Showing 1–20 of 20 results for author: Paranthaman, M

Fabrication of highly dense isotropic Nd-Fe-B bonded magnets via extrusion-based additive manufacturing

Authors: Ling Li, Kodey Jones, Brian Sales, Jason L. Pries, I. C. Nlebedim, Ke **, Hongbin Bei, Brian Post, Michael Kesler, Orlando Rios, Vlastimil Kunc, Robert Fredette, John Ormerod, Aaron Williams, Thomas A. Lograsso, M. Parans Paranthaman

Abstract: Isotropic bonded magnets with a high loading fraction of 70 vol.% Nd-Fe-B are fabricated via an extrusion-based additive manufacturing, or 3D printing system that enables rapid production of large parts for the first time. The density of the printed magnet is 5.15 g/cm3. The room temperature magnetic properties are: intrinsic coercivity Hci = 8.9 kOe (708.2 kA/m), remanence Br = 5.8 kG (0.58 Tesla… ▽ More Isotropic bonded magnets with a high loading fraction of 70 vol.% Nd-Fe-B are fabricated via an extrusion-based additive manufacturing, or 3D printing system that enables rapid production of large parts for the first time. The density of the printed magnet is 5.15 g/cm3. The room temperature magnetic properties are: intrinsic coercivity Hci = 8.9 kOe (708.2 kA/m), remanence Br = 5.8 kG (0.58 Tesla), and energy product (BH)max = 7.3 MGOe (58.1 kJ/m3). The as-printed magnets are then coated with two types of polymers, both of which improve the thermal stability at 127 °C as revealed by flux aging loss measurements. Tensile tests performed at 25 °C and 100 °C show that the ultimate tensile stress (UTS) increases with increasing loading fraction of the magnet powder, and decreases with increasing temperature. AC magnetic susceptibility and resistivity measurements show that the 3D printed Nd-Fe-B bonded magnets exhibit extremely low eddy current loss and high resistivity. Finally, we show that through back electromotive force measurements that motors installed with 3D printed Nd-Fe-B magnets exhibit similar performance as compared to those installed with sintered ferrites. △ Less

Submitted 23 June, 2017; originally announced June 2017.

Optimization of a Non-arsenic Iron-based Superconductor for Wire Fabrication

Authors: Jonathan E. Mitchell, Daniel A. Hillesheim, Craig A. Bridges, M. Parans Paranthaman, Kris Gofryk, Mike Rindfleisch, Mike Tomsic, Athena S. Sefat

Abstract: We report on the optimization of synthesis of iron-selenide (non-arsenic) superconducting powders that are based on '122' composition, with optimal Tc = 38 K and Jc = 10^5 A/cm2 (4 K). We also report on the wire proof-of concept for these materials, by producing ~ 40 ft of wire that produce Ic. The 122 selenides are more difficult to synthesize and have more complex crystal structures compared to… ▽ More We report on the optimization of synthesis of iron-selenide (non-arsenic) superconducting powders that are based on '122' composition, with optimal Tc = 38 K and Jc = 10^5 A/cm2 (4 K). We also report on the wire proof-of concept for these materials, by producing ~ 40 ft of wire that produce Ic. The 122 selenides are more difficult to synthesize and have more complex crystal structures compared to '11' selenides (FeSe and FeSe1-xTex), but they do offer higher Tc and might provoke a natural extension for 11 work. △ Less

Submitted 9 December, 2014; originally announced December 2014.

Comments: 13 pages, 7 figures; Submitted to SuST

Journal ref: Superconductor Science & Technology 28, 045018 (2015)

Orienting oxygen vacancies for fast catalytic reaction

Authors: Hyoungjeen Jeen, Zhonghe Bi, Woo Seok Choi, Matthew F. Chisholm, Craig A. Bridges, M. Parans Paranthaman, Ho Nyung Lee

