Large saturation moment and high ferromagnetic transition temperature in a structurally disordered inverse Heusler alloy Fe2RuGe
Authors:
Sudip Chakraborty,
Shuvankar Gupta,
Vidha Bhasin,
Santanu Pakhira,
Céline Barreteau,
Jean-Claude Crivello,
Shambhu Nath Jha,
Dibyendu Bhattacharyya,
Maxim Avdeev,
Valérie Paul-Boncour,
Jean-Marc Greneche,
Eric Alleno,
Chandan Mazumdar
Abstract:
We report the successful synthesis of a new 4$d$ based polycrystalline inverse Heusler alloy Fe$_2$RuGe by an arc melting process and have studied in detail its structural, magnetic and transport properties complemented with first principle calculations. X-ray and neutron diffraction, Extended X-ray Absorption Fine Structure and $^{57}$Fe Mössbauer spectroscopic studies confirm the single phase na…
▽ More
We report the successful synthesis of a new 4$d$ based polycrystalline inverse Heusler alloy Fe$_2$RuGe by an arc melting process and have studied in detail its structural, magnetic and transport properties complemented with first principle calculations. X-ray and neutron diffraction, Extended X-ray Absorption Fine Structure and $^{57}$Fe Mössbauer spectroscopic studies confirm the single phase nature of the system where the Fe and Ru atoms are randomly distributed in the 4$c$ and 4$d$ Wyckoff positions in a ratio close to 50:50. The formation of the disordered structure is also confirmed by the theoretical energy minimization calculation. Despite the random cross-site disorder of Fe and Ru atoms, magnetic measurements suggest not only a high Curie temperature of $\sim$860\,K, but also a large saturation magnetic moment $\sim$4.9\,$μ_B$ per formula unit at 5\,K, considerably exceeding the theoretical limit (4\,$μ_B$ per formula unit) predicted by the Slater-Pauling rule. Only a few Fe-based inverse Heusler alloys are known to exhibit such high Curie temperatures. Neutron diffraction analysis coupled with the isothermal magnetization value indicates that the magnetic moments in Fe$_2$RuGe are associated with Fe-atoms only, which is also confirmed by Mössbauer spectrometry. Interestingly, in comparison to the cubic or hexagonal phase of the parent compound, Fe$_3$Ge, the Curie temperature of Fe$_2$RuGe has increased significantly despite the substitution of the nonmagnetic, yet isoelectronic element Ru in this structurally disordered compound. Our theoretical calculation reveals that the large Fe moment ($\sim2.8μ_B$/Fe) on the 4$b$ site can be attributed to a charge transfer from this Fe site towards its Ru neighbours. Such a substantial increase in magnetic moment due to electron charge transfer has not previously been reported in a Heusler alloy system.
△ Less
Submitted 26 June, 2023;
originally announced June 2023.
-
Influence of high pressure on the remarkable itinerant electron behaviour in Y$_{0.7}$Er$_{0.3}$Fe$_2$D$_{4.2}$ compounds
Authors:
Z. Arnold,
O. Isnard,
V. Paul-Boncour
Abstract:
Monoclinic Y$_{0.7}$Er$_{0.3}$Fe$_2$D$_{4.2}$ compound exhibits unusual magnetic properties with different field induced magnetic transitions. The deuteride is ferrimagnetic at low temperature and the Er and Fe sublattices present magnetic transitions at different temperatures. The Er moments are ordered below T$_{Er}$=55 K, whereas the Fe moments remain ferromagnetically coupled up to T$_{M0}$ =…
▽ More
