Synthesis of $c$-axis textured CaKFe$_4$As$_4$ superconducting bulk via spark plasma texturing technique
Authors:
Shigeyuki Ishida,
Yoshihisa Kamiya,
Yoshinori Tsuchiya,
Pavan Kumar Naik Sugali,
Yasunori Mawatari,
Akira Iyo,
Yoshiyuki Yoshida,
Hiroshi Eisaki,
Kenji Kawashima,
Hiraku Ogino
Abstract:
Grain alignment is a key factor that determines the performance of a superconducting bulk. In this study, the spark plasma texturing (SPT) technique was used to fabricate a CaKFe$_4$As$_4$ superconducting bulk. X-ray diffraction and electron backscatter diffraction revealed that the $c$-axes of the CaKFe$_4$As$_4$ grains in the SPT bulk are aligned, demonstrating that the SPT technique is effectiv…
▽ More
Grain alignment is a key factor that determines the performance of a superconducting bulk. In this study, the spark plasma texturing (SPT) technique was used to fabricate a CaKFe$_4$As$_4$ superconducting bulk. X-ray diffraction and electron backscatter diffraction revealed that the $c$-axes of the CaKFe$_4$As$_4$ grains in the SPT bulk are aligned, demonstrating that the SPT technique is effective in achieving $c$-axis texture. In addition, chemical composition analysis showed that oxide impurities, which affect the grain boundary characteristics that determine the inter-grain critical current density ($J_c$), are randomly distributed in the SPT bulk. Magnetization measurements showed high $J_c$ values of the SPT bulk, reaching 127 kA cm$^{-2}$ and 26 kA cm$^{-2}$ at 4.2 K under a self-field and magnetic field of 5 T, respectively. These results suggest that the SPT technique is a promising approach for obtaining a high-performance superconducting bulk material for high-field applications.
△ Less
Submitted 29 March, 2024;
originally announced March 2024.
-
Synthesis of CaKFe$_4$As$_4$ bulk samples with high critical current density using a spark plasma sintering technique
Authors:
Shigeyuki Ishida,
S. Pavan Kumar Naik,
Yoshinori Tsuchiya,
Yasunori Mawatari,
Yoshiyuki Yoshida,
Akira Iyo,
Hiroshi Eisaki,
Yoshihisa Kamiya,
Kenji Kawashima,
Hiraku Ogino
Abstract:
A high density CaKFe$_4$As$_4$ bulk sample was successfully synthesized using a spark plasma sintering (SPS) technique. The density of the synthesized sample was 5.02 g cm$^{-3}$, corresponding to 96.2% of the theoretical density of CaKFe$_4$As$_4$. Moreover, a reasonably high Vickers hardness of 1 GPa was measured. The electrical resistivity of the SPS bulk sample was as low as approximately 600…
▽ More
A high density CaKFe$_4$As$_4$ bulk sample was successfully synthesized using a spark plasma sintering (SPS) technique. The density of the synthesized sample was 5.02 g cm$^{-3}$, corresponding to 96.2% of the theoretical density of CaKFe$_4$As$_4$. Moreover, a reasonably high Vickers hardness of 1 GPa was measured. The electrical resistivity of the SPS bulk sample was as low as approximately 600 $μΩ$ cm at 300 K, which is smaller than that of the ordinary sintered polycrystalline sample by nearly one order of magnitude, and exhibited a sharp superconducting transition, with the transition width $Δ\textit{T}_c$ less than 2 K, indicating an improved grain connectivity. The critical current density of the SPS bulk sample, as calculated from the magnetization hysteresis loops (magnetic $\textit{J}_c$), reached 18 kA cm$^{-2}$ at 4.2 K under 5 T, which is the highest among the iron-based superconductor polycrystalline samples reported thus far.
△ Less
Submitted 29 March, 2024;
originally announced March 2024.
-
Predicting Generalization of AI Colonoscopy Models to Unseen Data
Authors:
Joel Shor,
Carson McNeil,
Yotam Intrator,
Joseph R Ledsam,
Hiro-o Yamano,
Daisuke Tsurumaru,
Hiroki Kayama,
Atsushi Hamabe,
Koji Ando,
Mitsuhiko Ota,
Haruei Ogino,
Hiroshi Nakase,
Kaho Kobayashi,
Masaaki Miyo,
Eiji Oki,
Ichiro Takemasa,
Ehud Rivlin,
Roman Goldenberg
Abstract:
$\textbf{Background}$: Generalizability of AI colonoscopy algorithms is important for wider adoption in clinical practice. However, current techniques for evaluating performance on unseen data require expensive and time-intensive labels.
$\textbf{Methods}…
▽ More
$\textbf{Background}$: Generalizability of AI colonoscopy algorithms is important for wider adoption in clinical practice. However, current techniques for evaluating performance on unseen data require expensive and time-intensive labels.
$\textbf{Methods}$: We use a "Masked Siamese Network" (MSN) to identify novel phenomena in unseen data and predict polyp detector performance. MSN is trained to predict masked out regions of polyp images, without any labels. We test MSN's ability to be trained on data only from Israel and detect unseen techniques, narrow-band imaging (NBI) and chromendoscoy (CE), on colonoscopes from Japan (354 videos, 128 hours). We also test MSN's ability to predict performance of Computer Aided Detection (CADe) of polyps on colonoscopies from both countries, even though MSN is not trained on data from Japan.
$\textbf{Results}$: MSN correctly identifies NBI and CE as less similar to Israel whitelight than Japan whitelight (bootstrapped z-test, |z| > 496, p < 10^-8 for both) using the label-free Frechet distance. MSN detects NBI with 99% accuracy, predicts CE better than our heuristic (90% vs 79% accuracy) despite being trained only on whitelight, and is the only method that is robust to noisy labels. MSN predicts CADe polyp detector performance on in-domain Israel and out-of-domain Japan colonoscopies (r=0.79, 0.37 respectively). With few examples of Japan detector performance to train on, MSN prediction of Japan performance improves (r=0.56).
$\textbf{Conclusion}$: Our technique can identify distribution shifts in clinical data and can predict CADe detector performance on unseen data, without labels. Our self-supervised approach can aid in detecting when data in practice is different from training, such as between hospitals or data has meaningfully shifted from training. MSN has potential for application to medical image domains beyond colonoscopy.
△ Less
Submitted 22 March, 2024; v1 submitted 14 March, 2024;
originally announced March 2024.
-
The unreasonable effectiveness of AI CADe polyp detectors to generalize to new countries
Authors:
Joel Shor,
Hiro-o Yamano,
Daisuke Tsurumaru,
Yotami Intrator,
Hiroki Kayama,
Joe Ledsam,
Atsushi Hamabe,
Koji Ando,
Mitsuhiko Ota,
Haruei Ogino,
Hiroshi Nakase,
Kaho Kobayashi,
Eiji Oki,
Roman Goldenberg,
Ehud Rivlin,
Ichiro Takemasa
Abstract:
$\textbf{Background and aims}…
▽ More
$\textbf{Background and aims}$: Artificial Intelligence (AI) Computer-Aided Detection (CADe) is commonly used for polyp detection, but data seen in clinical settings can differ from model training. Few studies evaluate how well CADe detectors perform on colonoscopies from countries not seen during training, and none are able to evaluate performance without collecting expensive and time-intensive labels.
$\textbf{Methods}$: We trained a CADe polyp detector on Israeli colonoscopy videos (5004 videos, 1106 hours) and evaluated on Japanese videos (354 videos, 128 hours) by measuring the True Positive Rate (TPR) versus false alarms per minute (FAPM). We introduce a colonoscopy dissimilarity measure called "MAsked mediCal Embedding Distance" (MACE) to quantify differences between colonoscopies, without labels. We evaluated CADe on all Japan videos and on those with the highest MACE.
$\textbf{Results}$: MACE correctly quantifies that narrow-band imaging (NBI) and chromoendoscopy (CE) frames are less similar to Israel data than Japan whitelight (bootstrapped z-test, |z| > 690, p < $10^{-8}$ for both). Despite differences in the data, CADe performance on Japan colonoscopies was non-inferior to Israel ones without additional training (TPR at 0.5 FAPM: 0.957 and 0.972 for Israel and Japan; TPR at 1.0 FAPM: 0.972 and 0.989 for Israel and Japan; superiority test t > 45.2, p < $10^{-8}$). Despite not being trained on NBI or CE, TPR on those subsets were non-inferior to Japan overall (non-inferiority test t > 47.3, p < $10^{-8}$, $δ$ = 1.5% for both).
$\textbf{Conclusion}$: Differences that prevent CADe detectors from performing well in non-medical settings do not degrade the performance of our AI CADe polyp detector when applied to data from a new country. MACE can help medical AI models internationalize by identifying the most "dissimilar" data on which to evaluate models.
△ Less
Submitted 17 December, 2023; v1 submitted 11 December, 2023;
originally announced December 2023.