Abstract: Catalysis is indispensable to chemical processes and relevant to many aspects of modern life. Owing to the intriguing electronic structures and good ionic properties, multivalent transition metal oxides have attracted attention as key catalysts for various energy and environmental applications. Here, we demonstrate that brownmillerite strontium cobaltite (SrCoO2.5) can be a good cathode material f… ▽ More Catalysis is indispensable to chemical processes and relevant to many aspects of modern life. Owing to the intriguing electronic structures and good ionic properties, multivalent transition metal oxides have attracted attention as key catalysts for various energy and environmental applications. Here, we demonstrate that brownmillerite strontium cobaltite (SrCoO2.5) can be a good cathode material for sold oxide fuel cells and rechargeable batteries due to the open oxygen frameworks. When the orientation of oxygen vacancy channels (OVCs) is properly controlled, one can drastically increase the surface oxygen exchange rate approximately up to two orders of magnitude. The improved oxygen reduction kinetics is attributed to a substantial decrease in the thermal activation energy. Importantly, the strong enhancement of crystallographic orientation-dependent oxygen reduction reaction required the creation of neither structural disorders nor chemical do**. Thus, our epitaxial approach can pave a novel pathway to providing precise interpretation of oxygen reduction reactions and to develo** oxide-based energy materials. △ Less

Submitted 3 October, 2013; originally announced October 2013.

Journal ref: Adv. Mater. 25, 6459 (2013)

Effective Vortex Pinning in MgB2 thin films

Authors: Y. Bugoslavsky, L. Cowey, T. J. Tate, G. K. Perkins, J. Moore, Z. Lockman, A. Berenov, J. L. MacManus-Driscoll, A. D. Caplin, L. F. Cohen, H Y Zhai, H M Christen, M P Paranthaman, D H Lowndes, M H Jo, M G Blamire

Abstract: We discuss pinning properties of MgB2 thin films grown by pulsed-laser deposition (PLD) and by electron-beam (EB) evaporation. Two mechanisms are identified that contribute most effectively to the pinning of vortices in randomly oriented films. The EB process produces low defected crystallites with small grain size providing enhanced pinning at grain boundaries without degradation of Tc. The PLD… ▽ More We discuss pinning properties of MgB2 thin films grown by pulsed-laser deposition (PLD) and by electron-beam (EB) evaporation. Two mechanisms are identified that contribute most effectively to the pinning of vortices in randomly oriented films. The EB process produces low defected crystallites with small grain size providing enhanced pinning at grain boundaries without degradation of Tc. The PLD process produces films with structural disorder on a scale less that the coherence length that further improves pinning, but also depresses Tc. △ Less

Submitted 2 July, 2002; originally announced July 2002.

Electrodynamic response of MgB2 sintered pellets and thin films

Authors: A. Andreone, G. Ausanio, E. Di Gennaro, G. Lamura, M. Salluzzo, J. Le Cochec, A. Gauzzi, C. Cantoni, M. Paranthaman, G. Giunchi, S. Ceresara

Abstract: We present a study of the electrodynamic response of MgB2 pellets and thin film samples exhibiting critical temperatures ranging between 26 and 38 K. We have performed accurate measurements of the surface impedance ZS =RS+iXS as a function of the temperature and of the magnitude of the electromagnetic field. The temperature variation and the field dependence of ZS was measured by a dielectric re… ▽ More We present a study of the electrodynamic response of MgB2 pellets and thin film samples exhibiting critical temperatures ranging between 26 and 38 K. We have performed accurate measurements of the surface impedance ZS =RS+iXS as a function of the temperature and of the magnitude of the electromagnetic field. The temperature variation and the field dependence of ZS was measured by a dielectric resonator cavity technique in the microwave region. In particular, the temperature variation of the magnetic penetration depth was also determined in the RF region by a single coil mutual inductance method. In the case of the films, for T<TC/2 a clear exponential behavior of the penetration depth is observed, which can be explained by a simple BCS s-wave model with a reduced value of the energy gap. On the contrary, pellets show no evidence of saturation, and the experimental results strictly follow a quadratic dependence down to the lowest temperatures. This behavior can be induced by the presence of metallic Mg inclusions that may locally depress the gap. The analysis of the field dependence of the surface impedance in the microwave region confirms that the electrodynamic response of MgB2 is dominated by different sources of dissipation, depending on the sample history, likely to be ascribed to the predominance of grain boundaries or normal regions on its surface. △ Less

Submitted 31 October, 2001; originally announced October 2001.