Monoclinic Y$_{0.7}$Er$_{0.3}$Fe$_2$D$_{4.2}$ compound exhibits unusual magnetic properties with different field induced magnetic transitions. The deuteride is ferrimagnetic at low temperature and the Er and Fe sublattices present magnetic transitions at different temperatures. The Er moments are ordered below T$_{Er}$=55 K, whereas the Fe moments remain ferromagnetically coupled up to T$_{M0}$ = 66 K. At T$_{M0}$ the Fe moments display a sharp ferromagnetic-antiferromagnetic transition (FM-AFM) through an itinerant electron metamagnetic (IEM) behaviour very sensitive to any volume change. Y$_{0.7}$Er$_{0.3}$Fe$_2$D$_{4.2}$ becomes paramagnetic above T$_N$=125 K. The pressure dependence of T$_{Er}$ and T$_{M0}$ have been extracted from magnetic measurements under hydrostatic pressure up to 0.49 GPa. Both temperatures decrease linearly upon applied pressure with dT$_{Er}$/dP=-126 and dTM0/dP=-140 K.GPa$^{-1}$ for a field of B=0.03 T. Both magnetic Er and ferromagnetic Fe order disappear at P=0.44(4) GPa. However, under a larger applied field B=5 T, dT$_{M0}$/dP=-156 K.GPa$^{-1}$ whereas dT$_{Er}$/dP=-134 K.GPa$^{-1}$ showing a weaker sensitivity to pressure and magnetic field. At 2 K the decrease of the saturation magnetization under pressure can be attributed to a reduction of the mean Er moment due to canting and/or crystal field effect. Above T$_{M0}$ the magnetization curves display a metamagnetic behaviour from AFM to FM state, which is also very sensitive to the applied pressure. The transition field B$_{trans}$, which increases linearly upon heating, is shifted to lower temperature upon applied pressure with dT=-17 K between 0 and 0.11 GPa. These results show a strong decoupling of the Er and Fe magnetic sublattices versus temperature, applied field and pressure.
△ Less
Submitted 4 May, 2023;
originally announced May 2023.
-
Magnetic, structural and magnetocaloric properties of Y$_{0.9}$Gd$_{0.1}$Fe$_{2}$H$_{x}$ hydrides
Authors:
V. Paul-Boncour,
K. Provost,
T. Mazet,
A. N Diaye,
E. Alleno,
F. Couturas
Abstract:
At 300 K, Y$_{0.9}$Gd$_{0.1}$Fe$_{2}$H$_{x}$ hydrides crystallize sequentially with increasing H concentration in various structures related to a lowering of the cubic MgCu$_{2}$ type structure of the parent alloy: cubic C1, monoclinic M1, cubic C2, monoclinic M2, cubic C3, orthorhombic O. Above 300 K, they undergo a first-order transition at a T$_{O-D}$ temperature driven by order-disorder of hyd…
▽ More
At 300 K, Y$_{0.9}$Gd$_{0.1}$Fe$_{2}$H$_{x}$ hydrides crystallize sequentially with increasing H concentration in various structures related to a lowering of the cubic MgCu$_{2}$ type structure of the parent alloy: cubic C1, monoclinic M1, cubic C2, monoclinic M2, cubic C3, orthorhombic O. Above 300 K, they undergo a first-order transition at a T$_{O-D}$ temperature driven by order-disorder of hydrogen atoms into interstitial sites. Their magnetic, structural and magnetocaloric properties have been investigated through magnetic measurements, and high-resolution synchrotron diffraction experiments. The magnetization at 5 K decreases slightly from 4 to 3.8 $μ_{B}$ for x = 3 to 3.9 H f.u., then with a larger slope for higher H content. A discontinuous decrease of the magnetic transition temperature is observed: M1 and C2 hydrides are ferrimagnetic with T$_{C}$ near 300 K, M2 hydride displays a sharp ferromagnetic-antiferromagnetic transition at T$_{FM-AFM}$ =144 K, whereas C3 and O hydrides present only a sharp increase of the magnetization below 15 K and a weak magnetization up to RT. Negative magnetic entropy variations ($Δ$S$_{M}$) are measured near T$_{C}$ for the M1 and C2 phases, near T$_{FM-AFM}$ for the M2 phase, whereas positive $Δ$S$_{M}$ peaks due to inverse MCE effect are found near T$_{O-D}$. A structural and magnetic phase diagram is proposed.
△ Less
Submitted 5 October, 2022;
originally announced October 2022.
