Polycrystalline γ-boron: As hard as polycrystalline cubic boron nitride
Authors:
Jiaqian Qin,
Norimasa Nishiyama,
Hiroaki Ohfuji,
Toru Shinmei,
Li Lei,
Duanwei He,
Tetsuo Irifune
Abstract:
The Vickers hardness of polycrystalline γ-B was measured using a diamond indentation method. The elastic properties of polycrystalline γ-B (B=213.9 GPa, G=227.2 GPa, and E=503.3 GPa) were determined using ultrasonic measurement at ambient condition. Under the loading force up to 20 N, our test gave an average Vickers hardness in the asymptotic-hardness region of 30.3 GPa. The average fracture toug…
▽ More
The Vickers hardness of polycrystalline γ-B was measured using a diamond indentation method. The elastic properties of polycrystalline γ-B (B=213.9 GPa, G=227.2 GPa, and E=503.3 GPa) were determined using ultrasonic measurement at ambient condition. Under the loading force up to 20 N, our test gave an average Vickers hardness in the asymptotic-hardness region of 30.3 GPa. The average fracture toughness was measured as 4.1MPa m1/2. Additionally, We also measured the hardness and elastic properties of polycrystalline β-B and PcBN for comparison. The hardness and elastic properties for polycrystalline γ-B was found to be very close to that of PcBN. Our results suggest that the polycrystalline γ-B could be a superhard polycrystalline material for industrial applications.
△ Less
Submitted 16 May, 2012; v1 submitted 8 March, 2012;
originally announced March 2012.
Phase relations in boron at pressure up to 18 GPa and temperature up to 2200 °C
Authors:
Jiaqian Qin,
Tetsuo Irifune,
Haruhiko Dekura,
Hiroaki Ohfuji,
Norimasa Nishiyama,
Li Lei,
Toru Shinmei
Abstract:
The phase relations in boron have been investigated at high pressure and high temperature using a multianvil apparatus, and the quenched sample has been analyzed by x-ray diffraction, Raman spectra and transmission electron microscopy. We demonstrate that γ-B28 can be synthesized over a wide P-T range, and T-B50 is obtained at higher temperatures and similar pressures. The phase boundary of the β-…
▽ More
The phase relations in boron have been investigated at high pressure and high temperature using a multianvil apparatus, and the quenched sample has been analyzed by x-ray diffraction, Raman spectra and transmission electron microscopy. We demonstrate that γ-B28 can be synthesized over a wide P-T range, and T-B50 is obtained at higher temperatures and similar pressures. The phase boundary of the β-B106, γ-B28 and T-B50 is determined at pressures between 7 and 18 GPa and the temperatures of 500-2200 °C. The results suggest that T-B50 might be an intermediate phase-metastable, formed for kinetic reasons (Ostwald rule) on the way from β-B106 to T-192 and γ-B28 to T-192.
△ Less
Submitted 5 November, 2011; v1 submitted 6 September, 2011;
originally announced September 2011.