Pressure dependence of the magnetic ground state in CePtSi2
Authors:
S. E. Dissanayake,
F. Ye,
W. Tian,
M. Matsuda,
H. Muto,
S. Suzuki,
T. Nakano,
S. Watanabe,
J. Gouchi,
Y. Uwatoko
Abstract:
CePtSi2 was reported to exhibit an antiferromagnetic order below T*=1.8 K at ambient pressure, a valence state change at ~1.2 GPa, and superconductivity in the range between 1.4 and 2.1 GPa with the maximum transition temperature of 0.14 K [T. Nakano et al., Phys. Rev. B 79, 172507 (2009)]. We have performed polycrystalline and single crystal neutron diffraction experiments to determine the magnet…
▽ More
CePtSi2 was reported to exhibit an antiferromagnetic order below T*=1.8 K at ambient pressure, a valence state change at ~1.2 GPa, and superconductivity in the range between 1.4 and 2.1 GPa with the maximum transition temperature of 0.14 K [T. Nakano et al., Phys. Rev. B 79, 172507 (2009)]. We have performed polycrystalline and single crystal neutron diffraction experiments to determine the magnetic structure under ambient and high pressures. We found that incommensurate magnetic peaks with the magnetic propagation vector of (0.32, 0, 0.11) at ambient pressure below T_{SDW}~1.25 K. Those magnetic peaks which originate from a spin-density-wave order with the easy axis along the c axis and an averaged ordered moment of 0.45(5) mu_B, suggesting that there may be an intermediate phase between T* and T_{SDW}. Applying pressures, the magnetic propagation vector shows no change and the magnetic order disappears around 1.0 GPa, which is much lower than the critical pressure for the superconducting phase. The results suggest that other than magnetic fluctuations may play a primary role in the superconducting pairing mechanism.
△ Less
Submitted 16 June, 2022;
originally announced June 2022.
Crystal Size Improvement of Bi-based Superconducting Whiskers under Stress-controlled Condition
Authors:
Sayaka Yamamoto,
Ryo Matsumoto,
Shintaro Adachi,
Yoshihiko Takano,
Hiroyuki Muto,
Hiromi Tanaka
Abstract:
Using stress-controlled amorphous precursors, we have successfully grown large $Bi_{2}$$Sr_{2}$$Ca_{\textit{n}-1}$$Cu_{\textit{n}}$$O_{\textit{y}}$ (Bi-based) high-transition temperature superconducting whiskers. Especially, under a high compressive stress attained by 1 GPa pelletizing, the crystal size of a whisker was significantly enhanced up to 9.5 mm length (growth period: 96 h) which is 2.4…
▽ More
Using stress-controlled amorphous precursors, we have successfully grown large $Bi_{2}$$Sr_{2}$$Ca_{\textit{n}-1}$$Cu_{\textit{n}}$$O_{\textit{y}}$ (Bi-based) high-transition temperature superconducting whiskers. Especially, under a high compressive stress attained by 1 GPa pelletizing, the crystal size of a whisker was significantly enhanced up to 9.5 mm length (growth period: 96 h) which is 2.4 times larger than that of the conventional amorphous-precursors method. In addition, by using the stress-controlled precursors, the number of the obtained Bi-based whiskers were also increased by a factor of 1.8.
△ Less
Submitted 1 November, 2019;
originally announced November 2019.