-
Na-catalyzed rapid synthesis and characterization of intercalated graphite CaC6
Authors:
Akira Iyo,
Hiroshi Fujihisa,
Yoshito Gotoh,
Shigeyuki Ishida,
Hiroshi Eisaki,
Hiraku Ogino,
Kenji Kawashima
Abstract:
In this study, we conducted experiments on CaC6 for elucidating the Na-catalyzed formation mechanism and achieving rapid mass synthesis of graphite intercalation compounds (GICs). Rapidly synthesized CaC6 was characterized by analysis of its crystal structure and physical properties. We found that the formation of the reaction intermediate Na-GIC (NaCx, x = 64) requires a larger amount of Na than…
▽ More
In this study, we conducted experiments on CaC6 for elucidating the Na-catalyzed formation mechanism and achieving rapid mass synthesis of graphite intercalation compounds (GICs). Rapidly synthesized CaC6 was characterized by analysis of its crystal structure and physical properties. We found that the formation of the reaction intermediate Na-GIC (NaCx, x = 64) requires a larger amount of Na than is intercalated between the graphite interlayers. The requirement for excess Na may provide insights into the mechanism of Na-catalyzed GIC formation. A Na-to-C molar mixing ratio of 1.5-2.0:6 was suitable for the efficient formation of CaC6 under heat treatment at 250°C for 2 h, and the catalytic Na remaining in the sample was demonstrably reduced to a Na:Ca ratio of approximately 3:97. The upper critical field Hc2 was enhanced approximately three times compared to those of previous reports. Based on X-ray diffraction and experimental parameter analysis, we concluded that the enhancement of Hc2 was attributed to the disordered stacking sequence in CaC6, possibly because of the rapid and low-temperature formation. Physical properties derived from specific heat measurements were comparable to those of high-quality CaC6, which is slowly synthesized using the molten Li-Ca alloy method. This study provides new avenues for future research and exploration in the rapid mass synthesis of GICs as practical materials, for applications such as battery electrodes and superconducting wires.
△ Less
Submitted 5 September, 2023;
originally announced September 2023.
-
Experimental investigation of electronic interactions in collapsed and uncollapsed LaFe2As2 phases
Authors:
Ilaria Pallecchi,
Elena Stellino,
Paolo Postorino,
Akira Iyo,
Hiraku Ogino,
Marco Affronte,
Marina Putti
Abstract:
The iron-based pnictide LaFe2As2 is not superconducting as-synthesized, but it becomes such below Tc around 12 K upon annealing, as a consequence of a structural transition from a phase with collapsed tetragonal crystal structure to an uncollapsed phase. In this work, we carry out specific heat, Raman spectroscopy and normal state electric and thermoelectric transport measurements in the collapsed…
▽ More
The iron-based pnictide LaFe2As2 is not superconducting as-synthesized, but it becomes such below Tc around 12 K upon annealing, as a consequence of a structural transition from a phase with collapsed tetragonal crystal structure to an uncollapsed phase. In this work, we carry out specific heat, Raman spectroscopy and normal state electric and thermoelectric transport measurements in the collapsed and uncollapsed LaFe2As2 phases to gain insight into the electron interactions and their possible role in the superconducting pairing mechanism. Despite clear features of strong electron-phonon coupling observed in both phases, neither the low energy phonon spectra nor the electron-phonon coupling show significant differences between the two phases. Conversely, the Sommerfield constants are significantly different in the two phases, pointing to much higher electron correlation in the superconducting uncollapsed phase and confirming theoretical studies.
△ Less
Submitted 17 July, 2023;
originally announced July 2023.
-
Dramatically Accelerated Formation of Graphite Intercalation Compounds Catalyzed by Sodium
Authors:
Akira Iyo,
Hiraku Ogino,
Shigeyuki Ishida,
Hiroshi Eisaki
Abstract:
Graphite intercalation compounds (GICs) have a variety of functions due to their rich material variations, and thus,innovative methods for their synthesis are desired for practical applications. We have discovered that Na has a catalytic property that dramatically accelerates the formation of GICs. We demonstrate that LiC6n (n = 1, 2), KC8, KC12n (n = 2, 3, 4), and NaCx are synthesized simply by m…
▽ More
Graphite intercalation compounds (GICs) have a variety of functions due to their rich material variations, and thus,innovative methods for their synthesis are desired for practical applications. We have discovered that Na has a catalytic property that dramatically accelerates the formation of GICs. We demonstrate that LiC6n (n = 1, 2), KC8, KC12n (n = 2, 3, 4), and NaCx are synthesized simply by mixing alkali metals and graphite powder with Na at room temperature (~25 °C), and AEC6 (AE = Ca, Sr, Ba) are synthesized by heating Na-added reagents at 250 °C only for a few hours. The NaCx, formed by the mixing of C and Na, is understood to act as a reaction intermediate for a catalyst, thereby accelerating the formation of GICs by lowering the activation energy of intercalation. The Na-catalyzed method, which enables the rapid and mass synthesis of homogeneous GIC samples in a significantly simpler manner than conventional methods, is anticipated to stimulate research and development for GIC applications.
△ Less
Submitted 27 March, 2023;
originally announced March 2023.
-
Posttreatment Effects on the Crystal Structure and Superconductivity of Ca-Free Double-Layered Cuprate Sr$_2$SrCu$_2$O$_{4+y}$F$_{2-y}$
Authors:
Hiroki Ninomiya,
Kenji Kawashima,
Hiroshi Fujihisa,
Shigeyuki Ishida,
Hiraku Ogino,
Yoshiyuki Yoshida,
Hiroshi Eisaki,
Yoshito Gotoh,
Akira Iyo
Abstract:
We report the effects of low-temperature postannealing on the structural and superconducting properties of the recently discovered Ca-free double-layered cuprate, Sr$_2$SrCu$_2$O$_{4+y}$F$_{2-y}$. Although the as-synthesized sample prepared under high pressure has a tetragonal structure with a rock-salt-type blocking layer (the so-called $T$-phase), we found that the symmetry of the structure lowe…
▽ More
We report the effects of low-temperature postannealing on the structural and superconducting properties of the recently discovered Ca-free double-layered cuprate, Sr$_2$SrCu$_2$O$_{4+y}$F$_{2-y}$. Although the as-synthesized sample prepared under high pressure has a tetragonal structure with a rock-salt-type blocking layer (the so-called $T$-phase), we found that the symmetry of the structure lowered to that of an orthorhombic system when annealed with CuF$_2$. The structural refinements reveal that such a topochemical reaction leads not only to the removal of excess O$^{2-}$ from the apical site but also to the intercalation of extra F$^-$ into the interstitial site. The orthorhombic phase exhibits bulk superconductivity at a critical temperature of 107 K, which is significantly higher than that of the $T$-phase ($\sim$50 K). Meanwhile, the $T$-phase turns into another structure possessing a fluorite-type blocking layer without apical fluorine (known as the $T^\prime$-phase) by annealing without CuF$_2$. Density functional theory calculations show that the $T^\prime$-phase is more stable than the $T$-phase. This is the first report on the formation of a $T^\prime$-type double-layered cuprate. Furthermore, the structural stability of the three phases of Sr$_2$SrCu$_2$O$_{4+y}$F$_{2-y}$ is discussed in terms of lattice matching between the blocking and conducting layers.
△ Less
Submitted 16 December, 2021;
originally announced December 2021.
-
Superconductivity-driven ferromagnetism and spin manipulation using vortices in the magnetic superconductor EuRbFe4As4
Authors:
Shigeyuki Ishida,
Daniel Kagerbauer,
Sigrid Holleis,
Kazuki Iida,
Koji Munakata,
Akiko Nakao,
Akira Iyo,
Hiraku Ogino,
Kenji Kawashima,
Michael Eisterer,
Hiroshi Eisaki
Abstract:
Magnetic superconductors are specific materials exhibiting two antagonistic phenomena, superconductivity and magnetism, whose mutual interaction induces various emergent phenomena, such as the reentrant superconducting transition associated with the suppression of superconductivity around the magnetic transition temperature (Tm), highlighting the impact of magnetism on superconductivity. In this s…
▽ More
Magnetic superconductors are specific materials exhibiting two antagonistic phenomena, superconductivity and magnetism, whose mutual interaction induces various emergent phenomena, such as the reentrant superconducting transition associated with the suppression of superconductivity around the magnetic transition temperature (Tm), highlighting the impact of magnetism on superconductivity. In this study, we report the experimental observation of the ferromagnetic order induced by superconducting vortices in the high-critical-temperature (high-Tc) magnetic superconductor EuRbFe4As4. Although the ground state of the Eu2+ moments in EuRbFe4As4 is helimagnetism below Tm, neutron diffraction and magnetization experiments show a ferromagnetic hysteresis of the Eu2+ spin alignment. We demonstrate that the direction of the Eu2+ moments is dominated by the distribution of pinned vortices based on the critical state model. Moreover, we demonstrate the manipulation of spin texture by controlling the direction of superconducting vortices, which can help realize spin manipulation devices using magnetic superconductors.
△ Less
Submitted 18 October, 2021;
originally announced October 2021.