-
Phase diagram and order-disorder transitions in Y$_{0.9}$Gd$_{0.1}$Fe$_{2}$H$_{x}$ hydrides (x $\le$ 2.9)
Authors:
V. Paul-Boncour,
K. Provost,
E. Alleno,
A. N Diaye,
F. Couturas,
E. Elkaim
Abstract:
Y$_{0.9}$Gd$_{0.1}$Fe$_{2}$, which crystallizes in a C15 cubic structure, can absorb up to 5 H/f.u. and its pressure-composition isotherm displays a multiplateau behavior related to the existence of several hydrides with different crystal structures. At room temperature Y$_{0.9}$Gd$_{0.1}$Fe$_{2}$H$_{x}$ hydrides (2.9 $\le$ x $\le$ 5) crystallize in three phases with cubic structure (C1, C2 and C3…
▽ More
Y$_{0.9}$Gd$_{0.1}$Fe$_{2}$, which crystallizes in a C15 cubic structure, can absorb up to 5 H/f.u. and its pressure-composition isotherm displays a multiplateau behavior related to the existence of several hydrides with different crystal structures. At room temperature Y$_{0.9}$Gd$_{0.1}$Fe$_{2}$H$_{x}$ hydrides (2.9 $\le$ x $\le$ 5) crystallize in three phases with cubic structure (C1, C2 and C3), two phases with monoclinic structures (M1 and M2), and one phase with orthorhombic structure (O), with the following sequence for increasing H concentration: C1, M1, C2, M2, C3, O. Each phase exists as single phase within a H homogeneity range, and they are separated from each other by two-phase domains. The reductions of crystal symmetry are related to various hydrogen orders into interstitial sites. Weak superstructure peaks were indexed by doubling the cubic cell parameter of the cubic C2 phase. Upon heating, the monoclinic M1 and M2 and the cubic C2 phases undergo order-disorder (O-D) transitions toward a disordered cubic structure CDis. These O-D transitions are reversible with thermal hysteresis effects. The cubic C3 and orthorhombic O phases transform into a disordered cubic phase accompanied by H desorption.
△ Less
Submitted 5 October, 2022;
originally announced October 2022.
-
Investigation of the phase occurrence and H sorption properties in the Y33.33Ni66.67-xAlx (0 <= x <= 33.33) system
Authors:
Hao Shen,
Valerie Paul-Boncour,
Michel Latroche,
Fermin Cuevas,
** Li,
Hui** Yuan,
Zhinian Li,
Junxian Zhang,
Lijun Jiang
Abstract:
The Y33.33Ni66.67-xAlx system has been investigated in the region 0 <= x <= 33.3. The alloys were synthesized by induction melting. Phase occurrence and structural properties were studied by X-Ray powder Diffraction (XRD). The Al solubility in each phase has been investigated by XRD and Electron Probe Micro-Analysis (EPMA). The hydrogenation properties were characterized by pressure-composition is…
▽ More
The Y33.33Ni66.67-xAlx system has been investigated in the region 0 <= x <= 33.3. The alloys were synthesized by induction melting. Phase occurrence and structural properties were studied by X-Ray powder Diffraction (XRD). The Al solubility in each phase has been investigated by XRD and Electron Probe Micro-Analysis (EPMA). The hydrogenation properties were characterized by pressure-composition isotherm measurements and kinetic curves at 473 K. For x = 0, the binary Y33.33Ni66.67 alloy crystallizes in the cubic superstructure with F4-3m space group and ordered Y vacancies. For 1.67 <= x <= 8.33, the alloys contain mainly Y(Ni, Al)2 and Y(Ni, Al)3 pseudobinary phases; while for 16.67 <= x <= 33.33 they are mainly formed by ternary line compounds Y3Ni6Al2, Y2Ni2Al and YNiAl. Contrary to the binary Y33.33Ni66.67, Y(Ni, Al)2 pseudo-binary compounds crystalize in C15 phase (space group Fd-3m ) with disordered Y vacancies. The solubility limit of Al in the C15 YNi2-yAly phase is y = 0.11 (i.e., x = 3.67). The Y(Ni, Al)3 phase changes from rhombohedral (PuNi3-type, R-3m) to hexagonal (CeNi3-type, P63/mmc) structure for x increasing from 5.00 to 6.67. Upon hydrogenation, the disproportion of C15 Y(Ni, Al)2 and losses of crystallinity of YNi and Y2Ni2Al are the main reasons causing capacity decay of Y33.33Ni66.67-xAlx (0 <= x <= 33.33) alloys upon cycling.
