Controlling spin pum** into superconducting Nb by proximity-induced spin-triplet Cooper pairs
Authors:
Alex K. Chan,
Murat Cubukcu,
Xavier Montiel,
Sachio Komori,
Alexander Vanstone,
Juliet E. Thompson,
Garry K. Perkins,
Mark Blamire,
Jason WA. Robinson,
Matthias Eschrig,
Hidekazu Kurebayashi,
Lesley F. Cohen
Abstract:
Proximity-induced long-range spin-triplet supercurrents, important for the field of superconducting spintronics, are generated in superconducting/ferromagnetic heterostructures when interfacial magnetic inhomogeneities responsible for spin mixing and spin flip scattering are present. The multilayer stack Nb/Cr/Fe/Cr/Nb has been shown to support such exotic currents when fabricated into Josephson j…
▽ More
Proximity-induced long-range spin-triplet supercurrents, important for the field of superconducting spintronics, are generated in superconducting/ferromagnetic heterostructures when interfacial magnetic inhomogeneities responsible for spin mixing and spin flip scattering are present. The multilayer stack Nb/Cr/Fe/Cr/Nb has been shown to support such exotic currents when fabricated into Josephson junction devices. However, creating pure spin currents controllably in superconductors outside of the Josephson junction architecture is a bottleneck to progress. Recently, ferromagnetic resonance was proposed as a possible direction, the signature of pure supercurrent creation being an enhancement of the Gilbert dam** below the superconducting critical temperature, but the necessary conditions are still poorly established. Consistent with theoretical prediction, we demonstrate conclusively that pum** pure spin currents into a superconductor is only possible when conditions supporting proximity-induced spin-triplet effects are satisfied. Our study is an important step forward for superconducting pure spin current creation and manipulation, considerably advancing the field of superconducting spintronics.
△ Less
Submitted 3 February, 2022;
originally announced February 2022.
-
Map** the dynamic interactions between vortex species in highly anisotropic superconductors
Authors:
M. Tesei,
G. K. Perkins,
A. D. Caplin,
L. F. Cohen,
T. Tamegai
Abstract:
Here we use highly sensitive magnetisation measurements performed using a Hall probe sensor on single crystals of highly anisotropic high temperature superconductors $Bi_{2}Sr_{2}CaCu_{2}O_{8}$ to study the dynamic interactions between the two species of vortices that exist in such superconductors. We observe a remarkable and clearly delineated high temperature regime that mirrors the underlying…
▽ More
Here we use highly sensitive magnetisation measurements performed using a Hall probe sensor on single crystals of highly anisotropic high temperature superconductors $Bi_{2}Sr_{2}CaCu_{2}O_{8}$ to study the dynamic interactions between the two species of vortices that exist in such superconductors. We observe a remarkable and clearly delineated high temperature regime that mirrors the underlying vortex phase diagram. Our results map out the parameter space over which these dynamic interaction processes can be used to create vortex ratchets, pumps and other fluxonic devices.
△ Less
Submitted 14 April, 2008;
originally announced April 2008.
-
Dynamic interactions between pancake vortex stacks and Josephson vortices in Bi2Sr2CaCu2O8 single crystals: relaxation and ratchets
Authors:
G. K. Perkins,
A. D. Caplin,
L. F. Cohen
Abstract:
We present a detailed study of the dynamic interactions between Josephson vortices and stacks of pancake vortices in a Bi2Sr2CaCu2O8 single crystal, obtained by measuring the effect of applied inplane magnetic field pulses on the c-axis magnetisation. The predominant interaction is to relax the system towards equilibrium. However, using a highly sensitive AC technique we are able to measure also…
▽ More
We present a detailed study of the dynamic interactions between Josephson vortices and stacks of pancake vortices in a Bi2Sr2CaCu2O8 single crystal, obtained by measuring the effect of applied inplane magnetic field pulses on the c-axis magnetisation. The predominant interaction is to relax the system towards equilibrium. However, using a highly sensitive AC technique we are able to measure also the forces acting to drive the system away from equilibrium, consistent with the existence of dragging interactions between the Josephson and pancake systems. Such forces were discussed recently as the basis of possible flux ratchet devices.
