad…
▽ More
SmFeAsO$_{1-x}$F$_x$ was irradiated in a fission reactor to a fast (E > 0.1 MeV) neutron fluence of 4x10^${21}$ m$^{-2}$. The introduced defects increase the normal state resistivity due to a reduction in the mean free path of the charge carriers. This leads to an enhancement of the upper critical field at low temperatures. The critical current density within the grains, Jc, increases upon irradiation. The second maximum in the field dependence of Jc disappears and the critical current density becomes a monotonically decreasing function of the applied magnetic field.
△ Less
Submitted 16 April, 2009;
originally announced April 2009.
-
Combined microstructural and magneto optical study of current flow in polycrystalline forms of Nd and Sm Fe-oxypnictides
Authors:
F. Kametani,
A. A. Polyanskii,
A. Yamamoto,
J. Jiang,
E. E. Hellstrom,
A. Gurevich,
D. C. Larbalestier,
Z. A. Ren,
J. Yang,
X. L. Dong,
W. Lu,
Z. X. Zhao
Abstract:
In order to understand why the inter- and intra-granular current densities of polycrystalline superconducting oxypnictides differ by three orders of magnitude, we have conducted combined magneto-optical and microstructural examinations of representative randomly oriented polycrystalline Nd and Sm single-layer oxypnictides. Magneto optical images show that the highest Jc values are observed withi…
▽ More
In order to understand why the inter- and intra-granular current densities of polycrystalline superconducting oxypnictides differ by three orders of magnitude, we have conducted combined magneto-optical and microstructural examinations of representative randomly oriented polycrystalline Nd and Sm single-layer oxypnictides. Magneto optical images show that the highest Jc values are observed within single grains oriented with their c axes perpendicular to the observation plane, implying that the intragranular current is anisotropic. The much lower intergranular Jc is at least partially due to many extrinsic factors, because cracks and a ubiquitous wetting As-Fe phase are found at many grain boundaries. However, some grain boundaries are structurally clean under high resolution transmission electron microscopy examination. Because the whole-sample global Jc(5K) values of the two samples examined are 1000-4000 A/cm2, some 10-40 times that found in random, polycrystalline YBa2Cu3O7-x, it appears that the dominant obstruction to intergranular current flow of many present samples is extrinsic, though some intrinsic limitation of current flow across grain boundaries cannot yet be ruled out.
△ Less
Submitted 19 September, 2008;
originally announced September 2008.
-
Evidence for two distinct scales of current flow in polycrystalline Sm and Nd iron oxypnictides
Authors:
A. Yamamoto,
A. A. Polyanskii,
J. Jiang,
F. Kametani,
C. Tarantini,
F. Hunte,
J. Jaroszynski,
E. E. Hellstrom,
P. J. Lee,
A. Gurevich,
D. C. Larbalestier,
Z. A. Ren,
J. Yang,
X. L. Dong,
W. Lu,
Z. X. Zhao
Abstract:
Early studies have found quasi-reversible magnetization curves in polycrystalline bulk rare-earth iron oxypnictides that suggest either wide-spread obstacles to intergranular current or very weak vortex pinning. In the present study of polycrystalline samarium and neodymium rare-earth iron oxypnictide samples made by high pressure synthesis, the hysteretic magnetization is significantly enhanced…
▽ More
Early studies have found quasi-reversible magnetization curves in polycrystalline bulk rare-earth iron oxypnictides that suggest either wide-spread obstacles to intergranular current or very weak vortex pinning. In the present study of polycrystalline samarium and neodymium rare-earth iron oxypnictide samples made by high pressure synthesis, the hysteretic magnetization is significantly enhanced. Magneto optical imaging and study of the field dependence of the remanent magnetization as a function of particle size both show that global currents over the whole sample do exist but that the intergranular and intragranular current densities have distinctively different temperature dependences and differ in magnitude by about 1000. Assuming that the highest current density loops are restricted to circulation only within grains leads to values of ~5 MA/cm2 at 5 K and self field, while whole-sample current densities, though two orders of magnitude lower are 1000-10000 A/cm2, some two orders of magnitude higher than in random polycrystalline cuprates. We cannot yet be certain whether this large difference in global and intragrain current density is intrinsic to the oxypnictides or due to extrinsic barriers to current flow, because the samples contain significant second phase, some of which wets the grain boundaries and produces evidences of SNS proximity effect in the whole sample critical current.
△ Less
Submitted 4 June, 2008;
originally announced June 2008.
