The mechanism of twin thickening and the elastic strain state of TWIP steel nanotwins
Authors:
T W J Kwok,
T P McAuliffe,
A K Ackerman,
B H Savitzky,
M Danaie,
C Ophus,
D Dye
Abstract:
A Twinning Induced Plasticity (TWIP) steel with a nominal composition of Fe-16.4Mn-0.9C-0.5Si-0.05Nb-0.05V was deformed to an engineering strain of 6\%. The strain around the deformation twins were mapped using the 4D-STEM technique. Strain map** showed a large average elastic strain of approximately 6\% in the directions parallel and perpendicular to the twinning direction. However, the large a…
▽ More
A Twinning Induced Plasticity (TWIP) steel with a nominal composition of Fe-16.4Mn-0.9C-0.5Si-0.05Nb-0.05V was deformed to an engineering strain of 6\%. The strain around the deformation twins were mapped using the 4D-STEM technique. Strain map** showed a large average elastic strain of approximately 6\% in the directions parallel and perpendicular to the twinning direction. However, the large average strain comprised of several hot spots of even larger strains of up to 12\%. These hot spots could be attributed to a high density of sessile Frank dislocations on the twin boundary and correspond to shear stresses of 1--1.5 GPa. The strain and therefore stress fields are significantly larger than other materials known to twin and are speculated to be responsible for the early thickness saturation of TWIP steel nanotwins. The ability to keep twins extremely thin helps improve grain fragmentation, \textit{i.e.} the dynamic Hall-Petch effect, and underpins the large elongations and strain hardening rates in TWIP steels.
△ Less
Submitted 30 September, 2022;
originally announced September 2022.
-
The influence of alloying on slip intermittency and the implications for dwell fatigue in titanium
Authors:
Felicity F. Worsnop,
Rachel E. Lim,
Joel V. Bernier,
Darren C. Pagan,
Yilun Xu,
Thomas P. McAuliffe,
David Rugg,
David Dye
Abstract:
Dwell fatigue, the reduction in fatigue life experienced by titanium alloys due to holds at stresses as low as 60% of yield, has been implicated in several uncontained jet engine failures. Dislocation slip has long been observed to be an intermittent, scale-bridging phenomenon, similar to that seen in earthquakes but at the nanoscale, leading to the speculation that large stress bursts might promo…
▽ More
Dwell fatigue, the reduction in fatigue life experienced by titanium alloys due to holds at stresses as low as 60% of yield, has been implicated in several uncontained jet engine failures. Dislocation slip has long been observed to be an intermittent, scale-bridging phenomenon, similar to that seen in earthquakes but at the nanoscale, leading to the speculation that large stress bursts might promote the initial opening of a crack. Here we observe such stress bursts at the scale of individual grains in situ, using high energy X-ray diffraction microscopy in Ti-7Al-O alloys. This shows that the detrimental effect of precipitation of ordered Ti_3Al is to increase the magnitude of rare pri<a> and bas<a> slip bursts associated with slip localisation. In contrast, the addition of trace O interstitials is beneficial, reducing the magnitude of bas<a> slip bursts and increasing the homogeneity between basal and prismatic <a> slip. This is further evidence that the formation of long paths for easy basal plane slip localisation should be avoided when engineering titanium alloys against dwell fatigue.
△ Less
Submitted 1 August, 2022; v1 submitted 28 March, 2022;
originally announced March 2022.
-
Quantitative precipitate classification and grain boundary property control in Co/Ni-base superalloys
Authors:
Thomas P McAuliffe,
Ioannis Bantounas,
Lucy R Reynolds,
Alex Foden,
Mark Hardy,
T Ben Britton,
David Dye
Abstract:
A correlative approach is employed to simultaneously assess structure and chemistry of (carbide and boride) precipitates in a set of novel Co/Ni-base superalloys. Structure is derived from electron backscatter diffraction (EBSD) with pattern template matching, and chemistry obtained with energy dispersive X-ray spectroscopy (EDS). It is found that the principal carbide in these alloys is Mo and W…
▽ More
A correlative approach is employed to simultaneously assess structure and chemistry of (carbide and boride) precipitates in a set of novel Co/Ni-base superalloys. Structure is derived from electron backscatter diffraction (EBSD) with pattern template matching, and chemistry obtained with energy dispersive X-ray spectroscopy (EDS). It is found that the principal carbide in these alloys is Mo and W rich with the M6C structure. An M2B boride, also exhibiting Mo and W segregation is observed at B levels above approximately 0.085 at.%. These phases are challenging to distinguish in an SEM with chemical information (EDS or backscatter Z-contrast) alone, without the structural information provided by EBSD. Only correlative chemical and structural fingerprinting is necessary and sufficient to fully define a phase. The identified phases are dissimilar to those predicted using ThermoCalc. We additionally perform an assessment of the grain boundary serratability in these alloys, and observe that significant amplitude is only obtained in the absence of pinning intergranular precipitates.