△ Less
Submitted 9 September, 2021;
originally announced September 2021.
-
Direct and indirect magnetocaloric effects near room temperature related to structural transitions in Y$_{0.9}$Pr$_{0.1}$Fe$_2$D$_{3.5}$ deuteride
Authors:
Valerie Paul-Boncour,
Aritz Herrero,
Vitalii Shtender,
Karine Provost,
Erik Elkaim
Abstract:
The structural and magnetic properties of Y$_{0.9}$Pr$_{0.1}$Fe$_2$D$_{3.5}$ deuteride have been investigated by synchrotron and neutron diffraction, magnetic measurements, and differential scanning calorimetry. Deuterium insertion induces a 23.5 % cell volume increase and a lowering of crystal symmetry compared to the cubic C15 parent compound (Fd-3m SG). The deuteride is monoclinic (P21/c SG) be…
▽ More
The structural and magnetic properties of Y$_{0.9}$Pr$_{0.1}$Fe$_2$D$_{3.5}$ deuteride have been investigated by synchrotron and neutron diffraction, magnetic measurements, and differential scanning calorimetry. Deuterium insertion induces a 23.5 % cell volume increase and a lowering of crystal symmetry compared to the cubic C15 parent compound (Fd-3m SG). The deuteride is monoclinic (P21/c SG) below 330 K and undergoes a first order transition between 330 and 350 K towards a pseudo-cubic structure (R-3m SG) with TO-D = 342(2) K. The compound is ferromagnetic, accompanied by a magnetostrictive effect below TC = 274 K. The analysis of the critical exponents indicates a second order type transition with a deviation from the isotropic 3D Heisenberg model towards the 3D XY model. This implies an easy plane of magnetization in agreement with cell parameter variation showing a planar magnetic orientation. A weak magnetic peak is even observed at the order-disorder transition with a maximum at 343 K. Magnetic entropy variations are characteristic of direct and reverse magnetocaloric effects at TC and TO-D respectively.
△ Less
Submitted 3 June, 2021;
originally announced June 2021.
-
TEM observations on palladium samples aged up to 8 years under tritium
Authors:
M. Segard,
E. Leroy,
B. Evin,
S. Thiebaut,
A. Fabre,
S. Challet,
V. Paul-Boncour
Abstract:
Transmission electron microscopy (TEM) experiments were carried out on aged under tritium palladium powder samples. The experiments were devoted to the study of the evolution of 3He bubbles (size, density) appearing during aging. The study, using a new sample preparation, was focused for the first time on long aging time, up to 8 years. The TEM results indicated the presence of nanometer size bubb…
▽ More
Transmission electron microscopy (TEM) experiments were carried out on aged under tritium palladium powder samples. The experiments were devoted to the study of the evolution of 3He bubbles (size, density) appearing during aging. The study, using a new sample preparation, was focused for the first time on long aging time, up to 8 years. The TEM results indicated the presence of nanometer size bubbles (2 - 3 nm in diameter) with densities close to 5x10^23 m-3.
△ Less
Submitted 3 June, 2021;
originally announced June 2021.
-
Investigation by STEM-EELS of helium density in nanobubbles formed in aged palladium tritides
Authors:
B. Evin,
E. Leroy,
M. Segard,
V. Paul-Boncour,
S. Challet,
A. Fabre,
M. Latroche
Abstract:
3He nanobubbles created by radioactive decay of tritium in palladium tritide are investigated after several years of aging. Scanning Transmission Electron Microscopy Electron Energy-Loss Spectroscopy (STEM-EELS) has been used to measure helium density from the helium K-edge around 23 eV. Helium densities were found between 20 and 140 (+/-30) He/nm3 and the corresponding nanobubble pressures range…
▽ More
3He nanobubbles created by radioactive decay of tritium in palladium tritide are investigated after several years of aging. Scanning Transmission Electron Microscopy Electron Energy-Loss Spectroscopy (STEM-EELS) has been used to measure helium density from the helium K-edge around 23 eV. Helium densities were found between 20 and 140 (+/-30) He/nm3 and the corresponding nanobubble pressures range between 0.1 and 3 (+/-0.2) GPa. Measuring helium density and map** He atoms by STEM-EELS enables to differentiate bubbles from empty cavities in the palladium tritide matrix.