-
Experimental and Computational Determination of Optimal Boron Content in Layered Superconductor Sc$_{20}$C$_{8-x}$B$_x$C$_{20}$
Authors:
Hiroki Ninomiya,
Terunari Koshinuma,
Taichiro Nishio,
Hiroshi Fujihisa,
Kenji Kawashima,
Izumi Hase,
Shigeyuki Ishida,
Hiraku Ogino,
Akira Iyo,
Yoshiyuki Yoshida,
Yoshito Gotoh,
Hiroshi Eisaki
Abstract:
It is generally difficult to quantify the amounts of light elements in materials because of their low X-ray-scattering power, as this means that they cannot be easily estimated via X-ray analyses. Meanwhile, the recently reported layered superconductor, Sc$_{20}$C$_{8-x}$B$_x$C$_{20}$, requires a small amount of boron, which is a light element, for its structural stability. In this context, here,…
▽ More
It is generally difficult to quantify the amounts of light elements in materials because of their low X-ray-scattering power, as this means that they cannot be easily estimated via X-ray analyses. Meanwhile, the recently reported layered superconductor, Sc$_{20}$C$_{8-x}$B$_x$C$_{20}$, requires a small amount of boron, which is a light element, for its structural stability. In this context, here, we quantitatively evaluate the optimal $x$ value using both the experimental and computational approaches. Using the high-pressure synthesis approach that can maintain the starting composition even after sintering, we obtain the Sc$_{20}$(C,B)$_{8}$C$_{20}$ phase by the reaction of the previously reported Sc$_{15}$C$_{19}$ and B (Sc$_{15}$B$_y$C$_{19}$). Our experiments demonstrate that an increase in $y$ values promotes the phase formation of the Sc$_{20}$(C,B)$_{8}$C$_{20}$ structure; however, there appears to be an upper limit to the nominal $y$ value to form this phase. The maximum $T_\mathrm{c}$ $(=7.6\text{ K})$ is found to correspond with the actual $x$ value of $x \sim 5$ under the assumption that the sample with the same $T_\mathrm{c}$ as the reported value $(=7.7\text{ K})$ possesses the optimal $x$ amount. Moreover, we construct the energy convex hull diagram by calculating the formation enthalpy based on first principles. Our computational results indicate that the composition of Sc$_{20}$C$_4$B$_4$C$_{20}$ $(x=4)$ is the most thermodynamically stable, which is reasonably consistent with the experimentally obtained value.
△ Less
Submitted 1 September, 2020;
originally announced September 2020.
-
Coupled Magnetic and Superconducting Transitions in Sr$_{2}$VO$_{3}$FeAs Under Pressure
Authors:
S. Holenstein,
F. Hummel,
Z. Guguchia,
S. Kamusella,
N. Barbero,
H. Ogino,
Z. Shermadini,
R. Khasanov,
A. Amato,
T. Shiroka,
H. -H. Klauss,
E. Morenzoni,
D. Johrendt,
H. Luetkens
Abstract:
We report muon spin rotation ($μ$SR) and magnetization measurements on superconducting Sr$_{2}$VO$_{3}$FeAs under pressure. At ambient pressure, Sr$_{2}$VO$_{3}$FeAs undergoes an antiferromagnetic transition of the V moments at $T_{N}$ and becomes superconducting at $T_{c}<T_{N}$. As a function of pressure, $T_{N}$ initially decreases while $T_{c}$ increases. Surprisingly, once…
▽ More
We report muon spin rotation ($μ$SR) and magnetization measurements on superconducting Sr$_{2}$VO$_{3}$FeAs under pressure. At ambient pressure, Sr$_{2}$VO$_{3}$FeAs undergoes an antiferromagnetic transition of the V moments at $T_{N}$ and becomes superconducting at $T_{c}<T_{N}$. As a function of pressure, $T_{N}$ initially decreases while $T_{c}$ increases. Surprisingly, once $T_{N}\approx T_{c}$ at 0.6~GPa, $T_{N}$ reverses its trend and increases together with $T_{c}$ suggesting that the static V magnetism is a prerequisite for superconductivity. We explain this cooperative coupling by a possible localization of the V 3$d$ states below the magnetic transition which enables the nesting of the Fermi surface necessary for superconductivity.
△ Less
Submitted 11 November, 2019;
originally announced November 2019.
-
Superconductivity in a Scandium Borocarbide with a Layered Crystal Structure
Authors:
Hiroki Ninomiya,
Kunihiko Oka,
Izumi Hase,
Kenji Kawashima,
Hiroshi Fujihisa,
Yoshito Gotoh,
Shigeyuki Ishida,
Hiraku Ogino,
Akira Iyo,
Yoshiyuki Yoshida,
Hiroshi Eisaki
Abstract:
The discovery of nearly room-temperature superconductivity in superhydrides has motivated further materials research for conventional superconductors. To realize the moderately high critical temperature $(T_\mathrm{c})$ in materials containing light elements, we explored new superconducting phases in a scandium borocarbide system. Here, we report the observation of superconductivity in a new terna…
▽ More
The discovery of nearly room-temperature superconductivity in superhydrides has motivated further materials research for conventional superconductors. To realize the moderately high critical temperature $(T_\mathrm{c})$ in materials containing light elements, we explored new superconducting phases in a scandium borocarbide system. Here, we report the observation of superconductivity in a new ternary Sc-B-C compound. The crystal structure, which was determined through a Rietveld analysis, belongs to tetragonal space group $P4/ncc$. By complementarily using the density functional theory calculations, a chemical formula of the compound was found to be expressed as Sc$_{20}$C$_{8-x}$B$_x$C$_{20}$($x=1\:\mathrm{or}\:2$). Interestingly, a small amount of B is essential to stabilize the present structure. Our experiments revealed the typical type-II superconductivity at $T_\mathrm{c}=7.7\:\mathrm{K}$. Additionally, we calculated the density of states within a first-principles approach and found that the contribution of the Sc-3d orbital was mainly responsible for the superconductivity.
△ Less
Submitted 30 October, 2019;
originally announced October 2019.
-
Unique defect structure and advantageous vortex pinning properties in superconducting CaKFe4As4
Authors:
Shigeyuki Ishida,
Akira Iyo,
Hiraku Ogino,
Hiroshi Eisaki,
Nao Takeshita,
Kenji Kawashima,
Keiichi Yanagisawa,
Yuuga Kobayashi,
Koji Kimoto,
Hideki Abe,
Motoharu Imai,
Jun-ichi Shimoyama,
Michael Eisterer
Abstract:
The lossless current-carrying capacity of a superconductor is limited by its critical current density (Jc). A key to enhance Jc towards real-life applications is engineering defect structures to optimize the pinning landscape. For iron-based superconductors (IBSs) considered as candidate materials for high-field applications, high Jc values have been achieved by various techniques to introduce art…
▽ More
The lossless current-carrying capacity of a superconductor is limited by its critical current density (Jc). A key to enhance Jc towards real-life applications is engineering defect structures to optimize the pinning landscape. For iron-based superconductors (IBSs) considered as candidate materials for high-field applications, high Jc values have been achieved by various techniques to introduce artificial pinning centres. Here we report extraordinary vortex pinning properties in CaKFe4As4 (CaK1144) arising from the inherent defect structure. Scanning transmission electron microscopy revealed the existence of nanoscale intergrowths of the CaFe2As2 phase, which is unique to CaK1144 formed as a line compound. The Jc properties in CaK1144 are found to be distinct from other IBSs characterized by a significant anisotropy with respect to the magnetic field orientation as well as a remarkable pinning mechanism significantly enhanced with increasing temperature. We propose a comprehensive explanation of the Jc properties based on the unique intergrowths acting as pinning centres.
△ Less
Submitted 10 July, 2019;
originally announced July 2019.
-
Do**-dependent critical current properties in K, Co, and P-doped BaFe2As2 single crystals
Authors:
Shigeyuki Ishida,
Dongjoon Song,
Hiraku Ogino,
Akira Iyo,
Hiroshi Eisaki,
Masamichi Nakajima,
Jun-ichi Shimoyama,
Michael Eisterer
Abstract:
In order to establish the do** dependence of the critical current properties in the iron-based superconductors, the in-plane critical current density (Jc) of BaFe2As2-based superconductors, Ba1-xKxFe2As2 (K-Ba122), Ba(Fe1-xCox)2As2 (Co-Ba122), and BaFe2(As1-xPx)2 (P-Ba122) in a wide range of do** concentration (x) was investigated by means of magnetization hysteresis loop (MHL) measurements on…
▽ More
In order to establish the do** dependence of the critical current properties in the iron-based superconductors, the in-plane critical current density (Jc) of BaFe2As2-based superconductors, Ba1-xKxFe2As2 (K-Ba122), Ba(Fe1-xCox)2As2 (Co-Ba122), and BaFe2(As1-xPx)2 (P-Ba122) in a wide range of do** concentration (x) was investigated by means of magnetization hysteresis loop (MHL) measurements on single-crystal samples. Depending on the dopant elements and their concentration, Jc exhibits a variety of magnetic-field (H) and temperature (T) dependences. (1) In the case of K-Ba122, MHL of the underdoped samples (x < 0.33) exhibits the second magnetization peak (SMP), which sustains high Jc at high H and high T, exceeding 10^5 A/cm2 at T = 25 K and H = 6 T for x = 0.30. On the other hand, SMP is missing in the optimally (x ~ 0.36-0.40) and overdoped (x ~ 0.50) samples, and consequently Jc rapidly decreases by more than one order of magnitude, although the change in Tc is within a few K. (2) For Co-Ba122, SMP is always present over the entire superconducting (SC) dome from the under (x ~ 0.05) to the overdoped (x ~ 0.12) region. However, the magnitude of Jc significantly changes with x, exhibiting a sharp maximum at x ~ 0.057, which is a slightly underdoped composition for Co-Ba122. (3) For P-Ba122, the highest Jc is attained at x = 0.30 corresponding to the highest Tc composition. For the overdoped samples, MHL is characterized by SMP located close to the irreversibility field. Common to the three do** variations, Jc becomes highest at the under-do** side of SC dome near the phase boundary between SC phase and the antiferromagnetic/orthorhombic phase. Also, the peak appears in a narrow range of do**, distinct from the Tc dome with broad maximum. These similarities in the three cases indicate that the observed do** dependence of Jc is intrinsic to the BaFe2As2-based superconductors.
