Site Split of Antiferromagnetic $α$-Mn Revealed by $^{55}$Mn Nuclear Magnetic Resonance
Authors:
Masahiro Manago,
Gaku Motoyama,
Shijo Nishigori,
Kenji Fujiwara,
Katsuki Kinjo,
Shunsaku Kitagawa,
Kenji Ishida,
Kazuto Akiba,
Shingo Araki,
Tatsuo C. Kobayashi,
Hisatomo Harima
Abstract:
The magnetic structure of antiferromagnetic $α$-Mn has been unclarified for almost 70 years since its magnetism was discovered. We measured the zero-field nuclear magnetic resonance spectra of antiferromagnetic $α$-Mn to obtain further insight into magnetism below $T_{\text{N}} = 95$ K. The site II spectra split into two sites with five subpeaks owing to quadrupole interaction, and this shows that…
▽ More
The magnetic structure of antiferromagnetic $α$-Mn has been unclarified for almost 70 years since its magnetism was discovered. We measured the zero-field nuclear magnetic resonance spectra of antiferromagnetic $α$-Mn to obtain further insight into magnetism below $T_{\text{N}} = 95$ K. The site II spectra split into two sites with five subpeaks owing to quadrupole interaction, and this shows that the ordered moments at site II are slightly tilted from the $[001]$ direction. The site III spectra revealed that this site splits into four sites below $T_{\text{N}}$. These findings clearly demonstrate that the antiferromagnetic $α$-Mn symmetry is lower than previously considered.
△ Less
Submitted 6 October, 2022;
originally announced October 2022.
-
Disappearance and Survival of Superconductivity in FeSe under High Pressure
Authors:
Kiyotaka Miyoshi,
Shota Yamamoto,
Atsushi Shiota,
Takuya Matsuoka,
Masaki Ohe,
Yumi Yamamoto,
Shijo Nishigori
Abstract:
Superconductivity in FeSe was investigated under high pressure through the measurements of DC magnetization by using a diamond anvil cell. We successfully observed that the disappearance of the superconductivity as a results of the appearance of the non-superconducting ortho I\hspace{-1pt}I phase above $\sim$7 GPa ($\sim$5 GPa), when Ar (glycerin) is used as the pressure transmitting media. Contra…
▽ More
Superconductivity in FeSe was investigated under high pressure through the measurements of DC magnetization by using a diamond anvil cell. We successfully observed that the disappearance of the superconductivity as a results of the appearance of the non-superconducting ortho I\hspace{-1pt}I phase above $\sim$7 GPa ($\sim$5 GPa), when Ar (glycerin) is used as the pressure transmitting media. Contrary to this, it has been found that the superconductivity even survives under pressure above 7 GPa, when the thickness ($t$) of a platelet-single crystal specimen is reduced. The survival of the superconductivity above 7 GPa is consistent with a previous observation under hydrostatic pressure by using a cubic anvil apparatus, suggesting that the hydrostaticity of the pressure is improved by reducing $t$. It is also inferred that the appearance of the ortho I\hspace{-1pt}I phase is due to uniaxial stress along the [001] direction.
△ Less
Submitted 24 June, 2021; v1 submitted 30 March, 2021;
originally announced March 2021.