△ Less
Submitted 25 May, 2021;
originally announced May 2021.
-
Thermodynamic and corrosion study of Sm$_{1-x}$Mg$_x$Ni$_y$ (y = 3.5 or 3.8) compounds forming reversible hydrides
Authors:
Véronique Charbonnier,
Nicolas Madern,
Judith Monnier,
Junxian Zhang,
Valérie Paul-Boncour,
Michel Latroche
Abstract:
AB5 compounds (A = rare earth, B = transition metal) have been widely studied as anodes for Ni-MH applications. However, they have reached their technical limitations and the search for new promising materials with high capacity is foreseen. ABy compounds (2 < y < 5) are good candidates. They are made by stacking [AB5] and [A2B4] units along the c crystallographic axis. The latter unit allows a la…
▽ More
AB5 compounds (A = rare earth, B = transition metal) have been widely studied as anodes for Ni-MH applications. However, they have reached their technical limitations and the search for new promising materials with high capacity is foreseen. ABy compounds (2 < y < 5) are good candidates. They are made by stacking [AB5] and [A2B4] units along the c crystallographic axis. The latter unit allows a large increase in capacity, while the [AB5] unit provides good cycling stability. Consequently, the AB3.8 composition (i.e. A5B19 with three [AB5] for one [A2B4]) is expected to exhibit better cycling stability than the AB3.5 (i.e. A2B7 with two [AB5] for one [A2B4]). Furthermore, substitution of rare earth by light magnesium improves both the capacity and cycling stability. In this paper, we compare the hydrogenation and corrosion properties of two binary compounds SmNi$_{3.5}$ and SmNi$_{3.8}$ and two pseudo-binary ones (Sm,Mg)Ni$_{3.5}$ and (Sm,Mg)Ni$_{3.8}$. A better solid-gas cycling stability is highlighted for the binary SmNi$_{3.8}$. The pseudo-binary compounds also exhibit higher cycling stability than the binary ones. Furthermore, their resistance to corrosion was investigated.
△ Less
Submitted 27 July, 2020;
originally announced July 2020.
-
Origin of the metamagnetic transitions in Y1-xErxFe2(H,D)4.2 compounds
Authors:
V. Paul-Boncour,
O. Isnard,
V. Shtender,
Y. Skourski,
M. Guillot
Abstract:
The structural and magnetic properties of Y1-xErxFe2 intermetallic compounds and their hydrides and deuterides Y1-xErxFe2H(D)4.2 have been investigated using X-ray diffraction and magnetic measurements under static and pulsed magnetic field up to 60 T. The intermetallics crystallize in the C15 cubic structure , whereas corresponding hydrides and deuterides crystallize in a monoclinic structure. Al…
▽ More
The structural and magnetic properties of Y1-xErxFe2 intermetallic compounds and their hydrides and deuterides Y1-xErxFe2H(D)4.2 have been investigated using X-ray diffraction and magnetic measurements under static and pulsed magnetic field up to 60 T. The intermetallics crystallize in the C15 cubic structure , whereas corresponding hydrides and deuterides crystallize in a monoclinic structure. All compounds display a linear decrease of the unit cell volume versus Er concentration; the hydrides have a 0.8% larger cell volume compared to the deuterides with same Er content. They are ferrimagnetic at low field and temperature with a compensation point at x = 0.33 for the intermetallics and x = 0.57 for the hydrides and deuterides. A sharp first order ferromagnetic-antiferromagnetic (FM-AFM) transition is observed upon heating at TFM-AFM for both hydrides and deuterides. These compounds show two different types of field induced transitions, which have different physical origin. At low temperature (T < 50 K), a forced ferri-ferromagnetic metamagnetic transition with Btrans1 = 8 T, related to the change of the Er moments orientation from antiparallel to parallel Fe moment, is observed. Btrans1 is not sensitive to Er concentration, temperature and isotope effect. A second metamagnetic transition resulting from antiferromagnetic to ferrimagnetic state is also observed. The transition field Btrans2 increases linearly versus temperature and relates to the itinerant electron metamagnetic behavior of the Fe sublattice. An onset temperature TM0 is obtained by extrapolating TFM-AFM (B) at zero field. TM0 decreases linearly versus the Er content and is 45(5) K higher for the hydrides compared to the corresponding deuteride. The evolution of TM0 versus cell volume shows that it cannot be attributed exclusively to a pure volume effect and that electronic effects should also be considered.
