Effect of Electrical Properties on Gd modified BiFeO3-PbZrO3
Authors:
S. K. Satpathy,
N. K. Mohanty,
A. K Behera,
K. C. Patra,
B. Behera,
P. Nayak
Abstract:
The 0.5(BiGdxFe1-xO3)-0.5(PbZrO3) composite was synthesized using a high temperature solid-state reaction technique. Preliminary X-ray structural analysis confirms the formation of the composite. The dielectric constant and loss tangent have been studied. The hysteresis loop suggest that the material is lossy. The impedance parameters were studied using an impedance analyzer in a wide range of fre…
▽ More
The 0.5(BiGdxFe1-xO3)-0.5(PbZrO3) composite was synthesized using a high temperature solid-state reaction technique. Preliminary X-ray structural analysis confirms the formation of the composite. The dielectric constant and loss tangent have been studied. The hysteresis loop suggest that the material is lossy. The impedance parameters were studied using an impedance analyzer in a wide range of frequency (102-106 Hz) at different temperatures for all samples. The Nyquist plot suggests the contribution of bulk effect as well as grain boundary effect and the bulk resistance deceases with rise in temperature for all samples. The electrical transport confirms the presence of hop** mechanism in the material. The dc conductivity increases with rise in temperature. The frequency variation of ac conductivity shows that the compound obeys Jonschers universal power law and confirms the Small Polaron (SP) tunneling effect due to low activation energy for all samples. Temperature dependence of dc and ac conductivity indicates that electrical conduction in the materials are thermally activated process.
△ Less
Submitted 1 May, 2014;
originally announced May 2014.
-
Investigation of Complex Impedance and Modulus Properties of Nd Doped 0.5BiFeO3-0.5PbTiO3 Multiferroic Composites
Authors:
Ajay Kumar Behera,
N. K. Mohanty,
S. K. Satpathy,
Banarji Behera,
P. Nayak
Abstract:
0.5BiNdxFe1-xO3-0.5PbTiO3 (x=0.05, 0.10, 0.15, 0.20) composites were successfully synthesized by a solid state reaction technique. At room temperature X-ray diffraction shows tetragonal structure for all concentrations of Nd doped 0.5BiFeO3-0.5PbTiO3 composites. The nature of Nyquist plot confirms the presence of bulk effects only for all compositions of Nd-doped 0.5BiFeO3-0.5PbTiO3 composites. Th…
▽ More
0.5BiNdxFe1-xO3-0.5PbTiO3 (x=0.05, 0.10, 0.15, 0.20) composites were successfully synthesized by a solid state reaction technique. At room temperature X-ray diffraction shows tetragonal structure for all concentrations of Nd doped 0.5BiFeO3-0.5PbTiO3 composites. The nature of Nyquist plot confirms the presence of bulk effects only for all compositions of Nd-doped 0.5BiFeO3-0.5PbTiO3 composites. The bulk resistance is found to decreases with the increasing in temperature as well as Nd concentration and exhibits a typical negative temperature coefficient of resistance (NTCR) behavior. Both the complex impedance and modulus studies have suggested the presence of non-Debye type of relaxation in the materials. Conductivity spectra reveal the presence of hop** mechanism in the electrical transport process of the materials. The activation energy of the composite increases with increasing Nd concentration and were found to be 0.28, 0.27, 0.31 and 0.32eV for x=0.05, 0.10, 0.15, 0.20 respectively at 200-275 oC for conduction process.
△ Less
Submitted 31 March, 2014;
originally announced March 2014.