△ Less
Submitted 16 August, 2005;
originally announced August 2005.
-
Electron diffusivities in MgB2 from point contact spectroscopy
Authors:
Y. Bugoslavsky,
Y. Miyoshi,
G. K. Perkins,
A. D. Caplin,
L. F. Cohen,
A. V. Pogrebnyakov,
X. X. Xi
Abstract:
We demonstrate that the variation of the Andreev reflection with applied magnetic field provides a direct means of comparing the properties of MgB2 with the theory for a dirty two-band superconductor, and we find good agreement between the two. The ratio of electron diffusivities in the s and p bands can be inferred from this experiment. We find that the field dependence of the density of states…
▽ More
We demonstrate that the variation of the Andreev reflection with applied magnetic field provides a direct means of comparing the properties of MgB2 with the theory for a dirty two-band superconductor, and we find good agreement between the two. The ratio of electron diffusivities in the s and p bands can be inferred from this experiment. We find that the field dependence of the density of states at the Fermi level in the p band is independent of the field direction, and that the anisotropic upper critical field is determined by the anisotropic diffusivity in the s band.
△ Less
Submitted 5 February, 2005;
originally announced February 2005.
-
Topological Hysteresis in the Intermediate State of Type-I Superconductors
Authors:
Ruslan Prozorov,
Russell W. Giannetta,
Anatolii A. Polyanskii,
Garry K. Perkins
Abstract:
Magneto-optical imaging of thick stress-free lead samples reveals two distinct topologies of the intermediate state. Flux tubes are formed upon magnetic field penetration (closed topology) and laminar patterns appear upon flux exit (open topology). Two-dimensional distributions of shielding currents were obtained by applying an efficient inversion scheme. Quantitative analysis of the magnetic in…
▽ More
Magneto-optical imaging of thick stress-free lead samples reveals two distinct topologies of the intermediate state. Flux tubes are formed upon magnetic field penetration (closed topology) and laminar patterns appear upon flux exit (open topology). Two-dimensional distributions of shielding currents were obtained by applying an efficient inversion scheme. Quantitative analysis of the magnetic induction distribution and correlation with magnetization measurements indicate that observed topological differences between the two phases are responsible for experimentally observable magnetic hysteresis.
△ Less
Submitted 7 July, 2005; v1 submitted 21 September, 2004;
originally announced September 2004.
-
First order magnetic transition in CeFe$_2$ alloys: Phase-coexistence and metastability
Authors:
S. B. Roy,
G. K. Perkins,
M. K. Chattopadhyay,
A. K. Nigam,
K. J. S. Sokhey,
P. Chaddah,
A. D. Caplin,
L. F. Cohen
Abstract:
First order ferromagnetic (FM) to antiferromagnetic (AFM) phase transition in doped-CeFe$_2$ alloys is studied with micro-Hall probe technique. Clear visual evidence of magnetic phase-coexistence on micrometer scales and the evolution of this phase-coexistence as a function of temperature, magnetic field and time across the first order FM-AFM transition is presented. Such phase-coexistence and m…
▽ More
First order ferromagnetic (FM) to antiferromagnetic (AFM) phase transition in doped-CeFe$_2$ alloys is studied with micro-Hall probe technique. Clear visual evidence of magnetic phase-coexistence on micrometer scales and the evolution of this phase-coexistence as a function of temperature, magnetic field and time across the first order FM-AFM transition is presented. Such phase-coexistence and metastability arise as natural consequence of an intrinsic disorder-influenced first order transition. Generality of this phenomena involving other classes of materials is discussed.
△ Less
Submitted 15 December, 2003;
originally announced December 2003.
