Effect of Self-Lubricating Carbon Materials on the Tribological Performance of Ultra-High-Molecular-Weight Polyethylene
Authors:
N. Camacho,
J. D. Escobedo-Rodríguez,
J. M. Alvarado-Orozco,
G. C. Mondragón-Rodríguez
Abstract:
Ultra-high-molecular-weight polyethylene (UHMWPE) has been the gold standard for total knee replacements. Due to the knee's natural movements, UHMWPE wear debris production is inevitable. The debris, at the micron and submicron level, results in the joint's mechanical instability, reduced mobility, increased pain, and implant loosening. Wear debris production has been linked to UHMWPE mechanical p…
▽ More
Ultra-high-molecular-weight polyethylene (UHMWPE) has been the gold standard for total knee replacements. Due to the knee's natural movements, UHMWPE wear debris production is inevitable. The debris, at the micron and submicron level, results in the joint's mechanical instability, reduced mobility, increased pain, and implant loosening. Wear debris production has been linked to UHMWPE mechanical properties; therefore, improvements to increase the UHMWPE mechanical properties will impact the component's longevity. Here, TiC coating and multiwalled carbon nanotubes (MWCNTs) were used to decrease the UHMWPE wear. After 400,000 cycles, the UHMWPE-MWCNT diminishes the mass loss compared to UHMWPE, and the combination with TiC decreased the material loss by ~ 43.7 % compared to the reference pair. Cold-flow and burnishing were the predominant wear modes.
△ Less
Submitted 14 October, 2020; v1 submitted 22 September, 2020;
originally announced September 2020.
-
Effect of pre-oxidation treatments on the structural, microstructural, and chemical properties of (Ni,Pt)Al systems
Authors:
J. E. Garcia-Herrera,
D. G. Espinosa-Arbelaez,
L. A. Caceres-Diaz,
G. C. Mondragon-Rodriguez,
H. Ruiz-Luna,
J. Gonzalez-Hernandez,
J. Munoz-Saldana,
J. M. Alvarado-Orozco
Abstract:
The effect of isothermal pre-oxidation treatments on the \b{eta}-(Ni,Pt)Al + René N5 system degradation is here reported. The oxidation treatments were carried out from 900 (mostly θ-Al2O3 growing conditions) to 1200°C (mainly α-Al2O3 growing conditions) for 5 h, under a purified Ar-stream with a fixed pO2= 1 x 10-5 atm. Results are discussed based on the correlation between the structural, micros…
▽ More
The effect of isothermal pre-oxidation treatments on the \b{eta}-(Ni,Pt)Al + René N5 system degradation is here reported. The oxidation treatments were carried out from 900 (mostly θ-Al2O3 growing conditions) to 1200°C (mainly α-Al2O3 growing conditions) for 5 h, under a purified Ar-stream with a fixed pO2= 1 x 10-5 atm. Results are discussed based on the correlation between the structural, microstructural and chemical properties of the \b{eta}-(Ni,Pt)Al BC showing that pre-oxidation parameters have an important effect on the multi-elemental counter diffusion phenomena along BC. For instance, a significant BC+IDZ thickness increase of 55% at 1200 °C was observed with respect to as-received sample just after 5 h of oxidation resulting in a severe BC degradation.
△ Less
Submitted 6 November, 2018;
originally announced November 2018.
-
Effect of Graded Bias Voltage on the Microstructure of arc-PVD CrN Films and its Response in Electrochemical & Mechanical Behavior
Authors:
M. L. Cedeño-Venté,
D. G. Espinosa-Arbeláez,
J. Manríquez-Rocha,
G. C. Mondragón-Rodríguez,
A. E. Gómez-Ovalle,
J. González-Hernández,
J. M. Alvarado-Orozco
Abstract:
The effect of graded or constant bias voltages (-40 V, -80 V and -40/60/80 V) on size grain and surface defects of arc PVD deposited CrN films was investigated. Corrosion resistance evaluated using electrochemical impedance spectroscopy (EIS) and potentiodynamic curves (Tafel) and the mechanical behavior evaluated by means of instrumented nanoindentation and scratch testing was correlated with the…
▽ More
The effect of graded or constant bias voltages (-40 V, -80 V and -40/60/80 V) on size grain and surface defects of arc PVD deposited CrN films was investigated. Corrosion resistance evaluated using electrochemical impedance spectroscopy (EIS) and potentiodynamic curves (Tafel) and the mechanical behavior evaluated by means of instrumented nanoindentation and scratch testing was correlated with the microstructural changes. It was found that the bias voltage variation affects corrosion behavior due to the presence of defects (i.e. open voids, droplets) which also affects the failure mechanisms and increasing spallation. High bias voltage (-80 V) increases nano-hardness and the elastic modulus due to the dense microstructure of the CrN coating.
△ Less
Submitted 16 October, 2018;
originally announced October 2018.