△ Less
Submitted 6 January, 2017;
originally announced January 2017.
-
Pressure Effects on Superconducting Properties of the BiS2-Based Superconductor Bi2(O,F)S2
Authors:
Tomoyuki Okada,
Hiraku Ogino,
Jun-ichi Shimoyama,
Kohji Kishio,
Nao Takeshita,
Naoki Shirakawa,
Akira Iyo,
Hiroshi Eisaki
Abstract:
Pressure effects on a recently discovered BiS2-based superconductor Bi2(O,F)S2 (Tc = 5.1 K) were examined via two different methods; high pressure resistivity measurement and high pressure annealing. The effects of these two methods on the superconducting properties of Bi2(O,F)S2 were significantly different although in both methods hydrostatic pressure is applied to the sample by the cubic-anvil-…
▽ More
Pressure effects on a recently discovered BiS2-based superconductor Bi2(O,F)S2 (Tc = 5.1 K) were examined via two different methods; high pressure resistivity measurement and high pressure annealing. The effects of these two methods on the superconducting properties of Bi2(O,F)S2 were significantly different although in both methods hydrostatic pressure is applied to the sample by the cubic-anvil-type apparatus. In high pressure resistivity measurement, Tc linearly decreased at the rate of -1.2 K GPa-1. In contrast, the Tc of 5.1 K is maintained after high pressure annealing under 2 GPa and 470°C of optimally doped sample despite significant change of lattice parameters. In addition, superconductivity was observed in fluorine-free Bi2OS2 after high pressure annealing. These results suggest that high pressure annealing would cause a unique effect on physical properties of layered compounds.
△ Less
Submitted 7 August, 2015;
originally announced August 2015.
-
Topotactic synthesis of a new BiS2-based superconductor Bi2(O,F)S2
Authors:
Tomoyuki Okada,
Hiraku Ogino,
Jun-ichi Shimoyama,
Kohji Kishio
Abstract:
A new BiS2-based superconductor Bi2(O,F)S2 was discovered. This is a layered compound consisting of alternate stacking structure of rock-salt-type BiS2 superconducting layer and fluorite-type Bi(O,F) blocking layer. Bi2(O,F)S2 was obtained as the main phase by topotactic fluorination of undoped Bi2OS2 using XeF2, which is the first topotactic synthesis of an electron-doped superconductor via reduc…
▽ More
A new BiS2-based superconductor Bi2(O,F)S2 was discovered. This is a layered compound consisting of alternate stacking structure of rock-salt-type BiS2 superconducting layer and fluorite-type Bi(O,F) blocking layer. Bi2(O,F)S2 was obtained as the main phase by topotactic fluorination of undoped Bi2OS2 using XeF2, which is the first topotactic synthesis of an electron-doped superconductor via reductive fluorination. With increasing F-content, a- and c-axis length increased and decreased, respectively, and Tc increased up to 5.1 K.
△ Less
Submitted 7 August, 2015;
originally announced August 2015.
-
Dependences on RE of Superconducting Properties of Transition Metal co-doped (Ca,RE)FeAs2 with RE = La-Gd
Authors:
Hiroyuki Yakita,
Hiraku Ogino,
Alberto Sala,
Tomoyuki Okada,
Akiyasu Yamamoto,
Kohji Kishio,
Akira Iyo,
Hiroshi Eisaki,
Jun-ichi Shimoyama
Abstract:
Dependence of superconducting properties of (Ca,RE)(Fe,TM)As2 [(Ca,RE)112, TM: Co, Ni)] on RE elements (RE = La-Gd) was systematically investigated. Improvement of superconducting properties by Co or Ni co-do** was observed for all (Ca,RE)112, which is similar to Co-co-doped (Ca,La)112 or (Ca,Pr)112. Tc of Co-co-doped samples decreased from 38 K for RE = La to 29 K for RE = Gd with decreasing io…
▽ More
Dependence of superconducting properties of (Ca,RE)(Fe,TM)As2 [(Ca,RE)112, TM: Co, Ni)] on RE elements (RE = La-Gd) was systematically investigated. Improvement of superconducting properties by Co or Ni co-do** was observed for all (Ca,RE)112, which is similar to Co-co-doped (Ca,La)112 or (Ca,Pr)112. Tc of Co-co-doped samples decreased from 38 K for RE = La to 29 K for RE = Gd with decreasing ionic radii of RE3+. However, Co-co-doped (Ca,Eu)112 showed exceptionally low Tc = 21 K probably due to the co-existence of Eu3+ and Eu2+ suggested by longer interlayer distance dFe-Fe of (Ca,Eu)112 than other (Ca,RE)112.
△ Less
Submitted 27 May, 2015;
originally announced May 2015.
-
Co-co-do** effect for (Ca,RE)FeAs2 sintered bulk
Authors:
Hiroyuki Yakita,
Hiraku Ogino,
Alberto Sala,
Tomoyuki Okada,
Kohji Kishio,
Akira Iyo,
Hiroshi Eisaki,
Jun-ichi Shimoyama
Abstract:
Superconducting properties of Co-co-doped (Ca,RE)FeAs2 ((Ca,RE)112: RE = La, Pr) were investigated. Co-co-do** increased Tc of (Ca,Pr)112 while Mn-co-do** suppressed superconductivity of (Ca,RE)112. Co-co-doped (Ca,La)112 showed large diamagnetic screening and sharper superconducting transition than Co-free (Ca,La)112. Tczero observed in resistivity measurements increased from 14 K to 30 K by…
▽ More
Superconducting properties of Co-co-doped (Ca,RE)FeAs2 ((Ca,RE)112: RE = La, Pr) were investigated. Co-co-do** increased Tc of (Ca,Pr)112 while Mn-co-do** suppressed superconductivity of (Ca,RE)112. Co-co-doped (Ca,La)112 showed large diamagnetic screening and sharper superconducting transition than Co-free (Ca,La)112. Tczero observed in resistivity measurements increased from 14 K to 30 K by Co-co-do**, while Tconset was not increased. The critical current density (Jc) of Co-co-doped (Ca,La)112 were approximately 2.1 x 104 Acm-2 and 3.2 x 103 Acm-2 at 2 K and 25 K, respectively, near zero field. These relatively high Jcs and large diamagnetic screening observed in susceptibility measurement as for polycrystalline bulks suggest bulk superconductivity of Co-co-doped (Ca,RE)112 compounds.
△ Less
Submitted 27 May, 2015;
originally announced May 2015.
-
Effects of post-annealing and cobalt co-do** on superconducting properties of (Ca,Pr)Fe2As2 single crystals
Authors:
Tomoyuki Okada,
Hiraku Ogino,
Hiroyuki Yakita,
Akiyasu Yamamoto,
Kohji Kishio,
Jun-ichi Shimoyama
Abstract:
In order to clarify the origin of anomalous superconductivity in (Ca,RE)Fe2As2 system, Pr doped and Pr,Co co-doped CaFe2As2 single crystals were grown by the FeAs flux method. These samples showed two-step superconducting transition with Tc1 = 25~42 K, and Tc2 < 16 K, suggesting that (Ca,RE)Fe2As2 system has two superconducting components. Post-annealing performed for these crystals in evacuated q…
▽ More
In order to clarify the origin of anomalous superconductivity in (Ca,RE)Fe2As2 system, Pr doped and Pr,Co co-doped CaFe2As2 single crystals were grown by the FeAs flux method. These samples showed two-step superconducting transition with Tc1 = 25~42 K, and Tc2 < 16 K, suggesting that (Ca,RE)Fe2As2 system has two superconducting components. Post-annealing performed for these crystals in evacuated quartz ampoules at various temperatures revealed that post-annealing at ~400°C increased the c-axis length for all samples. This indicates that as-grown crystals have a certain level of strain, which is released by post-annealing at ~400°C. Superconducting properties also changed dramatically by post-annealing. After annealing at 400°C, some of the co-doped samples showed large superconducting volume fraction corresponding to the perfect diamagnetism below Tc2 and high Jc values of 104~105 Acm-2 at 2 K in low field, indicating the bulk superconductivity of (Ca,RE)Fe2As2 phase occurred below Tc2. On the contrary, the superconducting volume fraction above Tc2 was always very small, suggesting that 40 K-class superconductivity observed in this system is originating in the local superconductivity in the crystal.
△ Less
Submitted 23 July, 2014;
originally announced July 2014.
-
Synthesis and physical properties of Ca1-xRExFeAs2 with RE = La ~ Gd
Authors:
Alberto Sala,
Hiroyuki Yakita,
Hiraku Ogino,
Tomoyuki Okada,
Akiyasu Yamamoto,
Kohji Kishio,
Shigeyuki Ishida,
Akira Iyo,
Hiroshi Eisaki,
Masaya Fujioka,
Yoshihiko Takano,
Marina Putti,
Jun-ichi Shimoyama
Abstract:
Synthesis of a series of layered iron arsenides Ca1-xRExFeAs2 (112) was attempted by heating at 1000 C under a high-pressure of 2 GPa. The 112 phase successfully forms with RE = La, Ce, Nd, Sm, Eu and Gd, while Tb, Dy and Ho substituted and RE free samples does not contain the 112 phase. The Ce, Nd, Sm, Eu and Gd doped Ca1-xRExFeAs2 are new compounds. All of them exhibit superconducting transition…
▽ More
Synthesis of a series of layered iron arsenides Ca1-xRExFeAs2 (112) was attempted by heating at 1000 C under a high-pressure of 2 GPa. The 112 phase successfully forms with RE = La, Ce, Nd, Sm, Eu and Gd, while Tb, Dy and Ho substituted and RE free samples does not contain the 112 phase. The Ce, Nd, Sm, Eu and Gd doped Ca1-xRExFeAs2 are new compounds. All of them exhibit superconducting transition except for the Ce doped sample. The behaviour of the critical temperature, with the RE ionic radii have been investigated.