△ Less
Submitted 2 September, 2020;
originally announced September 2020.
-
Spherical-angular dark field imaging and sensitive microstructural phase clustering with unsupervised machine learning
Authors:
Thomas P McAuliffe,
David Dye,
T Ben Britton
Abstract:
Electron backscatter diffraction is a widely used technique for nano- to micro-scale analysis of crystal structure and orientation. Backscatter patterns produced by an alloy solid solution matrix and its ordered superlattice exhibit only extremely subtle differences, due to the inelastic scattering that precedes coherent diffraction. We show that unsupervised machine learning (with PCA, NMF, and a…
▽ More
Electron backscatter diffraction is a widely used technique for nano- to micro-scale analysis of crystal structure and orientation. Backscatter patterns produced by an alloy solid solution matrix and its ordered superlattice exhibit only extremely subtle differences, due to the inelastic scattering that precedes coherent diffraction. We show that unsupervised machine learning (with PCA, NMF, and an autoencoder neural network) is well suited to fine feature extraction and superlattice/matrix classification. Remap** cluster average patterns onto the diffraction sphere lets us compare Kikuchi band profiles to dynamical simulations, confirm the superlattice stoichiometry, and facilitate virtual imaging with a spherical solid angle aperture. This pipeline now enables unparalleled map** of exquisite crystallographic detail from a wide range of materials within the scanning electron microscope.
△ Less
Submitted 12 October, 2020; v1 submitted 21 May, 2020;
originally announced May 2020.
-
4D-STEM elastic stress state characterisation of a TWIP steel nanotwin
Authors:
T P McAuliffe,
A K Ackerman,
B H Savitzky,
T W J Kwok,
M Danaie,
C Ophus,
D Dye
Abstract:
We measure the stress state in and around a deformation nanotwin in a twinning-induced plasticity (TWIP) steel. Using four-dimensional scanning transmission electron microscopy (4D-STEM), we measure the elastic strain field in a 68.2-by-83.1 nm area of interest with a scan step of 0.36 nm and a diffraction limit resolution of 0.73 nm. The stress field in and surrounding the twin matches the form e…
▽ More
We measure the stress state in and around a deformation nanotwin in a twinning-induced plasticity (TWIP) steel. Using four-dimensional scanning transmission electron microscopy (4D-STEM), we measure the elastic strain field in a 68.2-by-83.1 nm area of interest with a scan step of 0.36 nm and a diffraction limit resolution of 0.73 nm. The stress field in and surrounding the twin matches the form expected from analytical theory and is on the order of 15 GPa, close to the theoretical strength of the material. We infer that the measured back-stress limits twin thickening, providing a rationale for why TWIP steel twins remain thin during deformation, continuously dividing grains to give substantial work hardening. Our results support modern mechanistic understanding of the influence of twinning on crack propagation and embrittlement in TWIP steels.
△ Less
Submitted 20 October, 2020; v1 submitted 8 April, 2020;
originally announced April 2020.
-
Advancing characterisation with statistics from correlative electron diffraction and X-ray spectroscopy, in the scanning electron microscope
Authors:
T. P. McAuliffe,
A. Foden,
C. Bilsland,
D. Daskalaki-Mountanou,
D. Dye,
T. B. Britton
Abstract:
The routine and unique determination of minor phases in microstructures is critical to materials science. In metallurgy alone, applications include alloy and process development and the understanding of degradation in service. We develop a correlative method, exploring superalloy microstructures which are examined in the scanning electron microscope (SEM) using simultaneous energy dispersive X-ray…
▽ More
The routine and unique determination of minor phases in microstructures is critical to materials science. In metallurgy alone, applications include alloy and process development and the understanding of degradation in service. We develop a correlative method, exploring superalloy microstructures which are examined in the scanning electron microscope (SEM) using simultaneous energy dispersive X-ray spectroscopy (EDS) and electron backscatter diffraction (EBSD). This is performed at an appropriate length scale for characterisation of carbide phases' shape, size, location, and distribution. EDS and EBSD data are generated using two different physical processes, but each provide a signature of the material interacting with the incoming electron beam. Recent advances in post-processing, driven by "big data" approaches, include use of principal component analysis (PCA). Components are subsequently characterised to assign labels to a mapped region. To provide physically meaningful signals, the principal components may be rotated to control the distribution of variance. In this work, we develop this method further through a weighted PCA approach. We use the EDS and EBSD signals concurrently, thereby labelling each region using both EDS (chemistry) and EBSD (crystal structure) information. This provides a new method of amplifying signal-to-noise for very small phases in mapped regions, especially where the EDS or EBSD signal is not unique enough alone for classification.
△ Less
Submitted 14 January, 2020; v1 submitted 12 August, 2019;
originally announced August 2019.