-
Superconducting gap structure and pinning in disordered MgB2 films
Authors:
Y. Bugoslavsky,
Y. Miyoshi,
G. K. Perkins,
A. D. Caplin,
L. F. Cohen,
H. Y. Zhai,
H. M. Christen,
A. V. Pogrebnyakov,
X. X. Xi,
O. V. Dolgov
Abstract:
We have performed a comparative study of two thin films of magnesium diboride (MgB2) grown by different techniques. The critical current density at different temperatures and magnetic fields was evaluated from magnetisation curves, the structure of superconducting order parameter was obtained from point-contact spectroscopy, and the scattering rates were evaluated by fitting the temperature depe…
▽ More
We have performed a comparative study of two thin films of magnesium diboride (MgB2) grown by different techniques. The critical current density at different temperatures and magnetic fields was evaluated from magnetisation curves, the structure of superconducting order parameter was obtained from point-contact spectroscopy, and the scattering rates were evaluated by fitting the temperature dependent normal-state resistivity to the two-band model. The films have similar critical temperatures close to 39 K, but the upper critical fields were different by a factor of 2 (5.2T and 2.5 T at 20 K). We have found that the film with higher Hc2 also had stronger scattering in the sigma band and smaller value of the superconducting gap in this band. As the scattering in sigma band is primarily due to the defects in boron plane, our results are consistent with the assumption that disordering the boron planes leads to enhanced Hc2 and better pinning properties in magnetic field.
△ Less
Submitted 25 September, 2003;
originally announced September 2003.
-
The effect of magnetic field on the two superconducting gaps in MgB2
Authors:
Y. Bugoslavsky,
Y. Miyoshi,
G. K. Perkins,
A. D. Caplin,
L. F. Cohen,
A. V. Pogrebnyakov,
X. X. Xi
Abstract:
Double-gap superconductivity in an epitaxial MgB2 film has been studied by means of point-contact spectroscopy in magnetic field up to 8 Tesla. The relatively fast disappearance of the feature associated with the pi-band gap at a field around 1 T is caused by the line broadening due to strong pair breaking rather than to a collapse of the double-gap state. This pair breaking was found to increas…
▽ More
Double-gap superconductivity in an epitaxial MgB2 film has been studied by means of point-contact spectroscopy in magnetic field up to 8 Tesla. The relatively fast disappearance of the feature associated with the pi-band gap at a field around 1 T is caused by the line broadening due to strong pair breaking rather than to a collapse of the double-gap state. This pair breaking was found to increase linearly with field. Field dependences of the order parameters Delta_pi and Delta_sigma in the pi and sigma bands were measured in field applied parallel and perpendicular to the film, at T = 4.2 K. In perpendicular field, both order parameters survive to a common Hc2, which is about 6.5 T for this direction. In parallel field, the decrease of Delta_sigma is much more gradual, consistent with the Hc2 being about 4 times greater in this ori-entation. The difference in Delta_pi measured in the two field orientations is however smaller than the difference of Delta_sigma. We compare these results with the data on tunnelling spectroscopy and specific heat measurements of MgB2 single crystals and find consistency between the different experimental approaches.
△ Less
Submitted 1 September, 2003; v1 submitted 22 July, 2003;
originally announced July 2003.
-
Effects of proton irradiation and ageing on the superconducting properties of single crystalline and polycrystalline MgB2
Authors:
G. K. Perkins,
Y. Bugoslavsky,
A . D. Caplin,
J. Moore,
T. J. Tate,
R. Gwilliam,
J. Jun,
S. M. Kazakov,
J. Karpinski,
L. F. Cohen
Abstract:
We present magnetisation data on crystalline and polycrystalline MgB2 before and after irradiation with ~1MeV protons. In the virgin crystal the critical current density is below our noise floor of 103A/cm2 over most of the field range. However, after irradiation a peak occurs in the current density as a function of applied magnetic field as the upper critical field Hc2 is approached. After subs…
▽ More
We present magnetisation data on crystalline and polycrystalline MgB2 before and after irradiation with ~1MeV protons. In the virgin crystal the critical current density is below our noise floor of 103A/cm2 over most of the field range. However, after irradiation a peak occurs in the current density as a function of applied magnetic field as the upper critical field Hc2 is approached. After subsequent ageing over a time period of three months, the peak effect is greatly enhanced, exhibiting much stronger pinning over a wide field range, and the upper critical field is approximately doubled, accompanied by a 2K reduction in transition temperature. Similar studies were made on polycrystalline fragments, where irradiation leads to an increased irreversibility field (Jc is enhanced at high fields but decreased at low fields) and a suppression in transition temperature. However, after two years of ageing both parameters returned towards those of the virgin sample.