△ Less
Submitted 10 April, 2014;
originally announced April 2014.
-
Discovery of New Layered Iron Arsenide Superconductor (Ca,Pr)FeAs2
Authors:
Hiroyuki Yakita,
Hiraku Ogino,
Tomoyuki Okada,
Akiyasu Yamamoto,
Kohji Kishio,
Tetsuya Tohei,
Yuichi Ikuhara,
Yoshito Gotoh,
Hiroshi Fujihisa,
Kunimitsu Kataoka,
Hiroshi Eisaki,
Jun-ichi Shimoyama
Abstract:
A new iron-based superconductor (Ca,Pr)FeAs2 was discovered. Plate-like crystals of the new phase were obtained and crystal structure was investigated by single-crystal X-ray diffraction analysis. The structure was identified as the monoclinic system with space group P21/m, and is composed of two Ca(Pr) planes, anti-fluorite Fe2As2 layers, and As2 zigzag chain layers. Plate-like crystals composed…
▽ More
A new iron-based superconductor (Ca,Pr)FeAs2 was discovered. Plate-like crystals of the new phase were obtained and crystal structure was investigated by single-crystal X-ray diffraction analysis. The structure was identified as the monoclinic system with space group P21/m, and is composed of two Ca(Pr) planes, anti-fluorite Fe2As2 layers, and As2 zigzag chain layers. Plate-like crystals composed of the new phase showed superconductivity with Tc ~20 K in both magnetization and resistivity measurements.
△ Less
Submitted 6 November, 2013;
originally announced November 2013.
-
Transition Temperature and Upper Critical Field in SmFeAsO1-xFx Synthesized at Low Heating Temperatures
Authors:
S. J. Singh,
J. Shimoyama,
A. Yamamoto,
H. Ogino,
K. Kishio
Abstract:
Low-temperature synthesis is a promising and potentially effective method for improving superconducting properties. We report on the fabrication of polycrystalline samples of SmFeAsO1-xFx with nominal x content varying in a wide range of x = 0-0.35 synthesized at 900 deg C. This synthesis temperature is around 300 deg C lower than the conventional synthesis temperature. The variation in the lattic…
▽ More
Low-temperature synthesis is a promising and potentially effective method for improving superconducting properties. We report on the fabrication of polycrystalline samples of SmFeAsO1-xFx with nominal x content varying in a wide range of x = 0-0.35 synthesized at 900 deg C. This synthesis temperature is around 300 deg C lower than the conventional synthesis temperature. The variation in the lattice parameters and transition temperature (Tc) of various F-doped samples indicates that reduction of the unit cell volume (V) seems to be the main reason for the rise of Tc up to 57.8 K. Magnetoresistance measurements showed that the upper critical field slope (dHc2/dT) increased with increasing F concentration up to x = 0.2, where it reached a maximum value of -8 T/K corresponding to a coherence length of 10 angstrom. At still higher F do** levels, dHc2/dT and the low field Jc decreased; above 0.5 T, however, Jc had almost the same value. Compared with previous reports, the present synthesis route with low synthesis temperatures and commonly available FeF2 as the source of F is more effective at introducing F into the SmFeAsO system and thereby resulting in improved superconducting properties for the system. In addition, this new sample preparation method also reduces unnecessary problems such as the evaporation of F and reaction between the crucible and superconductor during the solid-state reaction.
△ Less
Submitted 18 March, 2013;
originally announced March 2013.
-
NMR Investigation of the iron-based superconductors Ca4(Mg,Ti)3Fe2As2O8-y and Ca5(Sc,Ti)4Fe2As2O11-y
Authors:
Y. Tomita,
H. Kotegawa,
Y. Tao,
H. Tou,
H. Ogino,
S. Horii,
K. Kishio,
J. Shimoyama
Abstract:
$^{75}$As and $^{45}$Sc NMR measurements unravel the electronic state for Fe-based superconductors with perovskite-type blocking layers Ca$_4$(Mg,Ti)$_3$Fe$_2$As$_2$O$_{8-y}$ ($T_c^{onset}=47$ K) and Ca$_5$(Sc,Ti)$_4$Fe$_2$As$_2$O$_{11-y}$ ($T_c^{onset}=41$ K). In Ca$_5$(Sc,Ti)$_4$Fe$_2$As$_2$O$_{11-y}$, the nuclear spin relaxation rate $1/T_1$ shows pseudogap behavior below $\sim80…
▽ More
$^{75}$As and $^{45}$Sc NMR measurements unravel the electronic state for Fe-based superconductors with perovskite-type blocking layers Ca$_4$(Mg,Ti)$_3$Fe$_2$As$_2$O$_{8-y}$ ($T_c^{onset}=47$ K) and Ca$_5$(Sc,Ti)$_4$Fe$_2$As$_2$O$_{11-y}$ ($T_c^{onset}=41$ K). In Ca$_5$(Sc,Ti)$_4$Fe$_2$As$_2$O$_{11-y}$, the nuclear spin relaxation rate $1/T_1$ shows pseudogap behavior below $\sim80$ K, suggesting that the electronic state is similar to that of LaFeAs(O,F) system with moderate electron do**. The presence of the pseudogap behavior gives an interpretation that the hole-like band (so-called $γ$ pocket) is located just below the Fermi level from the analogy to LaFeAs(O,F) system and the disappearance of the $γ$ pocket yields the suppression of the low-energy spin fluctuations. On the other hand, in Ca$_4$(Mg,Ti)$_3$Fe$_2$As$_2$O$_{8-y}$ satisfying the structural optimal condition for higher $T_c$ among the perovskite systems, the extrinsic contribution, which presumably originates in the Ti moment, is observed in $1/T_1T$; however, the moderate temperature dependence of $1/T_1T$ appears by its suppression under high magnetic field. In both systems, the high $T_c$ of $\sim40$ K is realized in the absence of the strong development of the low-energy spin fluctuations. The present results reveal that the structural optimization does not induce the strong development of the low-energy spin fluctuations. If we consider that superconductivity is mediated by spin fluctuations, the structural optimization is conjectured to provide a benefit to the development of the high-energy spin fluctuations irrespective to the low-energy part.
△ Less
Submitted 22 October, 2012;
originally announced October 2012.
-
Strongly connected ex-situ MgB2 polycrystalline bulks fabricated by solid-state self-sintering
Authors:
Hiroya Tanaka,
Akiyasu Yamamoto,
Jun-ichi Shimoyama,
Hiraku Ogino,
Kohji Kishio
Abstract:
We have investigated the microstructure, normal-state electrical connectivity, and critical current density of ex-situ MgB2 polycrystalline bulks prepared by systematically varying the sintering conditions under low pressure. Samples heated at a high temperature of ~900°C for a long period showed an increased packing factor, a larger intergrain contact area, and a significantly enhanced electrical…
▽ More
We have investigated the microstructure, normal-state electrical connectivity, and critical current density of ex-situ MgB2 polycrystalline bulks prepared by systematically varying the sintering conditions under low pressure. Samples heated at a high temperature of ~900°C for a long period showed an increased packing factor, a larger intergrain contact area, and a significantly enhanced electrical connectivity, all of which indicate solid-state self-sintering of MgB2. Sintered ex-situ MgB2 bulks from a laboratory-made ball-milled powder exhibited a greatly enhanced connectivity of 28%, which is the highest connectivity of pressureless ex-situ MgB2 bulks, wires, and tapes. Surprisingly, grain growth did not occur during long-duration (~100 h) sintering in the sintered ex-situ MgB2 bulks. This is in marked contrast to in-situ processed MgB2 samples for which significant grain growth occurred during heat treatment at ~900°C, producing grains that are several tens of times larger than the initial boron grains. Consequently, the critical current density as a function of the external magnetic field at 20 K progressively improved with sintering due to the relatively small grain size and good intergrain connectivity. We thus conclude that solid-state self-sintering is an effective approach for producing strongly connected, dense ex-situ MgB2 polycrystals without grain growth.
△ Less
Submitted 20 September, 2012;
originally announced September 2012.
-
Antiferromagnetic Order and Superconductivity in Sr4(Mg0.5-xTi0.5+x)2O6Fe2As2 with Electron Do**: 75As-NMR Study
Authors:
Keisuke Yamamoto,
Hidekazu Mukuda,
Hiroaki Kinouchi,
Mitsuharu Yashima,
Yoshio Kitaoka,
Mamoru Yogi,
Shinya Sato,
Hiraku Ogino,
Jun-ichi Shimoyama
Abstract:
We report an 75As-NMR study on iron (Fe)-based superconductors with thick perovskitetype blocking layers Sr4(Mg0.5-xTi0.5+x)2O6Fe2As2 with x=0 and 0.2. We have found that antiferromagnetic (AFM) order takes place when x=0, and superconductivity (SC) emerges below Tc=36 K when x=0.2. These results reveal that the Fe-pnictides with thick perovskitetype blocks also undergo an evolution from the AFM o…
▽ More
We report an 75As-NMR study on iron (Fe)-based superconductors with thick perovskitetype blocking layers Sr4(Mg0.5-xTi0.5+x)2O6Fe2As2 with x=0 and 0.2. We have found that antiferromagnetic (AFM) order takes place when x=0, and superconductivity (SC) emerges below Tc=36 K when x=0.2. These results reveal that the Fe-pnictides with thick perovskitetype blocks also undergo an evolution from the AFM order to the SC by do** electron carriers into FeAs planes through the chemical substitution of Ti+4 ions for Mg+2 ions, analogous to the F-substitution in LaFeAsO compound. The reason why the Tc=36 K when x=0.2 being higher than the optimally electron-doped LaFeAsO with Tc=27 K relates to the fact that the local tetrahedron structure of FeAs4 is optimized for the onset of SC.