Comments: To appear as a chapter in "Studies of High Temperature Superconductors", Vol. 41, A.V. Narlikar ed., Nova Sci. Publ., New York. (submitted October 5, 2001). 21 pages, 16 figures

The structure of the superconducting gap in MgB2 from point-contact spectroscopy

Authors: Y. Bugoslavsky, Y. Miyoshi, G. K. Perkins, A. V. Berenov, Z. Lockman, J. L. MacManus-Driscoll, L. F. Cohen, A. D. Caplin, H. Y. Zhai, M. P. Paranthaman, H. M. Christen, M. Blamire

Abstract: We have studied the structure of the superconducting gap in MgB2 thin films by means of point-contact spectroscopy using a gold tip. The films were produced by depositing pure boron on a sapphire substrate, using e-beam evaporation, followed by reaction with magnesium vapour. The films have a Tc of 38.6 +- 0.3 K and resistivity of about 20 microOhm cm at 40 K. The point-contact spectra prove dir… ▽ More We have studied the structure of the superconducting gap in MgB2 thin films by means of point-contact spectroscopy using a gold tip. The films were produced by depositing pure boron on a sapphire substrate, using e-beam evaporation, followed by reaction with magnesium vapour. The films have a Tc of 38.6 +- 0.3 K and resistivity of about 20 microOhm cm at 40 K. The point-contact spectra prove directly the existence of a multi-valued order parameter in MgB2, with two distinct values of the gap, DELTA1=2.3+-0.3 meV and DELTA2=6.2+-0.7 meV at 4.2 K. Analysis of the spectra in terms of the Blonder-Tinkham-Klapwijk model reveals that both gaps close simultaneously at the Tc of the film. Possible mechanisms that can explain the intrinsic co-existence of two values of the gap are discussed. △ Less

Submitted 15 October, 2001; originally announced October 2001.

Comments: 9 pages, 9 figures

Study of the microwave electrodynamic response of MgB2 thin films

Authors: A. Andreone, A. Cassinese, C. Cantoni, E. Di Gennaro, G. Lamura, M. G. Maglione, M. Paranthaman, M. Salluzzo, R. Vaglio

Abstract: We present a study on the power dependence of the microwave surface impedance in thin films of the novel superconductor MgB2. 500 nm thick samples exhibiting critical temperatures ranging between 26 and 38 K are synthesized by an ex-situ post-anneal of e-beam evaporated boron in the presence of an Mg vapor at 900 C. Preliminary results on films grown in situ by a high rate magnetron sputtering t… ▽ More We present a study on the power dependence of the microwave surface impedance in thin films of the novel superconductor MgB2. 500 nm thick samples exhibiting critical temperatures ranging between 26 and 38 K are synthesized by an ex-situ post-anneal of e-beam evaporated boron in the presence of an Mg vapor at 900 C. Preliminary results on films grown in situ by a high rate magnetron sputtering technique from stoichiometric MgB2 and Mg targets are also reported. Microwave measurements have been carried out employing a dielectrically loaded niobium superconducting cavity operating at 19.8 GHz and 4 K. The study shows that the electrodynamic response of MgB2 films is presently dominated by extrinsic sources of dissipation, appearing already at low microwave power, likely to be ascribed to the presence of grain boundaries and normal inclusions in the samples. △ Less

Submitted 27 September, 2001; v1 submitted 25 September, 2001; originally announced September 2001.

Comments: 10 pages, 3 figures, proceedings of the conference EUCAS 2001, submitted to Physica C

Microwave Power, DC Magnetic Field, Frequency and Temperature Dependence of the Surface Resistance of MgB2

Authors: A. A. Zhukov, A. Purnell, Y. Miyoshi, Y. Bugoslavsky, Z. Lockman, A. Berenov, J. L. MacManus-Driscoll, L. F. Cohen, H. Y. Zhai, H. M. Christen, M. P. Paranthaman, D. H. Lowndes, M. H. Jo, M. G. Blamire, Ling Hao, J. C. Gallop

Abstract: The microwave power, dc magnetic field, frequency and temperature dependence of the surface resistance of MgB2 films and powder samples were studied. Sample quality is relatively easy to identify by a number of characteristics, the most clear being the breakdown in the omega squared law for poor quality samples. Analysis of the experimental data suggests the most attractive procedure for high qu… ▽ More The microwave power, dc magnetic field, frequency and temperature dependence of the surface resistance of MgB2 films and powder samples were studied. Sample quality is relatively easy to identify by a number of characteristics, the most clear being the breakdown in the omega squared law for poor quality samples. Analysis of the experimental data suggests the most attractive procedure for high quality film growth for technical applications. △ Less

Submitted 21 September, 2001; originally announced September 2001.

