Fabrication of highly dense isotropic Nd-Fe-B bonded magnets via extrusion-based additive manufacturing
Authors:
Ling Li,
Kodey Jones,
Brian Sales,
Jason L. Pries,
I. C. Nlebedim,
Ke **,
Hongbin Bei,
Brian Post,
Michael Kesler,
Orlando Rios,
Vlastimil Kunc,
Robert Fredette,
John Ormerod,
Aaron Williams,
Thomas A. Lograsso,
M. Parans Paranthaman
Abstract:
Isotropic bonded magnets with a high loading fraction of 70 vol.% Nd-Fe-B are fabricated via an extrusion-based additive manufacturing, or 3D printing system that enables rapid production of large parts for the first time. The density of the printed magnet is 5.15 g/cm3. The room temperature magnetic properties are: intrinsic coercivity Hci = 8.9 kOe (708.2 kA/m), remanence Br = 5.8 kG (0.58 Tesla…
▽ More
Isotropic bonded magnets with a high loading fraction of 70 vol.% Nd-Fe-B are fabricated via an extrusion-based additive manufacturing, or 3D printing system that enables rapid production of large parts for the first time. The density of the printed magnet is 5.15 g/cm3. The room temperature magnetic properties are: intrinsic coercivity Hci = 8.9 kOe (708.2 kA/m), remanence Br = 5.8 kG (0.58 Tesla), and energy product (BH)max = 7.3 MGOe (58.1 kJ/m3). The as-printed magnets are then coated with two types of polymers, both of which improve the thermal stability at 127 °C as revealed by flux aging loss measurements. Tensile tests performed at 25 °C and 100 °C show that the ultimate tensile stress (UTS) increases with increasing loading fraction of the magnet powder, and decreases with increasing temperature. AC magnetic susceptibility and resistivity measurements show that the 3D printed Nd-Fe-B bonded magnets exhibit extremely low eddy current loss and high resistivity. Finally, we show that through back electromotive force measurements that motors installed with 3D printed Nd-Fe-B magnets exhibit similar performance as compared to those installed with sintered ferrites.
△ Less
Submitted 23 June, 2017;
originally announced June 2017.
-
Optimization of a Non-arsenic Iron-based Superconductor for Wire Fabrication
Authors:
Jonathan E. Mitchell,
Daniel A. Hillesheim,
Craig A. Bridges,
M. Parans Paranthaman,
Kris Gofryk,
Mike Rindfleisch,
Mike Tomsic,
Athena S. Sefat
Abstract:
We report on the optimization of synthesis of iron-selenide (non-arsenic) superconducting powders that are based on '122' composition, with optimal Tc = 38 K and Jc = 10^5 A/cm2 (4 K). We also report on the wire proof-of concept for these materials, by producing ~ 40 ft of wire that produce Ic. The 122 selenides are more difficult to synthesize and have more complex crystal structures compared to…
▽ More
We report on the optimization of synthesis of iron-selenide (non-arsenic) superconducting powders that are based on '122' composition, with optimal Tc = 38 K and Jc = 10^5 A/cm2 (4 K). We also report on the wire proof-of concept for these materials, by producing ~ 40 ft of wire that produce Ic. The 122 selenides are more difficult to synthesize and have more complex crystal structures compared to '11' selenides (FeSe and FeSe1-xTex), but they do offer higher Tc and might provoke a natural extension for 11 work.
△ Less
Submitted 9 December, 2014;
originally announced December 2014.
-
Orienting oxygen vacancies for fast catalytic reaction
Authors:
Hyoungjeen Jeen,
Zhonghe Bi,
Woo Seok Choi,
Matthew F. Chisholm,
Craig A. Bridges,
M. Parans Paranthaman,
Ho Nyung Lee
Abstract:
Catalysis is indispensable to chemical processes and relevant to many aspects of modern life. Owing to the intriguing electronic structures and good ionic properties, multivalent transition metal oxides have attracted attention as key catalysts for various energy and environmental applications. Here, we demonstrate that brownmillerite strontium cobaltite (SrCoO2.5) can be a good cathode material f…
▽ More
Catalysis is indispensable to chemical processes and relevant to many aspects of modern life. Owing to the intriguing electronic structures and good ionic properties, multivalent transition metal oxides have attracted attention as key catalysts for various energy and environmental applications. Here, we demonstrate that brownmillerite strontium cobaltite (SrCoO2.5) can be a good cathode material for sold oxide fuel cells and rechargeable batteries due to the open oxygen frameworks. When the orientation of oxygen vacancy channels (OVCs) is properly controlled, one can drastically increase the surface oxygen exchange rate approximately up to two orders of magnitude. The improved oxygen reduction kinetics is attributed to a substantial decrease in the thermal activation energy. Importantly, the strong enhancement of crystallographic orientation-dependent oxygen reduction reaction required the creation of neither structural disorders nor chemical do**. Thus, our epitaxial approach can pave a novel pathway to providing precise interpretation of oxygen reduction reactions and to develo** oxide-based energy materials.
△ Less
Submitted 3 October, 2013;
originally announced October 2013.