△ Less
Submitted 19 March, 2012;
originally announced March 2012.
-
Towards the Realization of Higher Connectivity in MgB2 Conductors: In-situ or Sintered Ex-situ?
Authors:
A. Yamamoto,
H. Tanaka,
J. Shimoyama,
H. Ogino,
K. Kishio,
T. Matsushita
Abstract:
The two most common types of MgB2 conductor fabrication technique - in-situ and ex-situ - show increasing conflicts concerning the connectivity, an effective current-carrying cross-sectional area. An in-situ reaction yields a strong intergrain coupling with a low packing factor, while an ex-situ process using pre-reacted MgB2 yields tightly packed grains, however, their coupling is much weaker. We…
▽ More
The two most common types of MgB2 conductor fabrication technique - in-situ and ex-situ - show increasing conflicts concerning the connectivity, an effective current-carrying cross-sectional area. An in-situ reaction yields a strong intergrain coupling with a low packing factor, while an ex-situ process using pre-reacted MgB2 yields tightly packed grains, however, their coupling is much weaker. We studied the normal-state resistivity and microstructure of ex-situ MgB2 bulks synthesized with varied heating conditions under ambient pressure. The samples heated at moderately high temperatures of ~900°C for a long period showed an increased packing factor, a larger intergrain contact area and a significantly decreased resistivity, all of which indicate the solid-state self-sintering of MgB2. Consequently the connectivity of the sintered ex-situ samples exceeded the typical connectivity range 5-15% of the in-situ samples. Our results show self-sintering develops the superior connectivity potential of ex-situ MgB2, though its intergrain coupling is not yet fulfilled, to provide a strong possibility of twice or even much higher connectivity in optimally sintered ex-situ MgB2 than in in-situ MgB2.
△ Less
Submitted 6 January, 2012; v1 submitted 29 November, 2011;
originally announced November 2011.
-
Successive transition from superconducting to antiferromagnetic phase in (Ca_6(Al, Ti)_4O_y)Fe_2As_2 studied via ^{75}As and ^{27}Al NMR
Authors:
T. Nakano,
N. Fujiwara,
S. Tsutsumi,
H. Ogino,
K. Kishio,
J. Shimoyama
Abstract:
An unusual successive phase transition from superconducting (SC) to antiferromagnetic (AF) phases was discovered via ^{75}As and ^{27}Al nuclear magnetic resonance (NMR) in (Fe_2As_2)(Ca_6(Al, Ti)_4O_y) with four (Al, Ti)O layers intercalated between FeAs planes. Although the spatially-uniform AF ordering is clearly visible from ^{27}Al spectra, the ordered moments are very small and the low-frequ…
▽ More
An unusual successive phase transition from superconducting (SC) to antiferromagnetic (AF) phases was discovered via ^{75}As and ^{27}Al nuclear magnetic resonance (NMR) in (Fe_2As_2)(Ca_6(Al, Ti)_4O_y) with four (Al, Ti)O layers intercalated between FeAs planes. Although the spatially-uniform AF ordering is clearly visible from ^{27}Al spectra, the ordered moments are very small and the low-frequency fluctuation is much suppressed, contrary to existing pnictides with localized magnetic elements. Furthermore, the temperature (T) dependence of the fluctuation at both nuclei is very similar throughout the entire temperature range. These facts suggest that some hybridization between Ti and Fe orbitals induces a uniform electronic state within FeAs and (Al, Ti)O layers accompanied by the SC and AF transitions. The iron-based pnictide with Ti-doped blocking layers is the first high-T_c compound having metallic blocking layers.
△ Less
Submitted 11 August, 2011; v1 submitted 14 July, 2011;
originally announced July 2011.
-
Pressure Dependence of Superconducting Transition Temperature on Perovskite-Type Fe-Based Superconductors and NMR Study of Sr2VFeAsO3
Authors:
Hisashi Kotegawa,
Yuuki Tao,
Hideki Tou,
Hiraku Ogino,
Sigeru Horii,
Kohji Kishio,
Jun-ichi Shimoyama
Abstract:
We report the pressure dependences of the superconducting transition temperature (T_c) in several perovskite-type Fe-based superconductors through the resistivity measurements up to ~4 GPa. In Ca_4(Mg,Ti)_3Fe_2As_2O_y with the highest T_c of 47 K in the present study, the T_c keeps almost constant up to ~1 GPa, and starts to decrease above it. From the comparison among several systems, we obtained…
▽ More
We report the pressure dependences of the superconducting transition temperature (T_c) in several perovskite-type Fe-based superconductors through the resistivity measurements up to ~4 GPa. In Ca_4(Mg,Ti)_3Fe_2As_2O_y with the highest T_c of 47 K in the present study, the T_c keeps almost constant up to ~1 GPa, and starts to decrease above it. From the comparison among several systems, we obtained a tendency that low T_c with the longer a-axis length at ambient pressure increases under pressure, but high T_c with the shorter a-axis length at ambient pressure hardly increases. We also report the ^75As-NMR results on Sr_2VFeAsO_3. NMR spectrum suggests that the magnetic ordering occurs at low temperatures accompanied by some inhomogeneity. In the superconducting state, we confirmed the anomaly by the occurrence of superconductivity in the nuclear spin lattice relaxation rate 1/T_1, but the spin fluctuations unrelated with the superconductivity are dominant. It is conjectured that the localized V-3d moments are magnetically ordered and their electrons do not contribute largely to the Fermi surface and the superconductivity in Sr_2VFeAsO_3.
△ Less
Submitted 28 September, 2010;
originally announced September 2010.
-
Second Homologous Series of Iron Pnictide Oxide Superconductors (Fe2As2)(Can+2(Al,Ti)nOy)[n = 2,3,4]
Authors:
Hiraku Ogino,
Kenji Machida,
Akiyasu Yamamoto,
Kohji Kishio,
Jun-ichi Shimoyama,
Tetsuya Tohei,
Yuichi Ikuhara
Abstract:
We have discovered a new homologous series of iron pnictide oxides (Fe2As2)(Can+2(Al,Ti)nOy)[n = 2,3,4]. These compounds have perovskite-like blocking layers between Fe2As2 layers. The structure of new compounds are tetragonal with space groups of P4/nmm for n = 2 and 4 and P4mm for n = 3, which are similar to those of (Fe2As2)(Can+1(Sc,Ti)nOy)[n = 3,4,5] found in our previous study. Compounds wit…
▽ More
We have discovered a new homologous series of iron pnictide oxides (Fe2As2)(Can+2(Al,Ti)nOy)[n = 2,3,4]. These compounds have perovskite-like blocking layers between Fe2As2 layers. The structure of new compounds are tetragonal with space groups of P4/nmm for n = 2 and 4 and P4mm for n = 3, which are similar to those of (Fe2As2)(Can+1(Sc,Ti)nOy)[n = 3,4,5] found in our previous study. Compounds with n = 3 and 4 have new crystal structures with 3 and 4 sheets of perovskite layers, respectively, including a rock salt layer in each blocking layer. The a-axis lengths of the three compounds are approximately 3.8 A, which are close to those of FeSe and LiFeAs. (Fe2As2)(Ca6(Al,Ti)4Oy) exhibited bulk superconductivity in magnetization measurement with Tc(onset)~36 K and resistivity drop was observed at ~39 K. (Fe2As2)(Ca5(Al,Ti)3Oy) also showed large diamagnetism at low temperatures. These new compounds indicate considerable rooms are still remaining for new superconductors in layered iron pnictides.
△ Less
Submitted 1 October, 2010; v1 submitted 16 August, 2010;
originally announced August 2010.
-
A New Iron Pnictide Oxide (Fe2As2)(Ca5(Mg,Ti)4Oy) and a New Phase in Fe-As-Ca-Mg-Ti-O system
Authors:
Hiraku Ogino,
Yasuaki Shimizu,
Naoto Kawaguchi,
Kohji Kishio,
Jun-ichi Shimoyama,
Tetsuya Tohei,
Yuichi Ikuhara
Abstract:
A new layered iron arsenide oxide (Fe2As2)(Ca5(Mg,Ti)4Oy) and its structural derivative were found in the Fe-As-Ca-Mg-Ti-O system. The crystal structure of (Fe2As2)(Ca5(Mg,Ti)4Oy) is identical to that of (Fe2As2)(Ca5(Sc,Ti)4Oy), which was reported in our previous study. The lattice constants of this compound are a = 3.86(4) A and c = 41.05(2) A. In addition, another phase with a thicker blocking l…
▽ More
A new layered iron arsenide oxide (Fe2As2)(Ca5(Mg,Ti)4Oy) and its structural derivative were found in the Fe-As-Ca-Mg-Ti-O system. The crystal structure of (Fe2As2)(Ca5(Mg,Ti)4Oy) is identical to that of (Fe2As2)(Ca5(Sc,Ti)4Oy), which was reported in our previous study. The lattice constants of this compound are a = 3.86(4) A and c = 41.05(2) A. In addition, another phase with a thicker blocking layer was found. The structure of the compound and its derivative was tentatively assigned through STEM observation as (Fe2As2)(Ca8(Mg,Ti)6Oy) with sextuple perovskite-type sheets divided by a rock salt layer. The interlayer Fe-Fe distance of this compound is ~30 A. The compound and its derivative exhibited bulk superconductivity, as found from magnetization and resistivity measurements.