Comments: 14 Pages, 4 Figures

Temperature dependence of the microwave surface impedance measured on different kinds of MgB$_2$ samples

Authors: A. A. Zhukov, L. F. Cohen, A. Purnell, Y. Bugoslavsky, A. Berenov, J. L. MacManus-Driscoll, H. Y Zhai, Hans M. Christen, Mariappan P. Paranthaman, Douglas H. Lowndes, M. A. Jo, M. C. Blamire, Ling Hao, J. Gallop

Abstract: In this paper we present the results of measurements of the microwave surface impedance of a powder sample and two films of MgB$_2$. One film has $T_c=30$ K and is not textured, the other is partially c-axis orientated with $T_c=38$ K. These samples show different types of temperature dependence of the field penetration depth: linear for the powder sample, exponential with $Δ/kT_c<1.76$ (film wi… ▽ More In this paper we present the results of measurements of the microwave surface impedance of a powder sample and two films of MgB$_2$. One film has $T_c=30$ K and is not textured, the other is partially c-axis orientated with $T_c=38$ K. These samples show different types of temperature dependence of the field penetration depth: linear for the powder sample, exponential with $Δ/kT_c<1.76$ (film with $T_c=30$ K) and strong coupling behaviour with $Δ/kT_c\sim 2.25$ (film with $T_c=38$ K). The results are well described in terms of an anisotropic gap model or presence of a slightly deficient MgB$_2$ phase. The data set for all samples - taken as a whole cannot be fitted into a two gap scenario. △ Less

Submitted 15 July, 2001; v1 submitted 11 July, 2001; originally announced July 2001.

Comments: 4 pages, 3 figures

Far-infrared optical conductivity gap in superconducting MgB2 films

Authors: R. A. Kaindl, M. A. Carnahan, J. Orenstein, D. S. Chemla, H. M. Christen, H. Zhai, M. Paranthaman, D. H. Lowndes

Abstract: We report the first study of the optical conductivity of MgB2 covering the range of its superconducting energy gap. Terahertz time-domain spectroscopy is utilized to determine the complex, frequency-dependent conductivity of thin films. The imaginary part reveals an inductive reponse due to the emergence of the superconducting condensate. The real part exhibits a strong depletion of oscillator s… ▽ More We report the first study of the optical conductivity of MgB2 covering the range of its superconducting energy gap. Terahertz time-domain spectroscopy is utilized to determine the complex, frequency-dependent conductivity of thin films. The imaginary part reveals an inductive reponse due to the emergence of the superconducting condensate. The real part exhibits a strong depletion of oscillator strength near 5 meV resulting from the opening of a superconducting energy gap. The gap ratio of 2Delta/kTc = 1.9 is well below the weak-coupling value, pointing to complex behavior in this novel superconductor △ Less

Submitted 18 June, 2001; originally announced June 2001.

Comments: 4 pages, 3 figures

Journal ref: Phys. Rev. Lett. 88, 027003 (2002).

Unusual Hall Effect in Superconducting MgB$_2$ Films: Analogy to High-T$_c$ Cuprates

Authors: R. **, M. Paranthaman, H. Y. Zhai, H. M. Christen, D. K. Christen, D. Mandrus

Abstract: We have investigated the temperature and magnetic field dependence of the Hall coefficient of two well-characterized superconducting MgB$_2$ films (T$_{c0}$=38.0 K) in both the normal and superconducting states. Our results show that the normal-state Hall coefficient R$_H$ is positive and increases with decreasing temperature, independent of the applied magnetic field. Below T$_c$(H), R$_H$ decr… ▽ More We have investigated the temperature and magnetic field dependence of the Hall coefficient of two well-characterized superconducting MgB$_2$ films (T$_{c0}$=38.0 K) in both the normal and superconducting states. Our results show that the normal-state Hall coefficient R$_H$ is positive and increases with decreasing temperature, independent of the applied magnetic field. Below T$_c$(H), R$_H$ decreases rapidly with temperature and changes sign before it reaches zero. The position and magnitude at which R$_H$ shows a minimum depends on the applied field. Quantitative analysis of our data indicates that the Hall response of MgB$_2$ behaves very similarly to that of high-T$_c$ cuprates: R$_H$ $\propto$ T and cot$θ_H$ $\propto$ T$^2$ in the normal state, and a sign reversal of R$_H$ in the mixed state. This suggests that the B-B layers in MgB$_2$, like the Cu-O planes in high-T$_c$ cuprates, play an important role in the electrical transport properties. △ Less

Submitted 23 April, 2001; originally announced April 2001.