-
Evidence for electromagnetic granularity in the polycrystalline iron-based superconductor LaO0.89F0.11FeAs
Authors:
A. Yamamoto,
J. Jiang,
C. Tarantini,
N. Craig,
A. A. Polyanskii,
F. Kametani,
F. Hunte,
J. Jaroszynski,
E. E. Hellstrom,
D. C. Larbalestier,
R. **,
A. S. Sefat,
M. A. McGuire,
B. C. Sales,
D. K. Christen,
D. Mandrus
Abstract:
The new rare-earth arsenate superconductors are layered, low carrier density compounds with many similarities to the high-Tc cuprates. An important question is whether they also exhibit weak-coupling across randomly oriented grain-boundaries. In this work we show considerable evidence for such weak-coupling by study of the dependence of magnetization in bulk and powdered samples. Bulk sample mag…
▽ More
The new rare-earth arsenate superconductors are layered, low carrier density compounds with many similarities to the high-Tc cuprates. An important question is whether they also exhibit weak-coupling across randomly oriented grain-boundaries. In this work we show considerable evidence for such weak-coupling by study of the dependence of magnetization in bulk and powdered samples. Bulk sample magnetization curves show very little hysteresis while remanent magnetization shows almost no sample size dependence, even after powdering. We conclude that these samples exhibit substantial electromagnetic granularity on a scale approximating the grain size, though we cannot yet determine whether this is intrinsic or extrinsic.
△ Less
Submitted 9 May, 2008;
originally announced May 2008.
-
Resistivity and Magneto-Optical Evidence for Variable and Incomplete Connectivity in Dense, High Critical Current Density C-alloyed Magnesium Diboride
Authors:
B. J. Senkowicz,
A. A. Polyanskii,
R. J. Mungall,
E. E. Hellstrom,
D. C. Larbalestier
Abstract:
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical imaging detected regions up to 0.5 mm in size which were nearly 100% dense with Jc 2-6 times that of the matrix. Evaluation of resistivity curves using the Rowell…
▽ More
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical imaging detected regions up to 0.5 mm in size which were nearly 100% dense with Jc 2-6 times that of the matrix. Evaluation of resistivity curves using the Rowell method predicts that only 10-50% of the cross sectional area carries the normal state measurement current, suggesting that considerable increases in Jc in these ~80% dense MgB2 samples would be possible with complete grain and particle connectivity.
△ Less
Submitted 29 March, 2006;
originally announced March 2006.
-
Topological Hysteresis in the Intermediate State of Type-I Superconductors
Authors:
Ruslan Prozorov,
Russell W. Giannetta,
Anatolii A. Polyanskii,
Garry K. Perkins
Abstract:
Magneto-optical imaging of thick stress-free lead samples reveals two distinct topologies of the intermediate state. Flux tubes are formed upon magnetic field penetration (closed topology) and laminar patterns appear upon flux exit (open topology). Two-dimensional distributions of shielding currents were obtained by applying an efficient inversion scheme. Quantitative analysis of the magnetic in…
▽ More
Magneto-optical imaging of thick stress-free lead samples reveals two distinct topologies of the intermediate state. Flux tubes are formed upon magnetic field penetration (closed topology) and laminar patterns appear upon flux exit (open topology). Two-dimensional distributions of shielding currents were obtained by applying an efficient inversion scheme. Quantitative analysis of the magnetic induction distribution and correlation with magnetization measurements indicate that observed topological differences between the two phases are responsible for experimentally observable magnetic hysteresis.
△ Less
Submitted 7 July, 2005; v1 submitted 21 September, 2004;
originally announced September 2004.
-
Magneto-optical studies of the uniform critical state in bulk MgB2
Authors:
A. A. Polyanskii,
A. Gurevich,
J. Jiang,
D. C. Larbalestier,
S. L. Bud'ko,
D. K. Finnemore,
G. Lapertot,
P. C. Canfield A. A. Polyanskii,
A. Gurevich,
J. Jiang,
D. C. Larbalestier,
S. L. Bud'ko,
D. K. Finnemore,
G. Lapertot,
P. C. Canfield
Abstract:
We present a detailed magneto-optical investigation of the magnetic flux penetration in polycrystalline MgB2 slabs made by direct reaction of B and Mg. Our results unambiguously indicate a uniform, Bean critical state magnetization behavior with almost no electromagnetic granularity. From the measured magnetic flux profiles we were able to extract the temperature dependence of the critical curre…
▽ More
We present a detailed magneto-optical investigation of the magnetic flux penetration in polycrystalline MgB2 slabs made by direct reaction of B and Mg. Our results unambiguously indicate a uniform, Bean critical state magnetization behavior with almost no electromagnetic granularity. From the measured magnetic flux profiles we were able to extract the temperature dependence of the critical current density Jc(T). The Jc(T) value reaches 1.8x10^5 A/cm2 at 10K and 0.12T, in good agreement with global magnetization measurements.