△ Less
Submitted 22 July, 2020;
originally announced July 2020.
-
Investigation of H Sorption and Corrosion Properties of Sm2MnxNi7-x (0<x<0.5) Intermetallic Compounds Forming Reversible Hydrides
Authors:
Nicolas Madern,
Veronique Charbonnier,
Judith Monnier,
Junxian Zhang,
Valerie Paul-Boncour,
Michel Latroche
Abstract:
Intermetallic compounds are key materials for energy transition as they form reversible hydrides that can be used for solid state hydrogen storage or as anodes in batteries. ABy compounds (A = Rare Earth (RE); B = transition metal; 2 < y < 5) are good candidates to fulfill the required properties for practical applications. They can be described as stacking of AB5 and AB2 sub-units along the c cry…
▽ More
Intermetallic compounds are key materials for energy transition as they form reversible hydrides that can be used for solid state hydrogen storage or as anodes in batteries. ABy compounds (A = Rare Earth (RE); B = transition metal; 2 < y < 5) are good candidates to fulfill the required properties for practical applications. They can be described as stacking of AB5 and AB2 sub-units along the c crystallographic axis. The latter sub-unit brings a larger capacity, while the former one provides a better cycling stability. However, ABy binaries do not show good enough properties for applications. Upon hydrogenation, they exhibit multiplateau behavior and poor reversibility, attributed to H induced amorphization. These drawbacks can be overcome by chemical substitutions on the A and/or the B sites leading to stabilized reversible hydrides. The present work focuses on the pseudo-binary Sm2MnxNi7-x system (0 <= x < 0.5). The structural, thermodynamic and corrosion properties are analyzed and interpreted by means of X-ray diffraction, chemical analysis, scanning electron microscopy, thermogravimetric analysis and magnetic measurements. Unexpected cell parameter variations are reported and interpreted regarding possible formation of structural defects and uneven Mn distribution within the Ni sublattice. Reversible capacity is improved for x > 0.3 leading to larger and flatter isotherm curves, allowing for reversible capacity >1.4 wt %. Regarding corrosion, the binary compound corrodes in alkaline medium to form rare earth hydroxide and nanoporous nickel. As for the Mn-substituted compounds, a new corrosion product is formed in addition to those above mentioned, as manganese initiates a sacrificial anode mechanism taking place at the early corrosion stage.
△ Less
Submitted 9 July, 2020;
originally announced July 2020.
-
Correlations between stacked structures and weak itinerant magnetic properties of La$_{2-x}$ Y$_x $ Ni$_7$ compounds
Authors:
Valérie Paul-Boncour,
Jean-Claude Crivello,
Nicolas Madern,
Junxian Zhang,
Léopold Diop,
Véronique Charbonnier,
Judith Monnier,
Michel Latroche
Abstract:
Hexagonal La$_2$Ni$_7$ and rhombohedral Y$_2$Ni$_7$ are weak itinerant antiferromagnet (wAFM) and ferromagnet (wFM), respectively. The crystal structure and magnetic properties of $A_2B_7$ intermetallic compounds ($A$ = La, Y, $B$ = Ni) have been investigated combining X-ray powder diffraction and magnetic measurements. The La$_{2-x}$Y$_x$Ni$_7$ intermetallic compounds with $0 \leq x \leq 1$ cryst…
▽ More
Hexagonal La$_2$Ni$_7$ and rhombohedral Y$_2$Ni$_7$ are weak itinerant antiferromagnet (wAFM) and ferromagnet (wFM), respectively. The crystal structure and magnetic properties of $A_2B_7$ intermetallic compounds ($A$ = La, Y, $B$ = Ni) have been investigated combining X-ray powder diffraction and magnetic measurements. The La$_{2-x}$Y$_x$Ni$_7$ intermetallic compounds with $0 \leq x \leq 1$ crystallize in the Ce$_{2}$Ni$_7$-type hexagonal structure with Y preferentially located in the [$AB_2$] units. The compounds with larger Y content ($1.2 \leq x < 2$) crystallize in both hexagonal and rhombohedral (Gd$_2$Co$_7$-type) structures