-
Plasma-assisted nitriding of M2 tool steel: An experimental and theoretical approach
Authors:
J. M. Gonzalez-Carmona,
G. C. Mondragon-Rodriguez,
J. E. Galvan-Chaire,
A. E. Gomez-Ovalle,
L. A. Caceres-Diaz,
J. Gonzalez-Hernandez,
J. M. Alvarado-Orozco
Abstract:
Present work was aimed to investigate the effect of nitriding time; 1, 1.5, 2.5 & 3.5 h, on surface characteristics & mechanical properties (surface nano-hardness, hardness Vickers, and adhesion) of AISI M2 tool steel. Mechanically effective compound (4 to 17.6 um) and diffusion layers (50.8 to 82.4 um) were obtained. Plasma nitriding considerably improved Surface engineering has been recognized a…
▽ More
Present work was aimed to investigate the effect of nitriding time; 1, 1.5, 2.5 & 3.5 h, on surface characteristics & mechanical properties (surface nano-hardness, hardness Vickers, and adhesion) of AISI M2 tool steel. Mechanically effective compound (4 to 17.6 um) and diffusion layers (50.8 to 82.4 um) were obtained. Plasma nitriding considerably improved Surface engineering has been recognized as a family of technologies used to modify or improve the surface properties of a substrate. Nano-hardness, E-moduli and resistance to scratch of AISI M2 steel. Surface properties enhancement was associated to two harmonious effects at the nano-scale resulted by (a) stable nitride phases formation such as: gamma-Fe4N, epsilon-Fe2,3N, and (b) no brittle nitride networks and no critical decarburization of the steel upon nitriding. Thermodynamic calculations are in agreement with the experimental findings.
△ Less
Submitted 15 October, 2018;
originally announced October 2018.
-
Theoretical-Experimental failure analysis of the c-Al0.66Ti0.33N-M2 steel system using nanoindentation instrumented and finite element analysis
Authors:
A. E. Gómez-Ovalle,
M. Torres,
J. M. Alvarado-Orozco,
S. M. A. Jimenez,
D. G. Espinosa-Arbelaez,
J. M. Gonzalez-Carmona,
J. Zárate-Medina,
J. González-Hernández,
G. C. Mondragón-Rodríguez
Abstract:
A theoretical-experimental methodology for failure analysis of the c-Al0.66Ti0.33N / Interface / M2 steel coating system is proposed here. This c-Al0.66Ti0.33N coating was deposited by the arc-PVD technique. For coating modeling the traction-separation law and the extended finite element method-XFEM were applied, the cohesive zones model was used for interface modeling and the Ramberg-Osgood law f…
▽ More
A theoretical-experimental methodology for failure analysis of the c-Al0.66Ti0.33N / Interface / M2 steel coating system is proposed here. This c-Al0.66Ti0.33N coating was deposited by the arc-PVD technique. For coating modeling the traction-separation law and the extended finite element method-XFEM were applied, the cohesive zones model was used for interface modeling and the Ramberg-Osgood law for substrate modeling. Experimental values using the instrumented nanoindentation technique, the scratch test and tensile stress test were obtained and introduced into the model. By means of nanoindentation the elastic modulus of coating, the fracture energy release rate and the nano-hardness. Normal and shear stress values of the interface were obtained with the scratch test, at the adhesive and cohesive critical loads. Vickers indentation was used to generate cracking patterns in the c-Al0.66Ti0.33N / Interface / M2 steel coating system. Radial and lateral cracks were generated and analyzed after transversal FIB cuts of the fracture zones. A finite element analysis was carried out to understand the relationship between the load-displacement curve and mechanical failure of in the system, associating the pop-in with nucleation, crack growth and cracking pattern. This works present a theoretical-experimental methodology for failure analysis of hard coatings (monolithic body) allowing to calculate fracture toughness of the coating material and model cracking patterns caused by contact mechanics.
△ Less
Submitted 13 October, 2018;
originally announced October 2018.
-
Diamond-Like Carbon Coatings on Plasma Nitrided M2 Steel: effect of deposition parameters on adhesion properties
Authors:
A. Moreno-Barcenas,
J. M Alvarado-Orozco,
J. M. Gonzalez Carmona,
G. C. Mondragon-Rodriguez,
J. Gonzalez-Hernandez,
A. Garcia-Garcia
Abstract:
Diamond-like carbon (DLC) coatings have excellent mechanical and tribological properties, as well as good wear and corrosion resistance. They are well established in medical, metalworking and automotive applications. However, further improvements are needed and substrate pre-treatment plays an important role in supporting and enforcing the adhesion and service performance of the DLC coatings. In t…
▽ More
Diamond-like carbon (DLC) coatings have excellent mechanical and tribological properties, as well as good wear and corrosion resistance. They are well established in medical, metalworking and automotive applications. However, further improvements are needed and substrate pre-treatment plays an important role in supporting and enforcing the adhesion and service performance of the DLC coatings. In this work, the synergetic effect of low-pressure arc plasma-assisted-nitriding (PAN) treatment of M2 steel and plasma-enhanced chemical vapor deposition (PECVD) on the DLC coatings adhesion was analyzed. Adhesion strength of a duplex DLC + nitriding coating system was compared to the performance of DLC-coatings applied on non-nitrided M2 steel substrates. The nitrided layer was analyzed by optical microscopy, X-ray diffraction, Vickers microhardness and atomic force microscopy. DLC coatings were analyzed using Raman spectroscopy revealing that DLC a-C:H type was obtained. The adhesion properties were analyzed by scratch testing supported by optical microscopy and Scanning Electron Microscope. Results showed an improvement of the DLC adhesion on the plasma nitrided surfaces.
△ Less
Submitted 12 October, 2018;
originally announced October 2018.