Absolute radiation tolerance of amorphous alumina coatings at room temperature
Authors:
A. Zaborowska,
Ł. Kurpaska,
M. Clozel,
E. J. Olivier,
J. H. O'Connell,
M. Vanazzi,
F. Di Fonzo,
A. Azarov,
I. Jóźwik,
M. Frelek-Kozak,
R. Diduszko,
J. H. Neethling,
J. Jagielski
Abstract:
In this study structural and mechanical properties of a 1 um thick Al2O3 coating, deposited on 316L stainless steel by Pulsed Laser Deposition (PLD), subjected to high energy ion irradiation were assessed. Mechanical properties of pristine and ion-modified specimens were investigated using the nanoindentation technique. A comprehensive characterization combining Transmission Electron Microscopy an…
▽ More
In this study structural and mechanical properties of a 1 um thick Al2O3 coating, deposited on 316L stainless steel by Pulsed Laser Deposition (PLD), subjected to high energy ion irradiation were assessed. Mechanical properties of pristine and ion-modified specimens were investigated using the nanoindentation technique. A comprehensive characterization combining Transmission Electron Microscopy and Grazing-Incidence X-ray Diffraction provided deep insight into the structure of the tested material at the nano- and micro- scale. Variation in the local atomic ordering of the irradiated zone at different doses was investigated using a reduced distribution function analysis obtained from electron diffraction data. Findings from nanoindentation measurements revealed a slight reduction in hardness of all irradiated layers. At the same time TEM examination indicated that the irradiated layer remained amorphous over the whole dpa range. No evidence of crystallization, void formation or element segregation was observed up to the highest implanted dose. Reported mechanical and structural findings were critically compared with each other pointing to the conclusion that under given irradiation conditions, over the whole range of doses used, alumina coatings exhibit excellent radiation resistance. Obtained data strongly suggest that investigated material may be considered as a promising candidate for next-generation nuclear reactors, especially LFR-type, where high corrosion protection is one of the highest prerogatives to be met.
△ Less
Submitted 24 April, 2023;
originally announced April 2023.
Iron-silica interaction during reduction of precipitated silica-promoted iron oxides using in situ XRD and TEM
Authors:
M. J. Coombes,
E. J. Olivier,
E. Prestat,
S. J. Haigh,
E. du Plessis,
J. H. Neethling
Abstract:
The effect of silica-promotion on the reduction of iron oxides in hydrogen was investigated using in situ X-ray diffraction and aberration-corrected transmission electron microscopy to understand the mechanism of reduction and the identity of the iron(II) silicate phase that has historically been designated as the cause of the iron-silica interaction in such materials. In the absence of a silica p…
▽ More
The effect of silica-promotion on the reduction of iron oxides in hydrogen was investigated using in situ X-ray diffraction and aberration-corrected transmission electron microscopy to understand the mechanism of reduction and the identity of the iron(II) silicate phase that has historically been designated as the cause of the iron-silica interaction in such materials. In the absence of a silica promoter the reduction of hematite to α-Fe proceeds via magnetite. Silica promoted amorphous iron oxide is reduced to α-Fe via stable magnetite and wüstite phases. During reduction of silica-promoted iron oxide, Fe0 diffuses out of the amorphous silica-promoted iron oxide matrix upon reduction from Fe2+ and coexists with an amorphous Fe-O-Si matrix. Certain portions of wüstite remain difficult to reduce to α-Fe owing to the formation of a protective silica-containing layer covering the remaining iron oxide regions. Given sufficient energy, this amorphous Fe-O-Si material forms ordered, crystalline fayalite.
△ Less
Submitted 12 May, 2021;
originally announced May 2021.