△ Less
Submitted 12 May, 2003;
originally announced May 2003.
-
Critical Fields and Critical Currents in MgB2
Authors:
A. D. Caplin,
Y. Bugoslavsky,
L. F. Cohen,
L. Cowey,
J. Driscoll,
J. Moore,
G. K. Perkins
Abstract:
We review recent measurements of upper (Hc2) and lower (Hc1) critical fields in clean single crystals of MgB2, and their anisotropies between the two principal crystallographic directions. Such crystals are far into the "clean limit" of Type II superconductivity, and indeed for fields applied in the c-direction, the Ginzburg-Landau parameter k is only about 3, just large enough for Type II behav…
▽ More
We review recent measurements of upper (Hc2) and lower (Hc1) critical fields in clean single crystals of MgB2, and their anisotropies between the two principal crystallographic directions. Such crystals are far into the "clean limit" of Type II superconductivity, and indeed for fields applied in the c-direction, the Ginzburg-Landau parameter k is only about 3, just large enough for Type II behaviour. Because m0Hc2 is so low, about 3 T for fields in the c-direction, MgB2 has to be modified for it to become useful for high-current applications. It should be possible to increase Hc2 by the introduction of strong electron scattering (but because of the electronic structure and the double gap that results, the scatterers will have to be chosen carefully). In addition, pinning defects on a scale of a few nm will have to be engineered in order to enhance the critical current density at high fields.
△ Less
Submitted 1 November, 2002;
originally announced November 2002.
-
Effective Vortex Pinning in MgB2 thin films
Authors:
Y. Bugoslavsky,
L. Cowey,
T. J. Tate,
G. K. Perkins,
J. Moore,
Z. Lockman,
A. Berenov,
J. L. MacManus-Driscoll,
A. D. Caplin,
L. F. Cohen,
H Y Zhai,
H M Christen,
M P Paranthaman,
D H Lowndes,
M H Jo,
M G Blamire
Abstract:
We discuss pinning properties of MgB2 thin films grown by pulsed-laser deposition (PLD) and by electron-beam (EB) evaporation. Two mechanisms are identified that contribute most effectively to the pinning of vortices in randomly oriented films. The EB process produces low defected crystallites with small grain size providing enhanced pinning at grain boundaries without degradation of Tc. The PLD…
▽ More
We discuss pinning properties of MgB2 thin films grown by pulsed-laser deposition (PLD) and by electron-beam (EB) evaporation. Two mechanisms are identified that contribute most effectively to the pinning of vortices in randomly oriented films. The EB process produces low defected crystallites with small grain size providing enhanced pinning at grain boundaries without degradation of Tc. The PLD process produces films with structural disorder on a scale less that the coherence length that further improves pinning, but also depresses Tc.
△ Less
Submitted 2 July, 2002;
originally announced July 2002.