with a progressive substitution of Y for La in the $A$ sites belonging to the [$AB_5$] units. Y$_2$Ni$_7$ crystallizes in the rhombohedral structure only. The average cell volume decreases linearly versus Y content, whereas the c/a ratio presents a minimum at $x = 1$ due to geometric constrains. The magnetic properties are strongly dependent on the structure type and the Y content. La$_{2}$Ni$_7$ displays a complex metamagnetic behavior with split AFM peaks. Compounds with x = 0.25 and 0.5 display a wAFM ground state and two metamagnetic transitions, the first one towards an intermediate wAFM state and the second one towards a FM state.T$_N$ and the second critical field increase with the Y content, indicating a stabilization of the AFM state. LaYNi$_7$, which is as the boundary between the two structure types, presents a very wFM state at low field and an AFM state as the applied field increases. All the compounds with $x > 1$ and containing a rhombohedral phase are wFM with $T_C$ = 53(2) K. In addition to the experimental studies, first principles calculations using spin polarization have been performed to interpret the evolution of both structural phase stability and magnetic ordering for $0 \leq x < 2$.
△ Less
Submitted 24 July, 2020; v1 submitted 6 May, 2019;
originally announced May 2019.
-
Relation between the weak itinerant magnetism in $A_2$Ni$_7$ compounds ($A$ = Y, La) and their stacked crystal structures
Authors:
Jean-Claude Crivello,
Valérie Paul-Boncour
Abstract:
The weak itinerant magnetic properties of $A_2$Ni$_7$ compounds with $A$ = {Y, La} have been investigated using electronic band structure calculations in the relation with their polymorphic crystal structures. These compounds crystallizes in two structures resulting from the stacking of two and three blocks of [$A_2$Ni$_4$ + 2 $A$Ni$_5$] units for hexagonal $2H$-La$_2$Ni$_7$ (Ce$_2$Ni$_7$ type) an…
▽ More
The weak itinerant magnetic properties of $A_2$Ni$_7$ compounds with $A$ = {Y, La} have been investigated using electronic band structure calculations in the relation with their polymorphic crystal structures. These compounds crystallizes in two structures resulting from the stacking of two and three blocks of [$A_2$Ni$_4$ + 2 $A$Ni$_5$] units for hexagonal $2H$-La$_2$Ni$_7$ (Ce$_2$Ni$_7$ type) and rhombohedral $3R$-Y$_2$Ni$_7$ (Gd$_2$Co$_7$ type) respectively. Experimentally, $2H$-La$_2$Ni$_7$ is a weak itinerant antiferromagnet whereas $3R$-Y$_2$Ni$_7$ is a weak itinerant ferromagnet. From the present first principles calculation within non-spin polarized state, both compounds present an electronic density of state with a sharp and narrow peak centered at the Fermi level corresponding to flat bands from $3d$-Ni. This induces a magnetic instability and both compounds are more stable in a ferromagnetic (FM) order compared to a paramagnetic state ($ΔE \simeq$ -35 meV/f.u.). The magnetic moment of each of the five Ni sites varies with their positions relative to the [$A_2$Ni$_4$] and [$A$Ni$_5$] units: they are minimum in the [$A_2$Ni$_4$] unit and maximum at the interface between two [$A$Ni$_5$] units. For $2H$-La$_2$Ni$_7$, an antiferromagnetic (AFM) structure has been proposed and found with an energy comparable to that of the FM state. This AFM structure is described by two FM unit blocks of opposite Ni spin sign separated by a non-magnetic layer at z = 0 and $\frac12$. The Ni ($2a$) atoms belonging to this intermediate layer are located in the [La$_2$Ni$_4$] unit and are at a center of symmetry of the hexagonal cell ($P6_3/mmc$) where the resultant molecular field is cancelled. Further non-collinear spin calculations have been performed to determine the Ni moment orientations which are found preferentially parallel to the $c$ axis for both FM and AFM structures.
△ Less
Submitted 7 January, 2020; v1 submitted 27 March, 2019;
originally announced March 2019.