Degradation of superconducting properties in MgB2 films by exposure to water

Authors: H Y Zhai, H M Christen, L Zhang, M Paranthaman, P H Fleming, D H Lowndes

Abstract: The effect of water exposure on MgB2 is studied by submerging an 800 nm thick MgB2 film into deionized water at room temperature for 1 hour, 4 hours, 10 hours, and 15 hours, and by analyzing the resulting material using scanning electron microscopy and resistance vs. temperature measurements. It is clearly observed that Tconset of these films (obtained by an ex-situ reaction of a e-beam evaporat… ▽ More The effect of water exposure on MgB2 is studied by submerging an 800 nm thick MgB2 film into deionized water at room temperature for 1 hour, 4 hours, 10 hours, and 15 hours, and by analyzing the resulting material using scanning electron microscopy and resistance vs. temperature measurements. It is clearly observed that Tconset of these films (obtained by an ex-situ reaction of a e-beam evaporated boron layer) remains unchanged throughout this process, indicating that at least a portion of the sample retains its original bulk-like properties. The data is consistent with an interpretation in which a portion of the exposed film - likely the region closest to the substrate - becomes superconducting only at about 25 K. It is possible that this low-Tc region already exists in the as-prepared film, and we observe that its Tc coincides with that of MgB2 films obtained by annealing precursor films prepared by pulsed laser deposition. Therefore the data presented here not only illustrate the degradation of MgB2 in water but also shed light onto the differences and similarities between films obtained via different routes. △ Less

Submitted 17 April, 2001; originally announced April 2001.

Comments: 5 pages, 2 Figures, 1 Tables, 19 references and big image of figure 2 added

Effect of Carbon-Do** in Bulk Superconducting MgB2 Samples

Authors: M. Paranthaman, J. R. Thompson, D. K. Christen

Abstract: Bulk superconducting samples of MgB2 were prepared by solid state reaction of stoichiometric quantities of Mg turnings and B in a sealed Ta cylinder at 890 C for 2 hours. The as-synthesized MgB2 samples had a Tc of 39 K, as defined as the onset of diamagnetism. The crystal symmetry was found to be hexagonal with lattice parameters, a=3.0856 A, and c=3.5199 A, similar to the literature values. To… ▽ More Bulk superconducting samples of MgB2 were prepared by solid state reaction of stoichiometric quantities of Mg turnings and B in a sealed Ta cylinder at 890 C for 2 hours. The as-synthesized MgB2 samples had a Tc of 39 K, as defined as the onset of diamagnetism. The crystal symmetry was found to be hexagonal with lattice parameters, a=3.0856 A, and c=3.5199 A, similar to the literature values. To study the effect of carbon do** in MgB2, various C-containing samples of x varying from 0 to 1.00 in MgB2-xCx were prepared. Magnetic characterizations indicate that the Tc onset is same for pure and C-doped samples for x = 0.05, and 0.10. However, the shielding signal decreased monotonically with C content, apparently due to the presence of carbon on the grain boundaries that isolates grains and prevents flow of supercurrents on the perimeter. △ Less

Submitted 4 April, 2001; originally announced April 2001.

Comments: 10 pages, 3 figures

Growth mechanism of superconducting MgB2 films prepared by various methods

Authors: H. Y. Zhai, H. M. Christen, L. Zhang, M. Paranthaman, C. Cantoni, B. C. Sales, P. H. Fleming, D. K. Christen, D. H. Lowndes

Abstract: The growth mechanisms of MgB2 films obtained by different methods on various substrates are compared via a detailed cross-sectional scanning electron microscopy (SEM) study. The analyzed films include (a) samples obtained by an ex-situ post-anneal at 900 degree of e-beam evaporated boron in the presence of an Mg vapor (exhibiting bulk-like Tc0 about 38.8 K), (b) samples obtained by the same ex-s… ▽ More The growth mechanisms of MgB2 films obtained by different methods on various substrates are compared via a detailed cross-sectional scanning electron microscopy (SEM) study. The analyzed films include (a) samples obtained by an ex-situ post-anneal at 900 degree of e-beam evaporated boron in the presence of an Mg vapor (exhibiting bulk-like Tc0 about 38.8 K), (b) samples obtained by the same ex-situ 900 degree anneal of pulsed laser deposition (PLD)-grown Mg+B precursors (exhibiting Tc0 ~ 25 K), and (c) films obtained by a low-temperature (600 - 630 degree) in-situ anneal of PLD-grown Mg+B precursors (with Tc0 about 24 K). A significant oxygen contamination was also present in films obtained from a PLD-grown precursors. On the other hand, it is clearly observed that the films obtained by the high-temperature reaction of e-beam evaporated B with Mg vapor are formed by the nucleation of independent MgB2 grains at the film surface, indicating that this approach may not be suitable to obtain smooth and (possibly) epitaxial films. △ Less

Submitted 17 April, 2001; v1 submitted 29 March, 2001; originally announced March 2001.