-
Super-conducting critical fields and anisotropy of a MgB2 single crystal
Authors:
G. K. Perkins,
J. Moore,
Y. Bugoslavsky,
L. F. Cohen,
J. Jun,
S. M. Kazakov,
J. Karpinski,
A. D. Caplin
Abstract:
Despite the intense activity in the year since the discovery of superconductivity in MgB2, key parameters, in particular the upper and lower critical fields Hc2 and Hc1 and their anisotropies, are not well-established, largely because of the difficulty of growing MgB2 crystals. Attempts have been made to deduce these parameters from experiments on polycrystalline material, but they have substant…
▽ More
Despite the intense activity in the year since the discovery of superconductivity in MgB2, key parameters, in particular the upper and lower critical fields Hc2 and Hc1 and their anisotropies, are not well-established, largely because of the difficulty of growing MgB2 crystals. Attempts have been made to deduce these parameters from experiments on polycrystalline material, but they have substantial uncertainties. Hc2 is particularly important for applications, as it is the field which quenches bulk super-conductivity. In terms of understanding MgB2, it is now clear that the conventional electron-phonon interaction is strong enough to account for the high transition temperature Tc, but the consequences of the double super-conducting gap for the anisotropy and its dependence on temperature, are uncertain. Here we describe detailed direct measurements of Hc1(T) and Hc2(T) for the two principal crystallographic directions in a clean single crystal of MgB2. For fields in the c-direction, $μ_0 H^c_{c1}(0)$ = $0.28 +- 0.01T$ and $μ_0 H^c_{c2}(0)$ is $3 +- 0.5T$; this ratio of critical fields is rather low and implies that MgB2 is only just a Type II super-conductor. The anisotropies of both critical fields are close to 2.
△ Less
Submitted 7 May, 2002; v1 submitted 2 May, 2002;
originally announced May 2002.
-
The structure of the superconducting gap in MgB2 from point-contact spectroscopy
Authors:
Y. Bugoslavsky,
Y. Miyoshi,
G. K. Perkins,
A. V. Berenov,
Z. Lockman,
J. L. MacManus-Driscoll,
L. F. Cohen,
A. D. Caplin,
H. Y. Zhai,
M. P. Paranthaman,
H. M. Christen,
M. Blamire
Abstract:
We have studied the structure of the superconducting gap in MgB2 thin films by means of point-contact spectroscopy using a gold tip. The films were produced by depositing pure boron on a sapphire substrate, using e-beam evaporation, followed by reaction with magnesium vapour. The films have a Tc of 38.6 +- 0.3 K and resistivity of about 20 microOhm cm at 40 K. The point-contact spectra prove dir…
▽ More
We have studied the structure of the superconducting gap in MgB2 thin films by means of point-contact spectroscopy using a gold tip. The films were produced by depositing pure boron on a sapphire substrate, using e-beam evaporation, followed by reaction with magnesium vapour. The films have a Tc of 38.6 +- 0.3 K and resistivity of about 20 microOhm cm at 40 K. The point-contact spectra prove directly the existence of a multi-valued order parameter in MgB2, with two distinct values of the gap, DELTA1=2.3+-0.3 meV and DELTA2=6.2+-0.7 meV at 4.2 K. Analysis of the spectra in terms of the Blonder-Tinkham-Klapwijk model reveals that both gaps close simultaneously at the Tc of the film. Possible mechanisms that can explain the intrinsic co-existence of two values of the gap are discussed.
△ Less
Submitted 15 October, 2001;
originally announced October 2001.