△ Less
Submitted 19 June, 2012; v1 submitted 18 June, 2010;
originally announced June 2010.
-
Superconductivity Above 40 K Observed in a New Iron Arsenide Oxide (Fe2As2)(Ca4(Mg,Ti)3Oy)
Authors:
Hiraku Ogino,
Yasuaki Shimizu,
Koichi Ushiyama,
Naoto Kawaguchi,
Kohji Kishio,
Jun-ichi Shimoyama
Abstract:
A new layered iron arsenide oxide (Fe2As2)(Ca4(Mg,Ti)3Oy) was discovered. Its crystal structure is tetragonal with a space group of I4/mmm consisted of the anti-fluorite type FeAs layer and blocking layer of triple perovskite cells and is identical with (Fe2As2)(Sr4(Sc,Ti)3O8) discovered in our previous study. The lattice constants of (Fe2As2)(Ca4(Mg,Ti)3Oy) are a = 3.877 A and c = 33.37 A. This c…
▽ More
A new layered iron arsenide oxide (Fe2As2)(Ca4(Mg,Ti)3Oy) was discovered. Its crystal structure is tetragonal with a space group of I4/mmm consisted of the anti-fluorite type FeAs layer and blocking layer of triple perovskite cells and is identical with (Fe2As2)(Sr4(Sc,Ti)3O8) discovered in our previous study. The lattice constants of (Fe2As2)(Ca4(Mg,Ti)3Oy) are a = 3.877 A and c = 33.37 A. This compound exhibited bulk superconductivity up to 43 K in susceptibility measurement without intentional carrier do**. A resistivity drop was observed at ~47 K and zero resistance was achieved at 42 K. These values correspond to the second highest Tc among the layered iron-based superconductors after REFeAsO system.
△ Less
Submitted 14 June, 2010; v1 submitted 11 June, 2010;
originally announced June 2010.
-
First Homologous Series of Iron Pnictide Oxide Superconductors (Fe2As2)(Can+1(Sc,Ti)nOy) [n = 3,4,5] with Extremely Thick Blocking Layers
Authors:
Hiraku Ogino,
Shinya Sato,
Kohji Kishio,
Jun-ichi Shimoyama,
Tetsuya Tohei,
Yuichi Ikuhara
Abstract:
We have discovered first homologous series of iron pnictide oxide superconductors (Fe2As2)(Can+1(Sc,Ti)nOy) [n = 3,4,5]. These compounds have extremely thick blocking layers up to quintuple perovskite oxide layers sandwiched by the Fe2As2 layers. These samples exhibited bulk superconductivity with relatively high Tc up to 42 K. The relationship between Tc and the iron-plane interlayer distance sug…
▽ More
We have discovered first homologous series of iron pnictide oxide superconductors (Fe2As2)(Can+1(Sc,Ti)nOy) [n = 3,4,5]. These compounds have extremely thick blocking layers up to quintuple perovskite oxide layers sandwiched by the Fe2As2 layers. These samples exhibited bulk superconductivity with relatively high Tc up to 42 K. The relationship between Tc and the iron-plane interlayer distance suggested that superconductivity due to the mono Fe2As2 layer is substantially 40 K-class.
△ Less
Submitted 18 August, 2010; v1 submitted 11 June, 2010;
originally announced June 2010.
-
New Iron Arsenide Oxides (Fe2As2)(Sr4(Sc,Ti)3O8), (Fe2As2)(Ba4Sc3O7.5), and (Fe2As2)(Ba3Sc2O5)
Authors:
Naoto Kawaguchi,
Hiraku Ogino,
Yasuaki Shimizu,
Kohji Kishio,
Jun-ichi Shimoyama
Abstract:
We synthesized new layered iron arsenide oxides (Fe2As2)(Sr4(Sc,Ti)3O8),(Fe2As2)(Ba4Sc3O7.5), and (Fe2As2)(Ba3Sc2O5). The crystal structures of these compounds are tetragonal with a space group of I4/mmm. The structure of (Fe2As2)(Sr4(Sc,Ti)3O8) and (Fe2As2)(Ba4Sc3O7.5) consists of the alternate stacking of antifluorite Fe2As2 layers and triple perovskite-type oxide layers. The interlayer distance…
▽ More
We synthesized new layered iron arsenide oxides (Fe2As2)(Sr4(Sc,Ti)3O8),(Fe2As2)(Ba4Sc3O7.5), and (Fe2As2)(Ba3Sc2O5). The crystal structures of these compounds are tetragonal with a space group of I4/mmm. The structure of (Fe2As2)(Sr4(Sc,Ti)3O8) and (Fe2As2)(Ba4Sc3O7.5) consists of the alternate stacking of antifluorite Fe2As2 layers and triple perovskite-type oxide layers. The interlayer distance between the Fe planes of (Fe2As2)(Ba4Sc3O7.5) is ~18.7 A. Moreover, the a-axis of (Fe2As2)(Ba3Sc2O5) is the longest among the layered iron pnictides, indicating the structural flexibility of the layered iron pnictide containing perovskite-type layers. The bulk sample of (Fe2As2)(Sr4(Sc0.6Ti0.4)3O8) exhibited diamagnetism up to 28 K in susceptibility measurements.
△ Less
Submitted 11 June, 2010;
originally announced June 2010.
-
Structural Features of Layered Iron Pnictide Oxides (Fe2As2)(Sr4M2O6)
Authors:
H. Ogino,
S. Sato,
Y. Matsumura,
N. Kawaguchi,
K. Ushiyama,
Y. Katsura,
S. Horii,
K. Kishio,
J. Shimoyama
Abstract:
Structural features of newly found perovskite-based iron pnictide oxide system have been systematically studied. Compared to REFePnO system, perovskite-based system tend to have lower Pn-Fe-Pn angle and higher pnictogen height owing to low electronegativity of alkaline earth metal and small repulsive force between pnictogen and oxygen atoms. As-Fe-As angles of (Fe2As2)(Sr4Cr2O6), (Fe2As2)(Sr4V2O6)…
▽ More
Structural features of newly found perovskite-based iron pnictide oxide system have been systematically studied. Compared to REFePnO system, perovskite-based system tend to have lower Pn-Fe-Pn angle and higher pnictogen height owing to low electronegativity of alkaline earth metal and small repulsive force between pnictogen and oxygen atoms. As-Fe-As angles of (Fe2As2)(Sr4Cr2O6), (Fe2As2)(Sr4V2O6) and (Fe2Pn2)(Sr4MgTiO6) are close to ideal tetrahedron and those pnictogen heights of about 1.40 A are close to NdFeAsO with optimized carrier concentration. These structural features of this system may leads to realization of high Tc superconductivity.
△ Less
Submitted 11 June, 2010;
originally announced June 2010.
-
Superconductivity in New Iron Pnictide Oxide (Fe2As2)(Sr4(Mg,Ti)2O6)
Authors:
Shinya Sato,
Hiraku Ogino,
Naoto Kawaguchi,
Yukari Katsura,
Kohji Kishio,
Jun-ichi Shimoyama,
Hisashi Kotegawa,
Hideki Tou
Abstract:
We have discovered a new iron pnictide oxide superconductor (Fe2As2)(Sr4(Mg,Ti)2O6). This material is isostructual with (Fe2As2)(Sr4M2O6) (M = Sc, Cr, V), which were found in previous studies. The structure of this compound is tetragonal with a space group of P4/nmm and consists of the anti-fluorite type FeAs layer and perovskite-type block layer. The lattice constants are a = 3.935 A and c = 15…
▽ More
We have discovered a new iron pnictide oxide superconductor (Fe2As2)(Sr4(Mg,Ti)2O6). This material is isostructual with (Fe2As2)(Sr4M2O6) (M = Sc, Cr, V), which were found in previous studies. The structure of this compound is tetragonal with a space group of P4/nmm and consists of the anti-fluorite type FeAs layer and perovskite-type block layer. The lattice constants are a = 3.935 A and c = 15.952 A for (Fe2As2)(Sr4MgTiO6). Bulk superconductivity with Tc(onset) of ~26 K was observed for a partially Co substituted sample. Moreover, Co-free and Ti-rich samples exhibited higher Tc(onset)'s above 35 K, which were further enhanced by applying high pressures up to ~43 K.
△ Less
Submitted 9 December, 2009;
originally announced December 2009.