Comments: 1 table, 4 figures, 17 references, 16 pages PDF file

Soft x-ray spectroscopy measurements of the p-like density of states of B in MgB2 and evidence for surface boron oxides on exposed surfaces

Authors: T. A. Callcott, L. Lin, G. T. Woods, G. P. Zhang, J. R. Thompson, M. Paranthaman, D. L. Ederer

Abstract: Soft X-ray absorption and fluorescence measurements are reported for the K-edge of B in MgB2. The measurements confirm a high density of B pxy(sigma)-states at the Fermi edge and extending to approximately 0.9 eV above the edge. A strong resonance is observed in elastic scattering through a core-exciton derived from out-of-plane pz(pi*)-states. Another strong resonance, observed in both elastic… ▽ More Soft X-ray absorption and fluorescence measurements are reported for the K-edge of B in MgB2. The measurements confirm a high density of B pxy(sigma)-states at the Fermi edge and extending to approximately 0.9 eV above the edge. A strong resonance is observed in elastic scattering through a core-exciton derived from out-of-plane pz(pi*)-states. Another strong resonance, observed in both elastic and inelastic spectra, is identified as a product of surface boron oxides. △ Less

Submitted 28 March, 2001; originally announced March 2001.

Comments: 7 pages total, 4 figures, submitted to Phys. Rev. Lett

Superconducting magnesium diboride films on Silicon with Tc0 about 24K grown via vacuum annealing from stoichiometric precursors

Authors: H. Y. Zhai, H. M. Christen, L. Zhang, C. Cantoni, M. Paranthaman, B. C. Sales, D. K. Christen, D. H. Lowndes

Abstract: Superconducting magnesium diboride films with Tc0 ~ 24 K and sharp transition \~ 1 K were successfully prepared on silicon substrates by pulsed laser deposition from a stoichiometric MgB2 target. Contrary to previous reports, anneals at 630 degree and a background of 2x10^(-4) torr Ar/4%H2 were performed without the requirement of Mg vapor or an Mg cap layer. This integration of superconducting… ▽ More Superconducting magnesium diboride films with Tc0 ~ 24 K and sharp transition \~ 1 K were successfully prepared on silicon substrates by pulsed laser deposition from a stoichiometric MgB2 target. Contrary to previous reports, anneals at 630 degree and a background of 2x10^(-4) torr Ar/4%H2 were performed without the requirement of Mg vapor or an Mg cap layer. This integration of superconducting MgB2 films on silicon may thus prove enabling in superconductor-semiconductor device applications. Images of surface morphology and cross-section profiles by scanning electron microscopy (SEM) show that the films have a uniform surface morphology and thickness. Energy dispersive spectroscopy (EDS) reveals these films were contaminated with oxygen, originating either from the growth environment or from sample exposure to air. The oxygen contamination may account for the low Tc for those in-situ annealed films, while the use of Si as the substrate does not result in a decrease in Tc as compared to other substrates. △ Less

Submitted 31 March, 2001; v1 submitted 28 March, 2001; originally announced March 2001.

Comments: 5 pages, 4 figures, 15 references; due to file size limit, images were blured

Superconducting MgB(2) films via precursor post-processing approach

Authors: M. Paranthaman, C. Cantoni, H. Y. Zhai, H. M. Christen, T. Aytug, S. Sathyamurthy, E. D. Specht, J. R. Thompson, D. H. Lowndes, H. R. Kerchner, D. K. Christen

Abstract: Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam evaporation; a post-anneal at 890 deg C in the presence of bulk MgB(2) and Mg metal produced highly crystalline MgB(2) films. X-ray diffraction indicated that the films… ▽ More Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam evaporation; a post-anneal at 890 deg C in the presence of bulk MgB(2) and Mg metal produced highly crystalline MgB(2) films. X-ray diffraction indicated that the films exhibit some degree of c-axis alignment, but are randomly oriented in-plane. Transport current measurements of the superconducting properties show high values of the critical current density and yield an irreversibility line that exceeds that determined by magnetic measurements on bulk polycrystalline materials. △ Less

Submitted 27 March, 2001; originally announced March 2001.