△ Less
Submitted 25 July, 2001;
originally announced July 2001.
-
Electronic anisotropy, magnetic field-temperature phase diagram and their dependence on resistivity in c-axis oriented MgB2 thin films
Authors:
S. Patnaik,
L. D. Cooley,
A. Gurevich,
A. A. Polyanskii,
J. Jiang,
X. Y. Cai,
A. A. Squitieri,
M. T. Naus,
M. K. Lee,
J. H. Choi,
L. Belenky,
S. D. Bu,
J. Letteri,
X. Song,
D. G. Schlom,
S. E. Babcock,
C. B. Eom,
E. E. Hellstrom,
D. C. Larbalestier
Abstract:
An important predicted, but so far uncharacterized, property of the new superconductor MgB2 is electronic anisotropy arising from its layered crystal structure. Here we report on three c-axis oriented thin films, showing that the upper critical field anisotropy ratio Hc2par/Hc2perp is 1.8 to 2.0, the ratio increasing with higher resistivity. Measurements of the magnetic field-temperature phase d…
▽ More
An important predicted, but so far uncharacterized, property of the new superconductor MgB2 is electronic anisotropy arising from its layered crystal structure. Here we report on three c-axis oriented thin films, showing that the upper critical field anisotropy ratio Hc2par/Hc2perp is 1.8 to 2.0, the ratio increasing with higher resistivity. Measurements of the magnetic field-temperature phase diagram show that flux pinning disappears at H* ~ 0.8Hc2perp(T) in untextured samples. Hc2par(0) is strongly enhanced by alloying to 39 T for the highest resistivity film, more than twice that seen in bulk samples.
△ Less
Submitted 28 April, 2001;
originally announced April 2001.
-
Strongly linked current flow in polycrystalline forms of the new superconductor MgB2
Authors:
D. C. Larbalestier,
M. O. Rikel,
L. D. Cooley,
A. A. Polyanskii,
J. Y. Jiang,
S. Patnaik,
X. Y. Cai,
D. M. Feldmann,
A. Gurevich,
A. A. Squitieri,
M. T. Naus,
C. B. Eom,
E. E. Hellstrom,
R. J. Cava,
K. A. Regan,
N. Rogado,
M. A. Hayward,
T. He,
J. S. Slusky,
P. Khalifah,
K. Inumaru,
M. Haas
Abstract:
The discovery of superconductivity at 39 K in MgB2[1] raises many issues. One of the central questions is whether this new superconductor resembles a high-temperature-cuprate superconductor or a low-temperature metallic superconductor in terms of its current carrying characteristics in applied magnetic fields. In spite of the very high transition temperatures of the cuprate superconductors, thei…
▽ More
The discovery of superconductivity at 39 K in MgB2[1] raises many issues. One of the central questions is whether this new superconductor resembles a high-temperature-cuprate superconductor or a low-temperature metallic superconductor in terms of its current carrying characteristics in applied magnetic fields. In spite of the very high transition temperatures of the cuprate superconductors, their performance in magnetic fields has several drawbacks[2]. Their large anisotropy restricts high bulk current densities to much less than the full magnetic field-temperature (H-T) space over which superconductivity is found. Further, weak coupling across grain boundaries makes transport current densities in untextured polycrystalline forms low and strongly magnetic field sensitive[3,4]. These studies of MgB2 address both issues. In spite of the multi-phase, untextured, nano-scale sub-divided nature of our samples, supercurrents flow throughout without the strong sensitivity to weak magnetic fields characteristic of Josephson-coupled grains[3]. Magnetization measurements over nearly all of the superconducting H-T plane show good temperature scaling of the flux pinning force, suggestive of a current density determined by flux pinning. At least two length scales are suggested by the magnetization and magneto optical (MO) analysis but the cause of this seems to be phase inhomogeneity, porosity, and minority insulating phase such as MgO rather than by weakly coupled grain boundaries. Our results suggest that polycrystalline ceramics of this new class of superconductor will not be compromised by the weak link problems of the high temperature superconductors, a conclusion with enormous significance for applications if higher temperature analogs of this compound can be discovered.
△ Less
Submitted 12 February, 2001;
originally announced February 2001.