-
Enhancement of the high-field critical current density of superconducting MgB2 by proton irradiation
Authors:
Y. Bugoslavsky,
L. F. Cohen,
G. K. Perkins,
M. Polichetti,
T. J. Tate,
R. Gwilliam,
A. D. Caplin
Abstract:
A relatively high critical temperature, Tc, approaching 40 K, places the recently-discovered superconductor magnesium diboride (MgB2) intermediate between the families of low- and copper-oxide-based high-temperature superconductors (HTS). Supercurrent flow in MgB2 is unhindered by grain boundaries, unlike the HTS materials. Thus, long polycrystalline MgB2 conductors may be easier to fabricate, a…
▽ More
A relatively high critical temperature, Tc, approaching 40 K, places the recently-discovered superconductor magnesium diboride (MgB2) intermediate between the families of low- and copper-oxide-based high-temperature superconductors (HTS). Supercurrent flow in MgB2 is unhindered by grain boundaries, unlike the HTS materials. Thus, long polycrystalline MgB2 conductors may be easier to fabricate, and so could fill a potentially important niche of applications in the 20 to 30 K temperature range. However, one disadvantage of MgB2 is that in bulk material the critical current density, Jc, appears to drop more rapidly with increasing magnetic field than it does in the HTS phases. The magnitude and field dependence of Jc are related to the presence of structural defects that can "pin" the quantised magnetic vortices that permeate the material, and prevent them from moving under the action of the Lorentz force. Vortex studies suggest that it is the paucity of suitable defects in MgB2 that causes the rapid decay of Jc with field. Here we show that modest levels of atomic disorder, induced by proton irradiation, enhance the pinning, and so increase Jc significantly at high fields. We anticipate that chemical do** or mechanical processing should be capable of generating similar levels of disorder, and so achieve technologically-attractive performance in MgB2 by economically-viable routes.
△ Less
Submitted 3 May, 2001; v1 submitted 9 April, 2001;
originally announced April 2001.
-
Microwave Surface Resistance in MgB2
Authors:
A. A. Zhukov,
K. Yates,
G. K Perkins,
Y. Bugoslavsky,
M. Polichetti,
A. Berenov,
J. Driscoll,
A. D. Caplin,
L. F. Cohen,
Ling Hao,
J. Gallop
Abstract:
Measurements of the temperature dependence of the surface resistance at 3 GHz of 100 micron size grains of MgB_2 separated powder are presented and discussed. The microwave surface resistance data is compared to experimental results of Nb, Bi_2Sr_2CaCu_2O_{8+δ} (BSCCO) and theoretical predictions of s-wave weak coupling electron-phonon theory (BCS).
Measurements of the temperature dependence of the surface resistance at 3 GHz of 100 micron size grains of MgB_2 separated powder are presented and discussed. The microwave surface resistance data is compared to experimental results of Nb, Bi_2Sr_2CaCu_2O_{8+δ} (BSCCO) and theoretical predictions of s-wave weak coupling electron-phonon theory (BCS).
△ Less
Submitted 30 March, 2001; v1 submitted 28 March, 2001;
originally announced March 2001.
-
Critical currents and vortex dynamics in super-conducting MgB2
Authors:
Y. Bugoslavsky,
G. K. Perkins,
X. Qi,
L. F. Cohen,
A. D. Caplin
Abstract:
The recently-discovered MgB2 super-conductor has a transition temperature Tc approaching 40K, placing it intermediate between the families of low and high temperature super-conductors (LTS and HTS). In practical applications, super-conductors are permeated by quantised magnetic flux vortices, and when a current flows there is dissipation unless the vortices are "pinned" in some way, and so inhib…
▽ More
The recently-discovered MgB2 super-conductor has a transition temperature Tc approaching 40K, placing it intermediate between the families of low and high temperature super-conductors (LTS and HTS). In practical applications, super-conductors are permeated by quantised magnetic flux vortices, and when a current flows there is dissipation unless the vortices are "pinned" in some way, and so inhibited from moving under the influence of the Lorentz force. This vortex motion sets the limiting critical current density Jc in the super-conductor. Vortex behaviour has proved to be more complicated in the HTS than in LTS materials. While this has stimulated extensive theoretical and experimental research, it has impeded applications. Clearly it is important to explore vortex behaviour in MgB2; here we report on Jc, and also on the creep rate S, which is a measure of how fast the "persistent" currents decay. Our results show that naturally-occurring grain boundaries are highly transparent to supercurrent, and suggest that the steep decline in Jc with increasing magnetic field H reflects a weakening of the vortex pinning energy, possibly because this compound forms naturally with a high degree of crystalline perfection.
△ Less
Submitted 20 February, 2001;
originally announced February 2001.