Comments: PDF file with 10 pages total, including 4 figures

High temporal stability of supercurrents in MgB(2) materials

Authors: J. R. Thompson, M. Paranthaman, D. K. Christen, K. D. Sorge, H. J. Kim, J. G. Ossandon

Abstract: Fine grained polycrystalline samples of MgB(2) superconductor were synthesized from the elements to contain < 5 % of impurity phases, according to X-ray powder diffractometry. The superconductive transition was sharp with a midpoint Tc = 38.5 K. The magnetization in the vortex state was studied as a function of applied field H, temperature T, and time t. From the equilibrium magnetization, the L… ▽ More Fine grained polycrystalline samples of MgB(2) superconductor were synthesized from the elements to contain < 5 % of impurity phases, according to X-ray powder diffractometry. The superconductive transition was sharp with a midpoint Tc = 38.5 K. The magnetization in the vortex state was studied as a function of applied field H, temperature T, and time t. From the equilibrium magnetization, the London penetration depth was obtained. The supercurrent density J(T,H,t) in the vortex state (derived from the irreversible magnetization) decreases approximately linearly with T, in contrast to the quasi-exponential falloff in high-Tc superconductors. The current is highly stable in time, with normalized decay rates S = -d ln(J)/d ln(t) well below those in high-Tc materials. These results are compared with those of other superconductors. △ Less

Submitted 25 March, 2001; originally announced March 2001.

Comments: PDF file containing text and 6 figures, 12 pages total

Journal ref: Supercond. Sci. Technol. 14, L19-L19 (2001)

Superconducting magnesium diboride films with Tc \approx 24K grown by pulsed laser deposition with in-situ anneal

Authors: H. M. Christen, H. Y. Zhai, C. Cantoni, M. Paranthaman, B. C. Sales, C. Rouleau, D. P. Norton, D. K. Christen, D. H. Lowndes, .

Abstract: Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ annealing parameters shows an optimum temperature of about 600C in a background of 0.7 atm. of Ar/4%H2 for layers consisting of a mixture of magnesium and boron.… ▽ More Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ annealing parameters shows an optimum temperature of about 600C in a background of 0.7 atm. of Ar/4%H2 for layers consisting of a mixture of magnesium and boron. Contrary to ex-situ approaches (e.g. reacting boron films with magnesium vapor at 900C), these films are processed below the decomposition temperature of MgB2. This may prove enabling in the formation of multilayers, junctions, and epitaxial films in future work. Issues related to the improvement of these films and to the possible in-situ growth of MgB2 at elevated temperature are discussed. △ Less

Submitted 22 March, 2001; originally announced March 2001.

Comments: 5 pages, 4 figures

Journal ref: Physica C 353 (2001) 157-161

Conductive Buffer Layers and Overlayers for the Thermal Stability of Coated Conductors

Authors: Claudia Cantoni, Tolga Aytug, Darren T. Verebelyi, Mariappan Paranthaman, Eliot D. Specht, David P. Norton, David K. Christen

Abstract: We analyze fundamental issues related to the thermal and electrical stability of a coated conductor during its operation. We address the role of conductive buffer layers in the stability of Ni-based coated conductors, and the effect of a metallic cap layer on the electrical properties of Ni alloy-based superconducting tapes. For the first case we report on the fabrication of a fully conductive R… ▽ More We analyze fundamental issues related to the thermal and electrical stability of a coated conductor during its operation. We address the role of conductive buffer layers in the stability of Ni-based coated conductors, and the effect of a metallic cap layer on the electrical properties of Ni alloy-based superconducting tapes. For the first case we report on the fabrication of a fully conductive RABiTS architecture formed of bilayers of conductive oxides SrRuO3 and LaNiO3 on textured Ni tapes. For the second case we discuss measurements of current-voltage relations on Ag/YBa2Cu3O7-d and Cu/Ag/ YBa2Cu3O7-d prototype multilayers on insulating substrates. Limitations on the overall tape structure and properties that are posed by the stability requirement are presented. △ Less

Submitted 25 January, 2001; originally announced January 2001.

Comments: 4 pages, 5 figures

Journal ref: IEEE Trans. Applied Superconductivity, Vol. 11, No.1, pp. 3309-3312 March 2001