-
Magnetoelectric Effect in the Antiferromagnetic Ordered State of Ce$_{3}$TiBi$_{5}$ with Ce Zig-Zag Chains
Authors:
Masahiro Shinozaki,
Gaku Motoyama,
Masahiro Tsubouchi,
Masumi Sezaki,
Jun Gouchi,
Shijo Nishigori,
Tetsuya Mutou,
Akira Yamaguchi,
Kenji Fujiwara,
Kiyotaka Miyoshi,
Yoshiya Uwatoko
Abstract:
In this study, we investigate the magnetoelectric (ME) effect of the newly discovered antiferromagnetic (AFM) compound Ce$_{3}$TiBi$_{5}$ with a hexagonal structure (space group $P6_{3}$/$mcm$). In this system, Ce ions form zig-zag chains that extend along the $c$-axis. We focus on the lack of the local inversion symmetry at the Ce site, although the crystal structure has an inversion center. A th…
▽ More
In this study, we investigate the magnetoelectric (ME) effect of the newly discovered antiferromagnetic (AFM) compound Ce$_{3}$TiBi$_{5}$ with a hexagonal structure (space group $P6_{3}$/$mcm$). In this system, Ce ions form zig-zag chains that extend along the $c$-axis. We focus on the lack of the local inversion symmetry at the Ce site, although the crystal structure has an inversion center. A theoretical study has predicted that magnetization can be induced by an electric current in the AFM ordering on the zig-zag chain. We conducted magnetization measurements on Ce$_{3}$TiBi$_{5}$ under an applied constant electric current and a static magnetic field around the AFM ordering temperature of $T_{\rm N}$ = 5.0 K. We successfully observed of the current-induced magnetization below $T_{\rm N}$. The magnitude of the current-induced magnetization has a linear electric current dependence and exhibits no magnetic field dependence. This behavior is consistent with the theoretical prediction of the ME effect in the ferrotoroidal ordered state.
△ Less
Submitted 27 February, 2020;
originally announced February 2020.
-
Novel electronic states realized by the interplay between Li diffusion and Co$^{\rm 3+}$$/$Co$^{\rm 4+}$ charge ordering in Li$_{\rm x}$CoO$_2$
Authors:
Kiyotaka Miyoshi,
Kentaro Manami,
Ryo Sasai,
Shijo Nishigori,
Jun Takeuchi
Abstract:
Measurements of dc magnetization ($M$) and electrical resistivity ($ρ$) have been carried out as a function of temperature ($T$) for layered oxide Li$_{\rm x}$CoO$_2$ (0.51$\leq$$x$$\leq$1.0) using single crystal specimens. After slow cool of the specimens down to 10 K, both of the $M$($T$) and $ρ$($T$) curves are found to exhibit a clear anomaly due to the occurrence of Co$^{\rm 3+}$$/$Co…
▽ More
Measurements of dc magnetization ($M$) and electrical resistivity ($ρ$) have been carried out as a function of temperature ($T$) for layered oxide Li$_{\rm x}$CoO$_2$ (0.51$\leq$$x$$\leq$1.0) using single crystal specimens. After slow cool of the specimens down to 10 K, both of the $M$($T$) and $ρ$($T$) curves are found to exhibit a clear anomaly due to the occurrence of Co$^{\rm 3+}$$/$Co$^{\rm 4+}$ charge ordering (CO) at $T_{\rm S}$$\sim$155 K for 0.6$\leq$$x$$\leq$0.98 (at $T_{\rm S}$$\sim$180$-$190 K for 0.5$\leq$$x$$\leq$0.55). After rapid cool of the specimens, additional anomalies are observed related to the onset of Li diffusion at $T_{\rm F1}$$\sim$370 K and$/$or $T_{\rm F2}$=120$-$130 K. Due to phase mixing with compositions of nearly LiCoO$_2$ and Li$_{\rm 2/3}$CoO$_2$, the specimens with 0.7$\lesssim$$x$$\lesssim$0.9 show anomlies both at $T_{\rm F1}$ and $T_{\rm F2}$. For 0.6$\lesssim$$x$$\lesssim$0.9, the resistivity measured after rapid cool is found to be fairly larger than that measured after slow cool below $T_{\rm S}$. The enhanced resistivity can be explained by the scenario that disordered Co$^{\rm 3+}$$/$Co$^{\rm 4+}$ arrangements, which have been observed and revealed to have an insulating electronic structure contrasting to the regular CO state in the previous scanning tunneling microscopy measurements [Phys. Rev. Lett. {\bf 111}, 126104 (2013)], are realized due to the formation of an amorphous-like structure of Li ions after rapid cool via the interlayer Coulomb coupling. An electronic phase diagram for 0.5$\leq$$x$$\leq$1.0 is proposed.
△ Less
Submitted 1 November, 2018; v1 submitted 24 August, 2018;
originally announced August 2018.