-
Superconductivity at 39 K in New Iron Pnictide Oxide (Fe2As2)(Sr4(Mg,Ti)2O6)
Authors:
Shinya Sato,
Hiraku Ogino,
Naoto Kawaguchi,
Yukari Katsura,
Kohji Kishio,
Jun-ichi Shimoyama
Abstract:
We have discovered a new iron pnictide oxide superconductor (Fe2As2)(Sr4(Mg,Ti)2O6). This material is isostructual with (Fe2As2)(Sr4M2O6) (M = Sc, Cr), which was found in our previous study. The structure of this compound is tetragonal with a space group of P4/nmm and consists of the anti-fluorite type FeAs and perovskite-type blocking layers. The lattice constants are a = 3.935 A and c = 15.952…
▽ More
We have discovered a new iron pnictide oxide superconductor (Fe2As2)(Sr4(Mg,Ti)2O6). This material is isostructual with (Fe2As2)(Sr4M2O6) (M = Sc, Cr), which was found in our previous study. The structure of this compound is tetragonal with a space group of P4/nmm and consists of the anti-fluorite type FeAs and perovskite-type blocking layers. The lattice constants are a = 3.935 A and c = 15.952 A for (Fe2As2)(Sr4MgTiO6). In both magnetization and resistivity measurements, this compound exhibits superconductivity below 10 K. Moreover, ratio of Mg and Ti in this compound can be changed toward Ti-rich composition. (Fe2As2)(Sr4Mg1-xTi1+xO6) phase is obtained at 0 < x as a main phase, and Tc and superconducting volume fraction increase with increasing x. The highest Tc(onset) was confirmed at 39 K for x = 0.6 in resistivity measurement.
△ Less
Submitted 10 December, 2009; v1 submitted 16 September, 2009;
originally announced September 2009.
-
Evidence for Nodal superconductivity in Sr$_{2}$ScFePO$_{3}$
Authors:
K. A. Yates,
I. T. M. Usman,
K. Morrison,
J. D. Moore,
A. M. Gilbertson,
A. D. Caplin,
L. F. Cohen,
H. Ogino,
J. Shimoyama
Abstract:
Point contact Andreev reflection spectra have been taken as a function of temperature and magnetic field on the polycrystalline form of the newly discovered iron-based superconductor Sr2ScFePO3. A zero bias conductance peak which disappears at the superconducting transition temperature, dominates all of the spectra. Data taken in high magnetic fields show that this feature survives until 7T at 2…
▽ More
Point contact Andreev reflection spectra have been taken as a function of temperature and magnetic field on the polycrystalline form of the newly discovered iron-based superconductor Sr2ScFePO3. A zero bias conductance peak which disappears at the superconducting transition temperature, dominates all of the spectra. Data taken in high magnetic fields show that this feature survives until 7T at 2K and a flattening of the feature is observed in some contacts. Here we inspect whether these observations can be interpreted within a d-wave, or nodal order parameter framework which would be consistent with the recent theoretical model where the height of the P in the Fe-P-Fe plane is key to the symmetry of the superconductivity. However, in polycrystalline samples care must be taken when examining Andreev spectra to eliminate or take into account artefacts associated with the possible effects of Josephson junctions and random alignment of grains.
△ Less
Submitted 11 December, 2009; v1 submitted 20 August, 2009;
originally announced August 2009.
-
Contrasting Pressure Effects in Sr2VFeAsO3 and Sr2ScFePO3
Authors:
H. Kotegawa,
T. Kawazoe,
H. Tou,
K. Murata,
H. Ogino,
K. Kishio,
J. Shimoyama
Abstract:
We report the resistivity measurements under pressure of two Fe-based superconductors with a thick perovskite oxide layer, Sr2VFeAsO3 and Sr2ScFePO3. The superconducting transition temperature Tc of Sr2VFeAsO3 markedly increases with increasing pressure. Its onset value, which was Tc{onset}=36.4 K at ambient pressure, increases to Tc{onset}=46.0 K at ~4 GPa, ensuring the potential of the "21113"…
▽ More
We report the resistivity measurements under pressure of two Fe-based superconductors with a thick perovskite oxide layer, Sr2VFeAsO3 and Sr2ScFePO3. The superconducting transition temperature Tc of Sr2VFeAsO3 markedly increases with increasing pressure. Its onset value, which was Tc{onset}=36.4 K at ambient pressure, increases to Tc{onset}=46.0 K at ~4 GPa, ensuring the potential of the "21113" system as a high-Tc material. However, the superconductivity of Sr2ScFePO3 is strongly suppressed under pressure. The Tc{onset} of ~16 K decreases to ~5 K at ~4 GPa, and the zero-resistance state is almost lost. We discuss the factor that induces this contrasting pressure effect.
△ Less
Submitted 27 October, 2009; v1 submitted 11 August, 2009;
originally announced August 2009.
-
New Series of Nickel-Based Pnictide Oxide Superconductors (Ni2Pn2)(Sr4Sc2O6) (Pn = P, As)
Authors:
Yutaka Matsumura,
Hiraku Ogino,
Shigeru Horii,
Yukari Katsura,
Kohji Kishio,
Jun-ichi Shimoyama
Abstract:
We have discovered new nickel-based pnictide oxide superconductors, (Ni2Pn2)(Sr4Sc2O6) (Pn = P, As). These compounds have a tetragonal unit cell with a space group of P4/nmm and they consist of alternate stacking of anti-fluorite Ni2Pn2 layers and K2NiF4-type Sr4Sc2O6 blocking layers. Lattice parameters were a = 4.044 A and c = 15.23 A for (Ni2P2)(Sr4Sc2O6) and a = 4.078 A and c = 15.41 A for (N…
▽ More
We have discovered new nickel-based pnictide oxide superconductors, (Ni2Pn2)(Sr4Sc2O6) (Pn = P, As). These compounds have a tetragonal unit cell with a space group of P4/nmm and they consist of alternate stacking of anti-fluorite Ni2Pn2 layers and K2NiF4-type Sr4Sc2O6 blocking layers. Lattice parameters were a = 4.044 A and c = 15.23 A for (Ni2P2)(Sr4Sc2O6) and a = 4.078 A and c = 15.41 A for (Ni2As2)(Sr4Sc2O6), indicating their thicker blocking layers than that of LaNiPO (c ~ 8.1 A). Both (Ni2P2)(Sr4Sc2O6) and (Ni2As2)(Sr4Sc2O6) exhibited superconductivity with zero resistivity at 3.3 K and 2.7 K, respectively. The perfect diamagnetism observed in both compounds guaranteed their bulk superconductivity.
△ Less
Submitted 6 June, 2009; v1 submitted 5 April, 2009;
originally announced April 2009.
-
New iron-based arsenide oxides (Fe2As2)(Sr4M2O6)(M = Sc, Cr)
Authors:
Hiraku Ogino,
Yukari Katsura,
Shigeru Horii,
Kohji Kishio,
Jun-ichi Shimoyama
Abstract:
We have discovered new layered oxyarsenides (Fe2As2)(Sr4M2O6) (M = Sc, Cr: M-22426). These materials are isostructural with (Fe2P2)(Sr4Sc2O6), which was found in our previous study. The new compounds are tetragonal with a space group of P4/nmm and consist of the anti-fluorite type FeAs layer and perovskite-type blocking layer. The lattice constants are a = 4.050 A, c = 15.809 A for M = Sc and a…
▽ More
We have discovered new layered oxyarsenides (Fe2As2)(Sr4M2O6) (M = Sc, Cr: M-22426). These materials are isostructural with (Fe2P2)(Sr4Sc2O6), which was found in our previous study. The new compounds are tetragonal with a space group of P4/nmm and consist of the anti-fluorite type FeAs layer and perovskite-type blocking layer. The lattice constants are a = 4.050 A, c = 15.809 A for M = Sc and a = 3.918 A, c = 15.683 A for M = Cr. These compounds have long interlayer Fe-Fe distances corresponding to the c-axis length, the 15.8 A in Sc-22426 is the longest in the iron-based oxypnictide systems. Chemical flexibility of the perovskite block in this system was probed by chromium containing (Fe2As2)(Sr4Cr2O6). Different trends were found in bond angle and bond length of the new oxypnictides compared to the reported systems, such as REFePnO. Absence of superconductivity in these compounds is considered to be due to insufficient carrier concentration as in the case of undoped REFeAsO.
△ Less
Submitted 24 June, 2009; v1 submitted 30 March, 2009;
originally announced March 2009.
-
Superconductivity at 17 K in (Fe2P2)(Sr4Sc2O6): a new superconducting layered pnictide oxide with a thick perovskite oxide layer
Authors:
H. Ogino,
Y. Matsumura,
Y. Katsura,
K. Ushiyama,
S. Horii,
K. Kishio,
J. Shimoyama
Abstract:
A new layered oxypnictide (Fe2P2)(Sr4Sc2O6) have been synthesized by solid-state reaction. This material has an alternating layer stacking structure of anti-fluorite Fe2P2 and perovskite-based Sr4Sc2O6 oxide layers. Space group of the material is P4/nmm and lattice constants a and c are 4.016 A and 15.543 A, respectively. The interlayer Fe-Fe distance corresponding to the c-axis length is the lo…
▽ More
A new layered oxypnictide (Fe2P2)(Sr4Sc2O6) have been synthesized by solid-state reaction. This material has an alternating layer stacking structure of anti-fluorite Fe2P2 and perovskite-based Sr4Sc2O6 oxide layers. Space group of the material is P4/nmm and lattice constants a and c are 4.016 A and 15.543 A, respectively. The interlayer Fe-Fe distance corresponding to the c-axis length is the longest ever reported in the iron-based oxypnictide systems. In both magnetization and resistivity measurements, the present compound exhibited superconductivity below 17 K, which is much higher than that of LaFePO and the highest in arsenic-free iron-based oxypnictide systems under ambient pressure.
△ Less
Submitted 6 June, 2009; v1 submitted 19 March, 2009;
originally announced March 2009.