-
Effective Vortex Pinning in MgB2 thin films
Authors:
Y. Bugoslavsky,
L. Cowey,
T. J. Tate,
G. K. Perkins,
J. Moore,
Z. Lockman,
A. Berenov,
J. L. MacManus-Driscoll,
A. D. Caplin,
L. F. Cohen,
H Y Zhai,
H M Christen,
M P Paranthaman,
D H Lowndes,
M H Jo,
M G Blamire
Abstract:
We discuss pinning properties of MgB2 thin films grown by pulsed-laser deposition (PLD) and by electron-beam (EB) evaporation. Two mechanisms are identified that contribute most effectively to the pinning of vortices in randomly oriented films. The EB process produces low defected crystallites with small grain size providing enhanced pinning at grain boundaries without degradation of Tc. The PLD…
▽ More
We discuss pinning properties of MgB2 thin films grown by pulsed-laser deposition (PLD) and by electron-beam (EB) evaporation. Two mechanisms are identified that contribute most effectively to the pinning of vortices in randomly oriented films. The EB process produces low defected crystallites with small grain size providing enhanced pinning at grain boundaries without degradation of Tc. The PLD process produces films with structural disorder on a scale less that the coherence length that further improves pinning, but also depresses Tc.
△ Less
Submitted 2 July, 2002;
originally announced July 2002.
-
The structure of the superconducting gap in MgB2 from point-contact spectroscopy
Authors:
Y. Bugoslavsky,
Y. Miyoshi,
G. K. Perkins,
A. V. Berenov,
Z. Lockman,
J. L. MacManus-Driscoll,
L. F. Cohen,
A. D. Caplin,
H. Y. Zhai,
M. P. Paranthaman,
H. M. Christen,
M. Blamire
Abstract:
We have studied the structure of the superconducting gap in MgB2 thin films by means of point-contact spectroscopy using a gold tip. The films were produced by depositing pure boron on a sapphire substrate, using e-beam evaporation, followed by reaction with magnesium vapour. The films have a Tc of 38.6 +- 0.3 K and resistivity of about 20 microOhm cm at 40 K. The point-contact spectra prove dir…
▽ More
We have studied the structure of the superconducting gap in MgB2 thin films by means of point-contact spectroscopy using a gold tip. The films were produced by depositing pure boron on a sapphire substrate, using e-beam evaporation, followed by reaction with magnesium vapour. The films have a Tc of 38.6 +- 0.3 K and resistivity of about 20 microOhm cm at 40 K. The point-contact spectra prove directly the existence of a multi-valued order parameter in MgB2, with two distinct values of the gap, DELTA1=2.3+-0.3 meV and DELTA2=6.2+-0.7 meV at 4.2 K. Analysis of the spectra in terms of the Blonder-Tinkham-Klapwijk model reveals that both gaps close simultaneously at the Tc of the film. Possible mechanisms that can explain the intrinsic co-existence of two values of the gap are discussed.
△ Less
Submitted 15 October, 2001;
originally announced October 2001.
-
Microwave Power, DC Magnetic Field, Frequency and Temperature Dependence of the Surface Resistance of MgB2
Authors:
A. A. Zhukov,
A. Purnell,
Y. Miyoshi,
Y. Bugoslavsky,
Z. Lockman,
A. Berenov,
J. L. MacManus-Driscoll,
L. F. Cohen,
H. Y. Zhai,
H. M. Christen,
M. P. Paranthaman,
D. H. Lowndes,
M. H. Jo,
M. G. Blamire,
Ling Hao,
J. C. Gallop
Abstract:
The microwave power, dc magnetic field, frequency and temperature dependence of the surface resistance of MgB2 films and powder samples were studied. Sample quality is relatively easy to identify by a number of characteristics, the most clear being the breakdown in the omega squared law for poor quality samples. Analysis of the experimental data suggests the most attractive procedure for high qu…
▽ More
The microwave power, dc magnetic field, frequency and temperature dependence of the surface resistance of MgB2 films and powder samples were studied. Sample quality is relatively easy to identify by a number of characteristics, the most clear being the breakdown in the omega squared law for poor quality samples. Analysis of the experimental data suggests the most attractive procedure for high quality film growth for technical applications.
△ Less
Submitted 21 September, 2001;
originally announced September 2001.
-
Temperature dependence of the microwave surface impedance measured on different kinds of MgB$_2$ samples
Authors:
A. A. Zhukov,
L. F. Cohen,
A. Purnell,
Y. Bugoslavsky,
A. Berenov,
J. L. MacManus-Driscoll,
H. Y Zhai,
Hans M. Christen,
Mariappan P. Paranthaman,
Douglas H. Lowndes,
M. A. Jo,
M. C. Blamire,
Ling Hao,
J. Gallop
Abstract:
In this paper we present the results of measurements of the microwave surface impedance of a powder sample and two films of MgB$_2$. One film has $T_c=30$ K and is not textured, the other is partially c-axis orientated with $T_c=38$ K. These samples show different types of temperature dependence of the field penetration depth: linear for the powder sample, exponential with $Δ/kT_c<1.76$ (film wi…
▽ More
In this paper we present the results of measurements of the microwave surface impedance of a powder sample and two films of MgB$_2$. One film has $T_c=30$ K and is not textured, the other is partially c-axis orientated with $T_c=38$ K. These samples show different types of temperature dependence of the field penetration depth: linear for the powder sample, exponential with $Δ/kT_c<1.76$ (film with $T_c=30$ K) and strong coupling behaviour with $Δ/kT_c\sim 2.25$ (film with $T_c=38$ K). The results are well described in terms of an anisotropic gap model or presence of a slightly deficient MgB$_2$ phase. The data set for all samples - taken as a whole cannot be fitted into a two gap scenario.
△ Less
Submitted 15 July, 2001; v1 submitted 11 July, 2001;