-
Enhanced Superconductivity on the Tetragonal Lattice in FeSe under Hydrostatic Pressure
Authors:
Kiyotaka Miyoshi,
Koh Morishita,
Eriko Mutou,
Masatoshi Kondo,
Osamu Seida,
Kenji Fujiwara,
Jun Takeuchi,
Shijo Nishigori
Abstract:
Superconductivity under pressure in FeSe ($T_{\rm c}$$\sim$7.5 K) has been investigated using single-crystal specimens through the measurements of DC magnetization and electrical resistivity. A characteristic three-step increase in $T_{\rm c}$ has been found under hydrostatic pressure up to $\sim$34 K above 7 GPa. The structural transition from a tetragonal phase to an orthorhombic phase (…
▽ More
Superconductivity under pressure in FeSe ($T_{\rm c}$$\sim$7.5 K) has been investigated using single-crystal specimens through the measurements of DC magnetization and electrical resistivity. A characteristic three-step increase in $T_{\rm c}$ has been found under hydrostatic pressure up to $\sim$34 K above 7 GPa. The structural transition from a tetragonal phase to an orthorhombic phase ($T_{\rm s}$$\sim$87 K) is found to disappear at $P$$\sim$2.3 GPa, above which $T_{\rm c}$ increases rapidly, suggesting that the superconductivity is enhanced by the tetragonal environment. Under non-hydrostatic pressure, the increase in $T_{\rm c}$ is suppressed and the superconductive volume fraction is considerably reduced above 2 GPa, probably owing to the breaking of the tetragonal lattice symmetry by the uniaxial stress. The intimate correlation between the enhanced (suppressed) superconductivity and the tetragonality (orthorhombicity) in the phase diagram is a common feature of FeSe and other iron-pnictide superconductors.
△ Less
Submitted 18 November, 2013; v1 submitted 28 October, 2013;
originally announced October 2013.
-
Magnetic and Electronic Properties of Li$_x$CoO$_2$ Single Crystals
Authors:
K. Miyoshi,
C. Iwai,
H. Kondo,
M. Miura,
S. Nishigori,
J. Takeuchi
Abstract:
Measurements of electrical resistivity ($ρ$), DC magnetization ($M$) and specific heat ($C$) have been performed on layered oxide Li$_x$CoO$_2$ (0.25$\leq$$x$$\leq$0.99) using single crystal specimens. The $ρ$ versus temperature ($T$) curve for $x$=0.90 and 0.99 is found to be insulating but a metallic behavior is observed for 0.25$\leq$$x$$\leq$0.71. At $T_{\rm S}$$\sim$155 K, a sharp anomaly is…
▽ More
Measurements of electrical resistivity ($ρ$), DC magnetization ($M$) and specific heat ($C$) have been performed on layered oxide Li$_x$CoO$_2$ (0.25$\leq$$x$$\leq$0.99) using single crystal specimens. The $ρ$ versus temperature ($T$) curve for $x$=0.90 and 0.99 is found to be insulating but a metallic behavior is observed for 0.25$\leq$$x$$\leq$0.71. At $T_{\rm S}$$\sim$155 K, a sharp anomaly is observed in the $ρ$$-$$T$, $M$$-$$T$ and $C$$/$$T$$-$$T$ curves for $x$=0.66 with thermal hysteresis, indicating the first-order charactor of the transition. The transition at $T_{\rm S}$$\sim$155 K is observed for the wide range of $x$=0.46$-$0.71. It is found that the $M$$-$$T$ curve measured after rapid cool becomes different from that after slow cool below $T_{\rm F}$, which is $\sim$130 K for $x$=0.46$-$0.71. $T_{\rm F}$ is found to agree with the temperature at which the motional narrowing in the $^7$Li NMR line width is observed, indicating that the Li ions stop diffusing and order at the regular site below $T_{\rm F}$. The ordering of Li ions below $T_{\rm F}$$\sim$130 K is likely to be triggered and stabilized by the charge ordering in CoO$_2$ layers below $T_{\rm S}$.
△ Less
Submitted 10 August, 2010; v1 submitted 24 May, 2010;
originally announced May 2010.